Liquid-phase-epitaxy-grown InAsxSb1-x/GaAs for room-temperature 8-12 mu m infrared detectors

High-quality InAsxSb1-x (0 < x <= 0.3) films are grown on GaAs substrates by liquid phase epitaxy and electrical and optical properties of the films are investigated, revealing that the films exhibit Hall mobilities higher than 2x10(4) cm(2) V-1 s(-1) and cutoff wavelengths longer than 10 mu m at room temperature (RT). Photoconductors are fabricated from the films, and notable photoresponses beyond 8 mu m are observed at RT. In particular, for an InAs0.3Sb0.7 film, a photoresponse of up to 13 mu m with a maximum responsivity of 0.26 V/W is obtained at RT. Hence, the InAsxSb1-x films demonstrate attractive properties suitable for room-temperature, long-wavelength infrared detectors. (c) 2006 American Institute of Physics.

Determination of the interdiffusion coefficients of liquid Zn and Sn using Ta/Zn-Sn/Si trilayers

In this paper we present a new method for measuring diffusion coefficients in liquid metals under convection-less conditions with solid/liquid-liquid/solid trilayer. The advantage of this kind of trilayer is that effects from gravity-induced convection and Marangoni-convection can be omitted, so that the diffusion coefficient is determined more accurately. The Ta/Zn-Sn/Si trilayer were prepared with a multi-target ion-beam sputtering deposition technique and annealed in an electric furnace under an argon atmosphere. The interdiffusion of liquid zinc and tin at 500 degrees degree C was investigated. The diffusion concentration profiles were determined by energy dispersive spectroscopy. The interdiffusion coefficients range from 1.0x10(-6)cm(2)/s to 2.8x10(-6)cm(2)/s, which is less than previous values measured by capillary reservoir technique under 1g-environment where various convection exist. The precise interdiffusion coefficients of liquid zinc and tin result from the removing of disturbances of various kinds of convection.

Compensation ratio-dependent concentration of a VInH4 complex in n-type liquid encapsulated Czochralski InP

The concentration of hydroen-indium vacancy complex VInH4 in liquid encapsulated Czochralski undoped and Fe-doped n-type InP has been studied by low-temperature infrared absorption spectroscopy. The VInH4 complex is found to be a dominant intrinsic shallow donor defect with concentrations up to similar to 10(16) cm(-3) in as-grown liquid encapsulated Czochralski InP. The concentration of the VInH4 complex is found to increase with the compensation ratio in good agreement with the proposed defect formation model of Walukiewicz [W. Walukiewicz, Phys. Rev. B 37, 4760 (1998); Appl. Phys. Lett. 54, 2094 (1989)], which predicts a Fermi-level-dependent concentration of amphoteric defects. (C) 1998 American Institute of Physics, [S0003-6951(98)04435-0].

Threshold reduction in strained-layer InGaAs/GaAs quantum well lasers by liquid phase epitaxy regrowth

When liquid phase epitaxy regrowth at 780 degrees C for 2 h is applied to the samples after molecular beam epitaxy, a decrease of the threshold current density in strained InGaAs/GaAs quantum well lasers by a factor of 3 to 4 is obtained. We suggest that this improvement is attributed to the reduction of nonradiative centers associated with deep levels at the three regions of the active region, the graded layer and the cladding layer. Indeed, a significant reduction of deep center densities has been observed by using minority and majority carrier injection deep level transient spectroscopy measurements. (C) 1998 Elsevier Science B.V. All rights reserved.