Influence of growth pressure of a GaN buffer layer on the properties of MOCVD GaN

The influence of growth pressure of GaN buffer layer on the properties of MOCVD GaN on alpha-Al2O3 has been investigated with the aid of a home-made in situ laser reflectometry measurement system. The results obtained with in situ measurements and scanning electron microscope show that with the increase in deposition pressure of buffer layer, the nuclei increase in size, which roughens the surface, and delays the coalescence of GaN nuclei. The optical and crystalline quality of GaN epilayer was improved when buffer layer was deposited at high pressure.

Defects in GaN films grown on Si(111) substrates by metal-organic chemical vapour deposition

We report the transmission-electron microscopy study of the defects in wurtzitic GaN films grown on Si(111) substrates with AIN buffer layers by the metal-organic chemical vapour deposition method. The In0.1Ga0.9N/GaN multiple quantum well (MQW) reduced the dislocation density by obstructing the mixed and screw dislocations passing through the MQW. No evident reduction of the edge dislocations density by the MQW was observed. It was found that dislocations with screw component can be located at the boundaries of sub-grains slightly in-plane misoriented.

RBS/channeling study and photoluminscence properties of Er-implanted GaN

The Raman back scattering/channeling technique was used to analyze the damage recovery at different annealing temperatures and to determine the lattice location of the Er-implanted GaN samples. A better damage recovery was observed with increasing annealing temperature below 1000degreesC, but a complete recovery of the implantation damage cannot be achieved. For a sample annealed for at 900degreesC 30 min the Er and Ga angular scans across the <0001> axis was measured indicating that about 76% of Er ions occupies substitutional sites. Moreover, the photoluminscence (PL) properties of Er-implanted GaN thin films have been also studied. The experimental results indicate that those samples annealed at a higher temperature below 1000degreesC had a stronger 1539nm PL intensity. The thermal quenching of PL intensity for samples annealed at 900degreesC measured at temperatures from 15K to 300K is 30%.

Influence of high-temperature AIN buffer thickness on the properties of GaN grown on Si(111)

The influences of AlN buffer thickness on the optical and the crystalline properties of metalorganic chemical vapor deposition wurtzite GaN layers on Si(I 11) substrate have been investigated. High-resolution X-ray diffraction and photoluminescence measurement reveal that the thickness of AlN buffer exerts a strong influence on the distribution of dislocation and stress in GaN epilayer. The evidence is further reinforced by atomic force microscopic observation of AlN nucleation process. The optimum thickness of AlN buffer to effectively suppress Si diffusion has been determined by secondary-ion mass spectroscopy to be in the range of 13-20 nm. In addition, it is found that appropriate Si diffusion in AlN buffer helps to compensate the tensile strain in GaN, which subsequently improves the optical quality of GaN on Si(I 1, 1), and reduces the cracks over the GaN surface. (C) 2003 Elsevier B.V. All rights reserved.

Influences of reactor pressure of GaN buffer layers on morphological evolution of GaN grown by MOCVD

The morphological evolution of GaN thin films grown on sapphire by metalorganic chemical vapor deposition was demonstrated to depend strongly on the growth pressure of GaN nucleation layer (NL). For the commonly used two-step growth process, a change in deposition pressure of NL greatly influences the growth mode and morphological evolution of the following GaN epitaxy. By means of atomic force microscopy and scanning electron microscope, it is shown that the initial density and the spacing of nucleation sites on the NL and subsequently the growth mode of FIT GaN epilayer may be directly controlled by tailoring the initial low temperature NL growth pressure. A mode is proposed to explain the TD reduction for NL grown at relatively high reactor pressure. (C) 2003 Elsevier B.V. All rights reserved.

Microstructure of GaN films grown on Si(111) substrates by metalorganic chemical vapor deposition

We report the transmission electron microscopy (TEM) study of the microstructure of wurtzitic GaN films grown on Si(I I I) substrates with AlN buffer layers by metalorganic chemical vapor deposition (MOCVD) method. An amorphous layer was formed at the interface between Si and AlN when thick GaN film was grown. We propose the amorphous layer was induced by the large stress at the interface when thick GaN was grown. The In0.1Ga0.9N/GaN multiple quantum well (MQW) reduced the dislocation density by obstructing the mixed and screw dislocations from passing through the MQW. But no evident reduction of the edge dislocations by the MQW was observed. It was found that dislocations located at the boundaries of grains slightly in-plane misoriented have screw component. Inversion domain is also observed. (C) 2003 Elsevier B.V. All rights reserved.

Thickness measurement of GaN epilayer using high resolution X-ray diffraction technique

In this paper we propose a new method for measuring the thickness of the GaN epilayer, by using the ratio of the integrated intensity of the GaN epilayer X-ray diffraction peaks to that of the sapphire substrate ones. This ratio shows a linear dependence on the GaN epilayer thickness up to 2 mum. The new method is more accurate and convenient than those of using the relationship between the integrated intensity of GaN epilayer diffraction peaks and the GaN thickness. Besides, it can eliminate the absorption effect of the GaN epilayer.

Photoluminescence of Mg-doped GaN grown by metalorganic chemical vapor deposition

Two Mg-doped GaN films with different doping concentrations were grown by a metalorganic chemical vapor deposition technique. Photoluminescence (PL) experiments were carried out to investigate the optical properties of these films. For highly Mg-doped GaN, the PL spectra at 10 K are composed of a blue luminescence (BL) band at 2.857 eV and two excitonic luminescence lines at 3.342 eV and 3.282 eV, in addition to a L2 phonon replica at 3.212 eV. The intensity of the L1 line decreases monotonously with an increase,in temperature. However, the intensity of the L2 line first slowly increases at first, and then decreases quickly with an increase in temperature. The two lines are attributed to bound excitonic emissions at extended defects. The BL band is most likely due to the transition from deep donor Mg-V-N complex to Mg shallow acceptor. From the temperature dependence of the luminescence peak intensity of the BL band, the activation energy of acceptor Mg was found to be 290 meV. (C) 2003 American Vacuum Society.

Stress and its effect on optical properties of GaN epilayers grown on Si(111), 6H-SiC(0001), and c-plane sapphire

The stress states in unintentionally doped GaN epilayers grown on Si(111), 6H-SiC(0001), and c-plane sapphire, and their effects on optical properties of GaN films were investigated by means of room-temperature confocal micro-Raman scattering and photoluminescence techniques. Relatively large tensile stress exists in GaN epilayers grown on Si and 6H-SiC while a small compressive stress appears in the film grown on sapphire. The latter indicates effective strain relaxation in the GaN buffer layer inserted in the GaN/sapphire sample, while the 50-nm-thick AlN buffer adopted in the GaN/Si sample remains highly strained. The analysis shows that the thermal mismatch between the epilayers and the substrates plays a major role in determining the residual strain in the films. Finally, a linear coefficient of 21.1+/-3.2 meV/GPa characterizing the relationship between the luminescent bandgap and the biaxial stress of the GaN films is obtained. (C) 2003 American Institute of Physics.

Effects of reactor pressure on GaN nucleation layers and subsequent GaN epilayers grown on sapphire substrate

The influence of reactor pressure on GaN nucleation layer (NL) and the quality of subsequent GaN on sapphire is studied. The layers were grown by low-pressure metalorganic chemical vapor deposition (MOCVD) on c-plane sapphire substrates and investigated by in situ laser reflectometry, atomic force microscope, scanning electron microscope, X-ray diffraction and photoluminescence. With the increase of reactor pressure prior to high-temperature GaN growth, the size of GaN nuclei formed after annealing decreases, the spacing between nucleation sites increases and the coalescence of GaN nuclei is deferred. The optical and crystalline qualities of GaN epilayer were improved when NLs were deposited at high pressure. The elongated lateral overgrowth of GaN islands is responsible for the quality improvement. (C) 2003 Elsevier Science B.V. All rights reserved.

Thermal annealing behaviour of Pt on n-GaN Schottky contacts

The structural evolution and temperature dependence of the Schottky barrier heights of Pt contacts on n-GaN epilayer at various annealing temperatures were investigated extensively by Rutherford backscattering spectrometry, x-ray diffraction measurements, Auger electron spectroscopy, scanning electron microscopy and current-voltage measurements. The temperature dependence of the Schottky barrier heights may be attributed to changes of surface morphology of Pt films on the surface and variation of nonstoichiometric defects at the interface vicinity. Experimental results indicated the degradation of Pt contacts on n-GaN above 600 degreesC.

Metal-semiconductor-metal ultraviolet photodetector based on GaN

A metal-semiconductor-metal (MSM) ultraviolet photodetector has been fabricated using unintentionally doped n-GaN films grown on sapphire substrates. Its dark current, photocurrent under the illumination with lambda = 360 nm light, responsivity, and the dependence of responsivity on bias voltage were measured at room temperature. The dark current of the photodetector is 1.03 nA under 5 V bias, and is 15.3 nA under 10 V bias. A maximum responsivity of 0.166 A/W has been achieved under the illumination with lambda = 366 nm light and 15 V bias. It exhibits a typical sharp band-edge cutoff at the wavelength of 366 nm, and a high responsivity at the wavelength from 320 nm to 366 nm. Its responsivity under the illumination with lambda = 360 nm light increases when the bias voltage increases.

The growth morphologies of GaN layer on Si(111) substrate

The growth morphologies of metalorganic chemical vapor deposition (MOCVD) grown GaN layer on Si(111) substrate were studied using atomic force microscopy and transmission electron microscopy. It was found that the growth process of GaN/Si(111) consisted of two cycles of island growth and coalescence. These two cycles process differs markedly from that of one cycle process reported. The stress of evolving GaN layers on Si(111) was characterized by measuring the lattice constant c of GaN using X-ray diffraction (XRD) technique. It was proposed that the large tensile stress within the film during growth initiated this second island growth cycle, and the interaction between the GaN islands with high orientational fluctuation on the buffer layer induced this large tensile growth stress when coalescence occurred. (C) 2002 Elsevier Science B.V. All rights reserved.

Luminescence study of (11(2)over-bar0) GaN film grown by metalorganic chemical-vapor deposition

Investigations on photoluminescence properties of (11 (2) over bar0) GaN grown on (1 (1) over bar 02) Al2O3 substrate by metalorganic chemical-vapor deposition are reported. Several emission lines not reported before are observed at low temperature. The sharp peak at 3.359 eV is attributed to the exciton bound to the neutral acceptor. Another peak at 3.310 eV represents a free-to-bound, probably a free electron-to-acceptor, transition. The 3.241 and 3.170 eV lines are interpreted as phonon replica lines of the 3.310 eV line. The phonon energy is 70 meV, consistent with the energy of transverse optical E-1 phonon. The optical properties of the lines are analyzed. (C) 2003 American Institute of Physics.