Influence of the final temperature of investment healting on the tensile strength and Vickers hardness of CP TI and TI-6AL-4V alloy

The aim of the work was to evaluate the influence of the temperature of investment healting on the tensile strength and Vickers hardness of CP Ti and Ti-6Al-4V alloy casting. Were obtained for the tensile strength test dumbbell rods that were invested in the Rematitan Plus investment and casting in the Discovery machine cast. Thirty specimens were obtained, fiftten to the CP Titanium and fifteen to the Ti-6Al-4V alloy, five samples to each an of the three temperatures of investment: 430°C (control group), 480°C and 530°C. The tensile test was measured by means of a universal testing machine, MTS model 810, at a strain of 1.0 mm/min. After the tensile strenght test the specimens were secctioned, embedded and polished to hardness measurements, using a Vickers tester, Micromet 2100. The means values to tensile tests to the temperatures 430°C, 480 and 530: CP Ti (486.1 - 501.16 - 498.14 -mean 495.30 MPa) and Ti-6Al-4V alloy (961.33 - 958.26 - 1005.80 - mean 975.13 MPa) while for the Vickers hardness the values were (198.06, 197.85, 202.58 - mean 199.50) and (352.95, 339.36, 344.76 - mean 345.69), respectively. The values were submitted to Analysis of Variance (ANOVA) and Tukey' s Test that indicate differences significant only between the materials, but not between the temperature, for both the materias. It was conclued that increase of the temperature of investment its not chance the tensile strength and the Vickers hardness of the CP Titanium and Ti-6Al-4V alloy.

Evaluation of the performance of α-SiAlON tool when turning Ti-6Al-4V alloy without coolant

Due to their high hardness and wear resistance, Si3N4 based ceramics are one of the most suitable cutting tool materials for machining cast iron, nickel alloys and hardened steels. However, their high degree of brittleness usually leads to inconsistent results and sudden catastrophic failures. This necessitates a process optimization when machining superalloys with Si3N4 based ceramic cutting tools. The tools are expected to withstand the heat and pressure developed when machining at higher cutting conditions because of their high hardness and melting point. This paper evaluates the performance of α-SiAlON tool in turning Ti-6Al-4V alloy at high cutting conditions, up to 250 m min-1, without coolant. Tool wear, failure modes and temperature were monitored to access the performance of the cutting tool. Test results showed that the performance of α-SiAl0N tool, in terms of tool life, at the cutting conditions investigated is relatively poor due probably to rapid notching and excessive chipping of the cutting edge. These facts are associated with adhesion and diffusion wear rate that tends to weaken the bond strength of the cutting tool.

Retention strength of cobalt-chromium vs nickel-chromium titanium vs Cp titanium in a cast framework association of removable partial overdenture

Aim: There is little information considering the framework association between cast clasps and attachments. The aim of this study was to evaluate the retention strength of frameworks match circumferential clasps and extra resilient attachment cast in three different alloys (cobalt-chromium, nickel-chromium titanium and commercially pure titanium), using two undercut (0.25 and 0.75 mm) and considering different period of time (0, 1/2, 1, 2, 3, 4 and 5 years). Methods: Using two metallic matrices, representing a partially edentulous mandibular right hemiarch with the first molar crown, canine root and without premolars, 60 frameworks were fabricated. Three groups (n = 20) of each metal were cast and each group was divided into two subgroups (n = 10), corresponding the molar undercut of 0.25 mm and 0.75 mm. The nylon male was positioned at the matrix and attached to the acrylic resin of the prosthetic base. The samples were subjected to an insertion and removal test under artificial saliva environment. Results: The data were analyzed and compared with ANOVAs and Tukey's test at 95% of probability. The groups cast in cobaltchromium and nickel-chromium-titanium had the highest mean retention strength (5.58 N and 6.36 N respectively) without significant difference between them, but statistically different from the group cast in commercially pure titanium, which had the lowest mean retention strength in all the periods (3.46 N). The association frameworks using nickel-chromium-titanium and cobalt-chromium could be used with 0.25 mm and 0.75 mm of undercut, but the titanium samples seems to decrease the retention strength, mainly in the 0.75 mm undercut. The circumferential clasps cast in commercially pure titanium used in 0.75 mm undercuts have a potential risk of fractures, especially after the 2nd year of use. Conclusion: This in vitro study showed that the framework association between cast clasp and an extra resilient attachment are suitable to the three metals evaluated, but strongly suggest extra care with commercially pure titanium in undercut of 0.75 mm. Clinical significance: Frameworks fabricated in Cp Ti tend to decrease in retentive strength over time and have a potential risk of fracture in less than 0.75 mm of undercut.

Flexibility and torsional resistance of three nickel-titanium retreatment instrument systems

Aim To assess the dimensional characteristics, flexibility and torsional behaviour of nickel-titanium retreatment instruments. Methodology Using image analysis software and high-resolution digital images, the instrument length, tip angle, diameter at 3mm from the tip and the distance between the blades (pitch length) of the following eight instruments were measured (n=12 for each measurement parameter): the ProTaper Universal retreatment (PTU-R) D1, D2 and D3 instruments; the R-Endo R1, R2 and R3 retreatment instruments; and the Mtwo retreatment (Mtwo-R) sizes 25 and 15 retreatment instruments. Maximum torque and the angular deflection at fracture as well as the bending moment at 45° were measured (n=12) according to the International Standards Organisation (ISO) specification number 3630-1. Data were analysed using the analysis of variance (α=0.05). Results The length of the active part of the instruments was found to vary according to the depth of the canal into which they were designed to reach. The pitch length also increased along the active length. The PTU-R D1 and the Mtwo-R instruments had active tips. Measurements of the bending moment at 45° revealed that the Mtwo-R 15 instrument was the most flexible, whereas the PTU-R D1 was the least flexible. The maximum torque tended to increase as the instrument diameter at 3mm from the tip increased, whereas the angular deflection at fracture varied in the opposite direction. Conclusions The geometrical characteristics of the retreatment instruments and their flexibility and torsion behaviour were consistent with their intended clinical application. © 2011 International Endodontic Journal.

Analysis of the bioactive surface of Ti-35Nb-7Zr alloy after alkaline treatment and solution body fluid

The purpose of this work was to evaluate the Ti-35Nb-7Zr experimental alloy after surface treatment and soaking in solution body fluid (SBF) to form bonelike apatite. The Ti-35Nb-7Zr alloy was produced from commercially pure materials (Ti, Nb and Zr) by an arc melting furnace. All ingots were submitted to sequences of heat treatment (1100 °C/2 h and water quenching), cold working by swaging procedures and heat treatment (1100 °C/2 h and water quenching). Discs with 13 mm diameter and 3 mm in thickness were cut. The samples were immersed in NaOH aqueous solution with 5 M at 60 °C for 72 h, washed with distilled water and dried at 40 °C for 24 h. After the alkaline treatment, samples were heat treated in both conditions: at 450 and 600 °C for 1 h in an electrical furnace in air. Then, they were soaking in SBF for 24 h to form an apatite layer on the surface. The surfaces were investigated by using scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDX), infrared spectroscopy (FTIR) and contact angle measurements. The results indicate that calcium phosphate could form on surface of Ti-35Nb-7Zr experimental alloy. © Springer-Verlag Berlin Heidelberg 2013.

Growth of calcium phosphate coating on Ti-7.5Mo alloy after anodic oxidation

Titanium and its alloys are widely used as biomaterials due to their mechanical, chemical and biological properties. To enhance the biocompatibility of titanium alloys, various surface treatments have been proposed. In particular, the formation of titanium oxide nanotubes layers has been extensively examined. Among the various materials for implants, calcium phosphates and hydroxyapatite are widely used clinically. In this work, titanium nanotubes were fabricated on the surface of Ti-7.5Mo alloy by anodization. The samples were anodized for 20 V in an electrolyte containing glycerol in combination with ammonium fluoride (NH4F, 0.25%), and the anodization time was 24 h. After being anodized, specimens were heat treated at 450 °C and 600°C for 1 h to crystallize the amorphous TiO2 nanotubes and then treated with NaOH solution to make them bioactive, to induce growth of calcium phosphate in a simulated body fluid. Surface morphology and coating chemistry were obtained respectively using, field-emission scanning electron microscopy (FEG-SEM), AFM and X-ray diffraction (XRD). It was shown that the presence of titanium nanotubes induces the growth of a sodium titanate nanolayer. During the subsequent invitro immersion in a simulated body fluid, the sodium titanate nanolayer induced the nucleation and growth of nano-dimensioned calcium phosphate. It was possible to observe the formation of TiO2 nanotubes on the surface of Ti-7.5Mo. Calcium phosphate coating was greater in the samples with larger nanotube diameter. These findings represent a simple surface treatment for Ti-7.5Mo alloy that has high potential for biomedical applications. © (2013) Trans Tech Publications, Switzerland.

Effects of Dextrose and Lipopolysaccharide on the Corrosion Behavior of a Ti-6Al-4V Alloy with a Smooth Surface or Treated with Double-Acid-Etching

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Mechanical and chemical analyses across dental porcelain fused to CP titanium or Ti6Al4V

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Anelastic spectroscopy in Ti-13V-11Cr-3Al alloy

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Corrosion kinetics and topography analysis of Ti-6Al-4V alloy subjected to different mouthwash solutions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

COMPARISON BETWEEN MECHANICAL PROPERTIES AND MICROSTRUCTURE OF ALLOY TI-6AL4V, COLD WORK VERSUS PROTOTIPES BY DIRECT METAL LASER SINTERING

The present work aims to study the microstructure and mechanical properties of titanium alloys, widely used in the manufacture of orthopedic implants in order to compare a new manufacturing technology of implants, rapid prototyping in metals with conventional manufacturing processes. Rapid prototyping is being used in many areas of human knowledge to assist in the study and often in the manufacture of components for their own use. Nowadays with the advancement of software and equipment such as computed tomography and magnetic resonance imaging, we can reproduce any part of the human body in three-dimensional images with great perfection and it is used in the reproduction of implants, scaffolds, material aid and preparation in surgery. This work aims to do: A comparison between the microstructure of the alloy in the two manufacturing processes (prototyping and conventional), showing the grain size, the nature, form, quantity, and distribution of various ingredients or certain inclusions and study of mechanical properties of titanium in both cases.

Influence of corrosion on lipopolysaccharide affinity for two different titanium materials

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Biofilm formation on the surface of Ti–7.5Mo alloy after surface treatment

Purpose: In the present work, a susceptibility and efficacy of the Ti–7.5Mo alloy and Ti alloy to bacterial biofilm formation after surface treatment was evaluated. Methods and materials: The alloy Ti–7.5Mo was obtained in arc furnace under an argon atmosphere. Ingots were then homogenized under vacuum at 1100 °C for 86.4 ks to eliminate chemical segregation and after cold worked discs were cutting. Samples were immersed in NaOH aqueous solution (5 M) and treated at 450 °C. Biofilms were grown in Ti–7.5Mo discs immersed in sterile brain heart infusion broth (BHI)containing 5% sucrose, inoculated with microbial suspension (106 cells/ml) and incubated for 5 days. Next, the discs were placed in tubes with sterile physiological solution 0.9% sodium chloride (NaCl) and sonicated for to disperse the biofilms. Tenfold serial dilutions were carried and aliquots seeded in selective agar, which were then incubated for 48 h. Then, the numbers CFU/ml (log 10) were counted and analyzed statistically. Scanning electron microscopy (SEM) on discs with biofilms groups was performed, atomic force microscope (AFM) and contact angle. Results: The results show that there is a 5% difference in bacterial adhesion between pure titanium and Ti–7.5Mo alloy. Conclusion: It was concluded that the greater the roughness, the greater the hydrophilic effect.

Improved response of the Ti30Ta experimental alloy after surface treatment for dental applications

The purpose of the study was to evaluate the influence of the biomimetic surface treatment in osseointegration of experimental alloy Ti30Ta for dentistry applications. Methods and materials: Experimental alloy with Ta concentration of 30 wt% was produced from sheets of commercially pure titanium (99.9%) and tantalum (99.9%). Ingots were melted in an arc furnace under an argon atmosphere and re-melted ten times at least. They were homogenized under vacuum at 1100 °C for 86.4 ks to eliminate chemical segregation and cold-worked by swaging. Implants with 2.5 mm diameter and 2.0 mm of height were machined (Fig. 1a), treated and inserted in animals for in vivo study. The implants were submitted surface treatment according methodology development for our group. Analyzes were performed by Scanning Electron microscopy (SEM), Atomic Force Microscopy (AFM). Osteoblast morphology on Ti-30Ta alloys was examined after 4 and 7 days of incubation with MSCs using SEM imaging.

Bone tissue, cellular, and molecular responses to titanium implants treated by anodic spark deposition

A myriad of titanium (Ti) surface modifications has been proposed to hasten the osseointegration. In this context, the aim of this study was to perform histomorphometric, cellular, and molecular analyses of the bone tissue grown in close contact with Ti implants treated by anodic spark deposition (ASD-AK). Acid-etched (AE) Ti implants either untreated or submitted to ASD-AK were placed into dog mandibles and retrieved at 3 and 8 weeks. It was noticed that both implants, AE and ASD-AK, were osseointegrated at 3 and 8 weeks. Histomorphometric analysis showed differences between treatments only for bone-to-implant contact, being higher on AE implants. Although not backed by histomorphometric results, gene expression of key bone markers was higher for bone grown in close contact with ASD-AK and for cells harvested from these fragments and cultured until subconfluence. Cell proliferation at days 7 and 10 and alkaline phosphatase activity at day 10 was higher on AE surfaces. No statistical significant difference was noticed for extracellular matrix mineralization at 17 days. Our results have shown that the Ti fixtures treated by ASD-AK allowed in vivo osseointegration and induced higher expression of key markers of osteoblast phenotype, suggesting that this surface treatment could be considered to produce implants for clinical applications. (c) 2012 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 100A:30923098, 2012.