Investigation of Mn-implanted n-type Ge

Mn+ irons were implanted to n-type Ge(1 1 1) single crystal at room temperature with an energy of 100 keV and a dose of 3 x 10(16) cm(-2). Subsequently annealing was performed at 400degreesC for 1 h under flowing nitrogen gas. X-ray diffraction measurements show that as-implanted sample is amorphous and the structure of crystal is restored after annealing. Polycrystalline germanium is formed in annealed sample. There are no new phases found except germanium. The samples surface morphologies indicate that annealed sample has island-like feature while there is no such kind of characteristic in as-implanted sample. The elemental composition of annealed sample was analyzed by Auger electron spectroscopy. It shows that manganese ions are deeply implanted into germanium substrate and the highest manganese atomic concentration is 8% at the depth of 120 nm. The magnetic properties of samples were investigated by an alternating gradient magnetometer. The annealed sample shows ferromagnetic behavior at room temperature. (C) 2004 Elsevier B.V. All rights reserved.

Influence of thermal isolating grooves on the performance of the Mach-Zehnder interferometer-type thermo-optic variable optical attenuator

Two types of silicon-on-insulator thermo-optic variable optical attenuators (VOAs) based on a Mach-Zehnder interferometer and a multimode-interference coupler are fabricated, one with thermal isolating grooves to improve heating efficiency and the other without Comparison of optical and electrical properties, such as insertion losses, the maximum attenuation levels and the corresponding power consumptions, and the response times, is carried out between the two types of VOAs. The comparison results Indicate that use of thermal isolating grooves leads to better values for most characteristics and is an effective way to improve the performance of Mach-Zehnder interferometer-type thermo-optic devices. (c) 2005 Society of Photo-Optical Instrumentation Engineers.

A Si-based tunable narrow-band flat-top filter with multiple-step-type Fabry-Perot cavity structure

In the optical network, the quick and accurate alignment with wavelength is an important issue during the channel detection. At this point, a filter having flat-top response characteristic is an effective solution. Based on multiple-step-type Fabry-Perot cavity structure, a novel all-Si-based thermooptical tunable flat-top filter with narrow-band has been fabricated, using our patent silicon-on-reflector bonding technology. The device demonstrated a 1-dB flat-top width of 1 nm, 3-dB band of 3 nm, free spectra range of 8 nm, and the tuning range of 4.6 nm was obtained under the applied voltage of 4 V.

Photoinduced voltage shift in a three-barrier, two-well resonant tunneling structure integrated with a 1.2-mu m-thick n-type GaAs layer

By integrating a three-barrier, two-well resonant tunneling structure with a 1.2-mu m-thick, slightly doped n-GaAs layer, a photoinduced voltage shift on the order of magnitude of 100 mV in resonant current peaks has been verified at an irradiance of low light power density. The 1.2-mu m-thick, slightly doped n-GaAs layer manifests itself of playing an important role in enhancing photoelectric sensitivity. (c) 2005 Elsevier B.V. All rights reserved.

NIP a-Si : H solar cells on stanless steel with p-type nc-Si : H window layer

The successful application of boron-doped hydrogenated nanocrystalline silicon as window layer in a-Si: H nip solar cells on stainless steel foil with a thickness of 0.05 mm is reported. Open circuit voltage and fill factor of the fabricated solar cell were 0.90V and 0.70 respectively. The optical and structural properties of the p-layers have been investigated by using UV-VIS and Raman spectroscopy. It is confirmed that the p-layer is hydrogenated nanocrystalline silicon with a wide optical gap due to quantum size effect.

A new type of photoelectric response in a double barrier structure with a wide quantum well

We have calculated the photoelectric response in a specially designed double barrier structure. It has been verilied that a transfer of the internal photovoltaic effect in the quantum well to the tunnelling transport through above-barrier quasibound states of the emitter barrier may give rise to a remarkable photocurrent.

Low threshold current density 1.5 mu m strained-MQW laser by n-type modulation-doping

1.5 mu m. n-type modulation-doping InGaAsP/InGaAsP strained multiple quantum wells grown by low pressure metalorganic chemistry vapor decomposition technology is reported for the first time in the world. N-type modulation-doped lasers exhibit much lower threshold current densities than conventional lasers with undoped barrier layers. The lowest threshold current density we obtained was 1052.5 A/cm(2) for 1000 mu m long lasers with seven quantum wells. The estimated threshold current density for an infinite cavity length was 94.72A/cm(2)/well, reduced by 23.3% compared with undoped barrier lasers. The n-type modulation doping effects on the lasing characteristics in 1.5 mu m devices have been demonstrated.

2-ps passively mode-locked Nd : YVO4 laser using an output-coupling-type semiconductor saturable absorber mirror

We have demonstrated stable self-starting passive mode-locking in a diode-end-pumped Nd: YVO4 laser using a semiconductor saturable absorber mirror (SESAM). An ln(0.25)Ga(0.75)As single quantum-well SESAM, which was grown by the metalorganic chemical-vapor deposition technique at low temperature, acts as a passive mode-locking device and an output coupler at the same time. Continuous-wave mode-locked transform-limited pulses were obtained at 1064 nm with a pulse duration of 2.1 ps and an average output power of 1.28 W at a repetition rate of 96.5 MHz. (c) 2005 American Institute of Physics.

Magnetic properties of Mn-implanted n-type Ge

Mn+ ions were implanted into n-type Ge(1 1 1) single crystal at room temperature at an energy of 100 keV with a dose of 3 x 10(16) cm(-2). Subsequent annealing was performed on the samples at 400 degreesC and 600 degreesC in a flowing nitrogen atmosphere. The magnetic properties of the samples have been investigated by alternating gradient magnetometer at room temperature. The compositional properties of the annealed samples were studied by Auger electron spectroscopy and the structural properties were analyzed by X-ray diffraction measurements. Magnetization measurements reveal room-temperature ferromagnetism for the annealed samples. The magnetic analysis supported by compositional and structural properties indicates that forming the diluted magnetic semiconductor (DMS) MnxGe1-x after annealing may account for the ferromagnetic behavior in the annealed samples. (C) 2004 Elsevier B.V. All rights reserved.

Structure and magnetic properties of ScFe6Ga6-type RCo5Ga7 (R = Y, Tb, Dy, Ho and Er)

The structure and magnetic properties of the RCo5Ga7 (R = Y, Tb, Dy, Ho and Er) compounds with the ScFe6Ga6-type structure have been studied. The stability of RCo5Ga7 is closely related with the ratio of the metal radii R-RE/R-(Co,R-Ga). With R-RE/R-(Co,R-Ga) less than or equal to 1.36, the compounds can be stabilized in the ScFe6Ga6-type structure. The lattice of RCo5Ga7 shrinks as the atomic order of R increases, and it is consistent with the lanthanide contraction. The structure analysis based on X-ray diffraction patterns reveals that in the orthorhombic RCo5Ga7 (Immm), R occupies the 2a site, and Co enters into the 8k and the 4h sites, and Ga is at the 4e, 4f, 4g, 4h and 8k sites. The interatomic distances and the coordination numbers of RCo5Ga7 are provided from the refinement results. The short interatomic distance (less than 2.480 Angstrom) between the Co ions results in the negative magnetic interaction, which does not favor ferromagnetic ordering. The magnetic moment of YCo5Ga7 is absent, and RCo5Ga7 (R = Tb, Dy, Ho and Er) may have long-range magnetic ordering with the paramagnetic Curie temperature lower than 5 K. (C) 2004 Elsevier Inc. All rights reserved.