Design of polymeric stabilizers for size-controlled synthesis of monodisperse gold nanoparticles in water

A new methodology is described for the one-step aqueous preparation of highly monodisperse gold nanoparticles with diameters below 5 nm using thioether- and thiol-functionalized polymer ligands. The particle size and size distribution was controlled by subtle variation of the polymer structure. It was shown that poly(acrylic acid) (PAA) and poly(methacrylic acid) (PMAA) were the most effective stabilizing polymers in the group studied and that relatively low molar mass ligands (similar to 2500 g/mol) gave rise to the narrowest particle size distributions. Particle uniformity and colloidal stability to changes in ionic strength and pH were strongly affected by the hydrophobicity of the ligand end group. "Multidentate" thiol-terminated ligands were produced by employing dithiols and tetrathiols as chain-transfer agents, and these ligands gave rise to particles with unprecedented control over particle size and enhanced colloidal stability. It was found throughout that dynamic light scattering (DLS) is a very useful corroboratory technique for characterization of these gold nanoparticles in addition to optical spectroscopy and TEM.

Toward high-performance polymer solar cells: The importance of morphology control

Polymer solar cells have the potential to become a major electrical power generating tool in the 21st century. R&D endeavors are focusing on continuous roll-to-roll printing of polymeric or organic compounds from solution-like newspapers-to produce flexible and lightweight devices at low cost. It is recognized, though, that besides the functional properties of the compounds the organization of structures on the nanometer level-forced and controlled mainly by the processing conditions applied-determines the performance of state-of-the-art polymer solar cells. In such devices the photoactive layer is composed of at least two functional materials that form nanoscale interpenetrating phases with specific functionalities, a so-called bulk heterojunction. In this perspective article, our current knowledge on the main factors determining the morphology formation and evolution is introduced, and gaps of our understanding on nanoscale structure-property relations in the field of high-performance polymer solar cells are addressed. Finally, promising routes toward formation of tailored morphologies are presented.

Change of the dominant luminescent mechanism with increasing current density in molecularly doped organic light-emitting devices

We have fabricated and measured a series of electroluminescent devices with the structure of ITO/TPD/Eu(TTA)(3)phen (x):CBP/BCP/ ALQ/LiF/Al, where x is the weight percentage of Eu(TTA)3phen (from 0% to 6%). At very low current density, carrier trapping is the dominant luminescent mechanism and the 4% doped device shows the highest electroluminescence (EL) efficiency among all these devices. With increasing current density, Forster energy transfer participates in EL process. At the current density of 10.0 and 80.0mA/ cm(2), 2% and 3% doped devices show the highest EL efficiency, respectively. From analysis of the EL spectra and the EL efficiency-current density characteristics, we found that the EL efficiency is manipulated by Forster energy transfer efficiency at high current density. So we suggest that the dominant luminescent mechanism changes gradually from carrier trapping to Forster energy transfer with increasing current density. Moreover, the conversion of dominant EL mechanism was suspected to be partly responsible for the EL efficiency roll-off because of the lower EL quantum efficiency of Forster energy transfer compared with carrier trapping.

Efficient organic electroluminescent devices based on an organosamarium complex

Several organic electroluminescent devices with different device structures were fabricated based on an organosamarium complex Sm(HFNH)(3)phen[HFNH=4, 4, 5, 5, 6, 6, 6-heptafluoro-l-(2-naphthvl)hexane-1, 3-dione; phen=1, 10-phenanthroline] as emitter. Their electroluminescent properties were investigated in detail. Although the devices with the optimal structure ITO/TPD (50nm)/ Sm(HFNH)(3)phen (xwt%):CBP (50nm)/BCP (20nm)/AIQ (30nm)/LiF (1 nm),/Al (200nm) show high brightness (more than 400cd/m(2)) and high current efficiency (about 1 cd/A), there are emissions from CBP, BCP and even from AIQ existing in the electroluminescence (EL) spectra besides emission from Sm(HFNH)(3)Phen. The reason to this was discussed. The device with the structure ITO/TPD (50 nm)/ Sm(HFNH)(3)phen (50 nm)/AIQ (30 nm)/LiF (1 nm)/Al (200 nm) exhibits the maximum brightness of 118 cd/m(2) and current efficiency of 0.029 cd/A, and shows emissions from AIQ and Sm(HFNH)(3)phen at high voltages. However, with the BCP hole-block layer added, the device [ITO/TPD (50 nm)/Sm(HFNH)(3)phen (50 nm)/BCP (20 nm)/AIQ (30 nm)/LiF (1 nm)/Al (200 nm)] exhibits pure Sm3+ emission in 2 the EL spectra even at high voltages, with the maximum current efficiency of 0.29cd/A and brightness of 82cd/m(2)

Electrical properties in vanadyl-phthalocyanine-based metal-insulator-semiconductor devices

We investigated electrical properties of vanadyl phthalocyanine (VOPc) metal-insulator-semiconductor (MIS) devices by the measurement of capacitance and conductance, which were fabricated on ordered para-sexiphenyl (p-6P) layer by weak epitaxy growth method. The VOPc/p-6P MIS diodes showed a negligible hysteresis effect at a gate voltage of +/- 20 V and small hysteresis effect at a gate voltage of +/- 40 V due to the low interface trap state density of about 1x10(10) eV(-1) cm(-2). Furthermore, a high transition frequency of about 10 kHz was also observed under their accumulation mode. The results indicated that VOPc was a promising material and was suitable to be applied in active matrix liquid crystal displays and organic logic circuits.

A third-generation H2O2 biosensor based on horseradish peroxidase-labeled Au nanoparticles self-assembled to hollow porous polymeric nanopheres

A novel third-generation biosensor for hydrogen peroxide (H2O2) was developed by self-assembling gold nanoparticles to hollow porous thiol-functionalized poly(divinylbenzene-co-acrylic acid) (DVB-co-AA) nanospheres. At first, a cleaned gold electrode was immersed in hollow porous thiol-functionalized poly(DVB-co-AA) nanosphere latex to assemble the nanospheres, then gold nanoparticles were chemisorbed onto the thiol groups of the nanospheres. Finally, horseradish peroxidase (HRP) was immobilized on the surface of the gold nanoparticles. The immobilized horseradish peroxidase exhibited direct electrochemical behavior toward the reduction of hydrogen peroxide. The resulting biosensor showed a wide linear range of 1.0 mu M-8.0 mM and a detection limit of 0.5 mu M estimated at a signal-to-noise ratio of 3. Moreover, the studied biosensor exhibited high sensitivity, good reproducibility, and long-term stability.

Improved color purity and efficiency by a coguest emitter system in doped red light-emitting devices

We demonstrate red organic light-emitting diodes (OLEDs) with improved color purity and electroluminescence (EL) efficiency by codoping a green fluorescent sensitizer 10-(2-benzothiazolyl)-2,3,6,7-tetrahydro-1, 1, 7,7-tetramethyl-1H, 5H, 11H-(1)-benzopyropyrano(6,7-8-ij)quinolizin-11-one (C545T) as the second dopant and a red fluorescent dye 4-(dicyanomethylene)-2-t-butyl-6(1,1,7,7tetramethyljulolidyl-9-enyl)-4H-pyran (DCJTB) as the lumophore into tris(8-hydroquinoline) aluminum (Alq(3)) host. It was found that the C545 T dopant did not by itself emit but assisted the carrier trapping from the host Alq(3) to the red emitting dopant. The red OLEDs realized by this approach not only kept the purity of the emission color, but also significantly improved the EL efficiency. The current efficiency and power efficiency, respectively, reached 12 cd/A at a current density of 0.3 mA/cm(2) and 10lm/W at a current density of 0.02 mA/cm(2), which are enhanced by 1.4 and 2.6 times compared with devices where the emissive layer is composed of the DCJTB doped Alq(3), and a stable red emission (chromaticity coordinates: x = 0.64, y = 0.36) was obtained in a wide range of voltage. Our results indicate that the coguest system is a promising method for obtaining high-efficiency red OLEDs.

Nonvolatile memory devices based on gold nanoparticle and poly (N-Vinylcarbazole) composite

A rewritable polymer memory device based on gold nanoparticle doped poly (N-vinylcarbazole) (PVK), which can be easily fabricated by simple spin coating, has been described. An electrical bistable phenomenon is observed in the current-voltage characteristics of this device, and it is found that the electrical bistability is repeatable by proper writing voltage and erasing voltage. The unique behavior of the devices provides an interesting approach such that doping nanoparticles in polymer can be used to realize high performance nanovolatile polymer memory devices.

High efficiency tandem organic light-emitting devices with Al/WO3/Au interconnecting layer

An interconnecting layer of Al (2 nm)/WO3 (3 nm)/Au (16 nm) was studied for application in tandem organic light-emitting devices. It can be seen that the Al/WO3/Au structure plays the role of an excellent interconnecting layer. The introduction of WO3 in the connection unit significantly improves the device efficiency as compared to the case of Al/Au. Thus, the current efficiency of the two-unit tandem devices is enhanced by two factors with respect to the one-unit devices. The green two-unit tandem device of indium tin oxide/MoO3/4,4(')-N,N-'-bis[N-(1-naphthyl)-N-phenyl-amino]biphenyl(NPB)/tris(8-hydroxylquinoline) aluminum (Alq(3)):10-(2-benzothiazolyl)-1,1,7,7-tetramethyl-2,3,6,7-tetrahydro-1H,5H,11H-[1]benzopyrano[6,7,8-ij]quinolizin-11-one (C545T)/Alq(3)/LiF/Al/WO3/Au/MoO3/NPB/Alq(3):C545T/Alq(3)/LiF/Al showed a maximum current efficiency of 33.9 cd/A and a power efficiency of 12.0 lm/W.

Improved electron injection in organic light-emitting devices with a lithium acetylacetonate [Li(acac)]/aluminium bilayer cathode

Lithium acetylacetonate [Li(acac)] covered with aluminium was used as an efficient electron injection layer in organic light-emitting devices (OLEDs) consisting of NPB as the hole transport layer and Alq(3) as the electron transport and light emitting layer, resulting in lower turn- on voltage and increased current efficiency. The turn- on voltage (the voltage at a luminance of 1 cd m(-2)) was decreased from 5.5 V for the LiF/Al and 4.4 V for Ca/Al to 4.0 V for Li(acac)/Al, and the device current efficiency was enhanced from 4.71 and 5.2 to 7.0 cd A(-1). The performance tolerance to the layer thickness of Li(acac) is also better than that of the device with LiF. LiF can only be used when deposited as an ultra- thin layer because of its highly insulating nature, while the Li(acac) can be as thick as 5 nm without significantly affecting the EL performance. We suppose that the free lithium released from Li(acac) improves the electron injection when Li(acac) is covered with an Al cathode.

Improved efficiency by a fluorescent dye in red organic light-emitting devices based on a europium complex

By doping a fluorescent dye in the emissive layer, we realized high efficient red organic light-emitting diodes (OLEDs) based on a europium complex. The OLEDs realized by this method showed pure red emission at 612 nm with a full width at half maximum Of 3 nm. The Commission International de L'Eclairage Coordination keeps approximately the same as the emission of pure Eu3+. The maximum brightness and EL efficiency reached 2450 cd/m(2) at 20 V and 9.0 cd/A (6.0 lm/w) at a current density of 0.012 mA/cm(2), respectively. At the brightness of 100 cd/m(2), the current efficiency reached 4.4 cd/A.

Polymeric pH indicators immobilized PVA membranes for optical sensors of high basicity based on a kinetic process

Two kinds of polymeric pH indicators PPF (phenolphthalein-formaldehyde product) and CPF (o-cresolphthalein-formaldehyde product) immobilized cross-linked poly(vinyl alcohol) membranes (PPF-PVA and CPF-PVA) for optical intermittent determination of high basicity ([OH-] = 1-8 M) based on a kinetic process were developed. In our previous work, we had demonstrated that PPF-PVA and CPF-PVA could perform the determination of high pH values from pH 10.0 to 14.0. Here the discoloring kinetic behaviors of PPF-PVA and CPF-PVA were compared with those of free phenolphthalein, o-cresolphthalein and thymolphthalein. Experimental results and theoretical analysis indicated that the response behaviors of the optodes' membranes in concentrated NaOH solutions were diffusion-independent and still complied with the pseudo-first-order kinetics. In addition, two data analysis methods for determination were presented. One was directly based on the reduced absorbance: the other was based on the discoloring kinetic constant. It was found that the latter could perform a rapid (60 s) and reliable (relative standard deviation: 2.6%) determination for high basicity.

White electroluminescence from polyfluorene chemically doped with 1,8-napthalimide moieties

An efficient white light-emitting polymer was developed with blue polyfluorene (PFO) chemically doped with orange fluorescent 1, 8-naphthalimide moieties. The emission spectrum can be easily tuned by varying the content of 1, 8-naphthalimide moieties. A white polymeric light-emitting diode (WPLED) with a structure of indium tin oxide (ITO)/the complex of (3,4-ethylenedioxythiophene) and polystyrene sulfonic acid (PEDOT)/polymer/Ca/Al showed a current efficiency of 5.3 cd/A and a power efficiency of 2.8 Lm/W at 6 V with the Commission Internationale de L'Eclairage (CIE) coordinates at (0.25,0.35). Moreover, the WPLED from the copolymer showed a very stable white light emission at different driving voltage and brightness. The CIE coordinates of the WPLED were (0.25, 0.35), (0.26, O.36), and (0.26, 0.36) under driving voltages of 6, 8, and 10 V, corresponding to the brightness of 82, 3555, and 7530 cd/m(2), respectively. This approach for realization of white light emission is promising over the polymer blending system in terms of both efficiency and color stability.

Novel soluble N-phenyl-carbazole-containing PPVs for light-emitting devices: Synthesis, electrochemical, optical, and electroluminescent properties

Novel PPV derivatives (PCA8-PV and PCA8-MEHPV) containing N-phenyl-carbazole units on the back-bone were successfully synthesized by the Wittig polycondensation of 3,6-bisformyl-N-(4-octyloxy-phenyl)carbazole with the corresponding tributyl phosphonium salts in good yields. The newly formed and dominant trans vinylene double bonds were confirmed by FT-IR and NMR spectroscopy. The polymers (with (M) over bar (w) of 6289 for PCA8-PV and 7387 for PCA8-MEHPV) were soluble in common organic solvents and displayed high thermal stability (T(g)s are 110.7 degreesC for PCA8-PV and 92.2 degreesC for PCA8-MEHPV, respectively) because of the incorporation of the N-phenyl-carbazole units. Cyclic voltammetry investigations (onsets: 0.8 V for PCA8-PV and 0.7 V for PCA8-MEHPV) suggested that the polymers possess enhanced hole injection/transport properties, which can be also attributed to the N-phenyl-carbazole units on the backbone. Both the single-layer and the double-layer light-emitting diodes (LEDs) that used the polymers as the active layer emitted a greenish-blue or bluish-green light (the maximum emissions located 494 nm for PCA8-PV and 507 nm for PCA8-MEHPV, respectively).