Estudo de inibidores de corrosão em concreto armado, visando a melhoria na sua durabilidade

This thesis has as objective presents a methodology to evaluate the behavior of the corrosion inhibitors sodium nitrite, sodium dichromate and sodium molybdate, as well as your mixture, the corrosion process for the built-in steel in the reinforced concrete, through different techniques electrochemical, as well as the mechanical properties of that concrete non conventional. The addition of the inhibitors was studied in the concrete in the proportions from 0.5 to 3.5 % regarding the cement mass, isolated or in the mixture, with concrete mixture proportions of 1.0:1.5:2.5 (cement, fine aggregate and coarse aggregate), superplasticizers 2.0 % and 0.40 water/cement ratio. In the modified concrete resistance rehearsals they were accomplished to the compression, consistence and the absorption of water, while to analyze the built-in steel in the concrete the rehearsals of polarization curves they were made. They were also execute, rehearsals of corrosion potential and polarization resistance with intention of diagnose the beginning of the corrosion of the armors inserted in body-of-proof submitted to an accelerated exhibition in immersion cycle and drying to the air. It was concluded, that among the studied inhibitors sodium nitrite , in the proportion of 2.0 % in relation to the mass of the cement, presented the best capacity of protection of the steel through all the studied techniques and that the methodology and the monitoring techniques used in this work, they were shown appropriate to evaluate the behavior and the efficiency of the inhibitors

Estudo de inibidores de corrosão em concreto armado, visando a melhoria na sua durabilidade

This thesis has as objective presents a methodology to evaluate the behavior of the corrosion inhibitors sodium nitrite, sodium dichromate and sodium molybdate, as well as your mixture, the corrosion process for the built-in steel in the reinforced concrete, through different techniques electrochemical, as well as the mechanical properties of that concrete non conventional. The addition of the inhibitors was studied in the concrete in the proportions from 0.5 to 3.5 % regarding the cement mass, isolated or in the mixture, with concrete mixture proportions of 1.0:1.5:2.5 (cement, fine aggregate and coarse aggregate), superplasticizers 2.0 % and 0.40 water/cement ratio. In the modified concrete resistance rehearsals they were accomplished to the compression, consistence and the absorption of water, while to analyze the built-in steel in the concrete the rehearsals of polarization curves they were made. They were also execute, rehearsals of corrosion potential and polarization resistance with intention of diagnose the beginning of the corrosion of the armors inserted in body-of-proof submitted to an accelerated exhibition in immersion cycle and drying to the air. It was concluded, that among the studied inhibitors sodium nitrite , in the proportion of 2.0 % in relation to the mass of the cement, presented the best capacity of protection of the steel through all the studied techniques and that the methodology and the monitoring techniques used in this work, they were shown appropriate to evaluate the behavior and the efficiency of the inhibitors

Qualidade fisiológica de sementes de milho tratadas com molibdênio

O tratamento de sementes com micronutrientes, como o molibdênio, garante uma maior uniformidade de aplicação, sendo que, a quantidade a ser aplicada desse elemento nas sementes deve ser suficiente para provir à exigência para o desenvolvimento e produção da cultura. Assim, objetivou-se com o presente trabalho avaliar a qualidade fisiológica de sementes de milho tratadas com molibdênio. A qualidade das sementes foi avaliada por meio da determinação do teor de água, do teste de germinação, da primeira contagem de germinação e da emissão de raízes primárias. Os tratamentos testados consistiram de cinco híbridos (DOW CO32; DOW 2B587; DOW 2B688; PIONEER 30F35 e PIONEER 30K73) e cinco doses de molibdênio aplicadas via semente (0; 7,5; 22,5; 67,5; 202,5 g ha-1 de molibdênio). A fonte de molibdênio utilizada foi o molibdato de sódio dihidratado (39% de molibdênio), sendo que a aplicação do molibdênio foi efetuada por meio da mistura com o fungicida líquido de suspensão concentrada carboxina+thiram sobre as sementes. A qualidade fisiológica das sementes de milho é influenciada negativamente por doses crescentes de molibdênio aplicadas. O híbrido de milho DOW 2B587 obteve melhor resposta à aplicação da maior dose de molibdênio em relação aos demais híbridos estudados.

Efeito da aplicação foliar de boro e zinco sobre a produção e os teores de SST e ATT dos frutos da Pereira-Japonesa e da pinheira

Pulverizações foliares com produtos contendo micronutrientes, dentre os quais os produtos quelatizados, são utilizadas com relativa freqüência em frutíferas, sem o embasamento científico adequado, principalmente entre os agricultores mais tecnificados. Neste contexto, o objetivo deste trabalho foi verificar o efeito da aplicação via foliar de B e Zn sobre a produção e os teores de SST e ATT dos frutos da Pereira-Japonesa e da Pinheira. O experimento foi conduzido numa área irrigada, situada no cinturão verde do município de Ilha Solteira-SP. O solo da área foi classificado como Podzólico Vermelho-Escuro. Foram utilizadas plantas de Pereira-Japonesa, cultivar Okussankichi e de Pinheira. Os tratamentos utilizados foram: T1. apenas água; T2. ácido bórico; T3. sulfato de zinco; T4. T2 + T3; T5. ácido bórico + uréia + ácido cítrico + EDTA; T6. sulfato de zinco + uréia + ácido cítrico + EDTA; T7. T5 + T6; T8. ácido bórico + uréia + ácido cítrico + EDTA + molibdato de sódio + enxofre + cloreto de cálcio; T9. sulfato de zinco + ácido cítrico + EDTA + sulfato de Fe + sulfato de Mn + sulfato de Mg, e T10. T8+T9. Foram utilizadas doses de 110 g ha-1 de B e 250 g ha-1 de Zn, em cada aplicação. O delineamento experimental adotado foi o de blocos ao acaso, com quatro repetições e, para comparação de médias, foi utilizado o teste de Tukey. Com base nos resultados obtidos, pode-se concluir que: 1) a produção e os teores de SST e ATT dos frutos da pereira-japonesa e da pinheira não foram influenciados pela aplicação foliar de B e de Zn; b) a mistura de ácido bórico com quelatos foi eficiente no fornecimento de B às plantas de pereira- japonesa, o mesmo não ocorrendo para pinheira, c) o sulfato de zinco + produtos quelatizantes foram eficientes no aumento dos teores foliares de Zn somente na pereira.

Fertilizantes foliares em culturas perenes: pereira japonesa (Pyrus pyrifolia var. Culta), pinheira (Annona squamosa L.) e videira (Vitis labrusca L.)

Pós-graduação em Agronomia - FEIS

Estudo de metodologias de controle de qualidade do Mo-99 utilizado no preparo de geradores de Mo-99/Tc-99m

O 99mTc é o radionuclídeo mais utilizado em medicina nuclear. No Brasil os geradores de 99Mo/99mTc são produzidos exclusivamente pelo Centro de Radiofarmácia do IPEN-CNEN/SP, com 99Mo importado de diferentes fornecedores. O 99Mo (t1/2 = 66 h), por ser um produto de fissão do 235U, pode conter impurezas radionuclídicas prejudiciais à saúde humana. Dessa forma, para que o gerador seja utilizado de forma segura, é necessário que o 99Mo seja avaliado por ensaios de controle de qualidade e atenda à alguma especificação descrita em farmacopeia. A Farmacopeia Europeia (FE) apresenta monografia, com parâmetros (identificação, pureza radioquímica e pureza radionuclídica), métodos de análise, e limites, para avaliação da qualidade da solução de [99Mo] na forma de molibdato de sódio, que é utilizada como matéria-prima no preparo dos geradores de 99Mo/99mTc. No entanto, observa-se uma dificuldade na implementação e execução dos métodos por parte dos produtores de geradores, com pouca literatura sobre o assunto, provavelmente devido à falta de praticidade dos métodos propostos e à extensa lista de reagentes utilizados. Nesse trabalho foram avaliados vários parâmetros de qualidade do 99Mo descritos na monografia da FE. Foram estudados métodos de separação do 99Mo de suas impurezas radionuclídicas por extração em fase sólida (SPE) e por TLC. Após separação por SPE, foi proposta a quantificação de metais por ICP-OES para avaliar a porcentagem de retenção de Mo e a porcentagem de recuperação de Ru e Te e Sr em diversos tipos de cartuchos, em substituição ao uso de radiotraçadores. Observou-se que a marca de cartucho de SPE para separação do 99Mo recomendada pela FE apresentou baixa recuperação para Ru, quando comparado aos outros cartuchos de troca aniônica disponíveis no mercado. Amostras de 99Mo de diferentes fornecedores mundiais foram analisadas. Observou-se que é possível realizar a quantificação de 103Ru em amostras de 99Mo mesmo com tempos de decaimento acima de 4 semanas. Um método alternativo de separação do 99Mo do 131I por TLC apresentou resultados promissores. Não foi feita a quantificação das impurezas radionuclídicas emissoras beta e alfa. Todas as amostras analisadas apresentaram resultados dentro das especificações da FE para pureza radioquímica (>95%) e pureza radionuclídica.

Aplicação foliar de molibdênio em adubos verdes e o desempenho do feijoeiro em sucessão

The knowledge of molybdenum application in legumes on the availability of N, by BNF, increased enzymatic activity and the residual effect caused on crops growth and yield can contribute to the greater scientific understanding involved in green manure processes. The aim of this study was to evaluate the Mo application and the N from Crotalaria juncea and Canavalia ensiformis green manures on common bean performance. Were conducted field experiments for the crops succession system (green manures - common bean) and laboratory essays for the enzymatic activities. Green manure production was installed in a factorial arrangement 2 x 4, with two green manure legumes species, sunnhemp (Crotalaria juncea) and jack beans (Canavalia ensiformis), and four Mo doses (0, 40, 80, 120 g ha-1) in the form of sodium molybdate (Na2MoO4), foliar applied, in a randomized block design with four replicates. For succession crop (common bean) additional treatment was added, beans grown without any fertilization, following the same experimental design from the previous crop. The dry matter decomposition and the N mineralization of green manure were monitored through collection of residues over time, by using the litter bags method. In laboratory were carried out tests of nitrate reductase activity in green manures and common beans at 90 and 66 days after sowing, respectively. The sunnhemp responded linearly positively to the application of Mo as the dry matter and N accumulation. While the jack beans presented a negative quadratic response for dry matter and there was no adjustment of regression models to N. The jack beans showed a higher decomposition rate and N mineralization compared to sunnhemp. The half lives for decomposing 50% of dry matter on the soil was 123 and 104 days to sunnhemp and jack beans, respectively, and 50% of N present in the residues was mineralized at 93 and 85 days. In common bean, differed from the control for number of pods the dose of 40 g ha-1 of Mo in both species of green manures and the dose 80 g ha-1 of Mo in jack beans. For number of grains only in sunnhemp on the dose of 40 g ha-1 of Mo differ from the control. The nitrate reductase activity was influenced by developmental stage of green manure species. In common bean, the activity of nitrate reductase was up to three times higher than the dose 0 g ha-1 of Mo compared to treatment with application of Mo in both species. There was no effect of Mo doses or species of green manure on common bean yield.

Fixação de complexo de ferro II em matriz de poli(acrilato de sódio)

Neste trabalho estudou-se a complexação do poli(acrilato de sódio), PAS, com aminpentacianoferrato de sódio,APCF. As reações de complexação ocorreram imediatamente com a formação de uma coloração amarela com total solubilização do polímero na solução 0,032 M molar do complexo. As soluções mostraram-se estáveis por 48 h e após esse período observou-se alterações na natureza do complexo polimérico com a formação de precipitado. O UV foi usado como ferramenta de caracterização do complexo. O máximo de absorção obtido após dissolução imediata foi de 405 nm com desvio para o azul (398 nm) e um pequeno efeito hipercrômico. As amostras mantidas à temperatura ambiente por mais de 48 h deram origem a precipitados, que como a solução, absorveram com máximo de 364, 389 e 398 nm. O Complexo PAS-APCF foi também caracterizado através de FTIR por ATR e apresentou pequenas variações no espectro do material de partida (PAS). Um incremento na intensidade da deformação axial assimétrica do grupo carboxilato (1651 cm-1) e a presença do estiramento em 2055 cm-1 do grupo cianeto, diferentemente do APCF (2048 cm-1), confirmaram a formação do complexo PAS-APCF. As freqüências de absorção observadas para o complexo foram compatíveis com a presença de estruturas mono e bidentadas de complexação. As análises de TGA e DSC também foram utilizadas para a caracterização das estruturas. O estudo modelo envolvendo a complexação de sais sódicos de diácidos orgânicos de diferentes tamanhos de cadeia (oxalato, malonato, succinato, glutarato e adipato), diferentemente do PAS, promoveu um desvio para o vermelho na frequência máxima de absorção junto de um pequeno efeito hipercrômico (421 nm). Esta variação pode também ser observada quando do emprego de acetato de sódio, indicando, provavelmente, apenas a formação de estruturas monodentadas

Estudo de Eletrodeposição de Ligas Cu-Sn em Meio de Citrato de Sódio

Revestimentos produzidos a partir de ligas de Cu-Sn apresentam grande interesse em função de suas propriedades, originando uma grande capacidade de aplicação industrial, especialmente em indústrias de componentes e materiais eletrônicos. Tais ligas também têm sido comercialmente utilizadas como revestimentos em metais diferentes, como o aço, para protegê-los contra a corrosão e melhorar sua aparência. Na presente dissertação, técnicas de voltametria cíclica, cronoamperometria e voltametria de varredura anódica linear foram utilizadas para o estudo dos processos de deposição de Cu e/ou Sn a partir de dois conjuntos de soluções contendo CuCl2.2H2O e SnCl2.2H2O nas razões de Cu:Sn = 1:10 e 10:1, além de Na3C6H5O7 1,00 mol/L, em pH = 6,0. As curvas de voltametria cíclica realizadas sobre o eletrodo de grafita foram utilizadas para o cálculo das constantes de equilíbrio dos complexos de ambos os metais com citrato de sódio, bem como na determinação dos potenciais catódicos aplicados nos ensaios de cronoamperometria. Após a deposição da liga nos potenciais estipulados para cada uma das duas soluções, os revestimentos de liga Cu-Sn foram ressolubilizados em solução de NaNO3 0,5 mol/L, empregando varredura anódica linear para a avaliação de suas composições químicas. Os resultados iniciais mostraram que a variação da concentração de Cu (II) e do potencial aplicado influenciaram no teor de cobre na liga. Contudo, percebeu-se que o teor de estanho não sofreu grandes variações, independente das concentrações das soluções e do potencial aplicado. Na solução com maior concentração de cobre foram alcançados teores dos metais na liga em maior proximidade com o da liga de bronze comercial. Com base nesses resultados, foram produzidos revestimentos de ligas sobre substrato de aço carbono, a partir de soluções contendo CuCl2.2H2O e SnCl2.2H2O na razão de 10:1, empregando a técnica de cronoamperometria potenciostática. Quatro diferentes valores de potencial (-0,39V, -0,67V, -1,00V, -1,20V e -1,94V vs. Ag/AgClsat.) foram aplicados, obtendo-se camadas cujas colorações variaram do rosa claro ao marrom escuro, sempre sem brilho. A eficiência de corrente catódica (Ef) decresceu conforme o potencial aplicado se tornou mais negativo. Nesta mesma direção, verificou-se um aumento do teor de estanho na liga depositada e menores tamanhos de grão. Porém, quando o potencial tornou-se mais negativo (-1,20V e -1,94V), observou-se a presença de cristalitos de diferentes tamanhos e de dendritos. Revestimentos com melhores resistências à corrosão em solução de NaCl 0,5 mol/L foram produzidos nos potenciais de -1,00V e -1,20V, cujas composições foram 99,40 % m/m Cu / 0,60 % m/m Sn e 97,70 % m/m Cu / 2,30 % m/m Sn, respectivamente. As análises por DRX permitiram verificar que estes revestimentos eram constituídos, principalmente, da fase α-CuSn

Efeito do silicato de sódio em sorgo-sacarino.

2015

Inibidores do co-transportador renal de sódio-glicose 2

Projeto de Pós-Graduação/Dissertação apresentado à Universidade Fernando Pessoa como parte dos requisitos para obtenção do grau de Mestre em Ciências Farmacêuticas

Estudo da substituição parcial do cloreto de sódio por cloreto de potássio em presunto

Dissertação para obtenção do grau de mestre em Sistemas de Prevenção e Controlo Alimentar, Escola Superior Agrária do Instituto Politécnico de Santarém, 2011

Azeitona de mesa natural da cultivar Maçanilha com baixo teor de cloreto de sódio

Dissertação de mestrado, Tecnologia dos Alimentos, Instituto Superior de Engenharia, Universidade do Algarve, 2014

Análise do efeito de implementação de armazenamento térmico em banco de gelo e armazenamento elétrico em baterias Sódio-Enxofre (NaS) sobre o custo de exploração de edifícios de serviços

Trabalho Final de Mestrado para obtenção do grau de Mestre em Engenharia Mecânica

Conservantes em Formulações de Cloreto de Sódio 0,9% para Aplicação Tópica em Pediatria

As formulações de cloreto de sódio 0,9%, são na sua grande maioria utilizadas com bastante frequência sobretudo na população pediátrica. Tanto os cuidadores como os próprios profissionais de saúde as reconhecem e avaliam como um componente essencial para os cuidados de saúde desta população. No entanto, o grave problema destas formulações reside no facto de muitos dos consumidores após a sua utilização apresentarem reacções adversas, que não são justificáveis se apenas da composição da formulação fizerem parte água purificada e cloreto de sódio. Assim deve ser tida em conta a composição de cada apresentação farmacêutica, a fim de se averiguar quanto à presença de conservantes potencialmente perigosos e para deste modo alertar os possíveis consumidores destes produtos. O principal objectivo deste estudo foi a análise e avaliação da rotulagem e folheto de instruções das formulações de cloreto de sódio 0,9% para aplicação tópica em pediatria, a fim de se averiguar a utilização de conservantes na sua formulação e por conseguinte a sua conformidade para comercialização. Com o auxílio de uma check-list, foram avaliadas 34 apresentações de venda livre de formulações de cloreto de sódio 0,9% para aplicação tópica, no período de Janeiro a Março de 2014. Das 34 apresentações farmacêuticas analisadas, apenas uma dasapresentações não se encontrava descrita como dispositivo médico, mas sim como produto cosmético. Contudo quanto à marcação CE de conformidade, esta encontrava-se devidamente aposta em 94% das apresentações. No que às indicações terapêuticas diz respeito e como seria expectável, na sua maioria estas apresentações destinam-se em 51% dos casos para utilização nasal e em 33% dos casos para utilização oftálmica, sendo o modo de apresentação em gotas (88%) o mais encontrado para comercialização. Quanto à utilização de conservantes, constatou-se uma grande omissão e alguma imprecisão quanto às informações contidas na rotulagem e/ou folheto de instruções das formulações analisadas, expondo assim os indivíduos mais susceptíveis e em especial a população pediátrica ao risco de reacções adversas e que por vezes podem ser fatais. Por outro lado também podem ocorrer complicações aquando do uso inadvertido destasformulações com conservantes, por portadores de lentes de contacto ou sem a devida esterilidade para utilização oftálmica. Assim apesar de o soro fisiológico não ser considerado um medicamento, mas sim um dispositivo médico, deve ser contudo utilizado com algumas precauções, sobretudo nesta população pediátrica e sempre que possível aconselhado por um profissional treinado e consciente da problemática que os conservantes usados nestas formulações podem causar quando utilizados indevidamente.