Microstructural, dielectric and ferroelectric properties of calcium-modified lead titanate thin films derived by chemical processes

Ferroelectric Pb1-xCaxTiO3 (x = 0.24) thin films were formed on a Pt/Ti/SiO2/Si substrate by the polymeric precursor method using the dip-coating technique for their deposition. Characterization of the films bq X-ray diffraction showed a perovskite single phase with a tetragonal structure after annealing at 700 degreesC. Atomic force microscopy (AFM) analyses showed that the film had a smooth and crack-free surface with low surface roughness. In addition, the PCT thin film had a granular structure with an 80 nm grain size. The thickness of the films observed by the scanning electron microscopy (SEM) is 550 nm and there is a good adhesion between the film and substrate. For the electrical measurements metal-ferroelectric-metal of the type capacitors were obtained, where the thin films showed good dielectric and ferroelectric properties. The dielectric constant and dissipation factor at 1 kHz and measured at room temperature were found to be 457 and 0.03. respectively. The remanent polarization and coercive field for the: deposited films were P-r = 17 muC/cm(2) and E-c = 75 kV/cm, respectively. Moreover. The 550-nm-thick film showed a current density in the order of 10(-8) A/cm(2) at the applied voltage of 2 V. The high values of the thin film's dielectric properties are attributed to its excellent microstructural quality and the chemical homogeneity obtained by the polymeric precursor method. (C) 2001 Elsevier science Ltd. All rights reserved.

Electro-optical properties of Er-doped SnO2 thin films

Photoconductivity of SnO2 sol-gel films is excited, at low temperature, by using a 266 nm line-fourth harmonic-of a Nd:YAG laser. This line has above bandgap energy and promotes generation of electron-hole pairs, which recombines with oxygen adsorbed at grain boundary. The conductivity increases up to 40 times. After removing the illumination on an undoped SnO2 film, the conductivity remains unchanged, as long as the temperature is kept constant. Adsorbed oxygen ions recombine with photogenerated holes and are continuously evacuated from the system, leaving a net concentration of free electrons into the material, responsible for the increase in the conductivity. For Er doped SnO2, the excitation of conductivity by the laser line has similar behavior, however after removing illumination, the conductivity decreases with exponential-like decay. (C) 2003 Elsevier Ltd. All rights reserved.

Preparation and properties of ferroelectric Pb1-xCaxTiO3 thin films produced by the polymeric precursor method

Pb1- xCaxTiO3 thin films with x = 0.24 composition were prepared by the polymeric precursor method on Pt/Ti/SiO2/Si substrates. The surface morphology and crystal structure, and the ferroelectric and dielectric properties of the films were investigated. X-ray diffraction patterns of the films revealed their polycrystalline nature. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) analyses showed the surface of these thin films to be smooth, dense and crack-free with low surface roughness. The multilayer Pb1-xCaxTO3 thin films were granular in structure with a grain size of approximately 60-70 nm. The dielectric constant and dissipation factor were, respectively, 174 and 0.04 at a 1 kHz frequency. The 600-nm thick film showed a current density leakage in the order of 10(-7) A/cm(2) in an electric field of about 51 kV/cm. The C-V characteristics of perovskite thin films showed normal ferroelectric behavior. The remanent polarization and coercive field for the deposited films were 15 muC/cm(2) and 150 kV/cm, respectively. (C) 2001 Kluwer Academic Publishers.

Grazing incidence X-ray diffraction and atomic force microscopy analysis of BaBi2Ta2O9 thin films

Thin films of BaBi2Ta2O9 (BBT) composition were prepared through the metal organic decomposition method. The crystallinity, phase formation, crystallite size and morphology of the thin films were measured as a function of the type of substrate, stoichiometry of solution and process variables such as thickness and temperature. The thin films were investigated by grazing incidence X-ray diffractometry and atomic force microscopy (AFM) techniques. For the sample without excess of bismuth, diffraction peaks other than that of the BBT phase were observed. A well crystallized BBT single phase was observed for films prepared from a solution with 10% excess of bismuth, deposited on Si/Pt substrate, with a thickness up to 150 nm and sintered at temperatures of 700 degreesC. The thin BBT phase films heat-treated at 600 degreesC presented a diffraction pattern characteristic of samples with lower degree of crystallinity whereas for the thin films heat-treated at 800 degreesC, we observed the presence of other phases than the BBT. For the thin film deposited on the Sin+ substrate, we observe that the peaks corresponding to the BBT phase are broader than that observed on the samples deposited on the Pt and Si/Pt substrates. No variation of average crystallite size was observed as the excess of Bi increased from 10 to 20%. AFM images for the samples showed that the increasing the amount of bismuth promotes grain growth. The average surface roughness measured was in the range of 16-22 nm showing that the bismuth amount had no or little effect on the roughness of films. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Structural and electrical properties of SrBi2Nb2O9 thin films prepared by chemical aqueous solution at low temperature

SrBi2Nb2O9 (SBN) thin films were prepared by the polymeric precursors method and deposited by dip coating onto Pt/Ti/SiO2/Si(100) substrates. The dip-coated films were specular and crack-free and crystallized during firing at 700 degrees C. Microstructure and morphological evaluation were followed by grazing incident X-ray diffraction (GIXRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM). The films exhibited somewhat porous grain structure with rounded grains of about 100 nm. For the electrical measurements, gold electrodes of 300 mu m in diameter were sputter deposited on the top surface, forming a metal-ferroelectric-metal (MFM) configuration. The remanent polarization (P-r) and coercive field (E-c) were 5.6 mu C/cm(2) and 100 kV/cm, respectively. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Spectral redistribution of waveguided emission in BEH-PPV films

We report on spectral redistribution of the photoluminescence (PL) emission from the edge of thin-film planar waveguides of the conjugated polymer BEH-PPV [Poly(2,5-bis(2'-ethyl-hexyl)-1,4-phenylenevinylene] induced by self-absorption in the polymer film. The PL spectra present drastic changes and displace to longer wavelengths with increasing self-absorption. We observe an enhancement of the absolute PL intensity at longer wavelengths, which was interpreted as due to re-emission of self-absorbed photons. The significant efficiency for the PL re-emission suggests the use of self-absorption as a mechanism for tuning the emission into the near infrared.

Spectroscopic characterization of BPSCCO thin films grown by dip-coating technique

This work describes the growth of Bi2-xPbxSr2Can-1CunO2n+4 thin films by the dip-coating technique for 0.4 less than or equal to x less than or equal to 1. X-ray and Raman spectroscopic techniques were carried out in order to characterize the films at room temperature. From X-ray data it is observed that the films are multi-phased presenting phases 2201, 2212 and 2223 along with the undesirable Ca2PbO4 phase. It is also observed that phase 2212 becomes dominant when Pb content increases. The Raman modes observed agree with the overall features expected for these compounds. (C) 2003 Elsevier B.V. B.V. All rights reserved.

The influence of crystallization route on the properties of lanthanum-doped Bi4Ti3O12 thin films prepared from polymeric precursors

Pure and lanthanum-doped Bi4Ti3O12 thin films were deposited on Pt/Ti/SiO2/Si substrate using a polymeric precursor solution. The spin-coated films were specular and crack-free and crystalline after annealing at 700 degreesC for 2 h. Crystallinity and morphological evaluation were examined by X-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Multilayered films obtained using the intermediate-crystalline layer route present a dense microstructure with spherical grains. Films obtained using the intermediate-amorphous layer, present elongated grains around 250 nm in size. The dielectric and ferroelectric properties of the lanthanum-doped Bi4Ti3O12 films are strongly affected by the crystallization route. The hysteresis loops are fully saturated with a remnant polarization and drive voltage of the films, heat-treated by the intermediate-crystalline (P-r = 20.2 muC/cm(2) and V = 1.35 V) and for the film heat-treated by amorphous route (P-r = 22.4 muC/cm(2) and V = 2.99 V). (C) 2004 Elsevier B.V. All rights reserved.

Optical properties of potassium niobate thin films prepared by the polymeric precursor method

Thin films of potassium niobate were deposited on MgO (100) substrates by the polymeric precursor method and annealing in static air at 600 degreesC for 20 h. The obtained films were characterized by X-ray diffraction, atomic force microscopy (AFM) and the prism coupling method. The phi-scan diffraction evidenced the growth of the films with fourfold symmetry. AFM study shows that the films are homogeneous, dense and present a smooth surface. The refractive index and optical losses were strongly influenced by the degree of crystallinity. (C) 2004 Elsevier B.V. All rights reserved.

Influence of the solution pH on the morphological, structural and electrical properties of Bi3.50La0.50Ti3O12 thin films obtained by the polymeric precursor method

Lanthanum-doped Bi4Ti3O12 thin films (BLT) were deposited on Pt/Ti/SiO2/Si substrates using a polymeric precursor solution. The spin-coated films were specular, crack-free and crystalline after annealing at 700 degrees C for 2 h. Crystallinity and morphological evaluation were examined by X ray diffraction (YRD) and atomic force microscopy (AFM). The stability of the formed complex is of extreme importance for the formation of the perovskite phase. Films obtained from acid pH solution present elongated grains around 200 ran in size, whereas films obtained from basic solution present a dense microstructure with spherical grains (100 nm). The dielectric and ferroelectric properties of the BLT films are strongly affected by the solution pH. The hysteresis loops are fully saturated with a remnant polarization and coercive voltage of P-r=20.2 mu C/cm(2) and V-c = 1.35 V and P-r= 15 mu C/cm(2) and V-c = 1.69 V for the films obtained from basic and acid solutions, respectively. (C) 2005 Elsevier B.V. All rights reserved.

Ferroelectric and piezoelectric properties of bismuth titanate thin films grown on different bottom electrodes by soft chemical solution and microwave annealing

Bismuth titanate (Bi4Ti3O12, BIT) films were evaluated for use as lead-free piezoelectric thin films in micro-electromechanical systems. The films were grown by the polymeric precursor method on LaNiO3/SiO2/Si (1 0 0) (LNO), RuO2/SiO2/Si (1 0 0) (RuO2) and Pt/Ti/SiO2/Si (1 0 0) (Pt) bottom electrodes in a microwave furnace at 700 degrees C for 10 min. The domain structure was investigated by piezoresponse force microscopy (PFM). Although the converse piezoelectric coefficient, d(33), regardless of bottom electrode is around (similar to 40 pm/V), those over RuO2 and LNO exhibit better ferroelectric properties, higher remanent polarization (15 and 10 mu C/cm(2)), lower drive voltages (2.6 and 1.3 V) and are fatigue-free. The experimental results demonstrated that the combination of the polymeric precursor method assisted with a microwave furnace is a promising technique to obtain films with good qualities for applications in ferroelectric and piezoelectric devices. (c) 2006 Elsevier Ltd. All rights reserved.

Hydrogen influence on gallium arsenide thin films prepared by rf-magnetron sputtering technique

We investigate the effect of the hydrogen intentional incorporation on the structural properties of the amorphous gallium arsenide prepared by rf-magnetron sputtering technique. The properties of the non-hydrogenated films are: band gap of 1.4 eV (E-04), Urbach energy of 110 meV, stoichiometric composition ([As]/[Ga] = 0.50), and dark conductivity of about 3.2 x 10(-5) (Omega.cm)(-1). Hydrogen was incorporated in the films by the introduction of an electronically controlled H-2 flux during deposition, keeping constant the other deposition parameters. It was observed that small hydrogen incorporation produces a great change in the structural properties of the films. The main changes result from the formation of GaAs nanocrystals with mean sizes of about 7 nm into the amorphous network.

SrBi2Nb2O9 thin films deposited by dip coating using aqueous solution

A new approach for SrBi2Nb2O9 (SBN) thin films synthesis using aqueous solution was successfully experienced. The deposition solution was prepared from Sr-Bi-Nb mixed-citrate solution, requiring no special atmosphere and using common reagents. Films were deposited by dip coating onto Pt/Ti/SiO2/Si(100) substrates and hear treated at temperatures ranging from 300 to 700 degrees C. The process of formation and crystallization of SrBi2Nb2O9 thin films, prepared by the aqueous solution method have been studied with particular emphasis on the microstructure of crystallized films. Crystalline phases formation were followed by grazing incident X-ray diffraction (GIXRD), microstructure characterization was evaluated by scanning electron microscopy (SEM) and surface roughness were observed using atomic for ce microscopy (AFM). To reach the desired thickness, substrates were dipped in the deposition solution twice, forming double-layered films. The thickness of each layer ranged from 80 to 100 nm. (C) 1999 Elsevier B.V. Limited. All rights reserved.

Local and global magnetic properties of Zn1-xCoxO and Mn-doped GaAs thin films

Amorphous and crystalline thin films of Mn-doped(0.5%-10%) GaAs and crystalline thin films of Zn1-xCoxO(x = 3%-20%) were investigated by means of magnetic susceptibility and electron spin resonance (ESR). For the Mn-doped GaAs samples, our results show the absence of ferromagnetic ordering for the amorphous films in the 300 > T > 2 K temperature range, in contrast to the ferromagnetism found in crystalline films for T-C < 110 K. A single ESR line with a temperature independent g-value (g similar to 2) is observed for the amorphous films, and the behavior of this ESR linewidth depends on the level of crystallinity of the film. For the Mn-doped GaAs crystalline films, only a ferromagnetic mode is observed for T < TC when the film is ferromagnetic. Turning now the Zn1-xCoxO films, ferromagnetic loops were observed at room temperature for these films. The magnetization data show an increasing of the saturation magnetization M. as a function of x reaching a maximum value for x approximate to 10%. ESR experiments at T = 300 K in the same films show a strong anisotropic ferromagnetic mode (FMR) for x = 0.10.

Correlation between the surface morphology and structure and the photoluminescence of amorphous PbTiO3 thin films obtained by the chemical route

A polymeric precursor method was used to synthesis PbTiO3 amorphous thin film processed at low temperature. The luminescence spectra of PbTiO3 amorphous thin films at room temperature revealed an intense single-emission band in the visible region, the visible emission band was found to be dependent on the thermal treatment history, Photoluminescence properties Versus different annealing temperatures were investigated. The experimental results (XRD, AFM, FL) indicate that the nature of photoluminescence (PL) must be related to the disordered structure of PbTiO3 amorphous thin films, Copyright (C) 2000 John Wiley & Sons, Ltd.