Micro-scale abrasion behaviour of electroless Ni-P-SiC coating on aluminium alloy

Electroless nickel (EN) and electroless nickel composite (ENC) coatings were deposited on aluminium alloy substrate, LM24. The micro abrasion test was conducted to study the wear behaviour of the coatings with the effect of SiC concentration. Microhardness of the coatings was tested also. The wear scars were analysed using optical microscope and scanning electron microscope (SEM). The wear resistance was found to be improved in composite coating that has higher microhardness as compared to particles free and the bare aluminium substrate. In as-deposited condition for the composite coating, the wear volume increases on increase in SiC percentage in the coating but is found to be minimum for lower SiC percentage. The increase in hardness on heat treatment at 400°C is due to the hardening or grain coarsening with the formation Ni3P.

Oxidation-induced Cu coating on steel surface

Copper is accumulated in recycled steels and is difficult to be removed during steelmaking processes when steel scrap is used as steel sources. Meanwhile, copper characteristic properties are of importance both to human beings and to animals and plants. In this paper, integrated copper coating was observed on the surface of copper-containing steels when the steels were heated at around 1150°C. However, the copper was separately scattered after heating at 1000°C. The forming mechanisms of copper coating will be discussed in detail. By choosing proper descaling reagent, self-generated oxidation-induced copper coating appeared on the steel surface. The method proposed in this work is environmentally friendly for nontoxic chemicals being used. In addition, this provides a new concept for producing protective composite by oxidizing from the substrate directly and there is no binding problem.

Oxidation-induced Cu coating on steel surface

Copper is accumulated in recycled steels and is difficult to be removed during steelmaking processes when steel scrap is used as steel sources. Meanwhile, copper characteristics are of importance both to human beings and to animals and plants. In this paper, integrated copper coating was observed on the surface of copper-containing steels when the steels were heated at around 1150°C. However, the copper was separately scattered in and under the surface rust after heating at 1000°C. The forming mechanisms of copper coating are discussed in detail. By choosing a proper descaling reagent, self-generated oxidation-induced copper coating appeared on the steel surface. The method proposed in this work is environmentally friendly for nontoxic chemicals being used. In addition, this provides a new concept for producing protective composite by oxidizing from the substrate directly and there is no bonding problem.

Hole-making Process and Its impacts on the Fatigue Response of Ti -6Al-4V Aircraft Alloy

In this work, the impact of conventional drilling and helical milling processes on the fatigue response Ti-6Al-4V (grade 5 titanium alloy) has been presented. Results show that the work pieces produced by helical milling has a 119% longer fatigue life compared with the drilled pieces under dry machining condition, and a 96% longer fatigue life for helical milled piece under lubricated condition. The use of cutting fluid has led to longer fatigue lives – 15% longer for drilling and 3% longer for helical milling. Other results such as the machined surface roughness, alloy surface and sub-surface microstructures have also been studied in details.

3D FEM simulation of helical milling hole process for titanium alloy Ti-6Al-4V

As an emerging hole-machining methodology, helical milling process has become increasingly popular in aeromaterials manufacturing research, especially in areas of aircraft structural parts, dies, and molds manufacturing. Helical milling process is highly demanding due to its complex tool geometry and the progressive material failure on the workpiece. This paper outlines the development of a 3D finite element model for helical milling hole of titanium alloy Ti-6Al-4V using commercial FE code ABAQUS/Explicit. The proposed model simulates the helical milling hole process by taking into account the damage initiation and evolution in the workpiece material. A contact model at the interface between end-mill bit and workpiece has been established and the process parameters specified. Furthermore, a simulation procedure is proposed to simulate different cutting processes with the same failure parameters. With this finite element model, a series of FEAs for machined titanium alloy have been carried out and results compared with laboratory experimental data. The effects of machining parameters on helical milling have been elucidated, and the capability and advantage of FE simulation on helical milling process have been well presented.

Modifications of Surface Properties of Beta Ti by Laser Surface Treatment

β -type Ti-alloy is a promising biomedical implant material as it has a low Young’s modulus but is also known to have inferior surface hardness. Various surface treatments can be applied to enhance the surface hardness. Physical vapour deposition (PVD) and chemical vapour deposition (CVD) are two examples of this but these techniques have limitations such as poor interfacial adhesion and high distortion. Laser surface treatment is a relatively new surface modification method to enhance the surface hardness but its application is still not accepted by the industry. The major problem of this process involves surface melting which results in higher surface roughness after the laser surface treatment. This paper will report the results achieved by a 100 W CW fiber laser for laser surface treatment without the surface being melted. Laser processing parameters were carefully selected so that the surface could be treated without surface melting and thus the surface finish of the component could be maintained. The surface and microstructural characteristics of the treated samples were examined using X-ray diffractometry (XRD), optical microscopy (OM), 3-D surface profile & contact angle measurements and nano-indentation test.

Modifications of Surface Properties of Beta Ti by Laser Gas Diffusion Nitriding

Beta-type Ti-alloy is a promising biomedical implant material as it has a low Young’s modulus and is also known to have inferior surface hardness. Various surface treatments can be applied to enhance the surface hardness. Physical vapor deposition and chemical vapor deposition are two examples of this but these techniques have limitations such as poor interfacial adhesion and high distortion. Laser surface treatment is a relatively new surface modification method to enhance the surface hardness but its application is still not accepted by the industry. The major problem of this process involves surface melting which results in higher surface roughness after the laser surface treatment. This paper will report the results achieved by a 100 W continuous wave (CW) fiber laser for laser surface treatment without the surface being melted. Laser processing parameters were carefully selected so that the surface could be treated without surface melting and thus the surface finish of the component could be maintained. The surface and microstructural characteristics of the treated samples were examined using x-ray diffractometry, optical microscopy, three-dimensional surface profile and contact angle measurements, and nanoindentation test.

Effects of Poly (ε-caprolactone) Coating on the Properties of Three-Dimensional Printed Porous Structures

Powder-based inkjet three-dimensional printing (3DP) to fabricate pre-designed 3D structures has drawn increasing attention. However there are intrinsic limitations associated with 3DP technology due to the weak bonding within the printed structure, which significantly compromises its mechanical integrity. In this study, calcium sulphate ceramic structures demonstrating a porous architecture were manufactured using 3DP technology and subsequently post-processed with a poly (ε-caprolactone) (PCL) coating. PCL concentration, immersion time, and number of coating layers were the principal parameters investigated and improvement in compressive properties was the measure of success. Interparticle spacing within the 3DP structures were successfully filled with PCL material. Consequently the compressive properties, wettability, morphology, and in vitro resorption behaviour of 3DP components were significantly augmented. The average compressive strength, Young’s modulus, and toughness increased 217%, 250%, and 315%, following PCL coating. Addition of a PCL surface coating provided long-term structural support to the host ceramic material, extending the resorption period from less than 7 days to a minimum of 56 days. This study has demonstrated that application of a PCL coating onto a ceramic 3DP structure was a highly effective approach to addressing some of the limitations of 3DP manufacturing and allows this advanced technology to be potentially used in a wider range of applications.

Fibre laser joining of highly dissimilar materials: Commercially pure Ti and PET hybrid joint for medical device applications

Laser transmission joining (LTJ) is growing in importance, and has the potential to become a niche technique for the fabrication of hybrid plastic-metal joints for medical device applications. The possibility of directly joining plastics to metals by LTJ has been demonstrated by a number of recent studies. However, a reliable and quantitative method for defining the contact area between the plastic and metal, facilitating calculation of the mechanical shear stress of the hybrid joints, is still lacking. A new method, based on image analysis using ImageJ, is proposed here to quantify the contact area at the joint interface. The effect of discolouration on the mechanical performance of the hybrid joints is also reported for the first time. Biocompatible polyethylene terephthalate (PET) and commercially pure titanium (Ti) were selected as materials for laser joining using a 200 W CW fibre laser system. The effect of laser power, scanning speed and stand-off distance between the nozzle tip and top surface of the plastic were studied and analysed by Taguchi L9 orthogonal array and ANOVA respectively. The surface morphology, structure and elemental composition on the PET and Ti surfaces after shearing/peeling apart were characterized by SEM, EDX, XRD and XPS.

Laser-fabricated PET-Ti Hybrid Joints for Medical Device Applications

Currently, micro-joining of plastic parts to metal parts in medical devices is achieved by using medical adhesives, For example, pacemakers, defibrillators and neurological stimulators are designed using silicone adhesive to seal the joint between the polyurethane connector module and the titanium can [1]. Nevertheless, the use of adhesive is problematic because it requires a long time to cure and has high tendency to produce leachable products which might be harmful to the human body. An alternative for directly joining plastics to metal without adhesive is therefore required. Laser transmission joining (LTJ) is growing in importance, and has the potential to gain the niche in micro-fabrication of plastics-metal hybrid joints for medical device applications. The possibility of directly joining plastics to metal by LTJ technique have been demonstrated by a number of studies in recent literature [2]. The widely-accepted understanding of LTJ between plastics and metal is that generation and rapid expansion of micro-bubbles at the plastics-metal interface exert high local pressure to press the melted plastics towards the metal surface features during the laser processing [2]. This subsequently creates the plastics-metal hybrid joint by the mechanisms of mechanical interlocking as well as chemical and physical bonds between the plastics and metal surfaces. Although the micro-bubbles can help promote the mechanical interlocking effect to increase the joint strength, the creation of bubble is a random and complex process depending on the complicated interactions between the laser intensity, thermal degradation properties of plastics, surface temperature and topographical features of metal. In an ideal situation, it is desirable to create the hybrid plastics-metal joint without bubbles. However, the mechanical performance of the hybrid plastics-metal joint without bubbles is still unknown, and systematic comparison between the hybrid joints with and without bubbles is lacking in literature. This becomes the objective of this study. In this work, the laser process parameters were carefully chosen from a preliminary study, such that different hybrid joints: with and without bubbles can be produced and compared. Biocompatible PET and commercially pure Ti were selected as materials for laser joining.

Estudo da maquinabilidade das ligas Ti-6Al-4V e Co-28Cr-6Mo na fresagem de dispositivos biomédicos

Os estudos de maquinabilidade de biomateriais e outros materiais aplicados na área médica são extensos. Todavia, muitos destes estudos recorrem a modelos de geometria regular e operações elementares de maquinagem. Relativamente a estas, os estudos académicos atualmente disponíveis mostram que a tecnologia preferencial é o torneamento, opção que se fundamenta na simplicidade de análise (corte ortogonal). Saliente-se ainda que, neste contexto, a liga de titânio Ti-6Al-4V constitui o biomaterial mais utilizado. Numa perspetiva complementar, refira-se que as publicações científicas evidenciam que a informação disponível sobre a fresagem Ti-6Al-4V não é muito extensa e a do Co-28Cr-6Mo é quase inexistente. A presente dissertação enquadra-se neste domínio e representa mais uma contribuição para o estudo da maquinabilidade das ligas de Titânio e de crómio-cobalto. A aplicação de operações de maquinagem complexas, através do recurso a programas informáticos de fabrico assistido por computador (CAM), em geometrias complexas, como é o caso das próteses femorais anatómicas, e o estudo comparativo da maquinabilidade das ligas Co-28Cr-6Mo e Ti-6Al-4V, constituem os objetivos fundamentais deste trabalho de doutoramento. Neste trabalho aborda-se a problemática da maquinabilidade das ligas metálicas usadas nos implantes ortopédicos, nomeadamente as ligas de titânio, de crómiocobalto e os aços Inoxidáveis. Efetua-se ainda um estudo da maquinagem de uma prótese femoral com uma forma geométrica complexa, onde as operações de corte foram geradas recorrendo às tecnologias de fabrico assistido por computador (CAD/CAM). Posteriormente, procedeu-se ao estudo da maquinabilidade das duas ligas usadas neste trabalho, dando uma atenção particular à determinação das forças de corte para diferentes velocidades de corte. Para além da monitorização da evolução da força de corte, o desgaste das ferramentas, a dureza e a rugosidade foram avaliadas, em função da velocidade de corte imposta. Por fim, com base nas estratégias de maquinagem adotadas, analisa-se a maquinabilidade e selecionam-se os parâmetros de corte mais favoráveis para as ligas de Titânio e Crómio-cobalto. Os resultados obtidos mostram que a liga de crómio-cobalto induz maior valor de força de corte do que a liga de titânio. Observa-se um aumento progressivo das forças de corte quando a velocidade de corte aumenta, até atingir o valor máximo para a velocidade de corte de 80m/min, após a qual, a força de corte tende a diminuir. Apesar do fabricante das ferramentas recomendar a velocidade de corte de 50 m/min para ambos os materiais, conclui-se que a velocidade de corte de 65 m/min induz o mesmo desgaste na ferramenta de corte no caso da liga de titânio, e menor desgaste no caso da liga de crómio-cobalto.

Piezoelectricity and ferroelectricity in amino acid glycine

Bioorganic ferroelectrics and piezoelectrics are becoming increasingly important in view of their intrinsic compatibility with biological environment and biofunctionality combined with strong piezoelectric effect and switchable polarization at room temperature. Here we study piezoelectricity and ferroelectricity in the smallest amino acid glycine, representing a broad class of non-centrosymmetric amino acids. Glycine is one of the basic and important elements in biology, as it serves as a building block for proteins. Three polymorphic forms with different physical properties are possible in glycine (α, β and γ), Of special interest for various applications are non-centrosymmetric polymorphs: β-glycine and γ-glycine. The most useful β-polymorph being ferroelectric took much less attention than the other due to its instability under ambient conditions. In this work, we could grow stable microcrystals of β-glycine by the evaporation of aqueous solution on a (111)Pt/Ti/SiO2/Si substrate as a template. The effects of the solution concentration and Pt-assisted nucleation on the crystal growth and phase evolution were characterized by X-ray diffraction analysis and Raman spectroscopy. In addition, spin-coating technique was used for the fabrication of highly aligned nano-islands of β-glycine with regular orientation of the crystallographic axes relative the underlying substrate (Pt). Further we study both as-grown and tip-induced domain structures and polarization switching in the β-glycine molecular systems by Piezoresponse Force Microscopy (PFM) and compare the results with molecular modeling and computer simulations. We show that β-glycine is indeed a room-temperature ferroelectric and polarization can be switched by applying a bias to non-polar cuts via a conducting tip of atomic force microscope (AFM). Dynamics of these in-plane domains is studied as a function of applied voltage and pulse duration. The domain shape is dictated by both internal and external polarization screening mediated by defects and topographic features. Thermodynamic theory is applied to explain the domain propagation induced by the AFM tip. Our findings suggest that β-glycine is a uniaxial ferroelectric with the properties controlled by the charged domain walls which in turn can be manipulated by external bias. Besides, nonlinear optical properties of β-glycine were investigated by a second harmonic generation (SHG) method. SHG method confirmed that the 2-fold symmetry is preserved in as-grown crystals, thus reflecting the expected P21 symmetry of the β-phase. Spontaneous polarization direction is found to be parallel to the monoclinic [010] axis and directed along the crystal length. These data are confirmed by computational molecular modeling. Optical measurements revealed also relatively high values of the nonlinear optical susceptibility (50% greater than in the z-cut quartz). The potential of using stable β-glycine crystals in various applications are discussed in this work.

O que é para ti um tubarão? percepções das crianças sobre os tubarões em contexto (educação) informal de ciências

Dissertação de mest., Didáctica e Inovação no Ensino das Ciências (Biologia/Geologia), Faculdade de Ciências e Tecnologia, Univ. do Algarve, 2011

Influências e efeitos dos SI/TI no desempenho profissional

Influências e efeitos dos SI/TI no desempenho profissional.