Generation of 207-femtosecond pulses from a ytterbium figure-of-eight fibre laser

We report the generation of 207-fs pulses with 1.2mW average power at 1036 nm directly from a passively mode-locked Yb-doped fibre laser with a nonlinear optical loop mirror for mode-locking and pairs of diffraction gratings for intracavity dispersion compensation. These results imply a 4-fold reduction in pulse duration over previously reported figure-of-eight cavity passively mode-locked Yb-doped fibre lasers. Stable pulse trains are produced at the fundamental repetition rate of the resonator, 24.0MHz. On the other hand, this laser offers a cleaner spectrum and greater stability and is completely self-starting.

Low Threshold Stretched-pulses Mode-locked Er3+-doped Fiber Laser with Ring Cavity

National Natural Science Foundationa of China(602537060，60408002)

40-GHz wavelength tunable mode-locked SOA-based fiber laser with 40-nm tuning range

A 40-GHz wavelength tunable mode-locked fiber ring laser based oil cross-gain modulation in a semiconductor optical amplifier (SOA) is presented. Pulse trains with a pulse width of 10.5 ps at 40-GHz repetition frequency are obtained. The laser operates with almost 40-nm tuning range. The relationship between the key laser parameters and the output pulse characteristics is analyzed experimentally.

Compact and efficient triple-pass optical parametric chirped pulse amplification

Compact and efficient triple-pass optical parametric chirped pulse amplification in a single crystal has been demonstrated. The signal was triple-pass amplified in a single nonlinear crystal by a nanosecond pump pulse. The first-pass optical parametric amplification is completely phase matched in the plane of the maximum effective nonlinearity, and the other two passes work symmetrically near to the first-pass optical parametric amplification plane. This architecture efficiently increases the overall gain, overcomes the optical parametric fluorescence, and clearly simplifies the amplification scheme.

HIGH-POWER 2-DIMENSIONAL QUANTUM-WIRE LASER ARRAYS

GaAs/AIGaAs two-dimensional quantum-well wire laser arrays fabricated by metal-organic chemical vapour deposition on nonplanar substrates have realised a linear light pulse output Fewer of over 100mW. This is the highest figure reported to date for all kinds of quantum-well wire lasers.

Pulse Compression by Filamentation in Argon with an Acoustic Optical Programmable Dispersive Filter for Predispersion Compensation

We have experimentally demonstrated pulses 0.4 mJ in duration smaller than 12 fs with an excellent spatial beam profile by self-guided propagation in argon. The original 52 fs pulses from the chirped pulsed amplification laser system are first precompressed to 32 fs by inserting an acoustic optical programmable dispersive filter instrument into the laser system for spectrum reshaping and dispersion compensation, and the pulse spectrum is subsequently broadened by filamentation in an argon cell. By using chirped mirrors for post-dispersion compensation, the pulses are successfully compressed to smaller than 12 fs.

5.3-W Nd:YVO_4 passively mode-locked laser by a novel semiconductor saturable absorber mirror

We report a diode end-pumped continuous wave (CW) passively mode-locked Nd:YVO4 laser with a homemade semiconductor saturable absorber mirror (SESAM). The maximum average output power is 5.3 W at the incident pump power of 17 W, which corresponds to an optical-optical conversion efficiency of 31.2% and slope efficiency of 34.7%. The corresponding optical spectrum has a 0.2-nm full width at half maximum (FWHM), and the pulse repetition rate is 83 MHz.

Material Growth and Device Fabrication of GaN-Based Blue-Violet Laser Diodes

Studies on first GaN-based blue-violet laser diodes(LDs) in China mainland are reported.High quality GaN materials as well as GaN-based quantum wells laser structures are grown by metal-organic chemical vapor deposition method.The X-ray double-crystal diffraction rocking curve measurements show the full-width half maximum of 180" and 185" for (0002) symmetric reflection and (10(-1)2) skew reflection,respectively.A room temperature mobility of 850cm2/(V·s) is obtained for a 3μm thick GaN film.Gain guided and ridge geometry waveguide laser diodes are fabricated with cleaved facet mirrors at room temperature under pulse current injection.The lasing wavelength is 405.9nm.A threshold current density of 5kA/cm2 and an output light power over 100mW are obtained for ridge geometry waveguide laser diodes.

Passive Q-switching of diode-pumped Yb:YAG microchip laser with ion-implanted GaAs

We reported a passive Q-switched diode laser pumped Yb:YAG microchip laser with an ion-implanted semi-insulating GaAs wafer. The wafer was implanted with 400-keV As^(+) in the concentration of 10^(16) ions/cm^(2). To decrease the non-saturable loss, we annealed the ion-implanted GaAs at 500 oC for 5 minutes and coated both sides of the ion-implanted GaAs with antireflection (AR) and highreflection (HR) films, respectively. Using GaAs wafer as an absorber and an output coupler, we obtained 52-ns pulse duration of single pulse.

Passive mode locking of an Yb:YAB laser with a low modulation depth SESAM

A passive mode-locked diode-pumped self-frequency-doubling Yb:YAB laser with a low modulation depth semiconductor saturable absorber mirror operating at 374 MHz is demonstrated. The measured pulse duration is 1.98 ps at the wavelength of 1044 nm. The maximum average power reaches 45 mW.

800nm Semiconductor Absorber with Low Temperature Method and Surface State Method Combined Absorber for Kerr Lens Modelocking of Ti∶Al2O3 Laser

A novel 800nm Bragg mirror type of semiconductor saturable absorption mirror with low temperature method and surface state method combined absorber is presented.With which passive Kerr lens mode locking of Ti∶Al2O3 laser pumped by argon ion laser is realized,which produces pulses as short as 40fs.The spectrum bandwidth is 56nm,which means that it can support the modelocking of 20fs.The pulse frequency is 97.5MHz;average output power is 300mW at the pump power of 4.45W.

Passively Mode Locked Diode-End-Pumped Nd∶YAG Laser with In0.25 Ga0.75 As as Output Coupler

A novel InGaAs(LT-In0.25 Ga0.75 As) absorber grown by metal organic chemical vapor deposition at low temperature is presented.Using it as well as an output coupler,passive mode locking,which produces pulses as short as several hundred picoseconds for diode-end-pumped Nd∶YAG laser at 1.06μm,is realized.The pulse frequency is 150MHz.

Stable mode-locking in an Yb:YAG laser with a fast SESAM

Stable mode-locking in a diode-pumped Yb:YAG laser was obtained with a very fast semiconductor saturable absorber mirror (SESAM). The pulse width was measured to be 4 ps at the central wavelength of 1047 nm. The average power was 200 mW and the repetition rate was 200 MHz.

Passive Q-Switching in a Flash-Lamp Pumped Nd∶YAG Laser with Ion-Implanted GaAs Wafer

A passive Q-switched flash-lamp-pumped Nd:YAG laser with the ion-implanted semi-insulating GaAs water is reported．The wafer is implanted with 400keV As~+ ions in the concentration of 10~(16)cm~(-2). Using GaAs wafer as an absorber and an output coupler．62ns pulse duration of single pulse is obtained.

Visible vertical cavity surface emitting laser

We have designed and fabricated the visible vertical-cavity surface-emitting lasers (VCSEL's) by using metalorganic vapor phase epitaxy (MOVPE). We use the 8 lambda optical cavities with 3 quantum wells in AlGaInP/AlGaAs red VCSEL's to reduce the drift leakage current and enhance the model gain in AlGaInP active region. The structure has a p-type stack with 36 DBR pairs on the top and an n-type with 55-1/2 pairs on the bottom. Using micro-area reflectance spectrum, we try to get a better concordance between the center wavelength of DBR and the emitting wavelength of the active region. We used a component graded layer of 0.05 lambda thick (x = 0.5 similar to 0.9) at the p-type DBR AlGaAs/AlAs interface to reduce the resistance of p-type DBR. We use selective oxidation to define the current injection path. Because the oxidation rate of a thick layer is faster than a thinner one, we grown a thick AlAs layer close to the active region. In this way, we got a smaller active region for efficient confinement of injected carriers (the aperture area is 3 x 3 mu m) to reduce the threshold and, at the same time, a bigger conductive area in the DBR layers to reduce the resistance. We employ Zn doping on the p-side of the junction to improve hole injection and control the Zn dopant diffusion to get proper p-i-n junction. At room temperature, pulse operation of the laser has been achieved with the low threshold current of 0.8mA; the wavelength is about 670nm.