Resumo:

We report the device performance of normal-incidence (In, Ga)As/GaAs quantum dot intersubband infrared photodetectors. A primary intersubband transition peak is observed at the wavelength of 13 mu m (E-0 --> E-1) and a secondary peak at 11 mu m (E-0 --> E-2). The measured energy spacing in the conduction band of the quantum dots is in good agreement with low temperature photoluminescence measurement and calculations. A peak detectivity of 1 x 10(10) cm Hz(1/2)/W at 13 mu m was achieved at 40 K for these devices. (C) 1998 American Institute of Physics. [S0003-6951(98)01440-5].

Relevância:

100.00% 100.00%

Publicador:

Resumo:

InAs/GaAs1−xSbx Quantum Dot (QD) infrared photodetectors are analyzed by photocurrent spectroscopy. We observe that the integrated responsivity of the devices is improved with the increasing Sb mole fraction in the capping layer, up to 4.2 times for x = 17%. Since the QD layers are not vertically aligned, the vertical transport of the carriers photogenerated within the QDs takes place mainly through the bulk material and the wetting layer of the additional QD regions. The lower thickness of the wetting layer for high Sb contents results in a reduced capture probability of the photocarriers, thus increasing the photoconductive gain and hence, the responsivity of the device. The growth of not vertically aligned consecutive QD layers with a thinner wetting layer opens a possibility to improve the performance of quantum dot infrared photodetectors.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

The dark current characteristics and temperature dependence for quantum dot infrared photodetectors have been investigated by comparing the dark current activation energies between two samples with identical structure of the dots-in-well in nanoscale but different microscale n-i-n environments. A sequential coupling transport mechanism for the dark current between the nanoscale and the microscale processes is proposed. The dark current is determined by the additive mode of two activation energies: E-a,E-micro from the built-in potential in the microscale and E-a,E-nano related to the thermally assisted tunneling in nanoscale. The activation energies E-a,E-micro and E-a,E-nano decrease exponentially and linearly with increasing applied electric field, respectively.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

Quantum dot infrared photodetectors (QDIPs) are very attractive for many applications such as infrared imaging, remote sensing and gas sensing, thanks to its promising features such as high temperature operation, normal incidence response and low dark current [1]. However, the key issue is to obtain a high-quality active region which requires an optimization of the nanostructure. By using GaAsSb capping layer, InAs QDs have improved their optical emission in the range between 1.15 and 1.3 m (at Sb composition of 14 %), due to a reduction of a compressive strain in QD and an increment of a QD height [2]. In this work, we have demonstrated strong and narrow intraband photoresponses at ~ 5 m from GaAsSb-capped InAs/GaAs QDIPs under normal light-incidence.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

The use of reduced graphene oxide (RGO) and graphene nanoribbons (GNRs) as infrared photodetectors is explored, based on recent results dealing with solar cells, light-emitting devices, photodetectors, and ultrafast lasers. IR detection is demonstrated by both RGO and GNRs (see image) in terms of the time-resolved photocurrent and photoresponse. The responsivity of the detectors and their functioning are presented.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

We report a bias voltage tunable two-color InAs/GaAs quantum dot infrared photodetector working under the normal incidence infared irradiation. The two-color detection of our device is realized by combining a photovoltaic and a photoconductive response by bias voltage tuning. The photovoltaic response is attributed to the transition of electron from the ground state to a high continuum state. The photoconductive response arises from the transition of electron from the ground state to the wetting layer state through the barrier via Fowler-Nordheim tunneling evidenced by a broad feature of the photocurrent peak on the high energy side. (C) 2008 American Institute of Physics.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

Theoretical calculation of electronic energy levels of an asymmetric InAs/InGaAS/GaAS quantum-dots-in-a-well (DWELL) structure for infrared photodetectors is performed in the framework of effective-mass envelope-function theory. Our calculated results show that the electronic energy levels in quantum dots (QDs) increase when the asymmetry increases and the ground state energy increases faster than the excited state energies. Furthermore, the results also show that the electronic energy levels in QDs decrease as the size of QDs and the width of quantum well (QW) in the asymmetric DWELL structure increase. Additionally, the effects of asymmetry, the size of QDs and the width of QW on the response peak of asymmetry DWELL photodetectors are also discussed.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

Finite difference time domain (FDTD) method is used for the simulation and analysis of electromagnetic field in the top coupling layer of GaAs/AlGaAs quantum well infrared photodetector (QWIP). Simulation results demonstrated the coupling efficiencies and distributions of electromagnetic (EM) field in a variety of 2D photonic crystal coupling layer structures. A photonic crystal structure for bi-color-QWIP is demonstrated with high coupling efficiency for two wavelengths.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

We demonstrate that by increasing the amount of (In, Ga)As deposit in a quantum dot layer, the intersublevel absorption wavelength for (In, Ga)As/GaAs quantum-dot infrared photodetectors can be blue-shifted from 15 to 10 mu m while the photoluminescence peak is red-shifted. We directly compare the measured energy spacing between intersublevels obtained from infrared absorption spectroscopy with those obtained from photoluminescence spectroscopy. We find that the intersublevel energy spacing determined from absorption measurements is much larger than that obtained from the photoluminescence measurements. (C) 2000 American Institute of Physics. [S0003-6951(00)04524-1].

Relevância:

100.00% 100.00%

Publicador:

Resumo:

A photovoltaic quantum dot infrared photodetector with InAs/GaAs/AlGaAs structures is reported. The detector is sensitive to normal incident light. At zero bias and 78 K, a clear spectral response in the range of 2 -7 mu m has been obtained with peaks at 3.1, 4.8 and 5.7 mu m. The bandgap energies of GaAs and Al0.2Ga0.8As at 78K are calculated and the energy diagram of the transitions in the Quantum-Dot Infrared Photodetector (QDIP) is given out. The photocurrent signals can be detected up to 110 K, which is state-of-the-art for photovoltaic QDIP. The photovoltaic effect in our detector is a result of the enhanced band asymmetry as we design in the structure.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

By considering all possible high order diffracted waves, the authors investigate the spectral response of two-dimensional gratings for quantum well infrared photodetectors (QWIPs). A new method is proposed that using long period gratings may improve grating quality and reduce the resulting cross talk in grating-coupled QWIPs. A sensitivity analysis indicates that the influence of variation of the grating constant on the coupling efficiency is less sensitive for the long period gratings than for the short ones. A large coupling efficiency has been demonstrated for long period gratings. The calculated wide grating response spectra are in good agreement with the experiment result. (C) 1996 American Institute of Physics.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

Asymmetric dark current and photocurrent versus voltage characteristic in the Double Barrier Quantum Wells (DBQWs) photovoltaic infrared photodetector has been studied. A model based on asymmetric potential barriers was proposed. The asymmetric potential thick barrier, which due to the Si dopant segregation during growth makes a major contribution to the asymmetrical I-V characteristic, calculations based on our model agree well with experimental results. This work also confirms the potential use of this DBQWs for infrared photodetector with large responsivity and little dark current under negative bias.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

The interband and intraband photocurrent properties of InAs/InAlAs/InP nanostructures have been studied. The doping effect on the photoluminescence properties of the quantum dots and the anisotropy of the quantum wire interband photocurrent properties are presented and discussed. With the help of interband excitation, an intraband photocurrent signal of the InAs nanostructures is observed. With the increase of the interband excitation power, the intraband photocurrent signal first increases and then decreases, which can be explained by the variance of the ground state occupation of the InAs nanostructures and the change of the mobility and lifetime of the electrons. The temperature dependence of the intraband photocurrent signal of the InAs nanostructures is also investigated.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

Quantum dot infrared photodetectors (QDIP) are in the center of research interest nowadays. However the real QDIP is inferior to those predicted in theory, in which the dot density is much higher than those reported. Through optimizing the growth conditions, we realized the control of high-density quantum dot growth. This will be very useful for future QDIP development.

Relevância:

100.00% 100.00%

Publicador:

Resumo:

Quantum dot infrared photodetectors (QDIPs) are very attractive for infrared imaging applications due to its promising features such as high temperature operation, normal incidence response and low dark current [1]. However, the key issue is to obtain a high quality active region which requires a structural optimization of the nanostructures. With using GaAsSb capping layer, the optical properties, such as the PL intensity and its full width at half maximum (FWHM), of InAs QDs have been improved in the range between 1.15 and 1.5 m, because of the reduction of the compressive strain in QDs and the increment of QD height [2]. In this work, we have demonstrated strong and narrow intraband photoresponse spectra from GaAsSb-capped InAs-based QDIPs