Preparation and spectroscopic properties of Er3+-doped high silica glass fabricated by sintering nanoporous glass

A compact nonporous high silica (SiO2 % > 96%) glass containing 3400 ppm Er3+ ions, which was about ten times higher than that in Er-doped silica fiber amplifier (EDSFA), was synthesized by sintering porous glass immersed into erbium nitrate solution. The 1532 nm fluorescence has a FWHM (Full Width at Half Maximum) of 45 nm wider than that of EDSFA and possesses the glass with potential application in broadband fiber amplifiers. The Judd-Ofelt theoretical analysis reflects that Er3+ ions are located in a higher covalent environment which are comparable to those of aluminosilicate glass. (c) 2005 Elsevier B.V. All rights reserved.

Blue-yellow ZnO homostructural light-emitting diode realized by metalorganic chemical vapor deposition technique

We report on the realization of ZnO homojunction light-emitting diodes (LEDs) fabricated by metalorganic chemical vapor deposition on (0001) ZnO bulk substrate. The p-type ZnO epilayer was formed by nitrogen incorporation using N2O gas as oxidizing and doping sources. Distinct electroluminescence (EL) emissions in the blue and yellow regions were observed at room temperature by the naked eye under forward bias. The EL peak energy coincided with the photoluminescence peak energy of the ZnO epilayer, suggesting that the EL emissions emerge from the ZnO epilayer. In addition, the current-voltage and light output-voltage characteristics of ZnO homojunction LEDs have also been studied. (c) 2006 American Institute of Physics.

Thermal, spectroscopic and laser properties of Yb3+Na+: CaF2 single crystals

The effects of Na+ doping level on the thermal conductivities, absorption and emission spectra, and fluorescence lifetimes of Yb3+ ,Na+ :CaF2 crystals were systematically studied. Sites structure, covalent force, and crystal field strength of Yb3+ :CaF2 crystals were markedly varied by codoping Na+ as charge compensator. The 2.0at% Yb3+ and 3.0at% Na+-codoped CaF2 crystal was demonstrated to operate in diode-pumped passively mode-locking scheme. Transform-limited 1 ps laser pulses were obtained, showing the crystal capable of producing ultra-short laser pulses. (c) 2006 Elsevier B.V. All rights reserved.

Yb掺杂原子数分数为0．5％的Yb：Y3Al5O12晶体的光谱分析

采用提拉法生长了Yb掺杂原子数分数为0．5％的Yb：Y3Al5O12。（Yb2YAG）晶体，对晶体的吸收光谱和荧光光谱进行了分析。与Yb掺杂原子数分数为5％的Yb：YAG晶体进行了对比，得出采用940nm激光二极管（LD）抽运晶体最为合适。原子数分数为0．5％的Yb：YAG晶体相对于原子数分数为5％的Yb：YAG晶体白吸收效应的影响要小。测量了原子数分数为0．5％的Yb：YAG晶体的荧光寿命为0．95ms，与理论值很接近。因此采用原子数分数为0．5%的Yb：YAG晶体作为激光工作物质将有利于高效、小型集成

不同Yb掺杂量的Yb：Y3Al5O12晶体的光谱分析

采用提拉法生长了Yb^3＋掺杂量分别为5．4at％，16．3at％，27．1at％，53．6at％和100at％的Yb：Y3Al5O12晶体．系统地表征和分析了Yb^3＋掺杂量对晶体吸收光谱和荧光光谱的影响．随着Yb^3＋掺杂量的增加，各峰值吸收系数呈线性增加的趋势．应用Smakula公式计算了各吸收峰对应的振荡强度，并分析了Yb^3＋掺杂量对振荡强度的影响．当Yb^3＋掺杂量增加到27．1at％时观察到了荧光猝灭现象；当Yb^3＋掺杂量增加到53．6at％时，荧光光谱的线形发生了很大的变化。

不同Yb掺质浓度的Yb：Y3Al5O12晶体激光性能的比较

采用提拉法生长了Yb^3＋掺质浓度为5％原子分数、50％原子分数和100％原子分数的Yb：Y3Al5O12（Yb：YAG）晶体。系统地分析了不同Yb^3＋掺质浓度晶体的吸收光谱和荧光光谱。从吸收峰和吸收系数可以看出采用940nm LD泵浦三种不同浓度的Yb：YAG晶体都比较合适。随着Yb^3＋离子掺质浓度的增高，晶体中出现的自吸收现象越为明显。通过对三种不同Yb掺质浓度晶体激光性能参数的计算，得出高掺质浓度Yb：YAG和YbAG晶体是有前景的激光增益介质。

Spectra analysis of a novel Ti-doped LiAlO2 single crystal

LiAlO2 single crystals doped with Ti at concentration 0.2 at.% are grown by the Czochralskl technique with dimensions Phi 42 x 55 mm. Ti ions in the crystal are quadrivalence proven by comparing the absorption and fluorescence spectra of pure LiAlO2 and Ti: LiAlO2. After air and Li-rich atmosphere annealing, the absorption peaks in the range of 600-800nm disappear. We conclude that 682 and 756nm absorption peaks are attributed to the V-Li and V-O absorptions, respectively. The peaks at 716nm and 798nm may stem from the V-Li(+) and F+ absorptions. The colour-centre model can be applied to explain the experimental phenomena. Ti4+-doping produces more lithium vacancies in the LiAlO2 crystal. The intensities of [LiO4] and the associated bonds remain unchanged, which improves the anti-hydrolyzation and thermal stability of LiAlO2 crystals.

Comparison of fluorescence spectra of Yb : Y3Al5O12 and Yb : YALO(3) single crystals

Yb:Y3Al5O12 (Yb:YAG) single crystals with Yb doping concentration 0.5 at.%, 5 at.%, 15 at.%, 25 at.%, 50 at.%, 100 at.% and Yb:YAlO3 (Yb:YAP) single crystals with Yb doping concentration 0.5 at.%, 5 at.%, 15 at.%, 30 at.% were grown by the Czochralski process. The fluorescence spectra of these crystals and the effects of self-absorption on the shape of the fluorescence spectra were studied. Through comparing the fluorescence spectra of Yb:YAG and Yb:YAP, all results indicate that the effects of self-absorption on the fluorescence spectra of Yb:YAP are remarkably stronger than that of Yb:YAG at the same Yb concentration. (c) 2006 Elsevier B.V. All rights reserved.

Synthesis and characterizations of Al-doped Zn0.95Ni0.05O nanocrystals

Nanocrystalline Zn0.95-xNi0.05AlxO (x = 0.01, 0.02, 0.05 and 0.10) diluted magnetic semiconductors have been synthesized by an autocombustion method. X-ray absorption spectroscopy, high-resolution transmission electron microscopy, energy-dispersive spectrometry and Ni 2p core-level photoemission spectroscopy analyses revealed that some of the nickel ions were substituted for Zn2+ into the ZnO matrix while others gave birth to NiO nanoclusters embedded in the ZnO particles. The Zn0.95Ni0.05O sample showed no enhancement of room-temperature ferromagnetism after Al doping. (C) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Yb∶Y3Al5O12晶体晶格振动光谱的研究

采用提拉法生长Y3Al5O12(YAG)晶体和Yb3+掺杂原子数分数分别为5%, 10%, 15%, 20%, 25%, 50%和100%的Yb∶Y3Al5O12(Yb∶YAG)晶体。系统表征和分析了Yb3+掺杂浓度对拉曼光谱的影响。随着Yb3+掺杂浓度的增加,晶体的振动模式没有明显的变化,晶体结构没有改变;在370 cm-1和785 cm-1附近,振动吸收峰的半峰全宽逐渐增大。分析得出,Yb3+掺杂浓度对晶体的晶格、对称性、荧光寿命均有影响,从而可能影响到晶体的光谱和激光性能。

共掺Na^＋的Yb^3＋：CaF2晶体的荧光分析与低阈值激光运转

基于975nm激发的室温下荧光光谱测量，系统地研究了在新型钠、镱共掺的氟化钙晶体中钠离子的作用机理，分析了掺钠离子浓度与激光阈值的关系，获得了具有最低激光阈值的掺杂浓度优化配比．激光实验表明对于2％Yb^3＋离子浓度的氟化钙，掺入3％的钠离子能够获得最低阈值的激光运转，这与理论和荧光分析完全一致．

La2O3对Yb：Y2O3透明陶瓷光谱性能的影响

研究了La2O3对Yb：Y2O3透明陶瓷光谱性能的影响，添加适量La2O3以后，Yb：Y2O3透明陶瓷的吸收峰和发射峰的位置不变，但由于La^3＋的离子半径大于Y^3＋的离子半径，在Y2O3中引入La^3＋离子后，导致Y2O3晶格常数变大，晶场强度变弱，同时降低了Y2O3晶体的有序度，致使发射峰强度有所下降，发射截面变小．过量的№La2O3（x=0．16）造成yb^3＋激活离子发射强度明显下降；其荧光寿命在添加La2O3后总体增大45％-60％.

射频磁控溅射法制备TiO2-xNX薄膜的结构性能研究

利用射频磁控溅射法室温下在Si（100）衬底上制备了N掺杂的TiO2薄膜，并且采用x射线衍射（XRD）、X射线光电子能谱（XPS）和透射光谱对薄膜进行了表征。XRD结果表明在纯Ar和N2（33．3％）／Ar气氛下制备的TiO2-xNx薄膜均为单一的金红石相，薄膜结晶性良好，呈高度（211）择优取向，而在N2（50．0％）／Ar下制备的薄膜结晶性明显变差；对于N掺杂的TiO2薄膜，XPS表明部分N原子进入TiO2晶格，并且以N—Ti—O、N—O键以及间隙式N原子形式存在；透射光谱表明掺N后的TiO2薄膜吸收边发生了红移。

Cooperative up-conversion luminescence of ytterbium doped yttrium lanthanum oxide transparent ceramic

The up-conversion luminescence of Yb3+-doped yttriurn lanthanum oxide transparent ceramic was investigated. It was ascribed to cooperative luminescence originated from the coupled states of the Yb3+ ion pairs. The proper doping of La2O3 can remove the cooperative luminescence of Yb3+ ion. But excessive La2O3 (at least 10 at.%) the cooperative up-conversion of Yb3+:Y2O3 is obtained again, and the intensity of up-conversion luminescence strengthens with the increase of La2O3 content. (c) 2007 Elsevier B.V. All rights reserved.

Growth and spectral properties of Er:Gd2SiO5 crystal

Er3+ -doped Gd2SiO5 (Er:GSO) single crystal with dimensions of circle divide 35 x 40 mm(3) has been grown by the Czochralski method. The absorption and fluorescence spectra of the Er:GSO crystal were measured at room temperature. The spectral parameters were calculated based on Judd-Ofelt theory, and the intensity parameters Omega(2), Omega(4) and Omega 6 are obtained to be 6.168 x 10(-20), 1.878 x 10(-20), and 1.255 x 10(-20) cm(2), respectively. The emission cross-section has been calculated by Fuechtbauer-Ladenbury formula. (c) 2007 Elsevier B.V. All rights reserved.