ZnO based nanowires grown by chemical vapour deposition for selective hydrogenation of acetylene alcohols

Vertically aligned ZnO nanowires (NWs) with a length of 1.5-10 mu m and a mean diameter of ca. 150 nm were grown by chemical vapour deposition onto a c-oriented ZnO seed layer which was deposited by atomic layer deposition on Si substrates. The substrates were then spin-coated with an ethanol solution containing Pd nanoparticles with an average size of 2.7 and 4.5 nm. A homogeneous distribution of the Pd nanoparticles on ZnO NWs has been obtained using both Pd particle series. The catalytic activity of the ZnO NWs and Pd/ZnO NWs catalysts was measured in the semihydrogenation of 2-methyl-3-butyn-2-ol at 303-343 K and a pressure of 2-10 bar. The effect of the solvent used on the catalytic performance of the Pd/ZnO NWs catalyst was studied. The Pd/ZnO catalysts showed alkene selectivity of up to 95% at an alkyne conversion of 99%. A kinetic model is proposed to explain the activity and selectivity of the ZnO support and Pd/ZnO catalysts.

SURFACE-ENHANCED RAMAN-SCATTERING STUDIES OF METALLOPORPHYRINS ON SILVER SOLS, MELLFS, AND ELECTRODES - EVIDENCE FOR REVERSIBLE PHOTOINDUCED DEMETALATION OF A SILVER(II) PORPHYRIN

A series of metalloporphyrins of the type M(TMPyP) (where M = Ag(II), Zn(II), Cu(II) and TMPyP = meso-tetrakis(4-N-methylpyridyl)porphyrin) have been investigated in solution and on the surface of silver sols, electrodes, and MELLFs (metal liquidlike films). Similar spectra were recorded on all three surfaces but significant differences in detailed behavior were found. In particular, a novel, reversible, and rapid photoinduced demetalation reaction has been observed for the AgII(TMPyP)/MELLF system. An apparently similar demetalation reaction for the same metalloporphyrin was observed on Ag electrodes but this reversed at a very much slower rate. No demetalation of Ag(II)(TMPyP) was observed with Ag sols nor with any of the other metalloporphyrins at any of the surfaces investigated. The implications of the findings in relation to the nature of the MELLF environment are briefly considered.

ON THE UNIVERSALITY OF 2-DIMENSIONAL DIFFUSION-LIMITED DEPOSITION

A history dependent stick probability is introduced to the diffusion-limited deposition model. The exponents in the scaling laws are calculated. The universality class is also discussed.

Bovine Serum Albumin Adsorption to Iron-Oxide Coated Sands Can Change Microsphere Deposition Mechanisms

Particulate colloids often occur together with proteins in sewage-impacted water. Using Bovine Serum Albumin (BSA) as a surrogate for protein in sewage, column experiments investigating the capacity of iron-oxide coated sands to remove latex microspheres from water revealed that microsphere attenuation mechanisms depended on antecedent BSA coverage. Dual pulse experiment (DPE) results suggested that where all BSA was adsorbed, subsequent multiple pore volume microsphere breakthrough curves reflected progressively reduced colloid deposition rates with increasing adsorbed BSA content. Modelling colloid responses suggested adsorption of 1 µg BSA generated the same response as blockage by between 7.1x108 and 2.3x109 deposited microspheres. By contrast, microsphere responses in DPEs where BSA coverage of the deposition sites approached/ reached saturation revealed the coated sand maintained a finite capacity to attenuate microspheres, even when incapable of further BSA adsorption. Subsequent microsphere breakthrough curves demonstrated the matrix’s colloid attenuation capacity progressively increased with continued microsphere deposition. Experimental findings suggested BSA adsorption on the sand surface approaching/ reaching saturation generated attractive deposition sites for colloids, which became progressively more attractive with further colloid deposition (filter ripening). Results demonstrate that adsorption of a single type of protein may either enhance or inhibit colloid mobility in saturated porous media.

Effect of glass substrate and deposition technique on the properties of sol gel TiO2 thin films

Na+ ions have a detrimental effect on the photocatalytic activity of thin sot gel films deposited on soda lime glass due to their diffusion into the film during the calcination process. Given that the content of sodium in glass substrate might be the crucial parameter in determining the activity of a photocatalyst, the aim of the present work was the comparison of the photoinduced properties of a thin TiO2 film prepared on three different glass substrates namely on quartz (Q) glass, borosilicate (BS) glass and soda lime (SL) glass which have different sodium content. The prepared layers were characterised by X-ray diffraction and UV-vis spectroscopy. The diffusion of Na+ from the substrate into the layers was determined by Glow Discharge Atomic Emission Spectroscopy. The photocatalytic activities of the films were assessed using two model pollutant test systems (resazurin/resorufin ink and stearic acid film), which appeared to correlate reasonably well. It was observed that TiO2 layer on SL glass has a brookite crystalline structure while the TiO2 layer on BS and Q glass has an anatase crystalline structure. On the other hand, the photodegradation of the model dye on TiO2 films deposited on Q and BS glass is about an order higher than on SL glass. The low sodium content of BS glass makes it the most suitable substrate for the deposition of photoactive sol gel TiO2 films. (C) 2011 Elsevier B.V. All rights reserved.

An Investigation into the Optimum Thickness of Titanium Dioxide Thin Films Synthesized by Using Atmospheric Pressure Chemical Vapour Deposition for Use in Photocatalytic Water Oxidation

Twenty eight films of titanium dioxide of varying thickness were synthesised by using atmospheric pressure chemical vapour deposition (CVD) of titanium(IV) chloride and ethyl acetate onto glass and titanium substrates. Fixed reaction conditions at a substrate temperature of 660 degrees C were used for all depositions, with varying deposition times of 5-60 seconds used to control the thickness of the samples. A sacrificial electron acceptor system composed of alkaline sodium persulfate was used to determine the rate at which these films could photo-oxidise water in the presence of 365 nm light. The results of this work showed that the optimum thickness for CVD films on titanium substrates for the purposes of water oxidation was approximate to 200 nm, and that a platinum coating on the reverse of such samples leads to a five-fold increase in the observed rate of water oxidation.

A novel reversible relative-humidity indicator ink based on methylene blue and urea

A new relative-humidity sensitive ink based on methylene blue and urea is described which can utilise the deliquescent nature of urea.

Reversible, fluorescence-based optical sensor for hydrogen peroxide

The preparation and characterisation are described of a robust, reversible, hydrogen peroxide optical sensor, based on the fluorescent quenching of the dye ion-pair [Ru(bpy)(3)(2+)(Ph4B-)(2)], by O-2 produced by the catalytic breakdown of H2O2, utilizing the inorganic catalyst RuO2 center dot xH(2)O. The main feature of this system is the one-pot formulation of a coating ink that, when dried, forms an active single-layer fluorescence-based H2O2 sensor, demonstrably capable of detecting H2O2 over the range of 0.01 to 1 M, with a relative standard deviation of ca. 4% and a calculated lower limit of detection of 0.1 mM. These sensors are sterilisable, using dry-heat, and stable when stored over 40 days, without exhibiting any loss in sensitivity or response characteristics.

Atmospheric Pressure Chemical Vapour Deposition of thin Films of Nb2O5 on Glass

A novel route involving atmospheric pressure chemical vapour deposition (APCVD) is reported for coating Nb2O5 onto glass substrates via the reaction of NbCl5 and ethyl acetate at 400-660degreesC. Raman spectroscopy is shown to be a simple diagnostic tool for the analysis of these thin films. The contact angle of water on Nb2O5-coated glass drops on UV irradiation from 60degrees to 5-20degrees. XPS Analysis showed that the Nb:O ratio of the film was 1:2.5. Glancing angle X-ray diffraction showed that all films were crystalline, with only a single phase being observed; this has some preferred orientation in the (201) plane of Nb2O5. The niobium(V) oxide materials show minimal photocatalytic ability to degrade organic material.

Anatase thin films on glass from the chemical vapor deposition of titanium(IV) chloride and ethyl acetate

Thin (50-500 nm) films of TiO2 may be deposited on glass substrates by the atmospheric pressure chemical vapor deposition (APCVD) reaction of TiCl4 with ethyl acetate at 400600 C. The TiO2 films are exclusively in the form of anatase, as established by Raman microscopy and glancing angle X-ray diffraction. X-ray photoelectron spectroscopy gave a 1:2 Ti:O ratio with Ti 2P(3/2) at 458.6 eV and O 1s is at 530.6 eV. The water droplet contact angle drops from 60degrees to

Atmospheric pressure chemical vapour deposition of titanium dioxide coatings on glass

Atmospheric pressure chemical vapour deposition of titanium dioxide coatings on glass substrates was achieved by the reaction of TiCl4 and a co-oxygen source (MeOH, EtOH, (PrOH)-Pr-i or H2O) at 500-650degreesC. The coatings show excellent uniformity, surface coverage and adherence. Growth rates were of the order of 0.3 mum min(-1) at 500degreesC. All films are crystalline and single phase with XRD showing the anatase TiO2 diffraction pattern; a = 3.78(1), c = 9.51(1) Angstrom. Optically, the films show minimal reflectivity from 300-1600 nm and 50-80% total transmission from 300-800 nm. Contact angles are in the range 20-40degrees for as-prepared films and 1-10degrees after 30 min irradiation at 254 nm. All of the films show significant photocatalyic activity as regards the destruction of an overlayer of stearic acid.

OXIDATION OF RUTHENIUM(II) TRIS(2,2'-BIPYRIDINE) IONS BY THALLIC IONS IN NITRIC-ACID, MEDIATED BY RUTHENIUM DIOXIDE HYDRATE - AN EXAMPLE OF REVERSIBLE HETEROGENEOUS REDOX CATALYSIS

The kinetics of the oxidation of Ru(bpy)32+ to Ru(bpy)33+ by T13+ ions, catalyzed by a dispersion of RuO2-xH2O in 3 mol dm-3 HNO3, are reported as a function of [Ru(bpy)32+], [Tl3+], [Tl+], [RuO2.xH2O], and temperature. The kinetics of Ru(bpy)32+ oxidation fit an electrochemical model of redox catalysis involving electron transfer between the two electrochemically reversible redox couples, i.e. Ru(bpy)33+/Ru(bpy)32+ and Tl3+/Tl+, mediated by the dispersion of microelectrode particles of RuO2.xH2O. In this model, the rate of reaction is assumed to be controlled by the diffusion of Ru(bpy)32+ toward, and Ru(bpy)33+ away from, the catalyst particles. The Arrhenius activation energy for the catalyzed reaction is 25.9 +/- 0.7 kJ mol-1, and the changes in enthalpy and entropy for the reaction are 36 +/- 2 kJ mol-1 and 127 +/- 6 J mol-1 K-1, respectively. This work describes a rare example of reversible heterogeneous redox catalysis.

A case study with a novel geometry for pulsed laser deposition

Aluminium thin films were deposited by a laser ablation technique from solid cylindrical targets rotated on a lead screw. Both smooth-surfaced targets and targets with screw threads cut into the area to he irradiated were used. The targets were irradiated with a focused circular spot size of 2.5 mm in diameter, at a power density equal to 5.4 +/- 0.2 x 10(8) W cm(-2). The polar distribution of the ablated atomic material was found to vary as a function of the target screw thread pitch, with the exponent n, in the polar distribution f(theta) = cos(n) theta, varying from 13.5 +/- 1.3 for no pitch to a minimum of 5 +/- 0.7 for a screw thread pitch of 0.2 mm. The use of such novel target geometries forms a possible basis for increasing thickness uniformity during the pulsed laser deposition of thin films.