Modification of ZnO films under high energy Xe-ion irradiations

ZnO films were deposited on (100) Si substrate by radio frequency magnetron sputtering. These films were irradiated at room temperature with 308 MeV Xe-ions to a fluence of 1.0 x 10(12), 1.0 x 10(13) or 1.0 x 10(14) Xe/cm(2). Then the samples were investigated using RBS, XRD, FESEM and PL analyses. The obtained experimental results showed that the deposited ZnO films were highly c-axis orientated and of high purity, 308 MeV Xe-ion irradiations could not change the c-axis oriented. The topography and PL properties of the ZnO films varied with increasing the Xe-ion irradiation fluence. For 1.0 x 10(13) or 1.0 x 10(14) Xe/cm(2) irradiated samples, surface cracks were observed. Furthermore, it was found that the 1.0 x 10(14) Xe/cm(2) irradiated sample exhibiting the strongest PL ability. The modification of structure and PL properties induced by 308 MeV Xe-ion irradiations were briefly discussed. (C) 2008 Elsevier B.V. All rights reserved.

Investigation of PL properties of C-doped SiO2/Si samples after high energy Pb ion irradiation

Amorphous SiO2 thin films with about 400-500 nm in thickness were thermally grown on single crystalline silicon. These SiO2/Si samples were firstly implanted at room temperature (RT) with 100 keV carbon ions to 2.0 x 10(17),5.0 X 10(17) or 1.2 x 10(18) ions/cm(2), then irradiated at RT by 853 MeV Pb ions to 5.0 x 10(11), 1.0 X.10(12) 2.0 x 10(12) or 5.0 x 10(12) ions/cm(2), respectively. The variation of photoluminescence (PL) properties of these samples was analyzed at RT using a fluorescent spectroscopy. The obtained results showed that Pb-ion irradiations led to significant changes of the PL properties of the carbon ion implanted SiO2 films. For examples, 5.0 x 10(12) Pb-ions/cm(2) irradiation produced huge blue and green light-emitters in 2.0 x 10(17) C-ions/cm(2) implanted samples, which resulted in the appearance of two intense PL peaks at about 2.64 and 2.19 eV. For 5.0 x 10(17) carbon-ions/cm(2) implanted samples, 2.0 x 10(12) Pb-ions/cm(2) irradiation could induce the formation of a strong and wide violet band at about 2.90 eV, whereas 5.0 x 10(12) Pb-ionS/cm(2) irradiation could,create double peaks of light emissions at about 2.23 and 2.83 eV. There is no observable PL peak in the 1.2 x 10(18) carbon-ions/cm(2) implanted samples whether it was irradiated with Pb ions or not. All these results implied that special light emitters could be achieved by using proper ion implantation and irradiation conditions, and it will be very useful for the synthesis of new type Of SiO2-based light-emission materials.

Color center formation in alpha-Al2O3 induced by high energy heavy ions

Single crystals of alpha-alumina were irradiated at room temperature with 1.157 (GeVFe)-Fe-56, 1.755 (GeVXe)-Xe-136 and 2.636 (GeVU)-U-238 ions to fluences range from 8.7 x 10(9) to 6 x 10(12) ions/cm(2). Virgin and irradiated samples were investigated by ultraviolet visible absorption measurements. The investigation reveals the presence of various color centers (F, F+, F-2(2+), F-2(+) and F-2 centers) appearing in the irradiated samples. It is found that the ratio of peak absorbance of F-2 to F centers increases with the increase of the atomic numbers of the incident ions from Fe, Xe to U ions, so do the absorbance ratio of F-2(2+) to F+ centers and of large defect cluster to F centers, indicating that larger defect clusters are preferred to be produced under heavier ion irradiation. Largest color center production cross-section was found for the U ion irradiation. The number density of single anion vacancy scales better with the energy deposition through processes of nuclear stopping, indicating that the nuclear energy loss processes determines the production of F-type defects in heavy ion irradiated alpha-alumina.