Low-Power Super-resolution Readout with Antimony Bismuth Alloy Film as Mask layer

Sb-Bi alloy films are proposed as a new kind of super-resolution mask layer with low readout threshold power. Using the Sb-Bi alloy film as a mask layer and SiN as a protective layer in a read-only memory disc, the super-resolution pits with diameters of 380 nm are read out by a dynamic setup, the laser wavelength is 780 nm and the numerical aperture of pickup lens is 0.45. The effects of the Sb-Bi thin film thickness, laser readout power and disc rotating velocity on the readout signal are investigated. The results show that the threshold laser power of super-resolution readout of the Sb-Bi mask layer is about 0.5 mW, and the corresponding carrier-to-noise ratio is about 20 dB at the film thickness of 50 nm. The super-resolution mechanism of the Sb-Bi alloy mask layer is discussed based on its temperature dependence of reflection.

Nano-polypyrrole supercapacitor arrays prepared by layer-by-layer assembling method in anodic aluminum oxide templates

A novel method for preparing nano-supercapacitor arrays, in which each nano-supercapacitor consisted of electropolymerized Polypyrrole (PPy) electrode / porous TiO2 separator / chemical polymerized PPy electrode, was developed in this paper. The nano-supercapacitors were fabricated in the nano array pores of anodic aluminum oxide template using the bottom-up, layer-by-layer synthetic method. The nano-supercapacitor diameter was 80 nm, and length 500 nm. Based on the charge/discharge behavior of nano-supercapacitor arrays, it was found that the PPy/TiO2/PPy array supercapacitor devices performed typical electrochemical supercapacitor behavior. The method introduced here may find application in manufacturing nano-sized electrochemical power storage devices in the future for their use in the area of microelectronic devices and microelectromechanical systems.

Structure and residual stress in gamma-LiAlO2, layer fabricated by vapor transport equilibration on (0001)sapphire

gamma-LiAlO2 layers with a highly preferred (1 0 0) orientation were prepared by vapor transport equilibration (VTE) technique on (0 0 0 1) sapphire substrate. Microststructure of the gamma-LiAlO2 layers was studied by XRD and SEM. In the temperature range from 750 to 1100 degrees C, the residual stress in the gamma-LiAlO2 layers varied from tensile to compressive with the increase of VTE temperature, and the critical point of the change between tensile and compressive stress is around 975 degrees C. (c) 2005 Elsevier B.V. All rights reserved.

The growth of gamma-LiAlO2 layer with a highly-preferred orientation on (0001) sapphire

Using vapor transport equilibration (VTE) technique we succeeded in the fabrication of single-phase gamma-LiAlO2 layer on (0001) sapphire substrate. X-ray diffraction indicated that the as-fabricated layer was highly textured with [100] orientation at proper VTE treatment temperature range from 1050 degrees C to 1100 degrees C. The main factors affecting the quality of the gamma-LiAlO2 layer were investigated by SEM and transmission spectra. These results reveal the possibility of fabricating gamma-LiAlO2 (100)//sapphire (0001) composite substrate for GaN-based epitaxial film by VTE.