Disruption of egg formation by Fasciola hepatica following treatment in vivo with triclabendazole in the sheep host

Eight indoor-reared cross-bred sheep with no prior exposure to Fasciola hepatica were infected by oral gavage with 200 metacercarial cysts of the triclabendazole (TCBZ)-susceptible Cullompton isolate of F. hepatica. Twelve weeks after infection, sheep were treated with 10 mg/kg triclabendazole. Two sheep were euthanised per time period; at 48 h, 72 h and 96 h post-treatment (pt). Two untreated control sheep were euthanised at 96 h pt. Flukes were recovered from the liver and, if present, from the gall bladder of the sheep. They were processed for whole mount analysis, histology and transmission electron microscopy of the female reproductive system; specifically, the uterus, vitelline follicles. Mehlis' gland and ovary.

Comparison of two assays, a faecal egg count reduction test (FECRT) and a coproantigen reduction test (CRT), for the diagnosis of resistance to triclabendazole in Fasciola hepatica in sheep

A sheep trial was performed to evaluate two diagnostic assays, a faecal egg count reduction test (FECRT) and a coproantigen reduction test (CRT), for the diagnosis of resistance of Fasciola hepatica to triclabendazole (TCBZ). The FECRT defines successful TCBZ treatment as a 95% or greater reduction in fluke faecal egg counts (FECs) at 14 days post-treatment (dpt). The CRT defines effective TCBZ treatment as faeces negative for Fasciola coproantigens at 14 dpt, as measured by the commercial BIO K201 coproantigen ELISA (Bio-X Diagnostics, Jemelle, Belgium).

Development of an egg hatch assay for the diagnosis of triclabendazole resistance in Fasciola hepatica: proof of concept.

The aim of this study was to develop an Egg Hatch Assay (EHA) test for the detection of triclabendazole (TCBZ) resistance in Fasciola hepatica. A number of fluke isolates were used, of differing sensitivity to TCBZ. Eggs were exposed to solutions of triclabendazole sulphoxide (TCBZ.SO) for 14 days, then triggered to hatch. Egg development was divided into 6 distinct and easily identifiable stages: dead, empty, unembryonated, cell division, eye spot and hatched. The number of eggs reaching those stages was recorded. Initially, the discriminating dose (1% hatch) was determined for the Cullompton isolate, used as TCBZ-susceptible (TCBZ-S) standard. Once this concentration had been resolved, the response of different isolates to this concentration was examined. The hatch rate of the Fairhurst isolate was not significantly different from that of the Cullompton isolate, confirming its TCBZ-S status. The Patagonia isolate has not been exposed to TCBZ in the field and should be TCBZ-S: the results of the EHA supported this. The egg hatch response of the Oberon and Dutch isolates differed significantly from that of the Cullompton isolate; the former isolates are regarded as TCBZ-resistant (TCBZ-R) and the results confirmed this. Another isolate, the Leon isolate, was originally described as being TCBZ-R, but has since been shown to be TCBZ-S. There was no difference in its response to TCBZ.SO in the EHA from the Cullompton (and Fairhurst and Patagonia) isolate(s), further indicating its TCBZ-S status. The impact of TCBZ.SO treatment on the component stages of egg development was determined and revealed differences between the isolates. In conclusion, the results of the study have shown that it is possible to discriminate between TCBZ-S and TCBZ-R isolates of F. hepatica on the basis of the response of their eggs to an EHA and the test could be used to evaluate the TCBZ sensitivity of unknown field isolates

Bovine Serum Albumin Adsorption to Iron-Oxide Coated Sands Can Change Microsphere Deposition Mechanisms

Particulate colloids often occur together with proteins in sewage-impacted water. Using Bovine Serum Albumin (BSA) as a surrogate for protein in sewage, column experiments investigating the capacity of iron-oxide coated sands to remove latex microspheres from water revealed that microsphere attenuation mechanisms depended on antecedent BSA coverage. Dual pulse experiment (DPE) results suggested that where all BSA was adsorbed, subsequent multiple pore volume microsphere breakthrough curves reflected progressively reduced colloid deposition rates with increasing adsorbed BSA content. Modelling colloid responses suggested adsorption of 1 µg BSA generated the same response as blockage by between 7.1x108 and 2.3x109 deposited microspheres. By contrast, microsphere responses in DPEs where BSA coverage of the deposition sites approached/ reached saturation revealed the coated sand maintained a finite capacity to attenuate microspheres, even when incapable of further BSA adsorption. Subsequent microsphere breakthrough curves demonstrated the matrix’s colloid attenuation capacity progressively increased with continued microsphere deposition. Experimental findings suggested BSA adsorption on the sand surface approaching/ reaching saturation generated attractive deposition sites for colloids, which became progressively more attractive with further colloid deposition (filter ripening). Results demonstrate that adsorption of a single type of protein may either enhance or inhibit colloid mobility in saturated porous media.

Effect of glass substrate and deposition technique on the properties of sol gel TiO2 thin films

Na+ ions have a detrimental effect on the photocatalytic activity of thin sot gel films deposited on soda lime glass due to their diffusion into the film during the calcination process. Given that the content of sodium in glass substrate might be the crucial parameter in determining the activity of a photocatalyst, the aim of the present work was the comparison of the photoinduced properties of a thin TiO2 film prepared on three different glass substrates namely on quartz (Q) glass, borosilicate (BS) glass and soda lime (SL) glass which have different sodium content. The prepared layers were characterised by X-ray diffraction and UV-vis spectroscopy. The diffusion of Na+ from the substrate into the layers was determined by Glow Discharge Atomic Emission Spectroscopy. The photocatalytic activities of the films were assessed using two model pollutant test systems (resazurin/resorufin ink and stearic acid film), which appeared to correlate reasonably well. It was observed that TiO2 layer on SL glass has a brookite crystalline structure while the TiO2 layer on BS and Q glass has an anatase crystalline structure. On the other hand, the photodegradation of the model dye on TiO2 films deposited on Q and BS glass is about an order higher than on SL glass. The low sodium content of BS glass makes it the most suitable substrate for the deposition of photoactive sol gel TiO2 films. (C) 2011 Elsevier B.V. All rights reserved.

An Investigation into the Optimum Thickness of Titanium Dioxide Thin Films Synthesized by Using Atmospheric Pressure Chemical Vapour Deposition for Use in Photocatalytic Water Oxidation

Twenty eight films of titanium dioxide of varying thickness were synthesised by using atmospheric pressure chemical vapour deposition (CVD) of titanium(IV) chloride and ethyl acetate onto glass and titanium substrates. Fixed reaction conditions at a substrate temperature of 660 degrees C were used for all depositions, with varying deposition times of 5-60 seconds used to control the thickness of the samples. A sacrificial electron acceptor system composed of alkaline sodium persulfate was used to determine the rate at which these films could photo-oxidise water in the presence of 365 nm light. The results of this work showed that the optimum thickness for CVD films on titanium substrates for the purposes of water oxidation was approximate to 200 nm, and that a platinum coating on the reverse of such samples leads to a five-fold increase in the observed rate of water oxidation.

Atmospheric Pressure Chemical Vapour Deposition of thin Films of Nb2O5 on Glass

A novel route involving atmospheric pressure chemical vapour deposition (APCVD) is reported for coating Nb2O5 onto glass substrates via the reaction of NbCl5 and ethyl acetate at 400-660degreesC. Raman spectroscopy is shown to be a simple diagnostic tool for the analysis of these thin films. The contact angle of water on Nb2O5-coated glass drops on UV irradiation from 60degrees to 5-20degrees. XPS Analysis showed that the Nb:O ratio of the film was 1:2.5. Glancing angle X-ray diffraction showed that all films were crystalline, with only a single phase being observed; this has some preferred orientation in the (201) plane of Nb2O5. The niobium(V) oxide materials show minimal photocatalytic ability to degrade organic material.

Anatase thin films on glass from the chemical vapor deposition of titanium(IV) chloride and ethyl acetate

Thin (50-500 nm) films of TiO2 may be deposited on glass substrates by the atmospheric pressure chemical vapor deposition (APCVD) reaction of TiCl4 with ethyl acetate at 400600 C. The TiO2 films are exclusively in the form of anatase, as established by Raman microscopy and glancing angle X-ray diffraction. X-ray photoelectron spectroscopy gave a 1:2 Ti:O ratio with Ti 2P(3/2) at 458.6 eV and O 1s is at 530.6 eV. The water droplet contact angle drops from 60degrees to

Atmospheric pressure chemical vapour deposition of titanium dioxide coatings on glass

Atmospheric pressure chemical vapour deposition of titanium dioxide coatings on glass substrates was achieved by the reaction of TiCl4 and a co-oxygen source (MeOH, EtOH, (PrOH)-Pr-i or H2O) at 500-650degreesC. The coatings show excellent uniformity, surface coverage and adherence. Growth rates were of the order of 0.3 mum min(-1) at 500degreesC. All films are crystalline and single phase with XRD showing the anatase TiO2 diffraction pattern; a = 3.78(1), c = 9.51(1) Angstrom. Optically, the films show minimal reflectivity from 300-1600 nm and 50-80% total transmission from 300-800 nm. Contact angles are in the range 20-40degrees for as-prepared films and 1-10degrees after 30 min irradiation at 254 nm. All of the films show significant photocatalyic activity as regards the destruction of an overlayer of stearic acid.

A case study with a novel geometry for pulsed laser deposition

Aluminium thin films were deposited by a laser ablation technique from solid cylindrical targets rotated on a lead screw. Both smooth-surfaced targets and targets with screw threads cut into the area to he irradiated were used. The targets were irradiated with a focused circular spot size of 2.5 mm in diameter, at a power density equal to 5.4 +/- 0.2 x 10(8) W cm(-2). The polar distribution of the ablated atomic material was found to vary as a function of the target screw thread pitch, with the exponent n, in the polar distribution f(theta) = cos(n) theta, varying from 13.5 +/- 1.3 for no pitch to a minimum of 5 +/- 0.7 for a screw thread pitch of 0.2 mm. The use of such novel target geometries forms a possible basis for increasing thickness uniformity during the pulsed laser deposition of thin films.

Use of a random phase plate as a KrF laser beam homogenizer for thin film deposition applications

Fabrication of devices based on thin film structures deposited using the pulsed laser deposition technique relies on reproducibility and control of deposition rates over substrate areas as large as possible. Here we present an application of the random phase plate technique to smooth and homogenize the intensity distribution of a KrF laser footprint on the surface of a target which is to be ablated. It is demonstrated that intensity distributions over millimeter-sized spots on the target can be made insensitive to the typical changes that occur in the near-field intensity distribution of the ultraviolet output from a KrF laser. (C) 1999 American Institute of Physics. [S0034-6748(99)02504-6].

THE ULTRASTRUCTURE AND IMMUNOGOLD LABELING OF PANCREATIC POLYPEPTIDE-IMMUNOREACTIVE CELLS ASSOCIATED WITH THE EGG-FORMING APPARATUS OF A MONOGENEAN PARASITE, DICLIDOPHORA-MERLANGI

An electron microscopical examination has been made of the fine structure and disposition of pancreatic polypeptide immunoreactive cells associated with the egg-forming apparatus in Diclidophora merlangi. The cell bodies are positioned in the parenchyma surrounding the ootype and taper to axon-like processes that extend to the ootype wall. The terminal regions of these processes branch and anastomose and, in places, the swollen endings or varicosities form synaptic appositions with the muscle fibres in the ootype wall. The cells are characterized by an extensive GER-Golgi system that is involved in the assembly and packaging of dense-cored vesicles. The vesicles accumulate in the axons and terminal varicosities, and their contents were found to be immunoreactive with antisera raised to the C-terminal hexapeptide amide of pancreatic polypeptide. It is concluded that the cells are neurosecretory in appearance and that, functionally, their secretions may serve to regulate ootype motility and thereby help co-ordinate egg production in the worm.