Synthesis of titanate nanostructures using amorphous precursor material and their adsorption/photocatalytic properties

This article reports on a new and swift hydrothermal chemical route to prepare titanate nanostructures (TNS) avoiding the use of crystalline TiO2 as starting material. The synthesis approach uses a commercial solution of TiCl3 as titanium source to prepare an amorphous precursor, circumventing the use of hazardous chemical compounds. The influence of the reaction temperature and dwell autoclave time on the structure and morphology of the synthesised materials was studied. Homogeneous titanate nanotubes with a high length/diameter aspect ratio were synthesised at 160 degrees C and 24 h. A band gap of 3.06 +/- 0.03 eV was determined for the TNS samples prepared in these experimental conditions. This value is red shifted by 0.14 eV compared to the band gap value usually reported for the TiO2 anatase. Moreover, such samples show better adsorption capacity and photocatalytic performance on the dye rhodamine 6G (R6G) photodegradation process than TiO2 nanoparticles. A 98% reduction of the R6G concentration was achieved after 45 min of irradiation of a 10 ppm dye aqueous solution and 1 g L-1 of TNS catalyst.

Quantificação de polifosfatos no bacalhau. Validação de um método de análise

O bacalhau (Gadus morhua) faz parte da dieta alimentar dos portugueses há vários séculos, sendo atualmente, um dos maiores consumidores deste peixe a nível mundial. Após o processo de salga, esta espécie possui características únicas como a consistência, cheiro, paladar e cor amarela. É precisamente devido à coloração do peixe que alguns produtores da Islândia, Noruega e Dinamarca requisitaram às autoridades da União Europeia (UE) a aprovação da utilização de polifosfatos no processo de salga húmida do bacalhau. Os polifosfatos são aditivos alimentares bastante usados no processamento do pescado pois previnem a oxidação dos lípidos e proteínas do músculo do bacalhau, evitando assim a indesejada mudança de cor do peixe. Apesar dos esforços da Associação dos Industriais do Bacalhau (AIB) e do governo português para a rejeição da proposta nórdica, tal não se verificou. Deste modo, no início do próximo ano já será possível a venda na UE de bacalhau com fosfatos. A quantificação do teor de fosfatos no bacalhau é geralmente efetuada por Espetrofotometria de absorção molecular no ultravioleta-visível (UV-Visível). Esta quantificação é baseada no método de determinação do fósforo total, através da hidrólise dos fosfatos a ortofosfatos com posterior medição da cor amarela, gerada pela reação destes com uma solução de molibdato-vanadato. O objetivo desta dissertação foi a validação de um método de análise para a quantificação dos polifosfatos no bacalhau. O método validado foi o descrito na norma NP 4495 para produtos de pesca e aquicultura. O desenvolvimento deste trabalho foi realizado em laboratório acreditado para águas e produtos alimentares (Equilibrium - Laboratório de Controlo de Qualidade e de Processos Lda, L0312). Foi ainda determinada a influência do teor de cloreto de sódio na quantificação dos polifosfatos e o teor de humidade, uma vez que este pode afetar o produto durante a sua comercialização. No processo de validação do método foram estudados diversos parâmetros, tais como a seletividade, linearidade, sensibilidade, limite de quantificação e precisão. Pela análise dos resultados obtidos conclui-se que o método para determinação de fosfatos no bacalhau se encontra validado, uma vez que satisfaz todas as especificações determinadas para cada parâmetro de validação avaliado.

Performance of concrete made with aggregates recycled from precasting industry waste: influence of the crushing process

The aim of this paper is to evaluate the influence of the crushing process used to obtain recycled concrete aggregates on the performance of concrete made with those aggregates. Two crushing methods were considered: primary crushing, using a jaw crusher, and primary plus secondary crushing (PSC), using a jaw crusher followed by a hammer mill. Besides natural aggregates (NA), these two processes were also used to crush three types of concrete made in laboratory (L20, L45 e L65) and three more others from the precast industry (P20, P45 e P65). The coarse natural aggregates were totally replaced by coarse recycled concrete aggregates. The recycled aggregates concrete mixes were compared with reference concrete mixes made using only NA, and the following properties related to the mechanical and durability performance were tested: compressive strength; splitting tensile strength; modulus of elasticity; carbonation resistance; chloride penetration resistance; water absorption by capillarity; water absorption by immersion; and shrinkage. The results show that the PSC process leads to better performances, especially in the durability properties.

Antibacterial activity of Ionic Liquids based on ampicillin against resistant bacteria

Antibacterial activity of novel Active Pharmaceutical Ingredient Ionic Liquids (API-ILs) based on ampicillin anion [Amp] have been evaluated. They showed growth inhibition and bactericidal properties on some sensitive bacteria and especially some Gram-negative resistant bacteria when compared to the [Na][Amp] and the initial bromide and chloride salts. For these studies were analysed the minimum inhibitory concentration (MIC) and minimum bactericidal concentration (MBIC) against sensitive Gram-negative bacteria Escherichia coli ATCC 25922 and Klebsiella pneumonia (clinically isolated), as well as sensitive Gram positive S. Aureus ATCC 25923, Staphylococcus epidermidis and Enterococcus faecalis and completed using clinically isolated resistent strains: E. coli TEM CTX M9, E. coli CTX M2 and E. coli AmpC Mox. From the obtained MIC values of studied APIs-ILs and standard [Na][Amp] were derived RDIC values (relative decrease of inhibitory concentration). High RDIC values of [C16Pyr][Amp] especially against two resistant Gram-negative strains E. coli TEM CTX M9 (RDIC>1000) and E. coli CTX M2 (RDIC>100) point clearly to a potential promising role of APIs-ILs as antimicrobial drugs especially against resistant bacterial strains.

Antimicrobial resistance and plasmid detection in strains of the Bacteroides fragilis group

Resistant populations of the Bacteroides fragilis group bacteria (two reference ones and two isolated from human and Callithrix penicillata marmoset) were obtained by the gradient plate technique, to clindamycin, penicillin G, metronidazole and mercuric chloride. All the four tested strains were originaly susceptible to the four antimicrobial drugs at the breakpoint used in this study. MICs determination for the four cultures gave constant values for each antimicrobial, on the several steps by the gradient plate technique. The intestinal human B. fragilis strains showed three DNA bands, that could be representative of only two plasmids in the closed covalently circular (CCC) form with molecular weights of approximately 25 and 2.5 Md. The results do not permit an association between the presence of plasmid in the human strain with the susceptibility to the studied drugs. The four strains were ß-lactamase negative in the two methods used, and no particular chromosomal genetic resistance marker was demonstred. The resistance (MIC) observed, after contact with penicillin G and mercuric chloride, were two-fold in the four tested strains

Durability performance of self-compacting concrete (SCC) with binary and ternary mixes of fly ash and limestone filler

The basic objective of this work is to evaluate the durability of self-compacting concrete (SCC) produced in binary and ternary mixes using fly ash (FA) and limestone filler (LF) as partial replacement of cement. The main characteristics that set SCC apart from conventional concrete (fundamentally its fresh state behaviour) essentially depend on the greater or lesser content of various constituents, namely: greater mortar volume (more ultrafine material in the form of cement and mineral additions); proper control of the maximum size of the coarse aggregate; use of admixtures such as superplasticizers. Significant amounts of mineral additions are thus incorporated to partially replace cement, in order to improve the workability of the concrete. These mineral additions necessarily affect the concrete’s microstructure and its durability. Therefore, notwithstanding the many well-documented and acknowledged advantages of SCC, a better understanding its behaviour is still required, in particular when its composition includes significant amounts of mineral additions. An ambitious working plan was devised: first, the SCC’s microstructure was studied and characterized and afterwards the main transport and degradation mechanisms of the SCC produced were studied and characterized by means of SEM image analysis, chloride migration, electrical resistivity, and carbonation tests. It was then possible to draw conclusions about the SCC’s durability. The properties studied are strongly affected by the type and content of the additions. Also, the use of ternary mixes proved to be extremely favourable, confirming the expected beneficial effect of the synergy between LF and FA. © 2015 RILEM.

Spent coffee grounds for biodiesel production and other applications

This work evaluates the possibility of using spent coffee grounds (SCG) for biodiesel production and other applications. An experimental study was conducted with different solvents showing that lipid content up to 6 wt% can be obtained from SCG. Results also show that besides biodiesel production, SCG can be used as fertilizer as it is rich in nitrogen, and as solid fuel with higher heating value (HHV) equivalent to some agriculture and wood residues. The extracted lipids were characterized for their properties of acid value, density at 15 °C, viscosity at 40 °C, iodine number, and HHV, which are negatively influenced by water content and solvents used in lipid extraction. Results suggest that for lipids with high free fatty acids (FFA), the best procedure for conversion to biodiesel would be a two-step process of acid esterification followed by alkaline transesterification, instead of a sole step of direct transesterification with acid catalyst. Biodiesel was characterized for its properties of iodine number, acid value, and ester content. Although these quality parameters were not within the limits of NP EN 14214:2009 standard, SCG lipids can be used for biodiesel, blended with higher-quality vegetable oils before transesterification, or the biodiesel produced from SCG can be blended with higher-quality biodiesel or even with fossil diesel, in order to meet the standard requirements.

Desenvolvimento de métodos de análise físico-química em águas usando um analisador multiparamétrico AQUAKEM

Trabalho Final de mestrado para obtenção do grau de Mestre em Engenharia Química e Biológica

Influence of the crushing process of recycled aggregates on concrete properties

This work intends to evaluate the (mechanical and durability) performance of concrete made with coarse recycled concrete aggregates (CRCA) obtained using two crushing processes: primary crushing (PC) and primary plus secondary crushing (PSC). This analysis intends to select the most efficient production process of recycled aggregates (RA). The RA used here resulted from precast products (P), with strength classes of 20 MPa, 45 MPa and 65 MPa, and from laboratory-made concrete (L) with the same compressive strengths. The evaluation of concrete was made with the following tests: compressive strength; splitting tensile strength; modulus of elasticity; carbona-tion resistance; chloride penetration resistance; capillary water absorption; and water absorption by immersion. These findings contribute to a solid and innovative basis that allows the precasting industry to use without restrictions the waste it generates. © (2015) Trans Tech Publications, Switzerland.

Performance of concrete made with recycled aggregates from Portuguese CDW recycling plants

The objective of this research is the production of concrete with recycled aggregates (RA) from various CDW plants around Portugal. The influence of the RA collection location and consequently of their composition on the characteristics of the concrete produced was analysed. In the mixes produced in this research RA from five plants (Valnor, Vimajas, Ambilei, Europontal and Retria) were used: in three of them coarse and fine RA were analysed and in the remaining ones only coarse RA were used. The experimental campaign comprised two tests in fresh concrete (cone of Abrams slump and density) and eight in hardened concrete (compressive strength in cubes and cylinders, splitting tensile strength, modulus of elasticity, water absorption by immersion and capillarity, carbonation and chloride penetration resistance). It was found that the use of RA causes a quality decrease in concrete. However, there was a wide results scatter according to the plant where the RAs were collected, because of the variation in composition of the RA. It was also found that the use of fine RA causes a more significant performance loss of the concrete properties analysed than the use of coarse RA. © (2015) Trans Tech Publications, Switzerland.

Phase behaviour of alternative solvents

Dissertation presented to obtain the Ph.D. degree in Chemistry (Physical Chemistry) at the Instituto de Tecnologia Química e Biológica da Universidade Nova de Lisboa

Conservantes em Formulações de Cloreto de Sódio 0,9% para Aplicação Tópica em Pediatria

As formulações de cloreto de sódio 0,9%, são na sua grande maioria utilizadas com bastante frequência sobretudo na população pediátrica. Tanto os cuidadores como os próprios profissionais de saúde as reconhecem e avaliam como um componente essencial para os cuidados de saúde desta população. No entanto, o grave problema destas formulações reside no facto de muitos dos consumidores após a sua utilização apresentarem reacções adversas, que não são justificáveis se apenas da composição da formulação fizerem parte água purificada e cloreto de sódio. Assim deve ser tida em conta a composição de cada apresentação farmacêutica, a fim de se averiguar quanto à presença de conservantes potencialmente perigosos e para deste modo alertar os possíveis consumidores destes produtos. O principal objectivo deste estudo foi a análise e avaliação da rotulagem e folheto de instruções das formulações de cloreto de sódio 0,9% para aplicação tópica em pediatria, a fim de se averiguar a utilização de conservantes na sua formulação e por conseguinte a sua conformidade para comercialização. Com o auxílio de uma check-list, foram avaliadas 34 apresentações de venda livre de formulações de cloreto de sódio 0,9% para aplicação tópica, no período de Janeiro a Março de 2014. Das 34 apresentações farmacêuticas analisadas, apenas uma dasapresentações não se encontrava descrita como dispositivo médico, mas sim como produto cosmético. Contudo quanto à marcação CE de conformidade, esta encontrava-se devidamente aposta em 94% das apresentações. No que às indicações terapêuticas diz respeito e como seria expectável, na sua maioria estas apresentações destinam-se em 51% dos casos para utilização nasal e em 33% dos casos para utilização oftálmica, sendo o modo de apresentação em gotas (88%) o mais encontrado para comercialização. Quanto à utilização de conservantes, constatou-se uma grande omissão e alguma imprecisão quanto às informações contidas na rotulagem e/ou folheto de instruções das formulações analisadas, expondo assim os indivíduos mais susceptíveis e em especial a população pediátrica ao risco de reacções adversas e que por vezes podem ser fatais. Por outro lado também podem ocorrer complicações aquando do uso inadvertido destasformulações com conservantes, por portadores de lentes de contacto ou sem a devida esterilidade para utilização oftálmica. Assim apesar de o soro fisiológico não ser considerado um medicamento, mas sim um dispositivo médico, deve ser contudo utilizado com algumas precauções, sobretudo nesta população pediátrica e sempre que possível aconselhado por um profissional treinado e consciente da problemática que os conservantes usados nestas formulações podem causar quando utilizados indevidamente.

Ligação Adesiva de Polímeros Particularmente Difíceis de Colar

As ligações adesivas têm sido cada vez mais utilizadas nos últimos anos em detrimento de outros métodos tais como a soldadura, ligações aparafusadas e ligações rebitadas. Os plásticos de Engenharia têm um papel cada vez mais preponderante na indústria, devido às suas excelentes propriedades. Neste trabalho foram considerados três polímeros diferentes, o Policloreto de Vinilo (PVC) e o Polipropileno (PP) dado o seu baixo custo e peso e a superfície quimicamente inerte e o Politetrafluoretileno (PTFE) devido às suas boas propriedades químicas e excelentes propriedades de deslizamento. No entanto, estes materiais possuem uma baixa energia de superfície e, por isso, são muito difíceis de colar com mais relevância para o PTFE. Assim, após um estudo preliminar foi escolhido, para realizar as colagens necessárias, um adesivo da Tamarron Technology “Tam Tech Adhesive”, próprio para este tipo de substratos difíceis de colar. Posteriormente foi efetuada a sua caraterização através de ensaios de provetes maciços à tração. O principal objetivo deste trabalho foi estudar juntas de sobreposição simples de materiais poliméricos difíceis de colar tais como o PTFE, PP e PVC com recurso a um adesivo que não necessitasse de preparação de superfície. Foram fabricadas juntas de sobreposição simples (JSS) segundo os métodos Lap Shear (LS) e Block Shear (BS) dos três materiais referidos anteriormente e realizados os respetivos ensaios para avaliar o comportamento mecânico das ligações adesivas. Os materiais utilizados como substratos foram também submetidos a ensaios de tração com a finalidade de obter o módulo de elasticidade e as suas propriedades de resistência. Os substratos envolvidos nas juntas adesivas não sofreram qualquer preparação especial das superfícies. Na maioria dos casos consistiu apenas numa limpeza das superfícies com álcool etílico. Contudo, para o PTFE também se experimentou a preparação por abrasão com lixa e por chama. Foi também efetuado um trabalho de simulação numérica por elementos finitos utilizando um modelo de dano coesivo triangular. As resistências ao corte obtidas são superiores em BS comparativamente a LS, exceção feita aos substratos de PTFE aonde os resultados são similares. O tratamento por chama melhorou a resistência mecânica das juntas. Verificou-se também que o modelo numérico simulou adequadamente o comportamento das juntas principalmente das LS.

Effects of ivermectin on Culex quinquefasciatus larvae

The effects of ivermectin, a semi-synthetic drug widely used for treatment of livestock parasitic diseases, were observed on Culex quinquefasciatus larvae. Toxic effects and mortality evaluation were carried out after 5, 15, 30 and 60 minutes of exposure to 1, 5 or 10 ppm of ivermectin solutions. Observations were made 24 and 48 hours after the beginning of the experiment, and loss of mobility, progressive paralysis and high mortality of larvae were recorded. The observed effects of ivermectin on the mosquito larvae is probably correlated with chloride channel activation on cell membranes.

Recovery of acid and base from brackish water by bipolar membrane electrodialysis

Nesta dissertação pretendeu-se estudar a viabilidade do uso de eletrodiálise com membranas bipolares (BM) na recuperação de ácido clorídrico e de hidróxido de sódio a partir de um efluente industrial que contém 1.4 mol/L de cloreto de sódio. Estas membranas mostraram ser uma ferramenta eficiente para a produção de ácidos e bases a partir do respetivo sal. Foi feita uma seleção de diferentes membranas bipolares (Neosepta, Fumatech e PCA) e aniónicas (PC-SA e PC-ACID 60) na tentativa de encontrar a combinação mais adequada para o tratamento do efluente. Dependendo do critério, o melhor arranjo de membranas é o uso de PC-ACID 60 (membrana aniónica), PC-SK (membrana catiónica) e membranas bipolares do tipo Neosepta para maior pureza dos produtos; membranas bipolares Fumatech para maior eficiência de dessalinização e membranas bipolares PCA para um maior grau de dessalinização. Tecnologicamente foi possível obter uma dessalinização de 99.8% em quatro horas de funcionamento em modo batch com recirculação de todas as correntes. Independentemente da combinação usada é recomendável que o processo seja parado quando a densidade de corrente deixa de ser máxima, 781 A/m2. Assim é possível evitar o aumento de impurezas nos produtos, contra difusão, descida instantânea do pH e uma dessalinização pouco eficiente. A nível piloto o principal fornecedor de membranas e unidade de tratamento “stack” é a marca alemã PCA. Sendo assim realizaram-se ensaios de repetibilidade, contra difusão, avaliação económica e upscaling utilizando as membranas bipolares PCA. A nível económico estudou-se o uso de dois tipos de unidades de tratamento; EDQ 380 e EDQ 1600, para diferentes níveis de dessalinização (50, 75 e 80%). Tendo em conta a otimização económica, é recomendável uma dessalinização máxima de 80%, uma vez que a eficiência de processo a este ponto é de 40%. A aplicação do método com a unidade EDQ 1600 para uma dessalinização de 50% é a mais vantajosa economicamente, com custos de 16 €/m3 de efluente tratado ou 0,78 €/kg Cl- removido. O número de unidades necessárias é 4 posicionados em série.