Study of ITO@PMMA composites by transmission electron microscopy

ITO nanowires were synthesized by carbothermal reduction process, using a co-evaporation method, and have controlled size, shape, and chemical composition. The electrical measurements of nanowires showed they have a resistance of about 102 Ω. In order to produce nanocomposites films, nanowires were dispersed in toluene using an ultrasonic cleaner, so the PMMA polymer was added, and the system was kept under agitation up to obtain a clear suspension. The PMMA polymer was filled with 1, 2, 5 and 10% in weight of nanowires, and the films were done by tape casting. The results showed that the electrical resistance of nanocomposites changed by over 7 orders of magnitude by increasing the amount of filler, and using 5 wt% of filler the composite resistance decreased from 1010 Ω to about 104 Ω, which means that percolation threshold of wires occurred at this concentration. This is an interesting result once for nanocomposites filled with ITO nanoparticles is necessary about 18% in weight to obtain percolation. The addition of filler up to 10 wt% decreased the resistance of the composite to 103 Ω, which is a value close to the resistance of wires. The composites were also analyzed by transmission electron microscopy (TEM), and the TEM results are in agreement with the electrical ones about percolation of nanowires. These results are promising once indicates that is possible to produce conductive and transparent in the visible range films by the addition of ITO nanowires in a polymeric matrix using a simple route. © 2011 Materials Research Society.

Giant Chemo-Resistance of SnO disk-like structures

Single crystalline SnO micro-disks, synthesized by a carbothermal reduction process, exhibited a nearly 1000-fold increase in resistance upon exposure to 100 ppm of NO2 without addition of catalysts or dopants nor the existence of nano-sized dimensions. Moreover, the SnO displayed a greater than 100-fold selectivity to NO2 over potential interferents including CO, H2 and CH4. The high sensor signal and exceptional selectivity for this novel sensor material are attributed to the existence of a high density of active lone pair electrons on the exposed (0 0 1) planes of the single crystalline SnO disks. This, thereby, identifies new means, not utilizing nano-dimensions, to achieve high gas sensitivity. © 2013 Elsevier B.V. All rights reserved.

O Comitê de Bacia e a gestão das águas no médio Paranapanema: um estudo sob a perspectiva do desenvolvimento sustentável

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo do crescimento e caracterização de nanofitas do sistema ITO

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Síntese de nanoestruturas de ZnO por redução carbotérmica e hidrotermal, assistido por micro-ondas: caracterização como sensor

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Planejamento da expansão de sistemas de transmissão usando a metaheurística de busca em vizinhança variável

Pós-graduação em Engenharia Elétrica - FEIS

Redução de mercúrio iônico por substâncias húmicas aquáticas

Pós-graduação em Química - IQ

Caracterização de estruturas de óxido de estanho modificado como sensores de gases

Pós-graduação em Química - IQ

Expressão diferencial de mRNA em células de cultivo infectadas ple herpesvírus bovino 5

Pós-graduação em Medicina Veterinária - FMVZ

An optimization study of PtSn/C catalysts applied to direct ethanol fuel cell: Effect of the preparation method on the electrocatalytic activity of the catalysts

The aim of this work was to perform a systematic study of the parameters that can influence the composition, morphology, and catalytic activity of PtSn/C nanoparticles and compare two different methods of nanocatalyst preparation, namely microwave-assisted heating (MW) and thermal decomposition of polymeric precursors (DPP). An investigation of the effects of the reducing and stabilizing agents on the catalytic activity and morphology of Pt75Sn25/C catalysts prepared by microwave-assisted heating was undertaken for optimization purposes. The effect of short-chain alcohols such as ethanol, ethylene glycol, and propylene glycol as reducing agents was evaluated, and the use of sodium acetate and citric acid as stabilizing agents for the MW procedure was examined. Catalysts obtained from propylene glycol displayed higher catalytic activity compared with catalysts prepared in ethylene glycol. Introduction of sodium acetate enhanced the catalytic activity, but this beneficial effect was observed until a critical acetate concentration was reached. Optimization of the MW synthesis allowed for the preparation of highly dispersed catalysts with average sizes lying between 2.0 and 5.0 nm. Comparison of the best catalyst prepared by MW with a catalyst of similar composition prepared by the polymeric precursors method showed that the catalytic activity of the material can be improved when a proper condition for catalyst preparation is achieved. (C) 2012 Elsevier B.V. All rights reserved.

Chemical mechanism of controlled nitric oxide release from trans-[RuCl([15]aneN(4))NO](PF6)(2) as a vasorelaxant agent

The nitrosyl ruthenium complex, trans-[RuCl([15]aneN(4))NO](PF6)(2), ([15]aneN(4) = 1,4,8,12-tetraazacyclopentadecane), exhibits vasorelaxation characteristics attributed to its nitric oxide release properties. The observed in vitro and in vivo vasodilation is dependent on noradrenaline concentration. We report here the chemical mechanism of the reaction between noradrenaline and trans-[RuCl([15]aneN(4))NO](PF6)(2) in aqueous phosphate buffer solution at pH 7.40. NO measurement by NO-sensor electrode, cyclic voltammetry, (PNMR)-P-31 and HPLC analysis were used to investigate the reduction process as the fundamental step for NO release characteristic of trans-[RuCl([15]aneN(4))NO](PF6)(2). A supramolecular species containing HPO4 (2-) as a bridging group between noradrenaline and trans-[RuCl([15]aneN(4))NO](PF6)(2) is suggested as an intermediate prior to the reduction of the nitrosyl ruthenium complex.

Direct ethanol fuel cell: Electrochemical performance at 90 degrees C on Pt and PtSn/C electrocatalysts

Carbon-supported Pt-based electrocatalysts were synthesized by Pechini method for the ethanol oxidation (EOR). Physicochemical characterizations were helpful to estimate the diameters of the obtained materials ranging from 2 nm to 5 nm. Main electrochemical experiments were carried out at 90 degrees C i.e. under the working conditions of performing the single 5 cm(2) direct ethanol fuel cell (DEFC). Pt(80)Sn(20)/C was the anode catalyst which has given the highest power density of 37 mW cm(-2). Importantly, the IR spectroscopy measurements associated with the qualitative analysis done at the output of the anodic compartment of the fuel cell have shown that ethanol oxidation on Pt(80)Sn(20)/C was mainly a two-electron sustainable process. (C) 2011 Elsevier B.V. All rights reserved.

Open circuit interaction of borohydride with oxidized platinum surfaces

An interesting method to investigate the effect of fuel crossover in low temperature fuel cells consists of studying the open circuit interaction between the reducing fuel and an oxide-covered catalyst. Herein we report the experimental study of the open circuit interaction between borohydride and oxidized platinum surfaces in alkaline media. When compared to the case of hydrogen and other small organic molecules, two remarkable new features were observed. Firstly, the interaction with borohydride resulted in a very-fast reduction process with transient times about two to three orders of magnitude smaller. The second peculiarity was that the decrease of the open circuit potential was found to occur in two-stages and this, previously unseen, feature was correlated with the two-hump profile found in the backward sweep in the cyclic voltammogram The consequences of our findings are discussed in connection with fundamental and applied aspects. (C) 2011 Elsevier B.V All rights reserved.

Defasagem idade-série a partir de distintas perspectivas teóricas

Age-grade gap from different theoretical perspectives. The purpose of this article is to analyze the determinants of the age-grade gap based on the human capital theory and some education sociology approaches. The article also shows the range and limitations of the Family Scholarship Transfer Programme (programa Bolsa Familia) in this age-grade gap reduction process. From the investigated theoretical aspects it can be concluded that this Programme would only show long-term effectiveness in the poverty reduction process if supported by at least a combination of programs and actions aimed at improving this educational indicator.

Preparation and characterisation of refractory whiskers and selected alumina composites

A whisker is a common name of single crystalline inorganic fibre of small dimensions, typically 0.5-1 μm in diameter and 20-50 μm in length. Whiskers are mainly used as reinforcement of ceramics. This work describes the synthesis and characterisation of new whisker types. Ti0.33Ta0.33Nb0.33CxN1-x, TiB2, B4C, and LaxCe1-xB6 have been prepared by carbothermal vapour–liquid–solid (CTR-VLS) growth mechanisms in the temperature range 900-1800°C, in argon or nitrogen. Generally, carbon and different suitable oxides were used as whisker precursors. The oxides reacted via a carbothermal reduction process. A halogenide salt was added to form gaseous metal halogenides or oxohalogenides and small amount of a transition metal was added to catalyse the whisker growth. In this mechanism, the whisker constituents are dissolved into the catalyst, in liquid phase, which becomes supersaturated. Then a whisker could nucleate and grow out under continuous feed of constituents. The syntheses of TiC, TiB2, and B4C were followed at ordinary synthesis conditions by means of mass spectrometry (MS), thermogravimetry (TG), differential thermal analysis (DTA) and quenching. The main reaction starting temperatures and reaction time for the different mixtures was revealed, and it was found that the temperature inside the crucible during the reactions was up to 100°C below the furnace set-point, due to endothermic nature of the reactions. Quench experiments showed that whiskers were formed already when reaching the temperature plateau, but the yield increased fast with the holding time and reached a maximum after about 20-30 minutes. Growth models for whisker formation have been proposed. Alumina based composites reinforced by (2-5 vol.%) TiCnano and TiNnano and 25 vol.% of carbide, and boride phases (whiskers and particulates of TiC, TiN, TaC, NbC, (Ti,Ta)C, (Ti,Ta,Nb)C, SiC, TiB2 and B4C) have been prepared by a developed aqueous colloidal processing route followed by hot pressing for 90 min at 1700°C, 28 MPa or SPS sintering for 5 minutes at 1200-1600°C and 75 MPa. Vickers indentation measurements showed that the lowest possible sintering temperature is to prefer from mechanical properties point of view. In the TiNnano composites the fracture mode was typically intergranular, while it was transgranular in the SiCnano composites. The whisker and particulate composites have been compared in terms of e.g. microstructure and mechanical properties. Generally, additions of whiskers yielded higher fracture toughness compared to particulates. Composites of commercially available SiC whiskers showed best mechanical properties with a low spread but all the other whisker phases, especially TiB2, exhibited a great potential as reinforcement materials.