On Ti-18Si-6B and Ti-7.5Si-22.5B powder alloys prepared by high-energy ball milling and sintering

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

SILVER DISSOLUTION ON COPPER-BASED ALLOYS

Electrical resistivity measurements and scanning electron microscopy was used to study the dissolution of silver on Cu-Ag and Cu-Al-Ag alloys. The results seem to indicate that the dissolution temperature is affected by the addition of aluminium.

Electrochemical behavior of metallic chromium in chloride media

The electrochemical behavior of metallic chromium in aqueous solutions containing chloride ions at different pH was studied by means of open-circuit potential vs. time measurements, cyclic voltammetry and electrochemical impedance spectroscopy. The composition of the surface oxides was analyzed by XPS. For solutions with pH<3 the formation of a passive layer occurs via a dissolution/precipitation process while for pH>3 the mechanism changes. XPS analysis revealed that Cr2O3 basically constitutes the passive layer.

MECHANISM OF ACTION OF COBALT IONS ON RAT OSSEOUS PLATE ALKALINE-PHOSPHATASE

Polidocanol-solubilized osseous plate alkaline phosphatase was modulated by cobalt ions in a similar way as by magnesium ions. For concentrations up to 1 mu M, the Chelex-treated enzyme was stimulated by cobalt ions, showing K-d = 6.0 mu M, V = 977.5 U/mg, and site-site interactions (n = 2.5). Cobalt-enzyme was highly unstable at 37 degrees C, following a biphasic inactivation process with inactivation constants of about 0.0625 and 0.0015 min(-1). Cobalt ions stimulated the enzyme synergistically in the presence of magnesium ions (K-d = 5.0 mu M; V = 883.0 U/mg) or in the presence of zinc ions (K-d = 75.0 mu M; V = 1102 U/mg). A steady-state kinetic model for the modulation of enzyme activity by cobalt ions is proposed.

Correlation of reactivity with structural factors in a series of Fe(II) substituted cobalt ferrites

A series of powdered cobalt ferrites, CoxFe3-xO4 with 0.66 <= x< 1.00 containing different amounts of Fe-II, were synthesized by a mild procedure, and their Fe and Co site occupancies and structural characteristics were explored using X-ray anomalous scattering and the Rietveld refinement method. The dissolution kinetics, measured in 0.1 M oxalic acid aqueous solution at 70 degrees C, indicate in all cases the operation of a contracting volume rate law. The specific rates increased with the Fell content following approximately a second-order polynomial expression. This result suggests that the transfer of Fe-III controls the dissolution rate, and that the leaching of a first layer of ions Co-II and Fe-II leaves exposed a surface enriched in slower dissolving octahedral Fe-III ions. Within this model, inner vicinal lattice Fe-II accelerates the rate of Fe-III transfer via internal electron hopping. A chain mechanism, involving successive electron transfers, fits the data very well. (C) 2006 Elsevier B.V. All rights reserved.

Thermal behavior of the Cu-10 mass%Al and Cu-10 mass%Al-4 mass%Ag alloys

The thermal behavior of the Cu-10 mass%Al and Cu-10 mass% Al-4 mass%Ag alloys was studied using classical differential thermal analysis (DTA), optical microscopy (OM) and X-ray diffractometry (XRD). The DTA curves were obtained for annealed and quenched samples. The results indicated that the presence of silver introduces new thermal events, associated to the formation of a silver-rich phase, to the shift of the equilibrium concentration to higher A1 contents and to the decomposition of the silver-rich phase in the same temperature range of the beta(1) phase decomposition.

EFFECT OF THE ADDITION OF CR AND NB ON THE MICROSTRUCTURE AND ELECTROCHEMICAL CORROSION OF HEAT-TREATABLE AL-ZN-MG ALLOYS

The effect of the addition of Cr and Nb on the microstructure and the electrochemical corrosion of the weldable, high-strength and stress corrosion cracking (SCC) resistant Al-5%Zn-1.67%Mg-0.23%Cu alloy (H) has been studied. Combined additions of the alloying elements, J (with Nb), L (with Cr) and O (with Cr and Nb) and different heat treatments, ST (cold-rolled), A (annealed), F (quenched), B (quenched and aged) and C (quenched in two steps and aged), to obtain different microstructures and hardness have been performed. To correlate the electrochemical corrosion with the microstructure of the specimens, corrosion potential (E(cor)) measurements in different chloride solutions were performed and optical microscopy, SEM, TEM and EDX were applied. In chloride solutions containing dissolved O-2 or H2O2, the present alloys were polarized up to the pitting attack. It was shown that the E(cor) measurements were very sensitive to the alloy composition and heat treatment, increasing in the order H < J < L < O < Al (for a given heat treatment) and F < A approximate to ST < B < C (for a given alloy). The MgZn2 precipitates of the annealed (A) and cold-rolled (ST) specimens were dissolved in chloride solutions containing oxidizing agents and pitting attack was shown to develop in the cavities where the precipitates were present. In the specimens B and C, the compositions of the precipitate free zones was found to be equal to that of the matrix solid solution and preferential intergranular attack was not evident, this being in agreement with their SCC resistance. The addition of Cr and Nb increased the pitting corrosion resistance. The effects of Cr and Nb were additive, that of Cr being predominant, either, in the E(cor) shift or in the increase in the pitting corrosion resistance.

Shear bond strengths of a ceramic system to alternative metal alloys

Statement of problem. The success of metal-ceramic restorations is influenced by the compatibility between base metal alloys and porcelains. Although porcelain manufacturers recommend their own metal systems as the most compatible for fabricating metal-ceramic prostheses, a number of alloys have been used.Purpose. This study evaluated the shear bond strength between a porcelain system and 4 alternative alloys.Material and methods. Two Ni-Cr alloys: 4 ALL and Wiron 99, and 2 Co-Cr alloys: IPS d.SIGN 20 and Argeloy NP were selected for this study. The porcelain (IPS d.Sign porcelain system) portion of the cylindrical inetal-ceramic specimens was 4 mm thick and 4 mm high; the metal portion was machined to 4 x 4 mm, with a base that was 5 nun thick and 1 mm high. Forty-four specimens were prepared (n=11). Ten specimens from each group were subjected to a shear load oil a universal testing machine using a 1 min/min crosshead speed. One specimen from each group was observed with a scanning electron microscope. Stress at failure (MPa) was determined. The data were analyzed with a 1-way analysis of variance (alpha=.05).Results. The groups, all including IPS d.Sign porcelain, presented the following mean bond strengths (+/-SD) in MPa: 4 ALL, 54.0 +/- 20.0; Wiron, 63.0 +/- 13.5; IPS d.SIGN 20, 71.7 +/- 19.2; Argeloy NP, 55.2 +/- 13.5. No significant differences were found among the shear bond strength values for the metal-ceramic specimens tested.Conclusion. None of the base metal alloys studied demonstrated superior bond strength to the porcelain tested.

Yield and nitrogen uptake of peanuts as affected by lime, cobalt, and molybdenum

Peanut response to lime has been associated to calcium (Ca) nutrition, but a higher nitrogen (N) uptake has been observed in limed plots probably due to an increase in molybdenum (Mo) availability. A two-year experiment was conducted to study the effects of Mo, cobalt (Co), and liming on peanut yields and N nutrition. Peanut seeds were treated with Mo and/or Co and grown in soil with base saturation about 13, 41, 57, and 71%. There was no effect of seed treatment with Co on peanut yields or N nutrition. Liming and Mo application increased N contents in the leaves. Nitrogen uptake was increased by Mo and liming in cv. Tatu and only by liming in cv. Tupa. Manganese (Mn) contents in the leaves were decreased by liming. The higher yields were observed when the Ca/Mn ratio in the leaves was above 25. In acid soils, low availability of Mo and Mn toxicity can impair N acquisition by peanut plants and decrease grain yields.

Electrochemical studies with copper-based alloys: open-circuit potential oscillations in alkaline media

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Coating residual stress effects on fatigue performance of 7050-T7451 aluminum alloy

The tendency of the aircraft industry is to enhance customer value by improving performance and reducing environmental impact. In view of availability, aluminum alloys have a historically tendency to faster insertion due to their lower manufacturing and operated production infrastructure. In landing gear components, wear and corrosion control of many components is accomplished by surface treatments of chrome electroplating on steel or anodizing of aluminum. One of the most interesting environmentally safer and cleaner alternatives for the replacement of hard chrome plating or anodizing is tungsten carbide thermal spray coating, applied by the high velocity oxy fuel (HVOF) process. However, it was observed that residual stresses originating from these coatings reduce the fatigue strength of a component.An effective process as shot peening treatment, considered to improve the fatigue strength, pushes the crack sources beneath the surface in most of medium and high cycle cases, due to the compressive residual stress field induced. The objective of this research is to evaluate a tungsten carbide cobalt (WC-Co) coating applied by the high velocity oxy fuel (HVOF) process, used to replace anodizing. Anodic films were grown on 7050-T7451 aluminum alloy by sulfuric acid anodizing, chromic acid anodizing and hard anodizing. The influence on axial fatigue strength of anodic films grown on the aluminum alloy surface is to degrade the stress-life performance of the base material. Three groups of specimens were prepared and tested in axial fatigue to obtain S-N curves: base material, base material coated by HVOF and base material shot peened and coated.Experimental results revealed increase in the fatigue strength of Al 7050-T7451 alloy associated with the WC 17% Co coating. on the other hand, a reduction in fatigue life occurred in the shot peened and coated condition. Scanning electron microscopy technique and optical microscopy were used to observe crack origin sites, thickness and coating/substrate adhesion. (c) 2007 Elsevier B.V. All rights reserved.

Investigation of the systems silica and silica containing chromium in alcohol medium

The purpose of this work is to obtain micrometer sized spherical particles of silica and silica-chromium from sodium silicate. Spherical particles were prepared by sol-gel method from hydrolysis to polycondensation of aqueous sodium silicate in alcohol medium. Chromium was added to the system for some samples. Compositions and morphologies were achieved by changing the precipitation agent. X-ray diffractometry, electrophoretic mobility, infrared spectroscopy and scanning electron microscopies were carried out on these particles to identify phases, determine particle mobility, morphology, particle sizes, shapes and order at short distance. Non-crystalline silica particles with spherical shapes and micrometric size were obtained. The surface potentials of the silica particles differed from that of the silica-chromium particles. (C) 1999 Elsevier B.V. B.V. All rights reserved.