Study on the orientation degree of Pb1-xLaxTiO3 thin films by the rocking curve technique and its morphological aspects

Thin films of perovskite-type materials such as PbTiO3, BaTiO3, (Pb,La)TiO3, (Pb, La)(ZrTi)O-3, KNbO3, and Pb(Mg,Nb)03 have been attracting great interest for applications like non-volatile memories, ultrasonic sensors and optical devices. Thin film should be epitaxially grown or at least highly textured since the properties of this anisotropic material depend on the crystallographic orientation. For optical devices, in particular, an epitaxial thin film without defects are essential to reduce optical propagation losses. Pb1-xLaxTiO3 (PLT) where x=0, 13 and 27% thin films were prepared by a chemical method (polymeric precursors method), and deposited by the spin coating technique onto substrates of SrTiO3 (STO) and LaAlO3 (LAO). The films were then beat treated at 500 degrees C in a controlled atmosphere of 0,. The orientation degree of the thin films was obtained from rocking curve technique, by means of X-ray difftaction analysis. A microstructural study revealed that the films were crack-free, homogeneous and have low roughness. (c) 2006 Elsevier B.V. All rights reserved.

Optical characterization of cubic AlGaN/GaN quantum wells

Cubic phase group III-nitrides were grown using RF plasma assisted Molecular Beam Epitaxy on GaAs (001) substrates. High-resolution X-ray diffraction, photoluminescence, cathodoluminescence and photoreflectance measurements were employed to characterize the structural and optical properties of GaN/AlxGa1-xN Multi Quantum Well (MQW) structures, in which both Aluminum content and well widths were varied. The observed quantized states are in agreement with first-principles based theoretical calculations.

A theoretical analysis of the TiO2/Sn doped (110) surface properties

We have used the periodic quantum-mechanical method with density functional theory at the B3LYP level in order to study TiO2/Sn doped (1 1 0) surfaces and have investigated the structural, electronic and energy band properties of these oxides. Our calculated relaxation directions for TiO2 is the experimental one and is also in agreement with other theoretical results. We also observe for the doped systems relaxation of lattice positions of the atoms. Modification of Sri, O and Ti charges depend on the planes and positions of the substituted atoms. Doping can modify the Fermi levels, energy gaps as well as the localization and composition of both valence and conduction band main components. Doping can also modify the chemical, electronic and optical properties of these oxides surfaces increasing their suitability for use as gas sensors and optoelectronic devices. (c) 2005 Elsevier B.V. All rights reserved.

Characterization of the reversible photoinduced optical changes in Sb-based glasses

Changes occurring in absorption coefficients when glasses in the SbPO4-WO3 binary system were irradiated by light, at the edge of the absorption band, were measured in real time. These glasses present good thermal and optical properties and photoinduced changes in the absorption coefficients are reversible by heat treatment around 150 degrees C. Subsequent recording/erasing cycles could be made without sample degradation. The sensitivity of the induced optical changes was studied for different wavelengths, light powers and energy of light dose exposures, and for different compositions of the glasses. The changes in the absorption coefficients of the glass samples were accompanied by a color change from yellow to blue, and were also characterized by visible spectroscopy. The color changes occurred through the entire volume of the glass (similar to 2 mm thickness) for the Ar-ion laser lines at the edge of the absorption band. (c) 2006 Elsevier B.V. All rights reserved.

Preparation, structural and optical characterization of BaWO4 and PbWO4 thin films prepared by a chemical route

Polycrystalline BaWO4 and PbWO4 thin films having a tetragonal scheelite structure were prepared at different temperatures. Soluble precursors such as barium carbonate, lead acetate trihydrate and tungstic acid, as starting materials, were mixed in aqueous solution. The thin films were deposited on silicon, platinum-coated silicon and quartz substrates by means of the spinning technique. The surface morphology and crystal structure of the thin films were investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray diffraction, and specular reflectance infrared Fourier transform spectroscopy, respectively. Nucleation stages and surface morphology evolution of thin films on silicon substrates have been studied by atomic force microscopy. XRD characterization of these films showed that BaWO4 and PbWO4 phase crystallize at 500 degreesC from an inorganic amorphous phase. FTIR spectra revealed the complete decomposition of the organic ligands at 500 degreesC and the appearance of two sharp and intense bands between 1000 and 600 cm(-1) assigned to vibrations of the antisymmetric stretches resulting from the high crystallinity of both thin films. The optical properties were also studied. It was found that BaWO4 and PbWO4 thin films have Eg = 5.78 eV and 4.20 eV, respectively, of a direct transition nature. The excellent microstructural quality and chemical homogeneity results confirmed that soft solution processing provides an inexpensive and environmentally friendly route for the preparation of BaWO4 and PbWO4 thin films. (C) 2003 Elsevier Ltd. All rights reserved.

Self-assembled FePt nanocrystals with large coercivity: Reduction of the fcc-to-L1(0) ordering temperature

Herein we report the synthesis and properties of Fe55Pt45 nanoparticles, both monodisperse and self-assembled into hexagonal close-packed and cubic arrays of 4.0 +/- 0.2 nm size in an L1(0) structure, obtained by a modified polyol process. The new synthetic route improved the control over the particle composition, thereby reducing the temperature required to convert from face-centered cubic (fcc) to face-centered tetragonal (fct) phase by some 30-50 degrees C without additives. Annealing at 550 degrees C for 30 min converts the self-assembled nanoparticles into ferromagnetic nanocrystals with large coercivity, H-C = 11.1 kOe. Reducing the fcc-to-fct (L1(0)) ordering temperature avoided particle coalescence and decreased the loss in particle positional order without compromising the magnetic properties, as is generally observed when additives are used.

Photoreflectance studies of optical transitions in cubic GaN grown on GaAs(001) substrates

The optical properties of cubic GaN epitaxial layers were investigated by modulated photoreflectance (PR) and photoluminescence in the temperature interval from 5 to 300 K. The epilayers were grown on GaAs(001) substrates by molecular beam epitaxy using a nitrogen RIF-activated plasma source. The PR spectra show a transition which is well fitted using the third-derivative functional form of the unperturbed dielectric function, which we interpret as band-to-band transition. Our results allow determination of the temperature dependence of the main gap of c-GaN and give insights into the residual strain in the film, as well as allow us to estimate the binding energy of the complex formed by an exciton bound to a neutral acceptor. (C) 2003 Elsevier B.V. B.V. All rights reserved.

Ferroelectric properties of mechanically synthesized nanosized barium titanate

Barium titanate ceramics were prepared through mechanochemical synthesis starting from fresh prepared barium oxide and titanium oxide in rutile form. Mixture of oxides was milled in zirconia oxide jar in the planetary ball-mill during 30, 60, 120 and 240 min. Extended time of milling directed to formation of higher amount of barium titanate perovskite phase. Barium titanate with good crystallinity was formed after 240 min. Sintering without pre-calcinations step was performed at 1330 degrees C for 2 hours with heating rate of 10 degrees C/min. The XRD, DSC, IR and TEM analyses were performed. Electric and ferroelectric properties were studied. Very well defined hysteresis loop was obtained.

Microstructural and optical characterization of CaWO4 and SrWO4 thin films prepared by a chemical solution method

Stoichiometric CaWO4 and SrWO4 thin films were synthesized using a chemical solution processing, the so-called polymeric precursor method. In this soft chemical method, soluble precursors such as strontium carbonate, calcium carbonate and tungstic acid, as starting materials, were mixed in an aqueous solution. The thin films were deposited on glass substrates by means of the spinning technique. The surface morphology and crystal structure of the thin films were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Nucleation stages and surface morphology evolution of the thin films on glass substrates were studied by atomic force microscopy. The films nucleate at 300 degreesC, after the coalescence of small nuclei into larger grains yielding a homogeneous dense surface. XRD characterization of these films showed that the CaWO4 and SrWO4 phases crystallize at 400 degreesC from an inorganic amorphous phase. No intermediate crystalline phase was identified. The optical properties were also studied. It was found that CaWO4 and SrWO4 thin films have an optical band gap, E-gap=5.27 and 5.78 eV, respectively, of a direct transition nature. The excellent microstructural quality and chemical homogeneity confirmed that this soft solution processing provides an inexpensive and environmentally friendly route for the preparation of CaWO4 and SrWO4 thin films. (C) 2003 Elsevier B.V. All rights reserved.

Thermo-optical characterization of tellurite glasses by thermal lens, thermal relaxation calorimetry and interferometric methods

In this work the thermal lens, thermal relaxation calorimetry and interferometric methods are applied to investigate the thermo-optical properties of tellurite glasses (in mol%: 80TeO(2)-20 Li2O(TeLi), 80TeO(2)-15Li(2)O-5TiO(2) (TeLiTi-5) and 80TeO(2)-10Li(2)O-10TiO(2) (TeLiTi-10)). Thermal diffusivity, thermal conductivity, specific heat and the temperature coefficients of refractive index, optical path length, thermal expansion and electronic polarizability were determined. The use of three independent methods was useful for a complete characterization of the studied tellurite glasses. In addition, our results showed that the thermal expansion coefficient and the temperature coefficient of the optical path length (dS/dT) were significantly modified with the introduction of titanium, which may be relevant for the application of these glasses in the photonic area. (c) 2006 Elsevier B.V. All rights reserved.

Influence of the network former on the properties of magnesium spinels

Undoped and/or doped with 1 mol% of Co2+ Mg2TiO4 and Mg2SnO4 powders were synthesized by the polymeric precursor method. The influence of the network former (Sn4+ or Ti4+) on the thermal, structural and optical properties was investigated. The recorded mass losses are due to the escape of water and adsorbed gases and to the elimination of the organic matter. Mg2TiO4 crystallizes at lower temperatures and also presents more ordered structure with a smaller unit call and having more intense green color than Mg2SnO4 has.

Effects of dispersion by Gd3+ upon europium diphenylphosphinate luminescence

A series of binary diphenylphosphinates with Eu3+ and Gd3+ were prepared. The compounds have the general formula Gd1-xEux(DPP)(3), where x ranges from 0 to 1. The spectroscopic measurements show interesting behavior. The intensity of the D-5(0) --> F-7(2) transitions decreases relative to D-5(0) --> F-7(1) With an increase in europium dispersion. Inside the temporal domain, the same decrease is observed with increasing delay after excitation. The lifetimes are also affected, which can be seen in the x = 1 compound, where the decay is a first-order process and lifetime values are 4.81 ms. In the binary compound, as an effect of dispersion, the lifetime of the D-5(0) level measured at the D-5(0) --> F-7(1) transition increases with europium dispersion, and the average along the series is 6.25 ms. The decay measured at the D-5(0) --> F-7(2) transitions reveals a second-order process with lifetimes ranging from 1.90 to 6.00 ms. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Effect of the order and disorder of BaMoO4 powders in photoluminescent properties

The study of the photoluminescent properties affected by order and disorder of the BaMoO4 powders is the principal objective in this work. BaMoO4 compounds were prepared using soft chemical process called Complex Polymerization Method. In this work, different deagglomeration types and different heating rates were used to promote different disorder degrees. Scheelite type phase (BaMoO4) was determined by X-ray Diffraction (XRD), Fourier Transformed Infra-Red (FTIR) and Raman spectroscopy after heat treating the sample at 400 degrees C. The room temperature luminescence spectra revealed an intense single-emission band in the visible region. Based on XRD and Raman data it was observed that the transition between the completely disordered structure to completely ordered structure is a good condition for photoluminescence (PL) emission. The best PL emission is obtained when the material possesses short range disorder, i.e., is periodically ordered (XRD), but some disorder as measured by Raman spectroscopy. The excellent optical properties observed for disordered BaMoO4 suggested that this material is a highly promising candidate for optical applications.

Study of the annealing temperature effect on the structural and luminescent properties of SrWO4:Eu phosphors prepared by a non-hydrolytic sol-gel process

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Study of structural and photoluminescent properties of Ca8Eu2(PO4)(6)O-2

In this work it is presented for the first time the nanostructured hydroxyapatites doped with 0.5, 1.0 and 2.0 wt% of Eu3+ prepared at room temperature by the mechanical alloying technique. X-ray diffraction powder (XRD), infrared (IR) and Raman scattering spectroscopy, scanning electron microscopy (SEM), microhardness measurements as well as luminescent data of Eu3+ were used to investigate the structural and optical properties of these nanomaterials. The electrical and dielectrical analyses were used with the intention of having a better comprehension about the electromagnetic fields in pure and doped hydroxyapatites.