Raman scattering and photoluminescence studies of Er-implanted and Er+ O coimplanted GaN

Raman measurements and photoluminescence (PL) were performed on the metal-organic chemical-vapor deposition epitaxially grown GaN before and after the implantation with Er and Er+O. Several Raman defect modes have emerged from the implantation-damaged samples. The structures around 300 and 595 cm(-1) modes are attributed to the disorder-activated Raman scattering, whereas the 670 cm(-1) peak is assigned to nitrogen-vacancy-related defect scattering. One additional peak at 360 cm(-1) arises after Er+O coimplantation. This Raman peak is attributed to the O-implantation-induced defect complex. The appearance of the 360 cm(-1) mode results in the decrease of the Er3+ -related infrared PL intensity for the GaN:Er+O samples. (C) 2004 American Institute of Physics.

Novel room temperature photoluminescence of Ge/Si islands in multilayer structure grown on silicon-on-insulator substrate

Novel room temperature photoluminescence (PL) of the Ge/Si islands in multilayer structure grown on silicon-on-insulator substrates is investigated. The cavity formed by the mirrors at the surface and the buried SiO2 interface has a strong effect on the PL emission. The peak position is consistent with the theoretical calculation and independent of the exciting power, which is the evidence of cavity effect on the room temperature photoluminescence. (C) 2004 Elsevier B.V. All rights reserved.

Effect of the ratio of TMIn flow to group III flow on the properties of InGaN/GaN multiple quantum wells

Triple-axis x-ray diffraction (TXRD) and photoluminescence (PL) spectra are used to assess the influence of the ratio of TMIn flow to group III flow on structural defects, such as dislocations and interface roughness, and optical properties of multiple quantum wells(MQWs). In this paper the mean densities of edge and screw dislocations in InGaN/GaN MQWs are obtained by W scan of every satellite peak of (0002) symmetric and (1012) asymmetric diffractions. At the same time, the interface roughness is measured by the radio of the full width at half maximum of satellite peaks to the peak orders. The experimental results showed that the density of dislocation, especially of edge dislocation, and interface roughness increase with the increase of the ratio, which leads to the decrease of PL properties. It also can be concluded that the edge dislocation acts as nonradiative recombination centers in InGaN/GaN MQWs. Also noticed is that the variation of the ratio has more influence on edge dislocation than on screw dislocation.

Study of infrared luminescence from Er-implanted GaN films

In this study, we report the dependences of infrared luminescence properties of Er-implanted GaN thin films (GaN:Er) on the kinds of substrates used to grow GaN, the growth techniques of GaN, the implantation parameters and annealing procedures. The experimental results showed that the photoluminescence (PL) intensity at 1.54 mum was severely influenced by different kinds of substrates. The integrated PL peak intensity from GaN:Er /Al2O3 (00001) was three and five times stronger than that from GaN:Er /Si (111) grown by molecular beam epitaxy (MBE) and by metalorganic chemical vapor deposition (MOCVD), respectively. The PL spectra observed from GaN:Er/Al2O3 (0001) grown by MOCVD and by MBE displayed a similar feature, but those samples grown by MOCVD exhibited a stronger 1.54 mum PL. It was also found that there was a strong correlation between the PL intensity with ion implantation parameters and annealing procedures. Ion implantation induced damage in host material could be only partly recovered by an appropriate annealing temperature procedure. The thermal quenching of PL from 15 to 300 K was also estimated. In comparison with the integrated PL intensity at 15 K, it is reduced by only about 30 % when going up to 300 K for GaN:Er/Al2O3 sample grown by MOCVD. Our results also show that the strongest PL intensity comes from GaN:Er grown on Al2O3 substrate by MOCVD. (C) 2004 Elsevier B.V. All rights reserved.

Structure and photoluminescence studies of Pr-implanted GaN

The structure and photoluminscence (PL) properties of Pr-implanted GaN thin films have been studied. RBS/channeling technique was used to explore the damage recovery at high annealing temperature and study the dependence of the radiation damage with ion implantation direction. A complete recovery of the ion implantation damage cannot be achieved at annealing temperatures up to 1050degreesC. It is found that the channeling implantation results in the decrease of the damage. The PL experimental results indicate that the PL efficiency increases exponentially with annealing temperature up to the maximum temperature of 1050degreesC. Moreover, the PL intensity is also seriously affected by ion implantation geometries. The PL intensity for the sample implanted along channeled direction is nearly 2 times more intense than that observed from the sample implanted along random direction. The thermal quenching of PL intensity from 10 to 300K for sample annealed at 1050degreesC is only 30%. (C) 2004 Elsevier B.V. All rights reserved.

Effect of trimethylgallium flow on the structural and optical properties of InGaN/GaN multiple quantum wells

InGaN/GaN multiple quantum wells (MQWs) are grown by metal-organic chemical vapour deposition on (0001) sapphire substrates. Triple-axis X-ray diffraction (TXRD) and photoluminescence (PL) spectra are used to assess the influence of trimethylgallium (TMGa) flow on structural defects, such as dislocations and interface roughness, and the optical properties of the MQWs. In this paper, a method, involving an ! scan of every satellite peak of TXRD, is presented to measure the mean dislocation density of InGaN/GaN MQWs. The experimental results show that under certain conditions which keep the trimethlyindium flow constant, dislocation density and interface roughness decrease with the increase of TMGa flow, which will improve the PL properties. It can be concluded that dislocations, especially edge dislocations, act as nonradiative recombination centres in InGaN/GaN MQWs. Also noticed is that changing the TMGa flow has more influence on edge dislocations than screw dislocations.

Cavity-enhanced photoluminescence of SiGe/Si multiquantum wells grown on silicon-on-insulator substrate

Sharp and strong room-temperature photoluminescence (PL) of the Si0.59Ge0.41/Si multiquantum wells grown on the silicon-on-insulator substrate is investigated. The cavity formed by the mirrors at the surface and the buried SiO2 interface enhances the PL emission and has a wavelength-selective effect on the luminescence. The peak position is consistent with the simulation result and independent of the exciting power, which indicates a strong cavity effect on the room-temperature PL. (C) 2004 American Institute of Physics.

Influence of Mg content on molecular-beam-epitaxy-grown ZnMgS ultraviolet photodetectors

Zn1-xMgxS-based Schottky barrier ultraviolet (UV) photodetectors were fabricated using the molecular-beam-epitaxy (MBE) technique. The influence of Mg content on MBE-grown Zn1-xMgxS-based UV photodetectors has been investigated in details with a variety of experimental techniques, including photoresponse (PR), capacitance-voltage, deep level transient Fourier spectroscopy (DLTFS) and photoluminescence (PL). The room-temperature PR results show that the abrupt long-wavelength cutoffs covering 325, 305 295. and 270 nm with Mg contents of 16%, 44%, 57%, and 75% in the Zn1-xMgxS active layers, respectively, were achieved. But the responsivity and the external quantum efficiency exhibited a slight decrease with the Mg content increasing. In good agreement with the PR results, both of the integrated intensity of the PL spectra obtained from Zn1-xMgxS thin films with different Mg compositions (x = 31% and 52%, respectively) and the DLTFS spectra obtained from Zn1-xMgxS-based (x = 5% and 45%, respectively) UV photodetector samples clearly revealed a significant concentration increase of the non-radiative deep traps with increasing Mg containing in the ZnMgS active layers. Our experimental results also indicate that the MBE-grown ZnMgS-based photodetectors can offer the promising characteristics for the detection of short-wavelength UV radiation. (C) 2004 Elsevier B.V. All rights reserved.

Dependence of implantation-induced damage with photoluminescence intensity in GaN : Er

Erbium was implanted with energies 200 or 400 keV into epitaxial (0 0 0 1) GaN grown on (0 0 0 1) Al2O3 substrate at room temperature (RT) and 400degreesC. Both random (10degrees tilt from c-axis) and channeled (along c-axis) implantations were studied. RBS/Channeling technique was used to study the dependences of the radiation damage with ion implantation energy, direction and temperature. It was found that the channeling implantation or elevating temperature implantation both resulted in the decrease of the damage. Moreover, the Photoluminscence (PL) properties of Er-implanted GaN thin filius were also studied. The experimental results indicate that the PL intensity can be enhanced by raising implantation energy or implanting along channeling direction. (C) 2004 Elsevier B.V. All rights reserved.

Optical properties of boron-doped Si nanowires

Raman scattering and photoluminescence (PL) of boron-doped silicon nanowires have been investigated. Raman spectra showed a band at 480 cm(-1), indicating that the crystallinity of the nanowires was suppressed by boron doping. PL taken from B-doped SiNWS at room temperature exhibited three distinct emission peaks at 1.34, 1.42. and 1.47 eV and the PL intensity was much stronger than that of undoped SiNWS. The increased PL intensity should be very profitable for nano-optoelectronics. (C) 2004 Elsevier B.V. All rights reserved.

Amorphous silicon carbide films prepared by H-2 diluted silane-methane plasma

This paper reports on the preparation and characterization of hydrogenated amorphous silicon carbide films prepared by H-2 diluted silane-methane plasma. Carbon-rich a-SiC:H film with band gap of up to 3.3 eV has been achieved. IR and UV Vis spectra were employed to characterize the chemical bonding and optical properties of as-prepared films. It is shown that hydrogen dilution is crucial in obtaining these wide band gap carbon-rich films. Raman and PL measurements were performed to probe the microstructure and photoelectronic properties of these films before and after annealing. Films with intermediate carbon concentration seem more defective and exhibit stronger photoluminescence and subband absorption than others. Films with different compositions exhibit different annealing behaviours. For silicon rich and carbon rich films, high temperature annealing results in the formation of silicon crystallites and graphite clusters, respectively. (C) 2003 Elsevier B.V. All rights reserved.

Temperature-induced switching-over of the luminescence transitions in GaInNAs/GaAs quantum wells

Photoluminescence (PL) spectra of the GaInNAs/GaAs single quantum well (SQW) with different N compositions are carefully studied in a range of temperatures and excitation power densities. The anomalous S-shape temperature dependence of the PL peak is analysed based on the competition and switching-over between the peaks related to N-induced localized states and the peak related to interband excitonic recombination. It is found that with increasing N composition, the localized energy increases and the turning point of the S-shape temperature dependence occurs at higher temperature, where the localized carriers in the bandtail states obtain enough thermal activation energy to be dissociated and delocalized. The rapid thermal annealing (RTA) effectively reduces the localized energy and causes a decrease of the switching-over temperature.

Luminescence emission originating from nitrogen doping of beta-Ga2O3 nanowires

Nitrogen-doped beta-Ga2O3 nanowires (GaO NWs) were prepared by annealing the as-grown nanowires in an ammonia atmosphere. The optical properties of the nitrogen-doped GaO NWs were studied by measurements of the photoluminescence and phosphorescence decay at the temperature range between 10 and 300 K. The experimental results revealed that nitrogen doping in GaO NWs induced a novel intensive red-light emission around 1.67 eV, with a characteristic decay time around 136 mus at 77 K, much shorter than that of the blue emission (a decay time of 457 mus). The time decay and temperature-dependent luminescence spectra were calculated theoretically based on a donor-acceptor pair model, which is in excellent agreement with the experimental data. This result suggests that the observed novel red-light emission originates from the recombination of an electron trapped on a donor due to oxygen vacancies and a hole trapped on an acceptor due to nitrogen doping.

Photoluminescence of Te isoelectronic centers in ZnS : Te under hydrostatic pressure

The photoluminescence of four epitaxial ZnS: Te samples with Te concentration from 0.5% to 3.1% was investigated at different temperature and ambient pressure. Two well-known emission bands related to the isolated Te-1 and Te-2 pair isoelectronic centers were observed for the samples with Te concentrations of 0.5% and 0.65%. For the samples with Te concentrations of 1.4% and 3.1%, only was the Te-2-related peak observed. The pressure behaviors of these emission bands, were studied at 15 K. The Te-1 -related band has faster pressure shift to higher energy than ZnS band gap. On the other hand, the pressure coefficient of Te-2 -related bands is smaller than that of the ZnS band gap. According to a Koster-Slater model, we found that the increase of the density bandwidth of the valence band with pressure is the main reason for the faster shift of the Te-1 centers, while the relatively large difference in the pressure behavior of the Te-1 and Te-2 centers is mainly due to the difference in the pressure-induced enhancement of the impurity potential on Te-1 and Te-2 centers.

Mode characteristics of semiconductor equilateral triangle microcavities with side length of 5-20 mu m

Semiconductor equilateral triangle microresonators (ETRs) with side length of 5, 10, and 20 mum are fabricated by the two-step inductively coupled plasma (ICP) etching technique. The mode properties of fabricated InGaAsP ETRs are investigated experimentally by photoluminescence (PL) with the pumping source of a 980-nm semiconductor laser and distinct peaks are observed in the measured PL spectra. The wavelength spacings of the distinct peaks agree very well with the theoretical longitudinal mode intervals of the fundamental transverse modes in the ETRs, which verifies that the distinct peaks are corresponding to the enhancement of resonant modes. The mode quality factors are calculated from the width of the resonant peaks of the PL spectra, which are about 100 for the ETR with side length of 20 mum.