A novel (W-Al)-C-Co composite cemented carbide prepared by mechanical alloying and hot-pressing sintering

Novel cemented carbides (W0.4Al0.6)C-0.5-Co With different cobalt contents were prepared by mechanical alloying and hot-pressing technique. Hot-pressing technique as a common technique was performed to fabricate the bulk bodies of the hard alloys. The novel cemented carbides have good mechanical properties compared with WC-Co. The density and operation cost of the novel material were much lower than the WC-Co system. It was easy to process submicroscale sintering with the novel materials and obtain the rounded particles in the bulk materials. There is almost no eta-phase in the (W0.4Al0.6)C-0.5-CO cemented carbides system although the carbon deficient obtains the astonishing value of 50%.

Large current gain and low operational voltage permeable metal-base organic transistors based on Au/Al double layer metal base

In order to realize the common-emitter characteristics of the tris(8-hydroxyquinoline) aluminium (Alq(3))-based organic transistors, we used Au/Al double metal layer as the base, thus the vertical metal-base transistors with structure of Al/n-Si/Au/Al/Alq(3)/LiF/Al were constructed. It was found that the contact properties between the base and the organic semiconductors play an important role in the device performance. The utilization of Au/Al double layer metal base allows the devices to operate at high gain in the common-emitter and common-base mode at low operational voltage.

Al/WO3/Au as the interconnecting layer for efficient tandem white organic light-emitting diodes

White light emission from tandem organic light-emitting diodes consisting of blue and red light units separated by a transparent interconnecting layer of Al/WO3/Au has been realized. The devices have a structure of indium-tin-oxide (ITO)/molybdenum oxide (MoO3) (8 nm)/N, N'-di(naphthalene-1-yl)-N, N'-diphenyl-benzidine (NPB)(100 nm)/p-bis(p-N, N-diphenyl-aminostyryl) benzene) (DSA-ph): 2-methyl-9,10-di(2-naphthyl) anthracene (MADN)(40 nm)/tris(8-hydroxylquinoline) aluminium (Alq(3)) (10 nm)/LiF(1 nm)/Al(2 nm)/WO3(3 nm)/Au(16 nm)/MoO3(5 nm)/NPB(60 nm)/Alq(3): 4-(dicyanomethylene)-2-t-butyl-6-(1,1,7,7-tetramethyljulolidyl-9-enyl)-4H-pyran (DCJTB)(30 nm)/Alq3(30 nm)/LiF(1 nm)/Al(150 nm).

The microstructures and mechanical properties of cast Mg-Zn-Al-RE alloys

The microstructures and mechanical properties of cast Mg-Zn-Al-RE alloys with 4 wt.% RE and variable Zn and At contents were investigated. The results show that the alloys mainly consist of alpha-Mg, Al2REZn2, Al4RE and tau-Mg-32(Al,Zn)(49) phases. and a little amount of the beta-Mg17Al12 phase will also be formed with certain Zn and At contents. When increasing the Zn or At content, the distribution of the Al2REZn2 and Al4RE phases will be changed from cluster to dispersed, and the content of tau-Mg-32(Al,Zn)(49) phase increased gradually. The distribution of the Al2REZn2 and Al4RE phases, and the content of beta- or tau-phase are critical to the mechanical properties of Mg-Zn-Al-RE alloys.

Synthesis of Liquid Polybutadiene Having Desired 1,2-Vinyl Content with Co(naph)(2)-Al-2(C2H5)(3)Cl-3-P(OPh)(3) Catalyst System

Liquid polybutadiene with desirable 1,2-units content was synthesized by Co(naph)(2)-Al-2(C2H5)(3)Cl-3-P(OPh)(3) catalyst system. It was shown that liquid polybutadiene having adequate 1,2-unit content (vinvl =35%-40%) molecular weight(M-n = 700-3500), and acceptabele conversion(>= 55%) can synthesized after optimizing polymerization conditions.

The structural composite effect of Au-WO3-Al interconnecting electrode on performance of each unit in stacked OLEDs

In this article, we report the effects of the thickness of metal and oxide layers of the Al/WO3/Au interconnecting structure on the electrical and optical characteristics of the and bottom units of the two-unit stacked organic-light-emitting-devices (OLEDs). It is found that light emission performance of the upper unit is sensitive to the transmittance of semitransparent Al/WO3/Au structure, which can be improved by changing the thickness of each layer of the Al/WO3/Au structure. It is important to note that the introduction WO3 between Al and Au significantly enhances the current efficiency of both the upper and bottom units with respect to that of the corresponding Al/Au structure without WO3. In addition, the emission spectra of both the upper and bottom units are narrower than that of the control device due to microcavity effect. Our results indicate that the All WO3/Au interconnecting structure is a good candidate for fabricating independently controllable high efficiency stacked OLEDs.

Effect of substituting cerium-rich mischmetal with lanthanum on microstructure and mechanical properties of die-cast Mg-Al-RE alloys

Die-cast Mg-4Al-4RE-0.4Mn (RE = Ce-rich mischmetal) and Mg-4Al-4La-0.4Mn magnesium alloys were prepared successfully and their microstructure, tensile and creep properties have been investigated. The results show that two binary Al-RE phases, Al11RE3 and Al2RE, are formed along grain boundaries in Mg-4Al-4RE-0.4Mn alloy, while the phase compositions of Mg-4Al-4La-0.4Mn alloy mainly consist of alpha-Mg phase and Al11La3 phase. And in Mg-4Al-4La-0.4Mn alloy the Al11La3 phase occupies a large grain boundary area and grows with complicated morphologies, which is characterized by scanning electron microscopy in detail. Changing the rare earth content of the alloy from Ce-rich mischmetal to lanthanum gives a further improvement in the tensile and creep properties, and the later could be attributed to the better thermal stability of Al11La3 phase in Mg-4Al-4La-0.4Mn alloy than that of Al11RE3 phase in Mg-4Al-4RE-0.4Mn alloy.

High efficiency tandem organic light-emitting devices with Al/WO3/Au interconnecting layer

An interconnecting layer of Al (2 nm)/WO3 (3 nm)/Au (16 nm) was studied for application in tandem organic light-emitting devices. It can be seen that the Al/WO3/Au structure plays the role of an excellent interconnecting layer. The introduction of WO3 in the connection unit significantly improves the device efficiency as compared to the case of Al/Au. Thus, the current efficiency of the two-unit tandem devices is enhanced by two factors with respect to the one-unit devices. The green two-unit tandem device of indium tin oxide/MoO3/4,4(')-N,N-'-bis[N-(1-naphthyl)-N-phenyl-amino]biphenyl(NPB)/tris(8-hydroxylquinoline) aluminum (Alq(3)):10-(2-benzothiazolyl)-1,1,7,7-tetramethyl-2,3,6,7-tetrahydro-1H,5H,11H-[1]benzopyrano[6,7,8-ij]quinolizin-11-one (C545T)/Alq(3)/LiF/Al/WO3/Au/MoO3/NPB/Alq(3):C545T/Alq(3)/LiF/Al showed a maximum current efficiency of 33.9 cd/A and a power efficiency of 12.0 lm/W.

Preparation of W-Al-Mo ternary alloys by mechanical alloying

Single phase WxAl(50)Mo(50)-X (X=40, 30, 20 and 10) powders have been synthesized directly by mechanical alloying (MA). The structural evolutions during MA and subsequent as-milled powders by annealing at 1400 degrees C have been analyzed using X-ray diffraction (XRD). Different from the Mo50Al50 alloy, W40Al50Mo10 and W30Al50Mo20 alloys were stable at 1400 degrees C under vacuum. The results of high-pressure sintering indicated that the microhardnesses of two compositions, namely W40Al50Mo10 and W30Al50Mo20 alloys have higher values compared with W50Al50 alloy.

High strength Ni based composite reinforced by solid solution W(Al) obtained by powder metallurgy

The solid-solution-particle reinforced W(Al)-Ni composites were successfully fabricated by using mechanical alloying (MA) and hot-pressing (HP) technique when the content of Ni is between 45 wt% and 55 wt%. Besides, samples of various original component ratio of Al50W50 to Ni have been fabricated, and the corresponding microcomponents and mechanical properties such as microhardness, ultimate tensile strength and elongation were characterized and discussed. The optimum ultimate tensile strength under the experiment conditions is 1868 MPa with elongation of 10.21 % and hardness of 6.62 GPa. X-ray diffraction (XRD), FE-SEM and energy dispersive analysis of X-rays (EDS) were given to analysis the components and morphology of the composite bulk specimens.

Fe(acac)_3-Al(i-Bu)_3对马来酸酐与茴香脑共聚的催化性能

研究了Fe(acac) 3 Al(i Bu) 3 (acac =乙酰丙酮 )催化体系对马来酸酐 (MA)与茴香脑 (ANE)共聚反应的催化性能 .动力学研究结果表明 ,MA与ANE共聚对单体的浓度呈一级反应 ,其表观活化能为 31 0kJ/mol.用IR和13 CNMR研究了共聚物的结构 ,结果表明聚合物是交替的 ,其中酸酐的含量为 4 5 6 % .用GPC测定了聚合物的分子量及其分布 ,结果表明分子量的分布较窄 ,PDI =1 19～ 1 4 2 .用DTA研究了聚合物的热力学性质 ,其分解温度为 5 0 1 1℃.

Synthesis, structural characterization and electrical property of new oxide ion conductors: La3MMo2O12 (M = In, Ga and Al)

New series of oxides, La3MMo2O12 (M = In, Ga and Al), have been prepared by the solid-state reaction. The composition and elemental distribution were analyzed by the energy-dispersive X-ray (EDX) analysis. As determined by the X-ray diffraction (XRD), these compounds have similar crystal structures that can be indexed on a monoclinic cell at room temperature. AC impedance spectra and the DC electrical conductivity measurements in various atmospheres indicate that they are oxide ion conductors with ionic conductivities between 10(-2) and 10(-3) S/cm at 800 degrees C. The conductivity decreases in the order of La3GaMo2O12 > La3AlMo2O12 > La3InMo2O12, implying that the effect of cell volume and polarization associated with In3+, Ga3+ and Al3+ play an important role in the anion transport of these materials. The reversible phase transition was observed in all these compounds as confirmed by the differential thermal analysis (DTA) and dilatometric measurements.