Comparative study of the mode-locking of Nd:GdVO4 and Nd:YAG lasers with semiconductor saturable absorber mirrors

Stable continuous-wave passive mode-locking of diode-end-pumped Nd:GdVO4 and Nd:YAG lasers withsemiconductor saturable absorber mirrors (SESAMs) are reported. The comparative study shows that theNd:GdVO4 crystal is efficient to decrease the Q-switched mode-locking tendency, and easier to continuous-wave (CW) mode lock than Nd:YAG.

Stable mode-locking in an Yb:YAG laser with a fast SESAM

Stable mode-locking in a diode-pumped Yb:YAG laser was obtained with a very fast semiconductor saturable absorber mirror (SESAM). The pulse width was measured to be 4 ps at the central wavelength of 1047 nm. The average power was 200 mW and the repetition rate was 200 MHz.

Single steady frequency and narrow line width external cavity semiconductor laser

A single longitudinal mode and narrow line width external cavity semiconductor laser is proposed. It is constructed with a semiconductor laser, collimator, a flame grating, and current and temperature control systems. The one facet of semiconductor laser is covered by high transmission film, and another is covered by high reflection film. The flame grating is used as light feedback element to select the mode of the semiconductor laser. The temperature of the constructed external cavity semiconductor laser is stabilized in order of 10(-3)degreesC by temperature control system. The experiments have been carried out and the results obtained-the spectral fine width of this laser is compressed to be less than 1.4MHz from its original line-width of more than 1200GHz and the output stability (including power and mode) is remarkably enhanced.

Low-frequency noise properties of GaN Schottky barriers deposited on intermediate temperature buffer layers

Metal-semiconductor-metal (MSM) structures were fabricated by RF-plasma-assisted MBE using different buffer layer structures. One type of buffer structure consists of an AlN high-temperature buffer layer (HTBL) and a GaN intermediate temperature buffer layer (ITBL), another buffer structure consists of just a single A IN HTBL. Systematic measurements in the flicker noise and deep level transient Fourier spectroscopy (DLTFS) measurements were used to characterize the defect properties in the films. Both the noise and DLTFS measurements indicate improved properties for devices fabricated with the use of ITBL and is attributed to the relaxation of residue strain in the epitaxial layer during growth process. (C) 2003 Elsevier Ltd. All rights reserved.

Frequency limitation in calibrating microwave test fixtures

The problem of frequency limitation arising in calibration of the test fixtures is investigated in this paper. It is found that at some frequencies periodically, the accuracy of the methods becomes very low, and. the denominators of the expressions of the required S-parameters approach zero. This conclusion can be drawn whether-the test fixtures, are symmetric or not. A good agreement between theory and experiment is obtained.

High electrical-to-green efficiency high stability intracavity-frequency-doubled Nd:YAG-LBO QCW 532 nm laser with a straight cavity

An electrical-to-green efficiency of more than 10% was demonstrated by intracavity-frequency-doubling a Q-switched diode-side-pumped Nd:YAG laser with a type II lithium triborate (LBO) crystal in a straight plano-concave cavity. An average power of 69.2 W at 532 nm was generated when electrical input power was 666 W. The corresponding electrical-to-green conversion efficiency is 10.4%. To the best of our knowledge, this is the highest electrical-to-green efficiency of second harmonic generation laser systems with side-pumped laser modules, ever reported. At about 66 W of green output power, the power fluctuation over 4 hours was better than +/-0.86%.

All-Optical Clock Recovery for 20 Gb/s Using an Amplified Feedback DFB Laser

We report all optical clock recovery based on a monolithic integrated four-section amplified feedback semiconductor laser (AFL), with the different sections integrated based on the quantum well intermixing (QWI) technique. The beat frequency of an AFL is continuously tunable in the range of 19.8-26.3 GHz with an extinction ratio above 8 dB, and the 3-dB linewidth is close to 3 MHz. All-optical clock recovery for 20 Gb/s was demonstrated experimentally using the AFL, with a time jitter of 123.9 fs. Degraded signal clock recovery was also successfully demonstrated using both the dispersion and polarization mode dispersion (PMD) degraded signals separately.

Flood frequency and routing processes at a confluence of the middle Yellow River in China

IEECAS SKLLQG

Blue-violet luminescence double peak of In-doped films prepared by radio frequency sputtering

ZnO films doped with different contents of indium were prepared by radio frequency sputtering technique. The structural, optical and emission properties of the films were characterized at room temperature using XRD, XPS, UV-vis-NIR and PL techniques. Results showed that the indium was successfully incorporated into the c-axis preferred orientated ZnO films, and the In-doped ZnO films are of over 80% optical transparency in the visible range. Furthermore, a double peak of blue-violet emission with a constant energy interval (similar to 0.17 eV) was observed in the PL spectra of the samples with area ratio of indium chips to the Zn target larger than 2.0%. The blue peak comes from the electron transition from the Zn-i level to the top of the valence band and the violet peak from the In-Zn donor level to the V-Zn level, respectively.

Structural and photoluminescent properties of ZnO films deposited by radio frequency reactive sputtering

Zinc oxide films with c-axis preferred orientation were deposited on silicon (100) substrates by radio frequency (RF) reactive sputtering. The properties of the samples were characterized by X-ray diffractometer, X-ray photoelectron spectroscopy and fluorescent-spectrophotometer. The effect of sputtering power and substrate temperature on the structural and photoluminescent (PL) properties of the ZnO films was investigated. The results indicated that when the sputtering power is 100 W and the substrate temperature is 300-400 degrees C, it is suitable for the growth of high c-axis orientation and small strain ZnO films. A violet peak at about 380 nm and a blue band at about 430 nm were observed in the room temperature photoluminescence spectra, and the origin of blue emission was investigated.