Cu原子簇触发形核下的深过冷Ag-Ge合金组织演变研究

采用玻璃包覆的方法获得具有较大过冷度的亚共晶、共晶以及过共晶Ag-Ge合金熔体，并通过高能离子束轰击Cu箔产生Cu原子团簇溅射到过冷合金熔体中来触发非均质形核过程。凝固后合金显微组织的分析结果表明：在深过冷合金熔体中引入Cu原子团簇，它对亚共晶、共晶以及过共晶Ag-Ge合金的显微组织演变有着不同的影响效果，分析了显微组织的演变规律与形成机制。

Investigation of Mn-Implanted n-Type Ge

Mn+ irons were implanted to n-type Ge(1 1 1) single crystal at room temperature with an energy of 100 keV and a dose of 3 x 10(16) cm(-2). Subsequently annealing was performed at 400degreesC for 1 h under flowing nitrogen gas. X-ray diffraction measurements show that as-implanted sample is amorphous and the structure of crystal is restored after annealing. Polycrystalline germanium is formed in annealed sample. There are no new phases found except germanium. The samples surface morphologies indicate that annealed sample has island-like feature while there is no such kind of characteristic in as-implanted sample. The elemental composition of annealed sample was analyzed by Auger electron spectroscopy. It shows that manganese ions are deeply implanted into germanium substrate and the highest manganese atomic concentration is 8% at the depth of 120 nm. The magnetic properties of samples were investigated by an alternating gradient magnetometer. The annealed sample shows ferromagnetic behavior at room temperature.

Magnetic Properties of Mn-Implanted n-Type Ge

Mn+ ions were implanted into n-type Ge(111) single crystal at room temperature at an energy of 100 keV with a dose of 3 x 1016 cm-2. Subsequent annealing was performed on the samples at 400 °C and 600 °C in a flowing nitrogen atmosphere. The magnetic properties of the samples have been investigated by alternating gradient magnetometer at room temperature. The compositional properties of the annealed samples were studied by Auger electron spectroscopy and the structural properties were analyzed by X-ray diffraction measurements. Magnetization measurements reveal room-temperature ferromagnetism for the annealed samples. The magnetic analysis supported by compositional and structural properties indicates that forming the diluted magnetic semiconductor (DMS) MnxGe1-x after annealing may account for the ferromagnetic behavior in the annealed samples.

在强激光下Ge平行板的动态F-P干涉效应

实验表明,在连续CO_2激光辐照下,Ge平行板透射光强度随时间呈准周期性的变化。基于平行平面板的多光束干涉理论,并考虑激光引起的温升对Ge片折射率和厚度的影响,得到的计算结果与实验相符合。这说明平行平面Ge在高功率连续CO_2激光作用下因折射率和厚度随温度的变化而具有一种动态的法布里-珀罗干涉效应。

52m长落管Ag-Ge合金的微重力凝固行为

利用52m长落管装置进行了Ag-15%Ge(质量分数)亚共晶和Ag-21%Ge(质量分数)过共晶合金微重力试验,分析了凝固后合金球体的显微组织,并和常规凝固条件下的同成分合金组织进行了比较.结果表明,落管实验能使合金获得较大的过冷度,使Ag-15%Ge(质量分数)亚共晶合金Ag初生固溶体相明显细化,枝晶特征消失并转变为细小不规则块状或近似球形;使Ag-21%Ge(质量分数)过共晶合金中Ge初生相组织细化、数量增多,但并不改变小平面晶体Ge相的侧面生长机制.

Mn注入n型Ge单晶的特性研究

采用离子能量为100keV,剂量为3×1016cm-2的离子注入技术,室温下往n型Ge(111)单晶衬底注入Mn+离子,注入后的样品进行400℃热处理。利用X-射线衍射法(XRD)和原子力显微镜(AFM)对注入后的样品进行了结构和形貌分析,俄歇电子能谱法(AES)进行了组分分析,交变梯度样品磁强计(AGM)进行了室温磁性测量。结果表明原位注入样品的结构是非晶的,热处理后发生晶化现象。没有在样品中观察到新相形成。Mn离子较深的注入进Ge衬底,在120nm处Mn原子百分比浓度达到最高为8%。热处理后的样品表现出了室温铁磁特性。

Photoinduced effects in amorphous Ge-Se films

With light illumination from an Ar ion laser, the photoinduced changes in vacuum evaporated amorphous GeSe2 films; were investigated with the X-ray diffraction (XRD), infrared absorption (IR), scanning electron microscope (SEM), transmitting electron microscope (TEM) and transmittance spectra analysis. It was observed that the optical transmittance edges of films shifted to shorter wavelength according to annealing and light illumination and the shift in well-annealed films could be recovered by annealing at 200 degrees C for 1 h in Ar air. The magnitude of shift increased with the increase of the intensity of illumination light and the illumination time. By sides, photoinduced crystallization was also observed in the exposed regions of GeSe2 films and more of it was observed with stronger intensity of illumination light.

Femtosecond optical Kerr effect study of Ge(10)AS(40)S(30)Se(20) film

The results of the femtosecond optical heterodyne detection of optical Kerr effect at 805 nm with the 80 fs ultrafast pulses in amorphous Ge10As40S30Se20 film is reported in this paper. The film shows an optical non-linear response of: 200 fs under ultrafast 80 fs-pulse excitation and the values of real and imaginary parts of non-linear susceptibility chi((3)) were 9.0 X 10(-12) and -4.0 X 10(-12) esu, respectively. The large third-order non-linearity and ultrafast response are attributed to the ultrafast distortion of the electron orbits surrounding the average positions of the nucleus of Ge, As, S and Se atoms. This Ge10As40S30Se20 chalcogenide glass would be expected as a promising material for optical switching technique. (c) 2005 Elsevier Ltd. All rights reserved.

Structural change of laser-irradiated Ge2Sb2Te5 films studied by electrical property measurement

Sheet resistance of laser-irradiated Ge2Sb2Te5 thin films prepared by magnetron sputtering was measured by the four-point probe method. With increasing laser power the sheet resistance undergoes an abrupt drop from 10(7) to 10(3) Omega/square at about 580 mW. The abrupt drop in resistance is due to the structural change from amorphous to crystalline state as revealed by X-ray diffraction (XRD) study of the samples around the abrupt change point. Crystallized dots were also formed in the amorphous Ge2Sb2Te5 films by focused short pulse laser-irradiated, the resistivities at the crystallized dots and the non-crystallized area are 3.375 x 10(-3) and 2.725 Omega m, sheet resistance is 3.37 x 10(4) and 2.725 x 10(7) Omega/square respectively, deduced from the I-V Curves that is obtained by conductive atomic force microscope (C-AFM). (C) 2008 Elsevier B.V. All rights reserved.

Dy^3＋掺杂Ge-Ga-Se硫系玻璃的性质(英文)

实验制备了Dy^3+掺杂Ge-Ga—Se系统硫系玻璃样品，测试了玻璃的密度、显微硬度、可见-红外透射光谱、荧光光谱以及荧光寿命。根据玻璃的密度计算了玻璃的摩尔体积以及致密度。讨论了玻璃的这些性能随系统平均配位数的变化关系。实验结果表明：该系统中配位数大于2．67的玻璃在1．3μm具有较好的发光性能，荧光寿命在440-530μs之间，当玻璃组成位于化学门槛即平均配位数为2．73时玻璃的发光强度最强。

Anomalous scattering factor determined by semicircle fitting near the K-absorption edge of Ge

It is shown that the locus of the f' + if '' plot in the complex plane, f' being determined from measured f '' by using the dispersion relation, looks like a semicircle very near the absorption edge of Ge. The semicircular locus is derived from a quantum theory of X-ray resonant scattering when there is a sharp isolated peak in f '' just above the K-absorption edge. Using the semicircular behavior, an approach is proposed to determine the anomalous scattering factors in a crystal by fitting known calculated values based on an isolated-atom model to a semicircular focus. The determined anomalous scattering factors f' show excellent agreement with the measured values just below the absorption edge. In addition, the phase determination of a crystal structure factor has been considered by using the semicircular behavior.

Precipitation of Ge nanoparticles from GeO2 glasses in transmission electron microscope

We show, using spatially resolved energy loss spectroscopy in a transmission electron microscopy (TEM), that GeO2 and GeO2-SiO2 glasses are extremely sensitive to high energy electrons. Ge nanoparticles can be precipitated in GeO2 glasses efficiently by the high-energy electron beam of a TEM. This is relevant to TEM characterization of luminescent Ge nanoparticles in silicate glasses, which may produce artificial results. (C) 2005 American Institute of Physics.

Precise determination of anomalous scattering factors of Ge by using X-ray resonant scattering

Variations of peak position of the rocking curve in the Bragg case are measured from a Ge thin crystal near the K-absorption edge. The variations are caused by a phase change of the real part of the atomic scattering factor. Based on the measurement, the values of the real part are determined with an accuracy of better than 1%. The values are the most reliable ones among those reported values so far as they are directly determined from the normal atomic scattering factors.

Détermination de l'âge des machoirons (Chrysichtys nigrodigitatus): première estimation de la croissance

Study of C. nigrodigitatus slices showed evidence of seasonal formation related to rainfall and could be used for ageing. A first estimation of the growth has thus been made.

Croissance et détermination de l'âge par lecture d'écailles d'un poisson plat de Côte d'Ivoire, Cynoglossus canariensis (Steind. 1882)

Cynoglossus canariensis has a very rapid growth. The rate of the males is 0,36 and the female one is 0,32. The asymptotic size is 55,0cm for the females and 50,5cm for the males. Females and males younger than three years (40cm), which represent 90 per cent of the Côte d'Ivoire stock have a similar growth, so the average equation: Lt=53,5 (1-e -0,34(t+1)) will be used.