Nondeactivating Nanosized Ionic Catalysts for Water-Gas Shift Reaction

The water-gas shift reaction (WGS) is an important reaction to produce hydrogen. In this study, we have synthesized nanosized catalysts where Pt ion is substituted in the +2 state in TiO2, CeO2, and Ce1-xTixO2-delta. These catalysts have been characterized by X-ray diffraction and X-ray photoelectron spectroscopy (XPS), and it has been shown that Pt2+ in these reducible oxides result in solid solutions like Ti0.99Pt0.01O2-delta, Ce0.8Ti0.15Pt0.02O2-delta, and Ce0.98Pt0.02O2-delta. These catalysts were tested for the water gas shift reaction both ill the presence and absence of hydrogen. It was shown that Ti0.99Pt0.01O2-delta exhibited higher catalytic activity than Ce0.83Ti0.15Pt0.02O2-delta and Ce0.98Pt0.02O2-delta. Further, experiments were conducted to determine the deactivation of these catalysts. There was no sintering of Pt and no carbonate formation; therefore, the catalyst did not deactivate even after prolonged reaction. There was no carbonate formation because of the highly acidic nature of Ti4+ ions in the catalysts.

Infrared spectra of some oxides of K2NiF4 and related structures

The i.r. spectra of some Ln2BO4 and LnSrBO4 compounds (Ln = La, Pr, Nd, Sm or Gd;B = Fe, Al, Co or Cu) with K2NiF4 or related structures have been studied in the range 800-300 cm−1. The BO6 octahedra in compounds with K2NiF4 structure are elongated. The assignment of the bands in terms of internal modes of sheets of bridged BO6 octahedra or square-planar BO4 sheets has been considered. The observed spectra are correlated with those of solid solutions of these oxides and of LnBO3 perovskites. Unusually high stretching frequencies found in some of the oxides are discussed in terms of the short B---O bonds in the basal plane and the Ln---O bonds along the c axis.

Infrared spectra of some oxides of K2NiF4 and related structures

The i.r. spectra of some Ln2BO4 and LnSrBO4 compounds (Ln = La, Pr, Nd, Sm or Gd;B = Fe, Al, Co or Cu) with K2NiF4 or related structures have been studied in the range 800-300 cm−1. The BO6 octahedra in compounds with K2NiF4 structure are elongated. The assignment of the bands in terms of internal modes of sheets of bridged BO6 octahedra or square-planar BO4 sheets has been considered. The observed spectra are correlated with those of solid solutions of these oxides and of LnBO3 perovskites. Unusually high stretching frequencies found in some of the oxides are discussed in terms of the short B---O bonds in the basal plane and the Ln---O bonds along the c axis.

Valence states and magnetic properties of LaNi1-xMnxO3 (for 0≤x≤0.2 and x=0.5)

Single-phase LaNi1-xMnxO3 samples in the compositional range 0solid solutions, and La2NiMnO6 was prepared from a mixture of carbonates. All the samples contained a disordered array of nickel and manganese ions. X-ray absorption and XPS measurements indicate the presence of Mn(III) and Ni(III) valence states at room temperature for x=0.1, 0.2 and 0.5. Magnetic susceptibility data suggest Mn4+ solute ions and Stoner-enhanced Pauli paramagnetism of the metallic solvent for x=0.01 with a smooth transition to Mn3+ solute ions and a spontaneously magnetised solvent conduction band at x=0.05. Below 200K, the x=0.05 sample forms superparamagnetic clusters, and below 40K there is evidence for an antiferromagnet spin-density wave. Comparisons with LaCo0.95Mn0.05O3 and La0.98Sr0.02CoO3 confirm that the long-range magnetic coupling occurs via solvent electrons in a narrow conduction band. The conductivity changes from that of a narrow-band metal for x<0.01 to that more characteristic of diffusive motion for x>0.05, but any motional enthalpy appears to remain small ( Delta Hm approximately=0). The x=0.1 sample exhibits ferrimagnetic spin glass behaviour below 40K, and the ferromagnetic interactions increase with manganese concentration. The oxide with x=0.50 is ferromagnetic with a well defined Curie temperature.

Atomic Layer Deposition of Electroluminescent ZnS, SrS, and BaS Thin Films

The light emitted by flat panel displays (FPD) can be generated in many different ways, such as for example alternating current thin film electroluminescence (ACTFEL), liquid crystal display (LCD), light emitting diode (LED), or plasma display panel (PDP) technologies. In this work, the focus was on ACTFEL devices and the goal was to develop new thin film processes for light emitting materials in ACTFEL devices. The films were deposited with the atomic layer deposition (ALD) method, which has been utilized in the manufacturing of ACTFEL displays since the mid-1980s. The ALD method is based on surface-controlled self-terminated reactions and a maximum of one layer of the desired material can be prepared during one deposition cycle. Therefore, the film thickness can be controlled simply by adjusting the number of deposition cycles. In addition, both large areas and deep trench structures can be covered uniformly. During this work, new ALD processes were developed for the following thin film materials: BaS, CuxS, MnS, PbS, SrS, SrSe, SrTe, SrS1-xSex, ZnS, and ZnS1-xSex. In addition, several ACTFEL devices were prepared where the light emitting material was BaS, SrS, SrS1-xSex, ZnS, or ZnS1-xSex thin film that was doped with Ce, Cu, Eu, Mn, or Pb. The sulfoselenide films were made by substituting the elemental selenium for sulfur on the substrate surface during film deposition. In this way, it was possible to replace a maximum of 90% of the sulfur with selenium, and the XRD analyses indicated that the films were solid solutions. The polycrystalline BaS, SrS, and ZnS thin films were deposited at 180-400, 120-460, and 280-500 °C, respectively, and the processes had a wide temperature range where the growth rate of the films was independent of the deposition temperature. The electroluminescence studies showed that the doped sulfoselenide films resulted in low emission intensity. However, the emission intensities and emission colors of the doped SrS, BaS, and ZnS films were comparable with those found in earlier studies. It was also shown that the electro-optical properties of the different ZnS:Mn devices were different as a consequence of different ZnS:Mn processes. Finally, it was concluded that because the higher deposition temperature seemed to result in a higher emission intensity, the thermal stability of the reactants has a significant role when the light emitting materials of ACTFEL devices are deposited with the ALD method.

Properties of Ammonium Nitrate based fertilisers

The text is divided into three parts; Properties, Application and Safety of Ammonium Nitrate (AN) based fertilisers. In Properties, the structures and phase transitions of ammonium and potassium nitrate are reviewed. The consequences of phase transitions affect the proper use of fertilisers. Therefore the products must be stabilised against the volume changes and consequent loss of bulk density and hardness, formation of dust and finally caking of fertilisers. The effect of different stabilisers is discussed. Magnesium nitrate, ammonium sulphate and potassium nitrate are presented as a good compromise. In the Application part, the solid solutions in the systems (K+,NH4+)NO3- and (NH4+,K+)(Cl-,NO3-) are presented based on studies made with DSC and XRD. As there are clear limits for solute content in the solvent lattice, a number of disproportionation transitions exist in these process phases, e.g., N3 (solid solution isomorphous to NH4NO3-III) disproportionates to phases K3 (solid solution isomorphous to KNO3-III) and K2 (solid solution isomorphous to KNO3-II). In the crystallisation experiments, the formation of K3 depends upon temperature and the ratio K/(K+NH4). The formation of phases K3, N3, and K2 was modelled as a function of temperature and the mole ratios. In introducing chlorides, two distinct maxima for K3 were found. Confirmed with commercial potash samples, the variables affecting the reaction of potassium chloride with AN are the particle size, time, temperature, moisture content and amount of organic coating. The phase diagrams obtained by crystallisation studies were compared with a number of commercial fertilisers and, with regard to phase composition, the temperature and moisture content are critical when the formation and stability of solid solutions are considered. The temperature where the AN-based fertiliser is solidified affects the amount of compounds crystallised at that point. In addition, the temperature where the final moisture is evaporated affects the amount and type of solid solution formed at this temperature. The amount of remaining moisture affects the stability of the K3 phase. The K3 phase is dissolved by the moisture and recrystallised into the quantities of K3, which is stable at the temperature where the sample is kept. The remaining moisture should not be free; it should be bound as water in the final product. The temperatures during storage also affect the quantity of K3 phase. As presented in the figures, K3 phase is not stable at temperatu¬res below 30 °C. If the temperature is about 40 °C, the K3 phase can be formed due to the remaining moisture. In the Safety part, self-sustaining decomposition (SSD), oxidising and energetic properties of fertilisers are discussed. Based on the consequence analysis of SSD, early detection of decomposition in warehouses and proper temperature control in the manufacturing process is important. SSD and oxidising properties were found in compositions where K3 exists. It is assumed that potassium nitrate forms a solid matrix in which AN can decompose. The oxidising properties can be affected by the form of the product. Granular products are inherently less oxidising. Finally energetic properties are reviewed. The composition of the fertiliser has an importance based on theoretical calculations supported by experimental studies. Materials such as carbonates and sulphates act as diluents. An excess of ammonium ions acts as a fuel although this is debatable. Based on the experimental work, the physical properties have a major importance over the composition. A high bulk density is of key importance for detonation resistance.

Structural transitions in (La,Ln)2CuO4 and La2(Cu,Ni)O4 systems

Solid solutions of the formula La2−xLnxCuO4 (Ln = Pr, Nd) possess the orthorhombic structure of La2CuO4 for small values of x and transform to the tetragonal Nd2CuO4 structure at a critical value of x. At the critical composition, there is an abrupt change in specific volume as well as the Image ratio. The material exhibits temperature-independent electrical resistivity below the critical value x and semiconducting behaviour above it. The specific volume and Image ratio smoothly decrease with increase in x in the La2Cu1−xNixO4 system, although the solid solution possess the tetragonal K2NiF4 structure when x>0.1. Compositions with x>0.1 exhibit a gradual semiconductor metal transition similar to that of La2NiO4, the transition temperature decreasing with increasing

In situ pump probe optical absorption studies on Sb/As2S3 nanomultilayered film

We report the in situ optical transmission change in the complete visible region of the electromagnetic spectrum to asses the kinetics of photo induced interdiffusion in Sb/As2S3 nanomultilayered film. The interdiffusion of Sb into As2S3 matrix results in the formation of Sb-As2S3 ternary solid solutions which is explained by the change in optical band gap, absorption coefficients and Tauc parameter (B-1/2) with evolution of time. The wavelength dependence of the time constants provides a better description of photo induced effects. The time evolution of the absorption coefficients and optical band gap are significantly faster in this process. (C) 2009 Elsevier B.V. All rights reserved.

Origin of activation of Lattice Oxygen and Synergistic Interaction in Bimetal-Ionic Ce0.89Fe0.1Pd0.01O2-delta Catalyst

Flourite-type nanocrystalline Ce0.9Fe0.1O2-delta and Ce0.89Fe0.1Pd0.01O2-delta solid solutions have been synthesized by solution combustion method,'.which show higher oxygen storage/release property (OSC) compared to CeO2 and Ce0.8Zr0.2O2. Temperature programmed reduction an XPS study reveal that the presence of Pd ion in Ce0.9Fe0.1O2-delta facilitates complete reduction of Fe3+ to Fe2+ state and partial reduction of Ce4+ to Ce3+ state at.temperatures as low as 105 degrees C compared to 400 degrees C for monometal-ionic Ce0.9Fe0.1O2-delta. Fe3+ ion is reduced to Fe2+ and not to Feo due to favorable redox potential for Ce4+ + Fe2+ -> Ce3+ + Fe3+ reaction. Using first-principles density functional theory calculation we determine M-O (M = Pd, Fe, Ce) bond lengths, and find that bond lengths vary from shorter (2.16 angstrom) to longer (2.9 angstrom) bond distances compared to mean Ce-O bond distance of 2.34 angstrom. for CeO2. Using these results in bond valence analysis, we show that oxygen with bond valences as low as -1.55 are created, leading to activation of lattice oxygen in the bimetal ionic catalyst. Temperatures of CO oxidation and NO reduction by CO/H-2 are lower with the bimetalionic Ce0.89Fe0.1Pd0.01O2-delta catalyst compared to monometal-ionic Ce0.9Fe0.1O2-delta and Ce0.99Pd0.01O2-delta catalysts. From XPS studies of Pd impregnated on CeO2 and Fe2O3 oxides, we show that the synergism leading to low temperature activation of lattice oxygen in bimetal-ionic catalyst Ce0.89Fe0.1Pd0.01O2-delta is due to low-temperature reduction of Pd2+ to Pd-0, followed by Pd-0 + 2Fe(3+) -> Pd2+ + 2Fe(2+), Pd-0 + 2Ce(4+) -> Pd2+ + 2Ce(3+) redox reaction.

Ce0.67Cr0.33O2.11: A New Low-Temperature O-2 Evolution Material and H-2 Generation Catalyst by Thermochemical Splitting of Water

Ce0.67Cr0.33O2.11 was synthesized by hydrothermal method using diethylenetriamine as complexing agent (Chem. Mater. 2008, 20, 7268). Ce0.67Cr0.33O2.11 being the only compound likes UO2+delta to have excess oxygen, it releases a large proportion of its lattice oxygen (0.167 M [O]/mole of compound) at relatively low temperature (465 degrees C) directly and it has been utilized for generation of H-2 by thermo-splitting of water. An almost stoichiometric amount of H-2 (0.152 M/Mole of compound) is generated at much lower temperature (65 degrees C). There is an almost comparable amount of oxygen release and hydrogen generation over this material at very low temperature comparedto other CeO2-MOx (Mn, Fe, Cu, and Ni) mixed-oxide solid solutions (O-2 evolution >= 1300 degrees C and H-2 generation at 1000 degrees C). The reversible nature of oxygen release and intake of this material is attributed to its fluorite Structure and coupling between the Ce4+/Ce3+ and Cr4+/6+/Cr3+ redox couples. Compound shows reversible oxygen release and intake by H2O absorption and subsequent hydrogen release to gain parent structure and hence this material can be utilized for generation of H-2 at very low temperature by thermo-chemical splitting of water.

Compatibility of RuO2 electrodes with PZT ceramics

Because of its high electrical conductivity and good diffusion barrier properties ruthenium dioxide (RuO2) is a good electrode material for use with ferroelectric lead zirconate-titanate (PZT) solid solutions. Under certain conditions, RuO2 can react with PZT to form lead ruthenate (Pb2Ru2O6.5) during processing at elevated temperatures resulting in lead depletion from PZT. The standard Gibbs energies of formation of RuO2 and Pb2Ru2O6.5 and activities of components of the PZT solid solution have been determined recently. Using this data along with older thermodynamic information on PbZrO3 and PbTiO3, the stability domain of Pb2Ru2O6.5 is computed as a function of PZT composition, temperature and oxygen partial pressure in the gas phase. The results show PbZrO3-rich compositions are more prone to react with RuO2 at all temperatures. Increasing temperature and decreasing oxygen partial pressure suppress the reaction. Graphically displayed are the reaction zones as a function of oxygen partial pressure and PZT composition at temperatures 973, 1173 and 1373 K.

Phase diagram of the system Ca-Ti-O at 1200 K

Phase relations in the system Ca-Ti-O have been established by equilibration of several samples at 1200 K for prolonged periods and identification of phases in quenched samples by optical and scanning electron microscopy, XRD and EDS. Samples representing 20 compositions in the ternary system were analyzed. There was negligible solid solubility of Ca in the phases along the binary Ti-O, and of Ti in CaO. Four ternary oxides were identified: CaTiO3, Ca4Ti3O10 and Ca3Ti2O7 containing tetravalent titanium, and CaTi2O4 containing trivalent titanium. Tie-lines link calcium titanite (CaTi2O4) with the three calcium titanates (CaTiO3, Ca4Ti3O10 and Ca3Ti2O7), CaO, oxygen excess TiO1+delta and stoichiometric TiO. Tie-lines connect CaTiO3 with TiO2-x, Magneli phases TinO2n-1 (28 >= n >= 4), Ti3O5, Ti2O3 and TiO1+delta. CaO was found to coexist with TiO, and Ti-O solid solutions alpha and beta. The phase diagram is useful for understanding the mechanisms and kinetics of direct calciothermic reduction of TiO2 to metal and electrochemical reduction of TiO2 using graphite anode and molten CaCl2 electrolyte.

Phase Diagram for the System RuO2-TiO2 in Air

There are conflicting reports in the literature regarding solid solubility in the system RuO2-TiO2. To resolve this issue a few experiments were conducted in air at 1673, 1723, and 1773 K. The results show limited terminal solid solubility. There is an extended solid-state miscibility gap that intersects the decomposition curve for the RuO2-rich solid solution generating a peritectoid reaction at 1698 K. The measured equilibrium compositions of the solid solutions are used to develop a thermodynamic description of the oxide solid solution with rutile structure. Using the subregular solution model, the enthalpy of mixing can be represented by the expression, Delta H-M/J center dot mol(-1) = XTiO2XRuO2 ( 34,100X(TiO2) + 30,750X(RuO2)). The binodal and spinodal curves and T-X phase diagram in air are computed using this datum and Gibbs energy of formation of RuO2 available in the literature. The computed results suggest that equilibrium was not attained during solubility measurements at lower temperatures reported in the literature.

Random existence of charge ordered stripes and its influence on the magnetotransport properties of La0.6Sr0.4MnO3 perovskite substituted with diamagnetic ions at Mn sublattice

Phase-singular solid solutions of La0.6Sr0.4Mn1-yMeyO3 (0 <= y <= 0.3) [Me=Li1+, Mg2+, Al3+, Ti4+, Nb5+, Mo6+ or W6+] [LSMey] perovskite of rhombohedral symmetry (space group: R (3) over barc) have been prepared wherein the valence of the diamagnetic substituent at Mn site ranged from 1 to 6. With increasing y-content in LSMey, the metal-insulator (TM-I) transition in resistivity-temperature rho(T) curves shifted to low temperatures. The magnetization studies M(H) as well as the M(T) indicated two groups for LSMey. (1) Group A with Me=Mg, Al, Ti, or Nb which are paramagnetic insulators (PIs) at room temperature with low values of M (< 0.5 mu(B)/Mn); the magnetic transition [ferromagnetic insulator (FMI)-PI] temperature (T-C) shifts to low temperatures and nearly coincides with that of TM-I and the maximum magnetoresistance (MR) of similar to 50% prevails near T-C (approximate to TM-I). (2) Group-B samples with Me=Li, Mo, or W which are FMIs with M-s=3.3-3.58 mu(B)/Mn and marginal reduction in T-C similar to 350 K as compared to the undoped LSMO (T-C similar to 378 K). The latter samples show large temperature differences Delta T=T-c-TM-I, reaching up to similar to 288 K. The maximum MR (similar to 60%) prevails at low temperatures corresponding to the M-I transition TM-I rather than around T-C. High resolution lattice images as well as microscopy analysis revealed the prevalence of inhomogeneous phase mixtures of randomly distributed charge ordered-insulating (COI) bistripes (similar to 3-5 nm width) within FMI charge-disordered regions, yet maintaining crystallographically single phase with no secondary precipitate formation. The averaged ionic radius < r(B)>, valency, or charge/radius ratio < CRR > cannot be correlated with that of large Delta T; hence cannot be used to parametrize the discrepancy between T-C and TM-I. The M-I transition is controlled by the charge conduction within the electronically heterogeneous mixtures (COI bistripes+FMI charge disordered); large MR at TM-I suggests that the spin-ordered FM-insulating regions assist the charge transport, whereas the T-C is associated with the bulk spin ordered regions corresponding to the FMI phase of higher volume fraction of which anchors the T-C to higher temperatures. The present analysis showed that the double-exchange model alone cannot account for the wide bifurcation of the magnetic and electric transitions, contributions from the charge as well as lattice degrees of freedom to be separated from spin/orbital ordering. The heterogeneous phase mixtures (COI+FMI) cannot be treated as of granular composite behavior. (c) 2008 American Institute of Physics.

Thermodynamic Properties and Phase Diagram for the System MoO2–TiO2

The activity of molybdenum dioxide (MoO2) in the MoO2–TiO2 solid solutions was measured at 1600 K using a solid-state cell incorporating yttria-doped thoria as the electrolyte. For two compositions, the emf was also measured as a function of temperature. The cell was designed such that the emf is directly related to the activity of MoO2 in the solid solution. The results show monotonic variation of activity with composition, suggesting a complete range of solid solutions between the end members and the occurrence of MoO2 with a tetragonal structure at 1600 K. A large positive deviation from Raoult's law was found. Excess Gibbs energy of mixing is an asymmetric function of composition and can be represented by the subregular solution model of Hardy as follows.The temperature dependence of the emf for two compositions is reasonably consistent with ideal entropy of mixing. A miscibility gap is indicated at a lower temperature with the critical point characterized by Tc (K)=1560 and . Recent studies indicate that MoO2 undergoes a transition from a monoclinic to tetragonal structure at 1533 K with a transition entropy of 9.91 J·(mol·K)−1. The solid solubility of TiO2 with rutile structure in MoO2 with a monoclinic structure is negligible. These features give rise to a eutectoid reaction at 1412 K. The topology of the computed phase diagram differs significantly from that suggested by Pejryd.