Degree of Conversion and Temperature Increase of a Composite Resin Light Cured with an Argon Laser and Blue LED

Different light sources and power densities used on the photoactivation process may provide changes in the degree of conversion (DC%) and temperature ( T) of the composite resins. Thus, the purpose of this study was to evaluate the DC (%) and T (degrees C) of the microhybrid composite resin (Filtek (TM) Z-250, 3M/ESPE) photoactivated with one argon laser and one LED (light-emitting diode) with different power densities. For the KBr pellet technique, the composite resin was placed into a metallic mould (2-mm thickness, 4-mm diameter) and photoactivated as follows: a continuous argon laser (CW) and LED LCUs with power density values of 100, 400, 700, and 1000 mW/cm(2) for 20 s. The measurements for DC (%) were made in a FTIR spectrometer Bomen ( model MB 102, Quebec, Canada). Spectroscopy ( FTIR) spectra for both uncured and cured samples were analyzed using an accessory of the reflectance diffusion. The measurements were recorded in absorbance operating under the following conditions: 32 scans, 4 cm(-1) resolution, 300 to 4000-cm(-1) wavelength. The percentage of unreacted carbon double bonds (% C=C) was determined from the ratio of absorbance intensities of aliphatic C=C (peak at 1638 cm(-1)) against an internal standard before and after the curing of the specimen: aromatic C-C (peak at 1608 cm(-1)). For T (degrees C), the samples were created in a metallic mould (2-mm thickness, 4-mm diameter) and photoactivated for 20 s. The thermocouple was attached to the multimeter allowing temperature readings. The DC (%) and T (degrees C) were submitted to ANOVA and Tukey`s test (p < 0.05). The degree of conversion values varied from 35.0 to 50.0% ( 100 to 1000 mW/cm(2)) for an argon laser and from 41.0 to 49% (100 to 1000 mW/cm(2)) for an LED. The temperature change values varied from 1.1 to 13.1 degrees C (100 to 1000 mW/cm(2)) for an argon laser and from 1.9 to 15.0 degrees C (100 to 1000 mW/cm(2)) for an LED. The power densities showed a significant effect on the degree of conversion and changes the temperature for both light-curing units.

Effect of different dental composite resins on the polymerization process

Dental composite resins possess good esthetic properties, and are currently among the most popular dental restorative materials. Both organic and inorganic phases might influence the material behavior, the filler particle features and rate are the most important factors related to improvement of the mechanical properties of resin composites. Thus, the objective of this study was to evaluate the effect of three different composite resins on the polymerization process by Vickers hardness test. The samples were prepared using three different composite resins, as follow: group I-P-60 (3M/ESPE); group II-Herculite XRV (Kerr), and group III-Durafill (Heraeus-Kulzer). The samples were made in a polytetrafluoroethylene mould, with a rectangular cavity measuring 7 mm in length, 4 mm in width, and 3 mm in thickness. The samples were photo-activated by one light-curing unit based on blue LEDs (Ultrablue III-DMC/Brazil) for 20 and 40 s of irradiation times. The Vickers hardness test was performed 24 h after the photo-activation until the standardized depth of 3 mm. The Vickers hardness mean values varied from 158.9 (+/- 0.81) to 81.4 (+/- 1.94) for P-60, from 138.7 (+/- 0.37) to 61.7 (+/- 0.24) for Herculite XRV, and from 107. 5 (+/- 0.81) to 44.5 (+/- 1.36) for Durafill composite resins photo-activated during 20 s for the 1st and 2nd mm, respectively. During 40 s of photo-activation, the Vickers hardness mean values were: from 181.0 (+/- 0.70) to 15.6 (+/- 0.29) for P-60, and from 161.8 (+/- 0.41) to 11.2 (+/- 0.17) for Herculite XRV composite resins, for the 1st and 3th mm, respectively. For Durafill composite resin the mean values varied from 120.1 (+/- 0.66) to 61.7 (+/- 0.20), for the 1st and 2nd mm, respectively. The variation coefficient (CV) was in the most of the groups lower than 1%, then the descriptive statistic analysis was used. The Vickers hardness mean values for Durafill were lower than P-60 and Herculite XRV composite resins for 20 and 40 s of irradiation time. The polymerization process was greatly affected by the composition of the composite resins.

Evaluation of dental pulp repair using low level laser therapy (688 nm and 785 nm) morphologic study in capuchin monkeys

The aim of this study was to evaluate the hypothesis that low-level laser therapy (LLLT) 688 nm and 785 nm accelerate dentin barrier formation and repair process after traumatic pulp exposure. The sample consisted of 45 premolars of capuchin monkeys (Cebus apella) with pulp exposure Class V cavities. All premolars were treated with calcium hydroxide (Ca(OH)(2)), divided in groups of 15 teeth each, and analyzed on 7(th), 25(th), and 60(th) day. Group GI - only Ca(OH)(2), GIF- laser 688 nm, and GIII - laser 785 nm. Laser beam was used in single and punctual dose with the parameters: continuous, 688 nm and 785 nm wavelength, tip`s area of 0.00785 cm(2), power 50 mW, application time 20 s, dose 255 J/cm(2), energy 2 J. Teeth were capped with Ca(OH)(2), Ca(OH)(2) cement and restored with amalgam. All groups presented pulp repair. On 25(th) day the thickness of the formed dentin barrier was different between the groups GI and GII (p < 0.05) and between groups GI and GIII (p < 0.01). On 60(th) day there was difference between GI and GIII (p < 0.01). It may be concluded that, LLLT 688 nm and 785 nm accelerated dentin barrier formation and consequently pulp repair process, with best results using infrared laser 785 nm. (c) 2009 by Astro Ltd. Published exclusively by WLLEY-VCH Verlag GmbH & Co. KGaA

Supramolecular Approach to Gold Nanoparticle/Triruthenium Cluster Hybrid Materials and Interfaces

A systematic and comprehensive study of the interaction of citrate-stabilized gold nanoparticles with triruthenium cluster complexes of general formula [Ru(3)(CH(3)COO)(6)(L)](+) [L = 4-cyanopyridine (4-CNpy), 4,4`-bipyridine (4,4`-bpy) or 4,4`-bis(pyridyl)ethylene (bpe)] has been carried out. The cluster-nanoparticle interaction in solution and the construction of thin films of the hybrid materials were investigated in detail by electronic and surface plasmon resonance (SPR) spectroscopy, Raman scattering spectroscopy and scanning electron microscopy (SEM). Citrate-stabilized gold nanoparticles readily interacted with [Ru(3)O(CH(3)COO)(6)(L)(3)](+) complexes to generate functionalized nanoparticles that tend to aggregate according to rates and extents that depend on the bond strength defined by the characteristics of the cluster L ligands following the sequence bpe > 4,4`-bpy >> 4-CNpy. The formation of compact thin films of hybrid AuNP/[Ru(3)O(CH(3)COO)(6)(L)(3)](+) derivatives with L = bpe and 4,4`-bpy indicated that the stability/lability of AuNP-cluster bonds as well as their solubility are important parameters that influence the film contruction process. Fluorine-doped tin oxide electrodes modified with thin films of these nanomaterials exhibited similar electrocatalytic activity but much higher sensitivity than a conventional gold electrode in the oxidation of nitrite ion to nitrate depending on the bridging cluster complex, demonstrating the high potential for the development of amperometric sensors.

Pt monolayer electrocatalysts for O-2 reduction: PdCo/C substrate-induced activity in alkaline media

We measured the activity of electrocatalysts, comprising Pt monolayers deposited on PdCo/C substrates with several Pd/Co atomic ratios, in the oxygen reduction reaction in alkaline solutions. The PdCo/C substrates have a core-shell structure wherein the Pd atoms are segregated at the particle`s surface. The electrochemical measurements were carried out using an ultrathin film rotating disk-ring electrode. Electrocatalytic activity for the O-2 reduction evaluated from the Tafel plots or mass activities was higher for Pt monolayers on PdCo/C compared to Pt/C for all atomic Pd/Co ratios we used. We ascribed the enhanced activity of these Pt monolayers to a lowering of the bond strength of oxygenated intermediates on Pt atoms facilitated by changes in the 5d-band reactivity of Pt. Density functional theory calculations also revealed a decline in the strength of PtOH adsorption due to electronic interaction between the Pt and Pd atoms. We demonstrated that very active O-2 reduction electrocatalysts can be devised containing only a monolayer Pt and a very small amount of Pd alloyed with Co in the substrate.

Análise de Argamassas Com Substituição Parcial do Cimento Portland Por Cinza Residual de Lenha de Algaroba

With the increase in cement consumption, it has quickly become one of the inputs most consumed by mankind over the last century. This has caused an increase in CO2 emissions, as cement production releases large quantities of this gas into the atmosphere. Adding this fact to the growing consciousness of environmental preservation, it has led to a search for alternatives to cement to complement its derivatives, in the form of waste materials like the ashes. This research aimed to analyze the properties of mortars in fresh and hardened state with partial replacement of Portland cement by residual algaroba wood ash (CRLA) potteries produced by the state of Rio Grande do Norte. The CRLA was collected and sieved, where part of it was ground and characterized in comparison with that just sifted, being characterized according to its chemical composition, grain size, fineness, density, bulk density and index of pozzolanic activity. It was found that the wood ash does not act as pozzolan, and grinding it has not changed its characteristics compared to those just sifted, not justifying its use. Two traces were adopted for this research: 1:3 (cement: fine sand) and 1:2:8 (cement: hydrated lime: medium sand); both in volume, using as materials the CRLA just sifted, CP II F-32 Portland cement, CH-I hydrated lime, river sand and water from the local utility. For each trace were adopted six percentages of partial replacement of cement for wood ash: 0% (control) 5%, 7%, 10%, 12% and 15%. In the fresh state, the mortars were tested towards their consistency index and mass density. In the hardened state, they were tested towards their tensile strength in bending, compressive strength and tensile adhesion strength, and its mass density in the hardened state. The mortar was also analyzed by scanning electron microscopy and X-ray diffraction. Furthermore, it was classified according to NBR 13281 (2005). The results showed that up to a content of 5% substitution and for both traces, the residual algaroba wood ash can replace Portland cement without compromising the mortars microstructure and its fresh and hardened state

Pulsed Nd:YAG laser seam welding of AISI 316L stainless steel thin foils

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Avaliação do Índice de Remanescente Adesivo utilizando braquetes com e sem tratamento na base e a interação com três sistemas de colagem

OBJETIVO: avaliar o Índice de Remanescente Adesivo (IRA) em dentes bovinos após a descolagem de braquetes com e sem tratamento na base. METODOLOGIA: foram utilizados três sistemas de colagem ortodôntica para os dois padrões de base. Os dentes bovinos foram divididos em seis grupos de 40, de acordo com a base do braquete e o sistema de colagem. Vinte e quatro horas após a colagem foram realizados os testes de compressão em uma máquina de ensaios. A avaliação do IRA foi realizada em um estereomicroscópio por três examinadores calibrados. Foi utilizado o teste não paramétrico de Kruskal-Wallis, seguido do método de Dunn, para fazer as comparações múltiplas entre todos os grupos. RESULTADOS E CONCLUSÕES: observou-se que o tratamento das bases dos braquetes com óxido de alumínio não foi determinante para o aumento da adesividade entre o braquete e o adesivo. O grupo em que se utilizou braquetes com tratamento na base e adesivo TXT (3M-Unitek) + Transbond Plus SEP (3M-Unitek) apresentou a maior parte das fraturas na interface dente-adesivo (escore 4).

The influence of temperature of three adhesive systems on bonding to ground enamel

This study evaluated the microtensile bond strength test (mu T), micromorphology of resin-enamel interface (RET) and etching patterns (EP) promoted by the etch-and-rinse adhesive, Prime&Bond NT (PB), and two self-etching adhesives, Clearfil SE Bond (SE) and Adper Prompt L-Pop (APR), to ground bovine enamel surfaces' when applied at temperatures of 5 degrees C (C), 40 degrees C (H) and 20 degrees C (R). Materials and Methods. Sixty-three bovine incisors were randomly divided into nine experimental groups (n=7) according to adhesive systems and temperatures. The buccal enamel surfaces were flattened with 600-grit SiC paper and abraded with a diamond bur under water-cooling. The adhesive systems were applied according to the manufacturer's instructions. After the restorative procedures, the specimens were sectioned into five slabs. Four slabs were prepared for mu T and one for interface analysis. For etching pattern analysis, the remaining 16 bovine enamel fragments were used (n=2). The adhesives were applied and the surfaces were rinsed with organic solvents after application. The specimens for RET and EP analysis were prepared for SEM analysis. Results. No significant differences among the adhesives were found at R temperature. However, at 5 degrees C, PB and APR presented lower bond strength than SE. At H temperature, higher bond strength was observed for PB than for APR and SE. At C and H temperature, formation of the interdiffusion zone was impaired and the treated enamel surfaces presented an undefined EP.

Estudo in vivo e in vitro com e sem termociclagem, da resistência ao cisalhamento de braquetes colados com fonte de luz halógena

OBJETIVO: avaliar a resistência de braquetes metálicos colados em dentes humanos com resina polimerizada com luz halógena por meio de ensaios mecânicos de cisalhamento. METODOLOGIA: para este estudo foram realizados ensaios in vivo com dinamômetro portátil digital e in vitro com máquina de ensaios mecânicos universal com e sem termociclagem, complementado pelo Índice de Adesivo Remanescente (IAR). Braquetes Edgewise Standard (Abzil) foram colados utilizando adesivo Transbond Plus Self Etching Primer (SEP) e Resina Transbond XT. Foram formados 3 grupos com 10 dentes em cada um deles. No GI os braquetes foram colados nos segundos pré-molares dos pacientes. Nos GII e GIII utilizaram-se primeiros pré-molares extraídos por motivos ortodônticos. Os ensaios mecânicos do GI foram realizados 24 horas após a polimerização diretamente na boca dos pacientes com dinamômetro portátil digital. No GII os corpos-de-prova foram armazenados em água destilada e levados à estufa a 37ºC durante 24 horas e, posteriormente, submetidos à termociclagem, com 1000 ciclos a 5 e 55ºC. No GIII os corpos-de-prova foram armazenados em água destilada em temperatura ambiente por 24 horas e posteriormente submetidos aos ensaios mecânicos. RESULTADOS: os valores médios da resistência ao cisalhamento em Megapascal foram de: GI = 4,39; GII = 7,11 e GIII = 7,35. Após a descolagem foram realizadas fotografias das áreas de colagem, tanto dos dentes submetidos a testes in vivo quanto in vitro e ampliadas 5x para facilitar a visualização. As imagens obtidas foram analisadas, classificadas de acordo com o IAR e, por meio de gráficos de dispersão, foi verificada a relação entre a resistência ao cisalhamento e este índice. CONCLUSÃO: a média dos ensaios mecânicos realizados in vivo foi estatisticamente menor em relação aos ensaios in vitro. Não houve diferenças na resistência ao cisalhamento in vitro entre o grupo termociclado e o não-termociclado. Não houve relação entre tensão de ruptura e tipo de falha.

Effect of acid etching time on the degradation of resin-dentin bonds in primary teeth

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of metal conditioners on the adhesive bonding of resin cements to cast titanium

Objective: To assess the effect of metal conditioners on the bond strength between resin cements and cast titanium. Method and Materials: Commercially pure titanium (99.56%) was cast using an arc casting machine. Surfaces were finished with 400-grit silicon carbide paper followed by air abrasion with 50-mu m aluminum oxide. A piece of double-coated tape with a 4-mm circular hole was then positioned on the metal surface to control the area of the bond. The prepared surfaces were then divided into 4 groups (n=10): G1, unprimed Panavia F; G2, Alloy Primer-Panavia F; G3, unprimed Bistite DC; G4, Metaltite-Bistite DC. Forty minutes after insertion of the resin cements, the specimens were detached from the mold and stored in water at 37 C for 24 hours. Shear bond strength was performed in a testing machine (MTS 810) at a crosshead speed of 0.5 mm/min. Data were analyzed using ANOVA and Tukey's test with a .05 significance level. The fractured surfaces were observed through an optical microscope at 10x magnification. Results: the G1 group demonstrated significantly higher shear bond strength (17.95 MPa) than the other groups. G3 (13.79 MPa) and G4 (12.98 MPa) showed similar mean values to each other and were statistically superior to G2 (9.31 MPa). Debonded surfaces generally presented adhesive failure between metal surfaces and resin cements. Conclusion: While the Metaltite conditioner did not influence the bond strength of the Bistite DC cement, the Alloy Primer conditioner significantly decreased the mean bond strength of the Panavia F cement.

Effect of microwave disinfection on the hardness and adhesion of two resilient liners

Statement of problem. Microwave irradiation has been suggested for denture disinfection. However, the effect of this procedure on the hardness and bond strength between resilient liners and denture base acrylic resin is not known.Purpose. This study evaluated the effect of water storage time and microwave disinfection on the hardness and peel bond strength of 2 silicone resilient lining materials to a heat-polymerized acrylic resin.Material and methods. Acrylic resin (Lucitone 199) specimens (75 X 10 X 3 mm) were stored in water at 37 degrees C (2 or 30 days) before bonding (n = 160). The resilient lining materials (GC Reline Extra Soft and Dentusil) were bonded to the denture base and divided into the following 4 groups (n = 10): Tests performed immediately after bonding (control); specimens immersed in water (200 mL) and irradiated twice, with 650 W for 6 minutes; specimens irradiated daily for 7 total cycles of disinfection; specimens immersed in water (37 degrees C) for 7 days. Specimens were submitted to a 180-degree peel test (at a crosshead speed of 10 mm/min) and the failure values (MPa) and mode of failure were recorded. Pretreatment and posttreatment hardness measurements (Shore A) of the resilient materials were also performed. Three-way analysis of variance, followed by the Tukey HSD test, was performed (alpha=.05).Results. The analysis revealed that, for all conditions, the mean failure strengths of GC Reline Extra Soft (0.95-1.19 MPa) were significantly higher (P<.001) than those of Dentusil (0.45-0.50 MPa). The adhesion of the liners was not adversely affected by water storage time of Lucitone 199 or microwave disinfection. All peel test failures were cohesive. There was a small but significant difference (P<.001) between the pretreatment (34.33 Shore A) and posttreatment (38.69 Shore A) hardness measurements.Conclusion. Microwave disinfection did not compromise the hardness of either resilient liners or their adhesion to the denture base resin Lucitone 199.

Effect of disinfection on adhesion of reline polymers

Cylinders (3.5 x 5.0 mm) of the reline resins Kooliner (K), New Truliner (N), Tokuso Rebase Fast (T), and Ufi Gel Hard (U) were bonded to cylinders (20 x 20 mm) of the denture base resin Lucitone 550 (L), and samples were divided into two controls and four test groups (n = 8). Shear tests (0.5 mm/min) were performed after polymerization or immersion in water (37 degrees C) for 7 days (controls); two or seven cycles of disinfection by immersion in sodium perborate (50 degrees C/10 min) or microwave irradiation (650 W/6 min). Statistical analyses (alpha = 0.05) revealed that two cycles of microwave and chemical disinfection increased the mean bond strengths of materials T (9.08 to 12.93 MPa) and L (18.89 to 23.02 MPa). For resin L, seven cycles of chemical (15.72 MPa) and microwave (17.82 MPa) disinfection decreased the shear bond strength compared with the respective control (21.74 MPa). Resins U (13.12 MPa), K (8.44 MPa), and N (7.98 MPa) remained unaffected.

Resistência de união entre dentes artificiais e resinas acrílicas para base protética

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)