Synthesis of PbTiO3 by use of polymeric precursors

Lead titanate powders were synthesized through the use of polymeric precursors according to the Pechini Process. The polymeric precursor was calcined at temperatures ranging from 300 to 600°C for 1 or 2 h. X-ray diffraction (XRD) showed that lead titanate crystallizes from the precursor at temperatures as low as 400°C. No intermediate carbonate phase was detected by Fourier transform infrared spectroscopy (FTIR) or by XRD. A powder with mean particle size of 150 nm was obtained after calcination of the precursor at 600°C for 1 h. © 1998 Elsevier Science B.V. All rights reserved.

Preparation and characterization of SrBi2Nb2O9 thin films made by polymeric precursors

A polymeric precursor solution was employed in preparing SrBi2Nb2O9 (SBN) powder and thin films dip coated onto Si(100) substrate. XRD results show that the SBN perovskite phase forms at temperatures as low as 600°C through an intermediate fluorite phase. This fluorite phase is observed for samples heat-treated at temperatures of 400 and 500°C. After heat treatment at temperatures ranging from 300 to 800°C, thin films were shown to be crack free. Grazing incident angle XRD characterization shows the occurrence of the fluorite intermediate phase for films also. The thickness of films, measured by MEV, was in the order of 80-100 nm.

Structural and surface morphology characterizations of oriented LiNbO3 thin films grown by polymeric precursor method

Polymeric precursor solution was used to deposit LiNbO3 thin films by dip coating on sapphire substrates. The effects of processing variables, such as heat treatment conditions and number of deposited layers, on crystallinity and morphology of the final films were investigated. X-ray diffraction patterns show the oriented growth of the films. The rocking curves, obtained around the (006) LiNbO3 peak, revealed that the shape peak and the FWHM value were influenced by the processing variables. According to these parameters, some films presented very homogeneous dense and smooth surfaces, as shown by the SEM and AFM studies.

Influence of heat treatment on LiNbO3 thin films prepared on Si(111) by the polymeric precursor method

The effects of heat-treatment temperature on LiNbO3 thin films prepared by the polymeric precursor method were investigated. The precursor solution was deposited on Si(111) substrates by dip coating. X-ray diffraction and thermal analyses revealed that the crystallization process occurred at a low temperature (420 °C) and led to films with no preferential orientation. High-temperature treatments promoted formation of the LiNb3O8 phase. Scanning electron microscopy, coupled with energy dispersive spectroscopy analyses, showed that the treatment temperature also affected the film microstructure. The surface texture - homogeneous, smooth, and pore-free at low temperature - turned into an `islandlike' microstructure for high-temperature treatments.

Direct amorphous-to-cubic perovskite phase transformation for lead titanate

The phase evolution of lead titanate processed by the polymeric precursor method was investigated by thermal analysis, X-ray diffraction, and high-resolution transmission electron microscopy. The results showed that the cubic perovskite PbTiO3 (PT) phase is formed from an inorganic amorphous precursor at a temperature of 444 °C. A gradual transition from cubic to tetragonal perovskite PT was observed with the increase of calcination time at this temperature. HRTEM results showed that the cubic PT particles have a size of around 5 nm. The identification of cubic PT as an intermediate phase supports the hypothesis that the chemical homogeneity was kept at the molecular level during the synthesis process, with no cation segregation.

Coordinate-space Faddeev-Hahn-type approach to three-body charge-transfer reactions involving exotic particles

Low-energy muon-transfer cross sections and rates in collisions of muonic atoms with hydrogen isotopes are calculated using a six-state close-coupling approximation to coordinate-space Faddeev-Hahn-type equations. In the muonic case satisfactory results are obtained for all hydrogen isotopes and the experimentaly observed strong isotopic dependence of transfer rates is also reproduced. A comparison with results of other theoretical and available experimental works is presented. The present model also leads to good transfer cross sections in the well-understood problem of antihydrogen formation in antiproton-positronium collision.

Constraining models with superlight gravitino, scalar and pseudoscalar particles

In some supergravity models there are light weakly coupled scalar (S)-and pseudoscalar (P) particles. These particles arise following a superlight gravitino. In these models the decay SIP → γγ exists. We examine constraints on this process considering these photons as responsible by the extragalactic background light. We also consider the amount of SIP particles produced through the fusion of the cosmic background photons and contributing to the effective number of light neutrino species during primordial nucleosynthesis. We obtain bounds on the gravitino mass complementary to the existing ones.

Formation of colloidal particles of hydrous iron oxide by forced hydrolysis

The mechanism of formation and growth of hydrous iron oxide (FeOOH) during the initial stages of forced hydrolyses of ferric chloride aqueous solution was studied by small angle X-ray scattering (SAXS). The effect of the hydrolysis temperature (60°C, 70°C and 80°C) and of the addition of urea on the formation of colloidal particles under isothermal conditions were investigated. Based on the experimental scattering functions in the Guinier range, we suggest the presence of elongated colloidal particles. The particle diameter and length, and their variation with time, were determined by fitting the form factor of prolate ellipsoids to the experimental scattering functions. We have assumed that our solutions are in a dilute state and that all colloidal particles are approximately of the same size. The colloidal particles have geometrical shapes similar to those of the subcrystals that build up the superstructure of β-FeOOH crystals, indicating that the formation of this hydrous iron oxide is governed by an aggregation process. Otherwise, the addition of urea hinders the growth and yields smaller particles, with a reduction in size greater than 50%. © 2000 Elsevier Science B.V. All rights reserved.

Preparation and properties of ferroelectric BaTiO3 thin films produced by the polymeric precursor method

Ferroelectric barium titanate thin films were produced by the polymeric precursor method. In this technique, the desired metal cations are chelated in a solution using a hydroxycarboxylic acid as the chelating agent. Barium carbonate and titanium IV isopropoxide were used as precursors for the citrate solution. Ethylene glycol and citric acid were used as polymerization/complexation agents for the process. The crystalline structure of the film annealed at 700 °C had a single perovskite phase with a tetragonal structure. The BaTiO3 film showed good P-E hysteresis loops and C-V characteristics due to the switched ferroelectric domains.

Preparation and characterization of BaBi2Nb2O9(BBN) ceramics synthetized by polymeric precursors method

Pure BBN powders and with addition of 1 and 2 wt% in excess of bismuth were obtained by Pechini Method. The powders calcined at 300°C/4h were analyzed by TG/DTA to study the temperature of organic matter decomposition. A systematic study of calcination temperature and time to the formation of the BBN phase was performed and the phase formation was accompanied by XRD. The calcined powders at 800°C during 2h were analyzed by infrared spectroscopy and by BET. The powders were isostaticaly pressed and sintered at temperatures ranging from 900°C to 1000°C. The ceramics were characterized by XRD to control the crystalline phase and by SEM to analyze the microstructure.

Effect of thermal treatment on the morphology of PLZT thin films prepared from polymeric precursor method

Lead lanthanum zirconate titanate (PLZT) thin films with (9/65/35) stoichiometry were prepared by dip coating from polymeric precursor method. The films deposited on silicon (100) substrates, were thermally treated from 450° to 700°C for 6 hours in order to study the influence of thermal treatment on the crystallinity, microstructure, grain size and roughness of the final film. X-ray diffraction results showed that PLZT phase crystallizes at low temperature (500°C) and present preferential orientation. It was observed by scanning electron microscopy (SEM) that it is possible to obtain dense thin films at temperatures around 650°C. The atomic force microscopy (AFM) studies showed that the grain size and roughness are strongly influenced by the annealing temperature.

Influence of barium and strontium addition on the ratio c/a of PZT obtained by the polymeric precursor method

Lead zirconate titanate powder, with Zr/Ti ratio of 50/50 was prepared by Pechini method after adding up to 10,0 mol% of Ba +2 and Sr +2 ions. Tetragonal phase is favored by the increase of barium and strontium concentration in the LiNbO 3 crystal lattice. The ratio c/a for tetragonal phase increases with the content of Ba +2 and Sr +2.

Protected magnetic particles: Silica on yttrium iron garnet

The formation of silica on core yttrium iron garnet presents a variety of different applications as corrosion resistance and stabilization of magnetic properties. Well-defined magnetic particles were prepared by heterocoagulating silica on yttrium iron garnet to protect the core. Yttrium iron garnet was obtained using a homogeneous nucleation process by controlling the chemical routes from cation hydrolysis in acid medium. The heterocoagulation was induced by tetraethyl orthosilicate hydrolysis in appropriate yttrium iron garnet dispersion medium. The presence of silica on yttrium iron garnet was characterized by vibrating sample magnetometry, X-ray photoemission spectroscopy, transmission electron microscopy, small area electron diffraction and differential thermal analysis. © 2001 Elsevier Science B.V. All rights reserved.

Magnetic properties of spindle-type iron fine particles obtained from hematite

Spindle-type iron fine particles have been prepared by reduction of silica-coated-hematite particles. Hydrogen reduction of the coated-hematite cores yielded uniform spindle-type iron particles, which were stabilized by surface oxidation. Narrow particle distributions are observed from TEM measurements. X-ray, Mössbauer and magnetization data are in agreement with the presence of nanosized α-Fe particles, having surface layer of spinel structure oxide. Mössbauer spectra show that the oxide surface is superparamagnetic at room temperature. © 2001 Elsevier Science B.V. All rights reserved.

A surface modification for hydrogen storage intermetallic particles by sol-gel method

A new process for the surface modification of hydrogen storage intermetallic particles used as anode material in secondary batteries is proposed in this article. The copper oxide particles coverage obtained by the sol-gel method is proposed to produce, under operational conditions of a Ni-MH battery, a metallic framework that tolerates the volume changes in charge/discharge cycles and does not inhibit the hydrogen absorption. Furthermore it was noticed an enhancement on the discharge capacity of the electrode material that can be related to a new hydrogen storage phase or to an inhibition of the surface oxidation promoted by the film coverage.