Temperature-induced switching-over of the luminescence transitions in GaInNAs/GaAs quantum wells

Photoluminescence (PL) spectra of the GaInNAs/GaAs single quantum well (SQW) with different N compositions are carefully studied in a range of temperatures and excitation power densities. The anomalous S-shape temperature dependence of the PL peak is analysed based on the competition and switching-over between the peaks related to N-induced localized states and the peak related to interband excitonic recombination. It is found that with increasing N composition, the localized energy increases and the turning point of the S-shape temperature dependence occurs at higher temperature, where the localized carriers in the bandtail states obtain enough thermal activation energy to be dissociated and delocalized. The rapid thermal annealing (RTA) effectively reduces the localized energy and causes a decrease of the switching-over temperature.

Nonradiative recombination centers in Ga(As,N) and their annealing behavior studied by Raman spectroscopy

Nitrogen-related defects in diluted Ga(As,N) have been detected by Raman scattering in resonance with the localized E+ transition. These defects are attributed to local vibrational modes of nitrogen dimers on Ga- and As-lattice sites. Rapid thermal annealing under appropriate conditions is found to be able to remove the nitrogen dimers. The required minimum annealing temperature coincides with the threshold-like onset of strong, near-band-gap photoluminescence. This finding suggests that the nitrogen dimers are connected with nonradiative recombination centers. (C) 2004 American Institute of Physics.

Origin and evolution of photoluminescence from Si nanocrystals embedded in a SiO2 matrix

A detailed analysis of the photoluminescence (PL) from Si nanocrystals (NCs) embedded in a silicon-rich SiO2 matrix is reported. The PL spectra consist of three Gaussian bands (peaks A,B, and C), originated from the quantum confinement effect of Si NCs, the interface state effect between a Si NC and a SiO2 matrix, and the localized state transitions of amorphous Si clusters, respectively. The size and the surface chemistry of Si NCs are two major factors affecting the transition of the dominant PL origin from the quantum confinement effect to the interface state recombination. The larger the size of Si NCs and the higher the interface state density (in particular, Si = O bonds), the more beneficial for the interface state recombination process to surpass the quantum confinement process, in good agreement with Qin's prediction in Qin and Li [Phys. Rev. B 68, 85309 (2003)]. The realistic model of Si NCs embedded in a SiO2 matrix provides a firm theoretical support to explain the transition trend.

Thermal quenching of luminescence from buried and surface InGaAs self-assembled quantum dots with high sheet density

Variable-temperature photoluminescence (PL) spectra of Si-doped self-assembled InGaAs quantum dots (QDs) with and without GaAs cap layers were measured. Narrow and strong emission peak at 1075 nm and broad and weak peak at 1310 nm were observed for the buried and surface QDs at low temperature, respectively. As large as 210 meV redshift of the PL peak of the surface QDs with respect to that of the buried QDs is mainly due to the change of the strain around QDs before and after growth of the GaAs cap layer. Using the developed localized-state luminescence model, we quantitatively calculate the temperature dependence of PL peaks and integrated intensities of the two samples. The results reveal that there exists a large difference in microscopic mechanisms of PL thermal quenching between two samples. (c) 2005 American Institute of Physics.

Optical properties and exciton localization in GaNas/GaAs

GaNAs/GaAs single quantum wells (SQWs) and dilute GaNAs bulk grown by molecular beam epitaxy(MBE) were studied by photoluminescence (PL), selectively-excited PL, and time-resolved PL. Exciton localization and delocalization were investigated in detail. Under short pulse laser excitation, the delocalization exciton emission was revealed in GaNAs/GaAs SQWs. It exhibits quite different optical properties from N-related localized states. In dilute GaNAs bulk, a transition of alloy band related recombination was observed by measuring the PL dependence on temperature and excitation intensity and time-resolved PL, as well. This alloy-related transition presents intrinsic optical properties. These results are very important for realizing the abnomal features of III-V-N semiconductors.

Recombination kinetics of Te isoelectronic centers in ZnSTe

The recombination kinetics of Te isoelectronic centers in ZnS1-xTex (0.0065 less than or equal to x less than or equal to 0.85) alloys is studied by time-resolved photoluminescence (TRPL) at low temperature. The measured radiative recombination lifetimes of different Te bound exciton states are quite different, varying from a few nanoseconds to tens of nanosecond. As the bound exciton state evolves from a single Te impurity (Te-1) to larger Te clusters (Te-n, n=2,3,4), the recombination lifetime increases. It reaches maximum (similar to40 ns) for the Te-4 bound states at x=0.155. The increase of the exciton lifetime is attributed to the increasing exciton localization effect caused by larger localization potential. In the large Te composition range (x > 0.155), the exciton recombination lifetime decreases monotonically with Te composition. It is mainly due to the hybridization between the Te localized states and the host valence band states. The composition dependences of the exciton binding energy and the photoluminescence (PL) line width show the similar tendency that further support the localization picture obtained from the TRPL measurement. (C) 2005 American Institute of Physics.

Effects of the wave function localization in AlInGaN quaternary alloys

Using the first-principles band-structure method and the special quasirandom structures approach, the authors have investigated the band structure of random AlxInyGa1-x-yN quaternary alloys. They show that the wave functions of the band edge states are more localized on the InN sites. Consequently, the photoluminescence transition intensity in the alloy is higher than that in GaN. The valence band maximum state of the quaternary alloy is also higher than GaN with the same band gap, indicating that the alloy can be doped more easily as p-type. (c) 2007 American Institute of Physics.

Electroluminescence afterglow from indium tin oxide/Si-rich SiO2/p-Si structure

Indium tin oxide/Si-rich SiO2/p-Si structured devices are fabricated to study the electroluminescence (EL) of the Si-rich SiO2 (SRO) material. The obvious peaks at similar to 1050nm and similar to 1260nm in the EL are ascribed to localized state transitions of amorphous Si (alpha-Si) clusters. The EL afterglow associated with alpha-Si clusters is observed from this structure at room temperature, while the afterglow is absent in the case of optical pumping. It is believed that carrier-induced defects act as trap centres in the alpha-Si clusters, resulting in the EL afterglow. The phenomenon of the EL afterglow indicates the limits of EL performance and electrical modulation of the SRO material with a larger fraction of alpha-Si clusters.

A study of the growth and optical properties of AlInGaN alloys

We have studied the growth and optical properties of AlInGaN alloys in this article. By the measurement of three samples, we found that the incorporation of In decreases with the increase of temperature, while there is nearly no change for the incorporation of Al. The sample grown at the lowest temperature had the best material and optical properties, which owes to the high In component, because the In component can reduce defects and improve the material quality. We also used the time-resolved photoluminescence(PL) to study the mechanism of recombination of carriers, and found that the time dependence of PL intensity was not in exponential decay, but in stretched-exponential decay. Through the study of the character of this decay, we come to the conclusion that the emission comes from the recombination of localized excitons. Once more, this localization exhibites the character of quantum dots, and the stretched, exponential decay results from the hopping of carriers between different localized states. In addition, we have used the relation of emission energy dependence of carrier's lifetime and the character of radiative recombination and non-radiative combination to confirm our conclusion.

Photoluminescence of Mg-doped GaN grown by metalorganic chemical vapor deposition

Two Mg-doped GaN films with different doping concentrations were grown by a metalorganic chemical vapor deposition technique. Photoluminescence (PL) experiments were carried out to investigate the optical properties of these films. For highly Mg-doped GaN, the PL spectra at 10 K are composed of a blue luminescence (BL) band at 2.857 eV and two excitonic luminescence lines at 3.342 eV and 3.282 eV, in addition to a L2 phonon replica at 3.212 eV. The intensity of the L1 line decreases monotonously with an increase,in temperature. However, the intensity of the L2 line first slowly increases at first, and then decreases quickly with an increase in temperature. The two lines are attributed to bound excitonic emissions at extended defects. The BL band is most likely due to the transition from deep donor Mg-V-N complex to Mg shallow acceptor. From the temperature dependence of the luminescence peak intensity of the BL band, the activation energy of acceptor Mg was found to be 290 meV. (C) 2003 American Vacuum Society.

Structural and optical properties of InAlGaN films grown directly on low-temperature buffer layer with (0001)sapphire substrate

Quaternary InAlGaN film has been grown directly on top of low-temperature-deposited GaN buffer layer by low-pressure metalorganic vapor phase epitaxy. High-resolution X-ray diffraction and photoluminescence (PL) results show that the film has good crystal quality and optical property. Temperature-dependent PL and time-resolved PL (TRPL) have been employed to study the carriers recombination dynamics in the film. The TRPL signals can be well fitted as a stretched exponential function exp[-(t/tau)(beta)] from 14 to 250 K, indicating that the emission is attributed to the radiative recombination of excitons localized in disorder quantum nanostructures such as quantum disks originating from indium (In) clusters or In composition fluctuation. The cross-sectional high-resolution electron microscopy measurement further proves that there exist the disorder quantum nanostructures in the quaternary. By investigating the dependence of the exponential parameter beta on the temperature, it is shown that the multiple trapping-detrapping mechanism dominates the diffusion among the localized states. The localized states are considered to have two-dimensional density of states (DOS) at 250 K, since radiative recombination lifetime tau(r) increases linearly with increasing temperature. (C) 2002 Elsevier Science B.V. All rights reserved.

Anomalous temperature dependence of photoluminescence in GaInNAs/GaAs multiple quantum wells

Photoluminescence (PL) spectra of GaInNAs/GaAs multiple quantum wells grown on a GaAs substrate by molecular beam epitaxy are measured in a range of temperatures and excitation power densities. The energy position of the dominant PL peak shows an anomalous S-shape temperature dependence instead of the Varshni relation. By careful inspection, especially for the PL under lower excitation power density, two near bandedge peaks are well identified. These are assigned to carriers localized in nitrogen-induced bound states and interband excitonic recombinations, respectively. It is suggested that the temperature-induced switch of such two luminescence peaks in relative intensity causes a significant mechanism responsible for the S-shape shift observed in GaInNAs. A quantitative model based on the thermal depopulation of carriers is used to explain the temperature dependence of the PL peak related to N-induced bound states.

Temperature and pressure dependences of the Mn2+ and donor-acceptor emissions in ZnS : Mn2+ nanoparticles

Temperature and pressure dependent measurements have been performed on 3.5 nm ZnS:Mn2+ nanoparticles. As temperature increases, the donor-acceptor (DA) emission of ZnS:Mn2+ nanoparticles at 440 nm shifts to longer wavelengths while the Mn2+ emission (T-4(1)-(6)A(1)) shifts to shorter wavelengths. Both the DA and Mn2+ emission intensities decrease with temperature with the intensity decrease of the DA emission being much more pronounced. The intensity decreases are fit well with the theory of thermal quenching. As pressure increases, the Mn2+ emission shifts to longer wavelengths while the DA emission wavelength remains almost constant. The pressure coefficient of the DA emission in ZnS:Mn2+ nanoparticles is approximately -3.2 meV/GPa, which is significantly smaller than that measured for bulk materials. The relatively weak pressure dependence of the DA emission is attributed to the increase of the binding energies and the localization of the defect wave functions in nanoparticles. The pressure coefficient of Mn2+ emission in ZnS:Mn2+ nanoparticles is roughly -34.3 meV/GPa, consistent with crystal field theory. The results indicate that the energy transfer from the ZnS host to Mn2+ ions is mainly from the recombination of carriers localized at Mn2+ ions. (C) 2002 American Institute of Physics.

Photoluminescence of Te isoelectronic traps in ZnSeTe/ZnSe quantum wells under hydrostatic pressure

The photoluminescence (PL) of ZnSe0.92TeD0.08/ZnSe superlattice quantum wells at 77K under hydrostatic pressure up to 7.8 GPa was studied. Strong PL peaks from excitons trapped in isoelectronic traps in ZnSe0.92Te0.08 were observed. It was found that the pressure coefficients of the PL, peaks from Te traps are about half of that of ZnSe. It demonstrates the localized characteristic of the potential of Te isoelectronic. traps. The excitons transition between Te traps in ZnSe1 Te-- x(x) and (CdSe)(1) /(ZnSe)(3) superlattice was also investigated.

Exciton localization in In0.15Ga0.85As/GaAs quantum wire structures grown on (553)B-oriented GaAs substrate

Using time-resolved photoluminescence (PL) measurements, we have studied the exciton localization effect in InGaAs/GaAs quantum wire (QWR) structures formed in corrugated narrow InGaAs/GaAs quantum wells (QWs) grown on (553)B GaAs substrate. The PL decay time in the QWR structure was found to be independent of the temperature for T < 70 K, showing a typical dynamical behavior of the localized excitons. This result is in striking contrast to the corresponding quantum well structures, where a linear increase of the PL decay time was observed. In addition, an increase of the exciton lifetime was observed at low temperature for the QWR structure as compared to a reference InGaAs/GaAs quantum well sample (1200 vs 400 ps). The observed longer decay time was attributed to the reduction in the spatial coherence of excitons in the QWR-like structure. In PL measurements, a significant polarization anisotropy was also found in our narrow InGaAs/GaAs QWs grown on (553)B GaAs. (C) 2001 American Institute of Physics.