Low-temperature synthesis of single-phase Co7Sb2O12

Polycrystalline Co7Sb2O12 compounds have been synthesized by a chemical route, which is based on a modified polymeric precursor method. In order to study the physical properties of the samples, X-ray diffraction (XRD), thermal analyses (TG and DSC), infrared spectroscopy (IR), specific surface area (BET), and magnetization measurements were performed on these materials. Characterization through XRD revealed that the samples are single-phase after a heat-treatment at 1100degreesC for 2h, while the X-ray patterns of the samples heat-treated at lower temperatures revealed the presence of additional Bragg reflections belonging to the Co6Sb2O6 phase. These data were analyzed by means of Rietveld refinement and further analyze showed that Co7Sb2O12 displays an inverse spinel crystalline structure. In this structure, the Co2+ ions occupy the eight tetrahedral positions, and the sixteen octahedral positions are randomly occupied by the Sb5+ and Co2+ ions. IR studies disclosed two strong absorption bands, v(1) and v(2), in the expected spectral range for a spinel-type binary oxide with space group Fd3m. Exploratory studies concerning the magnetic properties indicated that this sample presents a spin-glass transition at T-f similar to 64 K. (C) 2004 Elsevier B.V. All rights reserved.

Monodispersed spindle-type goethite nanoparticles from Fe-III solutions

A new synthetic route for producing monodispersed and single crystal acicular goethite particles with small particle size and a high axial ratio adequate for use as a high density magnetic recording media precursor is reported. It essentially consists of the hydrolysis of alkaline Fe-III suspensions in the presence of carbonate by a three-step procedure, the formation of ferrihydrite primary particles, the ferrihydrite dissolution and nucleation of goethite, and the growth of the goethite nuclei. Changing the temperature of heating during ageing achieved a separation of the two last stages. X-Ray diffraction, transmission electron microscopy, infrared spectroscopy and surface area data have been used to determine the mechanism responsible for the formation of goethite particles with controlled size and shape. The best conditions to prepare monodispersed goethite particles have been established. The results show that uniform goethite particles of (a) 60 nm length with an axial ratio of 6 and (b) 230 nm length with a high axial ratio of 10, can be obtained by using an [OH]/[Fe] molar ratio of 0.35 in the initial suspensions with carbonate or sodium hydroxide, respectively. The [OH]/[Fe] molar ratio determines the particle size and elongation by controlling the hydrolysis reaction rate, while the carbonate ions promote a constant [OH] in the solution, keeping the pH around 10 during the entire synthesis process. This procedure, associated with the appropriate temperature control, leads, under certain conditions, to highly homogeneous goethite particles with sizes smaller than those obtained using sodium hydroxide with the same [OH]/[Fe] ratio.

Experimental and theoretical study of the compound [Pd(dmba)(NCO)(imz)]

The compound [Pd(dmba)(NCO)(imz)] (dmba = N,N-dimethylbenzilamine; NCO = cyanate; imz = imidazole) was studied through experimental and theoretical methods. The complex was synthesized and characterized by IR and NMR spectroscopy. To an appropriate representation of the molecular environment, Gaussian basis sets for the constituent atoms of the compound were built and, after adequate supplementation with polarization and diffuse functions, they were used to study the molecule. Calculations of electronic and vibrational structure of two possible isomers were carried out, showing that the compound, which contains the NCO GROUP trans to the Pd-C bond, is 4.29 kcal/mol more stable than the analogous one, where the imz ligand is trans to the Pd-C bond. The calculated molecular parameters, bond distances, and bond angles showed that the geometry around the metallic center is square-planar with the cyanate being linear. The theoretical infrared spectrum of C(1) symmetry (electronic state (1)A) is in accordance with the experimental one. It also verified the contribution of Pd (4d(xz) + 4d(yz)) and Pd (4d(xy)) in the HOMO and LUMO orbitals, respectively. (c) 2006 Elsevier B.V. All rights reserved.

Synthesis and structural studies of (1,10-phenanthroline)(thiocyanate-N)-(triphenylphosphine)copper(I)

The compound (1,10-phenanthroline)(thiocyanate-N)(triphenylphosphine)copper(I), was synthesized and studied by IR spectroscopy and X-ray diffraction techniques. It is monomeric with the thiocyanate acting as a N-donor ligand. The copper atom shows a distorted tetrahedral coordination geometry.

Thermal and photochemical stability of poly(vinyl alcohol)/modified lignin blends

A kraft lignin derivative (KLD) obtained by reaction with p-aminobenzoic acid/phthalic anhydride was blended with poly(vinyl alcohol) (PVA) by solution casting from DMSO. PVA and PVA/KLD films were exposed to ultraviolet radiation (24, 48, and 96 h) and analyzed by thermogravimetry (TG), differential scanning calorimetry (DSC), infrared spectroscopy (FTIR), hydrogen nuclear magnetic resonance (H-1 NMR) spectroscopy, and scanning electron microscopy (SEM). PVA films show a loss of thermal stability due to irradiation. PVA/KLD reveals greater thermal stability than PVA and an increase in thermal stability after irradiation. These results suggest that the incorporation of KLD into PVA provides a gain in thermal and photochemical stability. FTIR, H-1 NMR, DSC, and TG results obtained for the blends suggest that intermolecular interactions between PVA and KLD chains are present. SEM micrographs revealed blend miscibility for a KLD blend content of up to 15 wt%, as observed at magnification of 1000 times. (c) 2005 Elsevier Ltd. All rights reserved.

The influence of temperature on the color of TiO2:Cr pigments

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Sufentanil-2-hydroxypropyl-beta-cyclodextrin inclusion complex for pain treatment: Physicochemical, cytotoxicity, and pharmacological evaluation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis, spectroscopic characterization and molecular modeling of a tetranuclear platinum(II) complex with thiazolidine-4-carboxylic acid

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Lithium thiazolidine-4-carboxylate: Synthesis, spectroscopic characterization and preliminary in vitro cytotoxic studies in human HeLa cells

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of the thermal treatment in the crystallization of NiWO4 and ZnWO4

NiWO4 and ZnWO4 were synthesized by the polymeric precursor method at low temperatures with zinc or nickel carbonate as secondary phase. The materials were characterized by thermal analysis (TG/DTA), infrared spectroscopy, UV-Vis spectroscopy and X-ray diffraction. NiWO4 was crystalline after calcination at 350 A degrees C/12 h while ZnWO4 only crystallized after calcination at 400 A degrees C for 2 h. Thermal decomposition of the powder precursor of NiWO4 heat treated for 12 h had one exothermic transition, while the precursor heat treated for 24 h had one more step between 600 and 800 A degrees C with a small mass gain. Powder precursor of ZnWO4 presented three exothermic transitions, with peak temperatures and mass losses higher than NiWO4 has indicating that nickel made carbon elimination easier.

Thermal behaviour of malonic acid, sodium malonate and its compounds with some bivalent transition metal ions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

A Novel Plasma Technique for Surface Treatment: The Plasma Expander

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Crystallization study of SrSnO3:Fe

Alkaline earth stannates have recently become important materials in ceramic technology due to its application as humidity sensor. In this work, alkaline earth stannates doped with Fe3+ were synthesized by the polymeric precursor method, with calcination at 300 A degrees C/7 h and between 400 and 1100 A degrees C/4 h. The powder precursors were characterized by TG/DTA after partial elimination of carbon. Characterization after the second calcination step was done by X-ray diffraction, infrared spectroscopy, and UV-vis spectroscopy. Results confirmed the formation of the SrSnO3:Fe with orthorhombic perovskite structure, besides SrCO3 as secondary phase. Crystallization occurred at 600 A degrees C, being much lower than the crystallization temperature of perovskites synthesized by solid state reaction. The analysis of TG curves indicated that the phase crystallization was preceded by two thermal decomposition steps. Carbonate elimination occurred at two different temperatures, around 800 A degrees C and above 1000 A degrees C.

Thermal behaviour of fumaric acid, sodium fumarate and its compounds with light trivalent lanthanides in air atmosphere

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

SrSnO3:Nd obtained by the polymeric precursor method

In this work, the synthesis of Nd-doped SrSnO3 by the polymeric precursor method, with calcination between 250 and 700 A degrees C is reported. The powder precursors were characterized by TG/DTA and high temperature X-ray diffraction (HTXRD). After heat treatment, the material was characterized by XRD and infrared spectroscopy. Ester and carbonate amounts were strictly related to Nd-doping. According to XRD patterns, the orthorhombic perovskite was obtained at 700 A degrees C for SrSnO3 and SrSn0.99Nd0.01O3. For Sr0.99Nd0.01SnO3, the kinetics displayed an important hole in the crystallization process, as no peak was observed in HTXRD up to 700 A degrees C, while a XRD patterns showed a crystalline material after calcination at 250 A degrees C.