The purpose of this study was to assess color alteration of the paints used for iris painting in artificial eyes. Five disks of heat cured acrylic resin were confectioned by microwave energy for each paint analyzed, in a total of 40 specimens. Each specimen consisted of a colorless acrylic resin disk and another of equal size, of scleral white colored acrylic resin, with the painting interposed between the two disks. The specimens were submitted to an accelerated aging process in a chamber under ultraviolet radiation for 1,008 hours. To assess color variation, a reflective spectrophotometer was used. The results were statistically analyzed by ANOVA and the Tukey test (p < 0.05). All the paints underwent chromatic alteration. The oil paint presented the highest resistance to accelerated aging.

Microhardness of glass ionomer cements indicated for the ART technique according to surface protection treatment and storage time

The aim of this study was to assess the microhardness of 5 glass ionomer cements (GIC) - Vidrion R (V, SS White), Fuji IX (F, GC Corp.), Magic Glass ART (MG, Vigodent), Maxxion R (MR, FGM) and ChemFlex (CF, Dentsply) - in the presence or absence of a surface protection treatment, and after different storage periods. For each GIC, 36 test specimens were made, divided into 3 groups according to the surface protection treatment applied - no protection, varnish or nail varnish. The specimens were stored in distilled water for 24 h, 7 and 30 days and the microhardness tests were performed at these times. The data obtained were submitted to the ANOVA for repeated measures and Tukey tests (α = 5%). The results revealed that the mean microhardness values of the GICs were, in decreasing order, as follows: F > CF = MR > MG > V; that surface protection was significant for MR, at 24 h, without protection (64.2 ± 3.6a), protected with GIC varnish (59.6 ± 3.4b) and protected with nail varnish (62.7 ± 2.8ab); for F, at 7 days, without protection (97.8 ± 3.7ab), protected with varnish (95.9 ± 3.2b) and protected with nail varnish (100.8 ± 3.4a); and at 30 days, for F, without protection (98.8 ± 2.6b), protected with varnish (103.3 ± 4.4a) and protected with nail varnish (101 ± 4.1ab) and, for V, without protection (46 ± 1.3b), protected with varnish (49.6 ± 1.7ab) and protected with nail varnish (51.1 ± 2.6a). The increase in storage time produced an increase in microhardness. It was concluded that the different GICs, surface protection treatments and storage times could alter the microhardness values.

Analytical model for heterogeneous crystallization kinetics of spherical glass particles

An analytical model developed to describe the crystallization kinetics of spherical glass particles has been derived in this work. A continuous phase transition from three-dimensional (3D)-like to 1D-like crystal growth has been considered and a procedure for the quantitative evaluation of the critical time for this 3D-1D transition is proposed. This model also allows straightforward determination of the density of surface nucleation sites on glass powders using differential scanning calorimetry data obtained under different thermal conditions. © 2009 The American Ceramic Society.

Color stability after accelerated aging of two silicones, pigmented or not, for use in facial prostheses

One of the greatest challenges faced by buccomaxillofacial prosthetists is to reproduce the patient's exact skin color and provide adequate esthetics. To reach this objective, professionals must use materials with easy characterization and that maintain color over long periods of time. The objective of this study was, thus, to evaluate the color stability of two types of silicones, Silastic 732 and Silastic MDX4-4210. Twenty-four test specimens were made from each type of silicone and were divided into a colorless group and groups intrinsically pigmented with ceramics, cosmetics or iron oxide. The specimens were submitted to an accelerated system of aging for non-metallic materials. Readings were carried out initially and after periods corresponding to 163, 351, 692 and 1,000 hours of aging, using a reflection spectrophotometer analysis, and color alterations were calculated by the CIE L*a*b* system. The data were submitted to variance analysis and Tukey's test at a 5% level of probability. The results demonstrated that, irrespective of the period of time analyzed, all the materials underwent some type of chromatic alteration (ΔE > 0). The test specimens made with Silastic 732 and MDX4-4210, without pigmentation, presented the lowest color alteration values after 1,000 hours of aging. Of the pigments, ceramic presented the lowest color alteration values and cosmetic powder presented the highest values. Thus, it may be concluded that the materials without the incorporation of pigments presented similar color alteration values, and did not differ statistically. The cosmetic powder used in this study was the pigment that most altered the color of the test specimens. © 2009 Sociedade Brasileira de Pesquisa Odontológica.

Effect of accelerated aging on the microhardness and color stability of flexible resins for dentures

Acrylic resins have been widely used due to their acceptable esthetics and desirable characteristics such as easy handling, good thermal conductivity, low permeability to oral fluids and color stability. Flexible resins were introduced on the market as an alternative to the use of conventional acrylic resins in the construction of complete and partial removable dentures. Although these resins present advantages in terms of esthetics and comfort, studies assessing chromatic and microhardness alterations of these materials are still scarce in the related literature. The aim of this study was to evaluate the chromatic and microhardness alterations of two commercial brands of flexible resins in comparison to the conventional resin Triplex when submitted to accelerated aging. The resins were manipulated according to manufacturers' instructions and inserted into a silicone matrix to obtain 21 specimens divided into 3 groups: Triplex, Ppflex and Valplast. Triplex presented the highest microhardness value (p < 0.05) for all the aging periods, which was significantly different from that of the other resins, followed by the values of Valplast and Ppflex. Comparison between the flexible resins (Ppflex and Valplast) revealed a statistically significant difference (p < 0.05) as regards color. The flexible resin Ppflex and the conventional resin Triplex presented no statistically significant difference (p < 0.05) as regards aging. The accelerated aging significantly increased the microhardness values of the resins, with the highest values being observed for Triplex. Valplast presented the greatest chromatic alteration after accelerated aging.

In vitro surface roughness of different glass ionomer cements indicated for ART restorations

Aim: The aim of this in vitro study was to evaluate the surface roughness of three glass ionomer cements (GICs) indicated for ART restorations. Methods: Ten cylindrical specimens of three commercial glass ionomers cements (Vidrion R - S.S. White, Maxxion R - FGM and Vitromolar DFL) were prepared (n=30) without surface finishing or protection. Twenty-four hours after preparation, the surface roughness measurements were obtained as the mean of three readings of the surface of each specimen by profilometry. The roughness values (Ra, μm) were subjected to one-way ANOVA and Tukey's test (p<0.05). Results: No statistically significant differences were observed between Vidrion R (0.18 ± 0.05) and Vitromolar (0.21 ± 0.05), whereas Maxxion R presented significantly higher roughness values than those of the other materials. Conclusions: It may be concluded that characteristics of particle size and composition of the different GICs affected their surface roughness 24 h after preparation.