Enhancement of oxidation rate of a-Si nanoparticles during dehydrogenation

Oxidation of amorphous silicon (a-Si) nanoparticles grown by plasma-enhanced chemical vapor deposition were investigated. Their hydrogen content has a great influence on the oxidation rate at low temperature. When the mass gain is recorded during a heating ramp in dry air, an oxidation process at low temperature is identified with an onset around 250°C. This temperature onset is similar to that of hydrogen desorption. It is shown that the oxygen uptake during this process almost equals the number of hydrogen atoms present in the nanoparticles. To explain this correlation, we propose that oxidation at low temperature is triggered by the process of hydrogen desorption

A surface and catalytic study of heterogenised Os-3(CO)(12) species in MCM-41 structures

Immobilised Os species prepared via chemical vapour deposition (CVD) of Os-3(CO)(12) onto MCM-41 are active and selective catalysts for the dihydroxylation of trans-stilbene in acetone and water, using N-methylmorpholine N-oxide as the oxidant. A detailed temperature programmed decomposition study of the solids enables to identify the active sites as Os-x(CO)(y) surface species. The initial loading of the MCM-41 with the trinuclear precursor, as well as the temperature of the post-synthesis oxidising treatment, are found to have a significant impact on the structure/geometry of the resulting surface species, and thus their catalytic properties. We show how it is also affected by the confined environment of the MCM-41 mesopores and especially the curvature of the 30 Angstrom diameter channels. Finally, a careful study of the catalytic properties of the materials together with a study of the reactivity of the reaction products under similar conditions enable to suggest a mechanism involving the reaction of the oxidant with the osmium carbonyl surface species to form the catalytically active Os-oxo sites, and the formation of an osmoate-type species (through adsorption of the alkene onto the Os-oxo site) which subsequently reacts with the solvent to produce the diol. (C) 2003 Elsevier B.V. All rights reserved.

All-optical switching device for infrared based on PbTe quantum dots

Multilayers of PbTe quantum dots embedded in SiO2 were fabricated by alternate use of Pulsed Laser Deposition (PLD) and Plasma Enhanced Chemical Vapor Deposition (PECVD) techniques. The morphological properties of the nanostructured material were studied by means of High Resolution Transmission Electron Microscopy (HRTEM), Grazing-Incidence Small-Angle X-ray scattering (GISAXS) and X-ray Reflectometry (XRR) techniques. A preliminary analysis of the GISAXS spectra provided information about the multilayer periodicity and its relationship to the size of the deposited PbTe nanoparticles. Finally multilayers were fabricated inside a Fabry-Perot cavity. The device was characterized by means of Scanning Electron Microscopy (SEM). Transmittance measurements show the device functionality in the infrared region. (C) 2007 Elsevier Ltd. All rights reserved.

Sequential IRMPD of XGe(OEt)(4)(-) ions: Gas-phase synthesis of novel oxy-germanium anions

The gas-phase ion/molecule reactions of F(-) and EtO(-) with Ge(OEt)(4) yield readily and exclusively pentacoordinated complexes XGe(OEt)(4)(-) (X = F, EtO) at pressures in the 10(-8) T range as observed by FT-ICR techniques. These hypervalent species are prone to undergo sequential fragmentations induced by infrared multiphoton excitation that lead to a variety of germyl and germanate anions. In the case of FGe(OEt)(4)(-), three primary competitive channels are observed in the IRMPD process that can be identified as (EtO)(3)GeO(-), F(EtO)(2)GeO(-) and (EtO)(3)Ge(-). Ab initio calculations have been carried out to characterize the primary fragmentation paths induced by IRMPD and the most favorable structure of the resulting anions. The gas-phase acidity of a number of these germanium-containing ions have been estimated by bracketing experiments and by theoretical calculations. Germanate anions such as (EtO)(3)GeO(-) undergo some interesting reactions with H(2)S to give rise to anions such as (EtO)(3)GeS(-) and (EtO)(2)Ge(OH)S(-). (C) 2010 Elsevier B.V. All rights reserved.

Anodic oxidation of wastewater containing the Reactive Orange 16 Dye using heavily boron-doped diamond electrodes

Boron-doped diamond (BDD) films grown on the titanium substrate were used to study the electrochemical degradation of Reactive Orange (RO) 16 Dye. The films were produced by hot filament chemical vapor deposition (HFCVD) technique using two different boron concentrations. The growth parameters were controlled to obtain heavily doped diamond films. They were named as E1 and E2 electrodes, with acceptor concentrations of 4.0 and 8.0 x 10(21) atoms cm(-3), respectively. The boron levels were evaluated from Mott-Schottky plots also corroborated by Raman`s spectra, which characterized the film quality as well as its physical property. Scanning Electron Microscopy showed well-defined microcrystalline grain morphologies with crystal orientation mixtures of (1 1 1) and (1 00). The electrode efficiencies were studied from the advanced oxidation process (AOP) to degrade electrochemically the Reactive Orange 16 azo-dye (RO16). The results were analyzed by UV/VIS spectroscopy, total organic carbon (TOC) and high-performance liquid chromatography (HPLC) techniques. From UV/VIS spectra the highest doped electrode (E2) showed the best efficiency for both, the aromaticity reduction and the azo group fracture. These tendencies were confirmed by the TOC and chromatographic measurements. Besides, the results showed a direct relationship among the BDD morphology, physical property, and its performance during the degradation process. (C) 2011 Elsevier B.V. All rights reserved.

Caracterização elétrica de estruturas metal/dielétrico high-k/Si

Foram estudadas as propriedades elétricas de estruturas MOS envolvendo materiais com Zr e Hf: Al/HfO2/Si, Al/HfAlO/Si, Al/ZrO2/Si e Al/ZrAlO/Si depositadas por JVD (Jet Vapor Deposition) submetidas a diferentes doses de implantação de nitrogênio e tratamentos térmicos; Au/HfO2/Si e Au/HfxSiyOz/Si preparadas por MOCVD (Metal-Organic Chemical Vapor Deposition) e Au/HfxSiyOz/SiO2/Si preparadas por sputtering reativo em O2 submetidas a tratamentos térmicos distintos. Para isso, além das medidas de C-V e I-V padrão, foi desenvolvido o método da condutância para estudo da densidade de estados na interface dielétrico/Si, o qual mostrou-se mais viável para as estruturas com dielétricos alternativos. A inclusão de Al na camada de dielétrico, bombardeamento por íons de nitrogênio, e tratamentos térmicos rápidos em atmosferas de O2 e N2 foram responsáveis por mudanças nas propriedades das amostras. Diversos mecanismos físicos que influenciam as propriedades elétricas dessas estruturas foram identificados e discutidos. Foi constatado que as interfaces com menores densidades de estados foram as das amostras preparadas por MOCVD e sputtering reativo.

Structural and optical properties of chlorinated plasma polymers

Amorphous hydrogenated chlorinated carbon (a-C:H:Cl) films were produced by the plasma polymerization of chloroform-acetylene-argon mixtures in a radiofrequency plasma enhanced chemical vapor deposition system. The main parameter of interest was the proportion of chloroform in the feed, R(C), which was varied from 0 to 80%. Deposition rates of 80 nm min (1) were typical for the chlorinated films. Infrared reflection-absorption spectroscopy revealed the presence of C-Cl groups in all the films produced with chloroform in the feed. X-ray photoelectron spectroscopy confirmed this finding, and revealed a saturation of the chlorine content at similar to 47 at.% for R(C)>= 40%. The refractive index and optical gap, E(04), of the films were roughly in the 1.6 to 1.7, and the 2.8 to 3.7 eV range. These values were calculated from transmission ultraviolet-visible-near infrared spectra. Chlorination leads to an increase in the water surface contact angle from similar to 40 degrees to similar to 77 degrees. (C) 2011 Elsevier B.V. All rights reserved.

Amorphous hydrogenated carbon films treated by SF(6) plasma

This work was performed to verify the chemical structure, mechanical and hydrophilic properties of amorphous hydrogenated carbon films prepared by plasma enhanced chemical vapor deposition, using acetylene/argon mixture as monomer. Films were prepared in a cylindrical quartz reactor, fed by 13.56 MHz radiofrequency. The films were grown during 5 min, for power varying from 25 to 125 W at a fixed pressure of 9.5 Pa. After deposition, all samples were treated by SF(6) plasma with the aim of changing their hydrophilic character. Film chemical structure investigated by Raman spectroscopy, revealed the increase of sp(3) hybridized carbon bonds as the plasma power increases. Hardness measurements performed by the nanoindentation technique showed an improvement from 5 GPa to 14 GPa following the increase discharge power. The untreated films presented a hydrophilic character, which slightly diminished after SF(6) plasma treatment.

Development of amorphous carbon protective coatings on poly(vinyl)chloride

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Properties of hydrogenated amorphous carbon films deposited by PECVD and modified by SF6 plasma

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Preparation and characterization of nanocrystalline h-BN films prepared by PECVD method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

XPS investigation of plasma-deposited polysiloxane films irradiated with helium ions

This work describes an XPS investigation of plasma-deposited polysiloxane films irradiated with 170 keV He+ ions at fluences, Phi, ranging from 1 x 10(14) to 1 x 10(16) cm(-2). Modifications in the atomic concentrations of the surface atoms with (D were revealed by changes in the [O]/[Si], [O]/[C] and [C]/[Si] atomic ratios. Surface chemical structure modifications were evidenced by the increasing C1s peak width and asymmetry as Phi was increased, due to the formation of ether and carboxyl functionalities. Moreover, structural transformations were indicated by the positive binding energy shift of the Si2p peaks, due to the increasing Si oxidation. Correlations of the XPS data with other results from previous work on polysiloxanes illustrate the role of ion beam-induced bond breaking on the structural modifications.

Infrared spectroscopy investigation of various plasma-deposited polymer films irradiated with 170 keV He+ ions

This work illustrates the advantages of using p-polarized radiation at an incidence angle of 70 degrees in contrast to the conventional unpolarized beam at normal (or near-normal) incidence for the infrared spectroscopic study of polycarbosilane, polysilazane and polysiloxane thin films synthesized by plasma enhanced chemical vapor deposition (PECVD) and subsequently irradiated with 170 keV He+ ions at fluences from 1 x 10(14) to 1 x 10(16) cm(-2). Several bands not seen using the conventional mode could be observed in the polarized mode. (c) 2006 Elsevier B.V. All rights reserved.