利用等效层的消偏振宽带减反膜设计

分析了倾斜入射条件下导致光学薄膜产生偏振的原因, 针对不同偏振态的等效导纳与等效相位进行了分析, 并计算了对称膜层在45°入射条件下不同偏振态的等效折射率与等效相位厚度, 采用等效层方法设计了光学性能良好的600～900 nm波段消偏振宽带减反膜。最后利用电子束蒸发技术制备了薄膜样品, 样品的光谱性能完全能够满足使用要求。其中在600～900 nm波段范围内, 平均反射率均小于1.38%, 反射率的偏振度均低于0.89％。另外, 通过对其理论及实验光学性能、角度敏感性、膜层厚度误差敏感性等方面的分析结果可

三倍频分光膜在1064 nm的破斑特性研究

采用电子束蒸发方式制备了两种不同材料组合的分光膜,分别对其在波长1064 nm激光辐照下的损伤阈值进行了测试,用Alpha-Step 500台阶仪对破斑进行了深度测量。实验结果表明,破斑呈现出表面层的剥落和深坑破坏两种形态。表面层的剥落深度在一定范围内不随能量密度的变化而变化；深坑破坏深浅不一,是膜内缺陷融化、汽化及喷发的综合作用的结果,是损伤阈值降低的主要原因。

4H-SiC基底Al_2O_3/SiO_2双层减反射膜的设计和制备

在4H-SiC基底上设计并制备了Al2O3/SiO2紫外双层减反射膜,通过扫描电镜(SEM)和实测反射率谱来验证理论设计的正确性。利用编程计算得到Al2O3和SiO2的最优物理膜厚分别为42.0nm和96.1nm以及参考波长λ=280nm处最小反射率为0.09%。由误差分析可知,实际镀膜时保持双层膜厚度之和与理论值一致有利于降低膜系反射率。实验中应当准确控制SiO2折射率并使Al2O3折射率接近1.715。用电子束蒸发法在4H-SiC基底上淀积Al2O3/SiO2双层膜,厚度分别为42nm和96nm。SEM截面图表明淀积的薄膜和基底间具有较强的附着力。实测反射率极小值为0.33%,对应λ=276nm,与理论结果吻合较好。与传统SiO2单层膜相比,Al2O3/SiO2双层膜具有反射率小,波长选择性好等优点,从而论证了其在4H-SiC基紫外光电器件减反射膜上具有较好的应用前景。

Working pressure dependence of properties of Al2O3 thin films prepared by electron beam evaporation

The effects of working pressure on properties of Al2O3 thin films are investigated. Transmittance of the Al2O3 thin film is measured by a Lambda 900 spectrometer. Laser-induced damage threshold (LIDT) is measured by a Nd:YAG laser at 355nm with a pulse width of 7ns. Microdefects were observed under a Nomarski microscope. The samples are characterized by optical properties and defect, as well as LIDT under the 355 nm Nd: YAG laser radiation. It is found that the working pressure has fundamental effect on the LIDT. It is the absorption rather than the microdefect that plays an important role on the LID T of Al2O3 thin film.

Al2O3/SiO2 films prepared by electron-beam evaporation as UV antireflection coatings on 4H-SiC

Al2O3/SiO2 films have been deposited as UV antireflection coatings on 4H-SiC by electron-beam evaporation and characterized by reflection spectrum, scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The reflectance of the Al2O3/SiO2 films is 0.33% and 10 times lower than that of a thermally grown SiO2 single layer at 276 nm. The films are amorphous in microstructure and characterize good adhesion to 4H-SiC substrate. XPS results indicate an abrupt interface between evaporated SiO2 and 4H-SiC substrate free of Si-suboxides. These results make the possibility for 4H-SiC based high performance UV optoelectronic devices with Al2O3/SiO2 films as antireflection coatings. (C) 2007 Elsevier B.V. All rights reserved.

Y2O3 stabilized ZrO2 thin films deposited by electron-beam evaporation: Optical properties, structure and residual stresses

This paper describes the preparation and the characterization Of Y2O3 stabilized ZrO2 thin films produced by electric-beam evaporation method. The optical properties, microstructure, surface morphology and the residual stress of the deposited films were investigated by optical spectroscopy, X-ray diffraction (XRD), scanning probe microscope and optical interferometer. It is shown that the optical transmission spectra of all the YSZ thin films are similar with those of ZrO2 thin film, possessing high transparency in the visible and near-infrared regions. The refractive index of the samples decreases with increasing of Y2O3 content. The crystalline structure of pure ZrO2 films is a mixture of tetragonal phase and monoclinic phase, however, Y2O3 stabilized ZrO2 thin films only exhibit the cubic phase independently of how much the added Y2O3 content is. The surface morphology spectrum indicates that all thin films present a crystalline columnar texture with columnar grains perpendicular to the substrate and with a predominantly open microporosity. The residual stress of films transforms tensile from compressive with the increasing Of Y2O3 molar content, which corresponds to the evolutions of the structure and packing densities. (C) 2008 Elsevier Ltd. All rights reserved.

沉积温度对氧化钇稳定氧化锆薄膜残余应力的影响

采用自制掺摩尔分数12%的Y2O3的ZrO2混合颗粒料为原料,在不同的沉积温度下用电子束蒸发方法沉积氧化钇稳定氧化锆(YSZ)薄膜样品。利用ZYGOMarkⅢ-GPI数字波面干涉仪对氧化钇稳定氧化锆薄膜的残余应力进行了研究,讨论了沉积温度对残余应力的影响。实验结果表明:随沉积温度升高,氧化钇稳定氧化锆薄膜中残余应力状态由张应力变为压应力,且压应力值随着沉积温度升高而增大;用X射线衍射仪表征了不同沉积温度下氧化钇稳定氧化锆薄膜的微观结构,探讨了薄膜微观结构与其应力的对应关系,并对比了纯ZrO2薄膜表现出的应力状态。

Influence of ZrO2 in HfO2 on reflectance of HfO2/SiO2 multilayer at 248 nm prepared by electron-beam evaporation

Influence of ZrO2 in HfO2 on the reflectance of HfO2/SiO2 multilayer at 248 nm was investigated. Two kinds of HfO2 with different ZrO2 content were chosen as high refractive index material and the same kind of SiO2 as low refractive index material to prepare the mirrors by electron-beam evaporation. The impurities in two kinds of HfO2 starting coating materials and in their corresponding single layer thin films were determined through glow discharge mass spectrum (GDMS) technology and secondary ion mass spectrometry (SIMS) equipment, respectively. It showed that between the two kinds of HfO2, either the bulk materials or their corresponding films, the difference of ZrO2 was much larger than that of the other impurities such as Ti and Fe. It is the Zr element that affects the property of thin films. Both in theoretical and in experimental, the mirror prepared with the HfO2 starting material containing more Zr content has a lower reflectance. Because the extinction coefficient of zirconia is relatively high in UV region, it can be treated as one kind of absorbing defects to influence the optical property of the mirrors. (C) 2008 Elsevier B.V. All rights reserved.

Influence of oxygen post-treatment on laser-induced damage of antireflection coatings prepared by electron-beam evaporation and ion beam assisted deposition

Antireflection coatings at the center wavelength of 1053 nm were prepared on BK7 glasses by electron-beam evaporation deposition (EBD) and ion beam assisted deposition (IBAD). Parts of the two kinds of samples were post-treated with oxygen plasma at the environment temperature after deposition. Absorption at 1064 nm was characterized based on surface thermal lensing (STL) technique. The laser-induced damage threshold (LIDT) was measured by a 1064-nm Nd:YAG laser with a pulse width of 38 ps. Leica-DMRXE Microscope was applied to gain damage morphologies of samples. The results revealed that oxygen post-treatment could lower the absorption and increase the damage thresholds for both kinds of as-grown samples. However, the improving effects are not the same. (c) 2008 Elsevier B.V. All rights reserved.

Optical properties and microstructure of Ta2O5 biaxial film

This study investigates the optical properties and microstructure of Ta2O5 film deposited with the glancing angle deposition technique. The tilted nanocolumn microstructure, examined with scanning electron microscopy, induces the optical anisotropy of thin film. The optical properties of thin film are characterized with an inverse synthesis method. Based on the Cauchy model, the dispersion equations of optical constants of film are determined from the transmittance spectra measured at normal and oblique incidence over 400-800 nm. The starting values derived with an envelope method quicken the optimization process greatly. The dispersion of the principal indices N-1, N-2, and N-3 and the thickness d of thin film are presented statistically. A good agreement between the measured optical properties and theoretical calculation is obtained, which validates the model established for thin film produced by glancing angle deposition. (C) 2008 Optical Society of America

High refractive index TiO2 film deposited by electron beam evaporation

The well known 'crystal seed' theory is first applied in this work to prepare TiO2 film: a high refractive index rutile TiO2 film is grown by electron beam evaporation on the rutile seed formed by 1100 degrees C annealing. The average n is larger than 2.4, by far the highest in all the authors' TiO2 films. The films are characterised by optical properties, microstructure and surface morphologies. It is found that the refractive index shows positive relation with the crystal structure, grain size, and packing density and roughness of the film. The film has lower density of granularity and nodule defects on the surface than those of the film deposited by magnetron sputtering. The result shows attractive application in complex filter and laser coatings.

Efficiency improvement of organic light-emitting diodes using 8-hydroxy-quinolinato lithium as an electron injection layer

Organic light-emitting diodes (OLEDs) using tris-(8-hydroxy-quinolinato) aluminum (Alq(3)) as an emitter, 8-hydroxy-quinolinato lithium (Liq) as an electron injection layer, were prepared. Experimental results show that the efficiency of device with Liq is three times higher than that without Liq. The device using Liq as an injection layer is less sensitive in efficiency to the Liq thickness than that using LiF. In addition to the Alq3 based devices, Liq is also very effective as an electron injection layer for 4,4'-bis(2,2-diphenylvinyl)-1,1'-biphenyl based blue OLED and poly (2-methoxy,5-(2-ethyl-hexyloxy)-1,4-phenylenevinylene) based orange polymer OLED. (c) 2004 Elsevier B.V. All rights reserved.