Bond durability in erbium:yttrium-aluminum-garnet laser-irradiated enamel

This study sought to evaluate the influence of thermocycling and water storage on the microtensile bond strength of composite resin bonded to erbium:yttrium-aluminum-garnet (Er:YAG)-irradiated and bur-prepared enamel. Eighty bovine incisors were selected and sectioned. Specimens were ground to produce a flat enamel surface. Samples were randomly assigned according to cavity preparation device: (I) Er:YAG laser and (II) high-speed turbine, and were subsequently restored with composite resin. They were subdivided according to the duration of water storage (WS)/number of thermocycles (TCs): 24 h WS/no TCs; 7 days WS/500 TCs; 1 month WS/2,000 TCs; 6 months WS/12,000 TCs. The teeth were sectioned into 1.0 mm(2)-thick slabs and subjected to tensile stress in a universal testing machine. Data were submitted to two-way analysis of variance (ANOVA) and Tukey`s test at a 0.05 significance level. The different periods of water storage and thermocycling did not influence the microtensile bond strength (A mu TBS) values in the Er:YAG laser-prepared groups. In bur-prepared enamel, the group submitted to 12,000 TCs/6 months` WS (IID) showed a significant decrease in bond strength values when compared to the group stored in water for 24 h and not submitted to thermocycling (IIA), but values were statistically similar to those obtained in all Er:YAG laser groups and in the bur- prepared groups degraded with 500 TCs/1 week WS (IIB) or 2,000 TCs/1 month WS (IIC). It may be concluded that adhesion of an etch-and-rinse adhesive to Er:YAG laser-irradiated enamel was not affected by the methods used to simulate degradation of the adhesive interface and was similar to adhesion in the bur-prepared groups in all periods of water storage and thermocycling.

Comparative Histopathological Analysis of Human Pulps after Class I Cavity Preparation with a High-Speed Air-Turbine Handpiece or Er:YAG Laser

The purpose of this study was to comparatively evaluate the response of human pulps after cavity preparation with different devices. Deep class I cavities were prepared in sound mandibular premolars using either a high-speed air-turbine handpiece (Group 1) or an Er: YAG laser (Group 2). Following total acid etching and the application of an adhesive system, all cavities were restored with composite resin. Fifteen days after the clinical procedure, the teeth were extracted and processed for analysis under optical microscopy. In Group 1 in which the average for the remaining dentin thickness (RDT) between the cavity floor and the coronal pulp was 909.5 mu m, a discrete inflammatory response occurred in only one specimen with an RDT of 214 mu m. However, tissue disorganization occurred in most specimens. In Group 2 (average RDT = 935.2 mu m), the discrete inflammatory pulp response was observed in only one specimen (average RDT = 413 mu m). It may be concluded that the high-speed air-turbine handpiece caused greater structural alterations in the pulp, although without inducing inflammatory processes.

Effect of dentin conditioning time on nanoleakage

Objectives: To study the nanoleakage pattern in the dentin hybrid layer by using different dentin adhesives. The null hypotheses tested in this study were: 1) dentin conditioning time does not affect nanoleakage within the hybrid layer; 2) the type of dentin adhesive used does not affect nanoleakage. Methods: Standardized Class V cavities were prepared in 30 intact human molars on the buccal and lingual surfaces. The specimens were randomly assigned to 2 total-etch dentin adhesives (OptiBond SOLO Plus [OPS, Kerr] and One-Step [ONS, BISCO Inc]) and 2 self-etch dentin adhesives (Clearfil SE Bond [CSE, Kuraray] and Adper Prompt L-Pop [APL, 3M ESPE]). The specimens were etched or conditioned for 15 seconds, 30 seconds or 60 seconds. Upon restoration of the Class V cavities with the proprietary resin composite, the specimens were isolated with nail polish except for a 2.0-mm rim around the restoration, and they were immersed in 50 wt% ammoniacal silver nitrate solution (pH=9.5) for 24 hours followed by 8 hours of immersion in photo-developing solution to reduce the silver ions to metallic silver. The specimens were fixed, dehydrated and processed for FESEM and TEM. Silver penetration was measured along the cervical wall, and data were analyzed with Kruskal-Wallis non-parametric tests at a significance level of 95%. Results: There were no statistically significant differences among the experimental groups for the factor conditioning time (p>0.926). There were significant differences for the variable dentin adhesive (p<0.0001). The least amount of nanoleakage within the hybrid layer occurred with CSE, while ONS resulted in the greatest penetration of silver ions. The adhesives OPS and APL ranked in the intermediary subset. Under TEM, all adhesives resulted in some degree of nanoleakage within the hybrid layer. Both spotted/reticular and water-tree nanoleakage patterns were observed. Significance: Longer conditioning times did not increase nanoleakage within the hybrid layer. Nanoleakage varied with the type of adhesive used.

Microshear Bond Strength of Self-etching Bonding Systems to Ultrasound Diamond Bur-prepared Dentin

Purpose: The aim of this study was to evaluate the influence of dentin abrasion on the microshear bond strength of two self-etching adhesive systems, using either an ultrasound diamond bur or a high-speed diamond bur.Materials and Methods: Twenty noncarious human third molars were sectioned mesiodistally into halves. The enamel was ground to expose a flat dentin surface on both sections. The dentinal surfaces were randomly assigned to two groups, depending on the method of smear layer preparation: ultrasound diamond bur (UB) or conventional diamond bur (CB). The prepared dentin surfaces received one of two self-etching systems: Clearfil SE Bond (CF) and One-Up Bond F (OB). A composite cylinder with a 0.95-mm diameter was bonded to each specimen and the microshear bond test was performed. The results were expressed in MPa and were subjected to two-way analysis of variance (ANOVA) and Tukey's test (alpha = 0.05).Results: There was no significant difference in dentin bond strength when comparing the conventional and ultrasonic abrasion methods. When the adhesive systems were compared, Clearfil SE Bond achieved higher bond strength means than did One-Up Bond F.Conclusion: The dentin surface preparation method did not influence the microshear bond strength and the Clearfil SE Bond adhesive system, independent of bur type used, Clearfil SE Bond showed higher bond strengths than did the One-Up Bond F adhesive system.

Bond Strength of Two Resin Cements on Dentin Using Different Cementation Strategies

Purpose:This study evaluated the microtensile bond strength of two resin cements to dentin either with their corresponding self-etching adhesives or employing the three-step etch-and-rinse technique. The null hypothesis was that the etch-and-rinse adhesive system would generate higher bond strengths than the self-etching adhesives.Materials and Methods:Thirty-two human molars were randomly divided into four groups (N = 32, n = 8/per group): G1) ED Primer self-etching adhesive + Panavia F; G2) All-Bond 2 etch-and-rinse adhesive + Panavia F; G3) Multilink primer A/B self-etching adhesive + Multilink resin cement; G4) All-Bond 2 + Multilink. After cementation of composite resin blocks (5 x 5 x 4 mm), the specimens were stored in water (37 degrees C, 24 hours), and sectioned to obtain beams (+/- 1 mm2 of adhesive area) to be submitted to microtensile test. The data were analyzed using 2-way analysis of variance and Tukey's test (alpha = 0.05).Results:Although the cement type did not significantly affect the results (p = 0.35), a significant effect of the adhesive system (p = 0.0001) was found on the bond strength results. Interaction terms were not significant (p = 0.88751). The etch-and-rinse adhesive provided significantly higher bond strength values (MPa) with both resin cements (G2: 34.4 +/- 10.6; G4: 33.0 +/- 8.9) compared to the self-etching adhesive systems (G1: 19.8 +/- 6.6; G3: 17.8 +/- 7.2) (p < 0.0001). Pretest failures were more frequent in the groups where self-etching systems were used.Conclusion:Although the cement type did not affect the results, there was a significant effect of changing the bonding strategy. The use of the three-step etch-and-rinse adhesive resulted in significantly higher bond strength for both resin cements on dentin.CLINICAL SIGNIFICANCEDual polymerized resin cements tested could deliver higher bond strength to dentin in combination with etch-and-rinse adhesive systems as opposed to their use in combination with self-etching adhesives.(J Esthet Restor Dent 22:262-269, 2010).

Micro-Shear Bond Strength of Different Adhesives to Human Dental Enamel

The aim of this study was to evaluate the micro-shear bond strength of 5 adhesive systems to enamel, one single-bottle acid-etch adhesive (O), two self-etching primers (P) and two all-in-one self-etching adhesives (S). Method: Sixty premolar enamel surfaces (buccal or lingual) were ground flat with 400- and 600-grit SiC papers and randomly divided into 5 groups (n=12), according to the adhesive system.. SB2 - Single Bond 2 (O); CSE - Clearfil SE Bond (P); ADS - AdheSE (P); PLP - Adper Prompt L-Pop (S); XE3 - Xeno III (S). Tygon tubing (inner diameter of 0.8mm) restricted the bonding area to obtain the resin composite (Z250) cylinders. After storage in distilled water at 37 degrees C for 24h and thermocycling, micro-shear testing was performed (crosshead speed of 0.5mm/min). Data were submitted to one-way ANOVA and Tukey test (a=5%). Samples were also subjected to stereomicroscopic and SEM evaluations after micro-shear testing. Mean bond strength values (MPa +/- SD) and the results of Tukey test were: SB2: 36.36(+/- 3.34)a; ADS: 33.03(+/- 7.83)a; XE3: 32.76(+/- 5.61)a; CSE: 30.61(+/- 6.68)a; PLP: 22.17(+/- 6.05)b. Groups with the same letter were not statistically different. It can be concluded that no significant difference was there between SB2, ADS, XE3 and CSE, in spite of different etching patterns of these adhesives. Only PLP presented statistically lower bond strengths compared with others. J Clin Pediatr Dent 35(3): 301-304, 2011

Polymerization shrinkage: effects of boundary conditions and filling technique of resin composite restorations

Objective: To evaluate the linear polymerization shrinkage (LPS) and the effect of polymerization shrinkage of a resin composite and resin-dentin bond strength under different boundary conditions and filling techniques.Methods: Two cavities (4 x 4 x 2 MM) were prepared in bovine incisors (n = 30). The teeth were divided into three groups, according to boundary conditions: In group TE, the total-etch technique was used. In group EE, only enamel was conditioned, and in group NE, none of the watts of the cavities were conditioned. A two-step adhesive system was applied to all cavities. The resin composite was inserted in one (B) or three increments (1), and tight-cured with 600 mW/cm(2) (80 s). The LPS (%) was measured in the top-bottom direction, by placing a probe in contact with resin composite during curing. Enamel and total mean gap widths were measured (400 x) in three slices obtained after sectioning the restorations. Then, the slices were sectioned again, either to obtain sticks from the adhesive interface from the bottom of the cavity or to obtain resin composite sticks (0.8 mm(2)) to be tested for tensile strength (Kratos machine, 0.5 mm/min). The data was subjected to a two-way repeated measures ANOVA and Tukey's test for comparison of the means (alpha = 0.05).Results: the highest percentage of LPS was found for the TE when bulk fitted, and the lowest percentage of LPS was found in the Hand NE when incrementally fitted. The resin dentin bond strength was higher and the total mean gap width was tower for TE group; no significant effect was detected for the main factor fitting techniques. No difference was detected for the tensile strength of resin composite among the experimental groups.Conclusions: the filling technique is not able to minimize effects of the polymerization shrinkage, and bonding to the cavity watts is necessary to assure reduced mean gap width and high bond strength values. (C) 2004 Elsevier Ltd. All rights reserved.

The effect of temperature on self-etching adhesive penetration.

The purpose of this study was to investigate the penetration of an aggressive self-etching adhesive system at refrigerated and room temperatures into ground and unground enamel surfaces. Thirty extracted human teeth were used to measure adhesive penetration into enamel by light microscopy analysis (x400). The unground enamel surfaces were cleaned with pumice and water using a rotary dental brush. For each specimen, part of the unground enamel was manually ground and part was kept intact. A self-etch adhesive was evaluated for its ability to penetrate ground and unground enamel surfaces at room temperature (25 degrees C), at 30 minutes after removal from the refrigerator, and immediately after removal from the refrigerator (6 degrees C). Data were analyzed using variance and the Tukey test, which revealed significant differences in length of penetration of this material when applied on ground and unground enamel surfaces and between the different temperatures used (P > .05). The self-etching system used in this study had significantly lower penetration into unground enamel and at 6 degrees C (P < .05). No statistical difference was found between the interactions of these factors. It was concluded that the self-etching system produced the best penetration into ground enamel surface at room temperature (25 degrees C) and at 30 minutes after removing the specimens from the refrigerator.

Observation of tags and hybrid layer of a single bottle conventional adhesive system and a self-etching adhesive system, on sound dentin.

This experimental light microscopy study investigated the formation of a hybrid layer and resin tags on sound dentin, after utilization of conventional and self-etching adhesive systems. After restorative procedures, the specimens were decalcified in a formic acid and sodium citrate solution, embedded in paraffin, sectioned at 6-microm thickness and stained by the Brown & Brenn method for analysis and measurement by light microscopy (AXIOPHOT) (400x). The results were statistically analyzed by analysis of variance, at a significance level of 5%. Based on the results, it could be concluded that the conventional adhesive allowed the formation of a thicker hybrid layer than the self-etching adhesive, with similar penetration into the dentinal tubules (resin tags).

Effects of surface treatment, hydration and application method on the bond strength of a silorane adhesive and resin system to dentine

Objectives: To evaluate the effects of surface treatment, surface hydration (SH) and application method (AM) on the tensile bond strength of the Silorane Adhesive System (SAS) to dentine. Methods: Ninety bovine teeth were used. For the control group (n = 10), each dentine surface was treated according to the manufacturer's instructions of the SAS. The remaining teeth were randomly distributed into two groups (n = 40), according to the type of dentine surface treatment (ST) - 37% phosphoric acid or Er:YAG Laser prior to the application of the SAS. Each group was further divided into 2 subgroups (n = 20), according to the SH status: dry (D) or wet (W). Each subgroup was further divided into 2 subgroups (n = 10), according to the application method [AM: Active (AC) mode or Passive (PA) mode]. A coat of resin composite (Filtek P90) was applied on the surface. Artificial ageing was performed with a thermo-mechanical cycling machine. The specimens were sectioned into 1 mm × 1 mm × 10 mm sticks and stressed to failure using a universal testing machine. The remaining teeth in each group were used for Scanning Electron Microscopy to examine the fractured area. Data were subjected to a three-way ANOVA, Tukey's test and Dunnet's test (α = 0.05). Results: The ANOVA showed significant differences for SH and AM, but not for ST. For SH, the results of Tukey's test were (in MPa): D-14.9(±3.8)a, W-17.1(±4.3)b; and for AM: PA-14. 9(±4.2)a, AC-17.1(±3.9) b. Conclusions: Acid etching, when combined with a moist dentine surface and the use of primer agitation, improves the bond strength of the SAS to dentine. Clinical Significance: According to the results of the present in vitro study, modification of the application protocols for the silorane-based adhesive system may improve its clinical performance. © 2012 Published by Elsevier Ltd.

Resistência de sistemas de união ao microcisalhamento de sistemas adesivos condiona-e-lava de 2 passos: efeito de diferentes tratamentos da superfície dentinária condicionada

Pós-graduação em Ciências Odontológicas - FOAR

Citotoxidade direta e transdentinária de sistemas adesivos com diferentes graus de hidrofilia sobre células odontoblastóides

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efeito da inibição de metaloproteinases da matriz dentinária na produção e estabilidade mecânica da união resina-dentina afetada por cárie

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo longitudinal da resistência adesiva aos substratos dentários de sistemas adesivos associados ou não ao Nd:YAG Laser

Pós-graduação em Odontologia Restauradora - ICT

Resistência ao microcisalhamento de diferentes sistemas adesivos no esmalte dental humano

Pós-graduação em Odontologia Restauradora - ICT