Synthesis and characterization of temperature- and light-responsive polymers and block copolymers

In summary, thermoresponsive polyacrylamides with various amounts of different photoswitchable side groups, i. e. azobenzene, salicylideneaniline and fulgimide were successfully prepared. As such, in a first step three different chromophores with an amine functionality were synthesized. The synthesis of the stimuli-responsive materials was based on the RAFT polymerization of activated ester acrylates followed by a polymer analogous reaction with different amines. The procedure has been designed to allow the synthesis of well-defined materials with functional groups. All copolymers prepared in this way showed a LCST in aqueous solution. The LCST was in general decreased by increasing the amount of hydrophobic dye incorporated into the thermoresponsive polymer. However, in the case of the fulgimide, the LCST was hardly affected by the chromophore. For azobenzene containing PNIPAM polymers and analogues, higher LCST values were measured after irradiation of the polymer sample solutions with UV-light (Delta LCSTmax = 7.3°C). A reversible light-induced solubility change within a certain temperature range was possible. In contrast to this, irradiated samples of salicylideneaniline containing thermoresponsive copolymers showed an irreversible increase in the LCST (Delta LCSTmax = 13.0°C). Fulgimide chromophores did not influence the LCST of PNIPAM based copolymers after UV-light exposure.rnSimilar to the thermoresponsive polyacrylamides with azobenzene side groups, poly(oligo(ethylene glycol) methyl ether methacrylate) [P(OEGMA)] polymers with azobenzene end groups showed a LCST shift upon UV-irradiation. These polymers were synthesized by RAFT polymerization using a functional chain transfer agent (CTA). For this, PFP-CTA was used as a RAFT-agent for end group functionalization of (thermoresponsive) polymers. In contrast to the statistically arranged copolymers with azobenzene side groups, P(OEGMA) polymers with terminal azobenzene showed a linear increase of the LCST shifts with increasing amount of chromophore (Delta LCSTmax = 4.3°C). Noteworthy, the chemical nature of the end group exhibited a strong influence on the LCST in the case of short thermoresponsive P(OEGMA) polymers.rnThe investigation on temperature- and lightresponsive polymers was transferred onto block copolymers capable to self-assemble into polymeric micelles. Therefore, PEO-b-PNIPAM block copolymers with azobenzene moieties were synthesized successfully. These polymers showed a “smart” behavior in aqueous solution, as the reversible formation and disruption of the micelles could either be controlled by temperature or using light as a stimulus. The usefulness of these materials was demonstrated by encapsulation of a hydrophobic dye in the core of the micelle. Such materials might have a great potential as a model system for several technical or biological applications.rnFinally, double thermoresponsive block copolymers forming micellar structures in a certain temperature range with functional end groups could successfully be synthesized. These “smart materials” based on POEGMA-b-PNIPMAM have been demonstrated to be very promising for a temperature selective immobilization on a protein surface. This might be a suitable concept for further biological applications.rnConcluding, different thermoresponsive copolymers and block copolymers with lightresponsive moieties arranged along the backbone or located at the chain ends were successfully prepared and investigated. By controlling the nature of functional groups and their respective incorporation ratios, the LCST could be dialed in precisely. Further, the LCST of the polymers could be triggered by light. A light-controlled disruption of micellar structures could be shown for functional block copolymers. The importance of end groups of thermoresponsive polymers was demonstrated by a temperature-controlled protein-polymer binding of a terminal biotin-functionalized double thermoresponsive polymer. The synthetic approaches and the material properties presented here should be promising for further research and applications beyond this dissertation.rn

Fluorenbasierende amphiphile Kammpolymere zur Ausbildung definierter Strukturen an Oberflächen und in Lösungen

Die Dissertation beschreibt die Darstellung und Charakterisierung von neuartigen, amphiphilen Carbazol- und Fluoren-(co)-polymeren, die infolge ihres strukturellen Aufbaus sowohl selbstorganisierende als auch optoelektronische Eigenschaften kombinierten. Zum einen wurden Kammpolymere mit konjugierten, steifen Rückgraten und flexiblen sowie konformativ schaltbaren Polyelektrolytseitenketten dargestellt und auf eine pH-abhängige Selbstorganisation in Lösung und an Oberflächen untersucht. Des Weiteren wurden neutrale, methanollösliche Polyfluorene synthetisiert, die in Kombination mit einem unpolaren Polyindenofluorenderivat zum Aufbau mehrschichtiger PLEDs mittels nasschemischer Verfahren eingesetzt wurden. Zum anderen fand die Synthese von amphiphilen Polyfluorenen statt, die als Emulgatoren zur Stabilisierung von inversen Emulsionen eingesetzt wurden. Dabei konnten mit Hilfe eines bereits für die Darstellung von anorganisch-organischen Kern-Schale-Partikeln etablierten in situ-Verfahrens formanisotrope, kristalline Zinkoxidkerne mit konjugierter Polymerhülle erhalten werden.

Photo-induced reversible assembly of colloidal polymer nanoparticles

Polymer nanoparticles functionalized on the surface with photo-responsive labels were synthesized. In a first synthetic step, polystyrene was copolymerized with the cross-linker divinylbenzene and poly(ethylene glycol) acrylate in a miniemulsion, to produce nano-sized spheres (~ 60 nm radius) with terminal hydroxyl groups, which were functionalized in a subsequent synthetic step with photo-responsive labels. For this purpose, two photo-active molecular structures were separately used: anthracene, which is well known to form covalently bonded dimers upon photo-excitation; and pyrene, which only forms short lived excited state dimers (excimers). Acid derivatives of these labels (9-anthracene carboxylic acid and 1-pyrene butyric acid) were bonded to the hydroxyl terminal groups of the nanoparticles through an esterification reaction, via the intermediate formation of the corresponding acid chloride.rnThe obtained labeled nanoparticles appeared to be highly hydrophobic structures. They formed lyophobic suspensions in water, which after analysis by dynamic light scattering (DLS) and ultramicroscopic particle tracking, appeared to equilibrate as a collection of singly dispersed nanoparticles, together with a few nanoparticle aggregates. The relative amount of aggregates decreased with increasing amounts of the surfactant sodium dodecyl sulfate (SDS), thus confirming that aggregation is an equilibrated state resulting from lyophobicity. The formation of such aggregates was corroborated using scanning electron microscopy (SEM). The photo-irradiation of the lyophobic aqueous suspensions of anthracene labeled nanoparticles (An-NP) resulted in the formation of higher aggregates, as evidenced by DLS and ultramicroscopy. The obtained state of aggregation could be reverted by sonication. The possibility to re-aggregate the system in subsequent photo-excitation and sonication cycles was established. Likewise, the photo-irradiation of lyophobic aqueous suspensions of pyrene-labeled nanoparticles (Py-NP) resulted in the formation of higher aggregates, as evidenced by DLS and ultramicroscopy. These appeared to remain aggregated due to hydrophobic interactions. This system could also be re-dispersed by sonication and re-aggregated in subsequent cycles of photo-excitation and sonication.

Functional silicones and silicone-containing block copolymers

Polysiloxanes can be synthesized and subsequently modified (i) by the attachment of small molecules that change the properties of the silicone in such a way that it becomes more hydrophilic, but under the premise that this does not go together with a loss of the silicone-specific features. This can be done by adding hydrophilic sidechains to a polysiloxane. Polyethers like poly(ethylene glycol) or hyperbranched polyether-polyols are suitable in this regard. In order to assure that the silicone properties retain, these side groups can be attached to only one part of the polysiloxane backbone, which results in a block copolymer that consists of a common polysiloxane and a second block of the modified structure. (ii) Polysiloxanes can be equipped with functional groups that are capable of initializing polymerization of a different monomer (macroinitiator approach). For example, hydroxyl groups are used to initiate the ring opening polymerization of cyclic esters, or ATRP macroinitiators can be synthesized to add a second block via controlled radical polymerization. Stimuli responsive polymers like poly(oligoethylene glycol methacrylate) (POEGMA) can be added via this route to create “smart” siloxane-containing block copolymers that respond to certain stimuli. rnAn important premise for all synthetic routes is to achieve the targeted structure in a process as simple as possible, because facile availability of the material is crucial with regard to industrial applicability of the invented products. rnConcerning characterization of the synthesized macromolecules, emphasize is put on their (temperature dependent) aggregation behavior, which can be investigated by several microscopic and scattering methods, their behavior at the interface between silicone oils and water and their thermal properties.rnrn

Functionalization and characterization of magnetic nanoparticles for biomedical applications

Die vorliegende Arbeit beschäftigt sich mit der Oberflächenfunktionalisierung von MnO Nanopartikeln (NP). Durch die Verwendung und Verbesserung verschiedener Polymere durch die Einbindung von Poly (Ethylen Glycol) (PEG), gelang es, die Löslichkeit dieser Nanopartikel in wässrigen Lösungen sowie in Körperflüssigkeiten zu erhöhen. Zusätzlich konnten diese Nanopartikel deutlich besser steril filtriert werden und zeigten eine erhöhte Aktivität alsrnKontrastmittel im MRT. Vorläufige Ergebnisse für die Verwendung von Silika als Schutzhülle für MnO NP werden ebenfalls kurz erläutert. Die verwendeten Polymere besaßen dabei zugängliche Aminogruppen, die eine weitere Funktionalisierung durch Bio-aktiver Gruppen ermöglichte. Der Nachweis einer erfolgreichen Bindung durch verschiedene Methoden wie SDS-PAGE, Western- und Northern Blot sowie die Verwendung unterschiedlicher FluoreszenzMessungen wird ebenfalls diskutiert. MnO NP und anderer magnetischer NP werden weiterhin auf ihr toxisches Verhalten gegenüber Caki1 und HeLa Zellen getestet. Dabei zeigte sich, dass MnO NP, im Gegensatz zu einigen Kupferoxiden, quasi nicht toxisch waren und das Proliferationsverhalten dieser Zellen quasi nicht beeinflussten. Weiterhin wurde ein Fluoreszenzfarbstoff, konkret Protoporphyrin IX, an die Oberfläche von MnO NP angebracht.Diese konnten dann erfolgreich als Kontrastmittel in der MRT verwendet werden und zeigten vielversprechende Ergebnisse für die Photodynamische Therapie. Desweiteren wird die Synthese des Antikörpers gegen p53 ausführlich erläutert. Dabei wurde genau darauf geachtet,dass dieser Antikörper dann an MnO NP gebunden werden kann.

Poly(lactide): from hyperbranched copolyesters to new block copolymers with functional methacrylates

The prologue of this thesis (Chapter 1.0) gives a general overview on lactone based poly(ester) chemistry with a focus on advanced synthetic strategies for ring-opening polymerization, including the emerging field of organo catalysis. This section is followed by a presentation of the state-of the art regarding the two central fields of the thesis: (i) polyfunctional and branched poly(ester)s in Chapter 1.1 as well as (ii) the development of new poly(ester) based block copolymers with functional methacrylates (Chapter 1.2). Chapter 2 deals with the synthesis of new, non-linear poly(ester) structures. In Chapter 2.1, the synthesis of poly(lactide)-based multiarm stars, prepared via a grafting-from method, is described. The hyperbranched poly(ether)-poly(ol) poly(glycerol) is employed as a hydrophilic core molecule. The resulting star block copolymers exhibit potential as phase transfer agents and can stabilize hydrophilic dyes in a hydrophobic environment. In Chapter 2.2, this approach is expanded to poly(glycolide) multiarm star polymers. The problem of the poor solubility of linear poly(glycolide)s in common organic solvents combined with an improvement of the thermal properties has been approached by the reduction of the total chain length. In Chapter 2.3, the first successful synthesis of hyperbranched poly(lactide)s is presented. The ring-opening, multibranching copolymerization of lactide with the “inimer” 5HDON (a hydroxyl-functional lactone monomer) was carefully examined. Besides a precise molecular characterization involving the determination of the degree of branching, we were able to put forward a reaction model for the formation of branching during polymerization. Several innovative approaches to amphiphilic poly(ester)/poly(methacrylate)-based block copolymers are presented in the third part of the thesis (Chapter 3). Block copolymer build-up especially relies on the combination of ring-opening and living radical polymerization. Atom transfer radical polymerization has been successfully combined with lactide ring-opening, using a “double headed” initiator. This strategy allowed for the realization of poly(lactide)-block-poly(2-hydroxyethyl methacrylate) copolymers, which represent promising materials for tissue engineering scaffolds with anti-fouling properties (Chapter 3.1). The two-step/one-pot approach forgoes the use of protecting groups for HEMA by a careful selection of the reaction conditions. A series of potentially biocompatible and partially biodegradable homo- and block copolymers is described in Chapter 3.2. In order to create a block copolymer with a comparably strong hydrophilic character, a new acetal-protected glycerol monomethacrylate monomer (cis-1,3- benzylidene glycerol methacrylate/BGMA) was designed. The hydrophobic poly(BGMA) could be readily transformed into the hydrophilic and water-soluble poly(iso-glycerol methacrylate) (PIGMA) by mild acidic hydrolysis. Block copolymers of PIGMA and poly(lactide) exhibited interesting spherical aggregates in aqueous environment which could be significantly influenced by variation of the poly(lactide)s stereo-structure. In Chapter 3.3, pH-sensitive poly(ethylene glycol)-b-PBGMA copolymers are described. At slightly acidic pH values (pH 4/37°C), they decompose due to a polarity change of the BGMA block caused by progressing acetal cleavage. This stimuli-responsive behavior renders the system highly attractive for the targeted delivery of anti-cancer drugs. In Chapter 3.4, which was realized in cooperation, the concept of biocompatible, amphiphilic poly(lactide) based polymer drug conjugates, was pursued. This was accomplished in the form of fluorescently labeled poly(HPMA)-b-poly(lactide) copolymers. Fluorescence correlation spectroscopy (FCS) of partially biodegradable block copolymer aggregates exhibited fast cellular uptake by human cervix adenocarcinoma cells without showing toxic effects in the examined concentration range (Chapter 4.1). The current state of further projects which will be pursued in future studies is addressed in Chapter 4. This covers the synthesis of biocompatible star block copolymers (Chapter 4.2) and the development of new methacrylate monomers for biomedical applications (Chapters 4.3 and 4.4). Finally, the further investigation of hydroxyl-functional lactones and carbonates which are promising candidates for the synthesis of new hydrophilic linear or hyperbranched biopolymers, is addressed in Chapter 4.5.

Multifunctional polyether architectures : versatile materials for surface attachment and functionalization

Chapter 1 of this thesis comprises a review of polyether polyamines, i.e., combinations of polyether scaffolds with polymers bearing multiple amino moieties. Focus is laid on controlled or living polymerization methods. Furthermore, fields in which the combination of cationic, complexing, and pH-sensitive properties of the polyamines and biocompatibility and water-solubility of polyethers promise enormous potential are presented. Applications include stimuli-responsive polymers with a lower critical solution temperature (LCST) and/or the ability to gel, preparation of shell cross-linked (SCL) micelles, gene transfection, and surface functionalization.rnIn Chapter 2, multiaminofunctional polyethers relying on the class of glycidyl amine comonomers for anionic ring-opening polymerization (AROP) are presented. In Chapter 2.1, N,N-diethyl glycidyl amine (DEGA) is introduced for copolymerization with ethylene oxide (EO). Copolymer microstructure is assessed using online 1H NMR kinetics, 13C NMR triad sequence analysis, and differential scanning calorimetry (DSC). The concurrent copolymerization of EO and DEGA is found to result in macromolecules with a gradient structure. The LCSTs of the resulting copolymers can be tailored by adjusting DEGA fraction or pH value of the environment. Quaternization of the amino moieties by methylation results in polyelectrolytes. Block copolymers are used for PEGylated gold nanoparticle formation. Chapter 2.2 deals with a glycidyl amine monomer with a removable protecting group at the amino moiety, for liberation of primary amines at the polyether backbone, which is N,N-diallyl glycidyl amine (DAGA). Its allyl groups are able to withstand the harsh basic conditions of AROP, but can be cleaved homogeneously after polymerization. Gradient as well as block copolymers poly(ethylene glycol)-PDAGA (PEG-PDAGA) are obtained. They are analyzed regarding their microstructure, LCST behavior, and cleavage of the protecting groups. rnChapter 3 describes applications of multi(amino)functional polyethers for functionalization of inorganic surfaces. In Chapter 3.1, they are combined with an acetal-protected catechol initiator, leading to well-defined PEG and heteromultifunctional PEG analogues. After deprotection, multifunctional PEG ligands capable of attaching to a variety of metal oxide surfaces are obtained. In a cooperative project with the Department of Inorganic and Analytical Chemistry, JGU Mainz, their potential is demonstrated on MnO nanoparticles, which are promising candidates as T1 contrast agents in magnetic resonance imaging. The MnO nanoparticles are solubilized in aqueous solution upon ligand exchange. In Chapter 3.2, a concept for passivation and functionalization of glass surfaces towards gold nanorods is developed. Quaternized mPEG-b-PqDEGA diblock copolymers are attached to negatively charged glass surfaces via the cationic PqDEGA blocks. The PEG blocks are able to suppress gold nanorod adsorption on the glass in the flow cell, analyzed by dark field microscopy.rnChapter 4 highlights a straightforward approach to poly(ethylene glycol) macrocycles. Starting from commercially available bishydroxy-PEG, cyclic polymers are available by perallylation and ring-closing metathesis in presence of Grubbs’ catalyst. Purification of cyclic PEG is carried out using α-cyclodextrin. This cyclic sugar derivative forms inclusion complexes with remaining unreacted linear PEG in aqueous solution. Simple filtration leads to pure macrocycles, as evidenced by SEC and MALDI-ToF mass spectrometry. Cyclic polymers from biocompatible precursors are interesting materials regarding their increased blood circulation time compared to their linear counterparts.rnIn the Appendix, A.1, a study of the temperature-dependent water-solubility of polyether copolymers is presented. Macroscopic cloud points, determined by turbidimetry, are compared with microscopic aggregation phenomena, monitored by continuous wave electron paramagnetic resonance (CW EPR) spectroscopy in presence of the amphiphilic spin probe and model drug (2,2,6,6-tetramethylpiperidin-1-yl)oxyl (TEMPO). These thermoresponsive polymers are promising candidates for molecular transport applications. The same techniques are applied in Chapter A.2 to explore the pH-dependence of the cloud points of PEG-PDEGA copolymers in further detail. It is shown that the introduction of amino moieties at the PEG backbone allows for precise manipulation of complex phase transition modes. In Chapter A.3, multi-hydroxyfunctional polysilanes are presented. They are obtained via copolymerization of the acetal-protected dichloro(isopropylidene glyceryl propyl ether)methylsilane monomer. The hydroxyl groups are liberated through acidic work-up, yielding versatile access to new multifunctional polysilanes.

Sulfur-containing polymers for surface attachment

Different concepts for the synthesis of sulfur-containing polymers as well as their adsorption onto gold surfaces were studied. The present work is divided into three parts. The main part focuses on the synthesis of poly(1,2-alkylene sulfides) (“polysulfides”) with complex architectures on the basis of polyether-based macroinitiators by the anionic ring-opening polymerization of ethylene sulfide and propylene sulfide. This synthetic tool kit allowed the synthesis of star-shaped, brush-like, comb-like and pom-pom-like polysulfides, the latter two with an additional poly(ethylene glycol) chain. Additionally, the number of polysulfide arms as well as the monomer composition could be varied over a wide range to obtain copolymers with multiple thioether functionalities.rnThe second section deals with the synthesis of a novel lipoic acid-based initiator for ring-opening polymerizations for lactones and epoxides. A straightforward approach was selected to accomplish the ability to obtain tailored polymers with a common used disulfide-anchoring group, without the drawbacks of post-polymerization functionalization. rnIn the third part, a new class of block-copolymers consisting of polysulfides and polyesters were investigated. For the first time this approach enabled the use of hydroxyl-terminated poly(propylene sulfide) as macroinitiator for the synthesis of a second block.rnThe adsorption efficiency of those different polymer classes onto gold nanoparticles as well as gold rnsupports was studied via different methods.rn

Eliminating Adhesion Errors in Nanoindentation of Compliant Polymers and Hydrogels

Nanoindentation is a valuable tool for characterization of biomaterials due to its ability to measure local properties in heterogeneous, small or irregularly shaped samples. However, applying nanoindentation to compliant, hydrated biomaterials leads to many challenges including adhesion between the nanoindenter tip and the sample. Although adhesion leads to overestimation of the modulus of compliant samples when analyzing nanoindentation data using traditional analysis techniques, most studies of biomaterials have ignored its effects. This paper demonstrates two methods for managing adhesion in nanoindentation analysis, the nano-JKR force curve method and the surfactant method, through application to two biomedically-relevant compliant materials, poly(dimethyl siloxane) (PDMS) elastomers and poly(ethylene glycol) (PEG) hydrogels. The nano-JKR force curve method accounts for adhesion during data analysis using equations based on the Johnson-Kendall-Roberts (JKR) adhesion model, while the surfactant method eliminates adhesion during data collection, allowing data analysis using traditional techniques. In this study, indents performed in air or water resulted in adhesion between the tip and the sample, while testing the same materials submerged in Optifree Express() contact lens solution eliminated tip-sample adhesion in most samples. Modulus values from the two methods were within 7% of each other, despite different hydration conditions and evidence of adhesion. Using surfactant also did not significantly alter the properties of the tested material, allowed accurate modulus measurements using commercial software, and facilitated nanoindentation testing in fluids. This technique shows promise for more accurate and faster determination of modulus values from nanoindentation of compliant, hydrated biological samples. Copyright 2013 Elsevier Ltd. All rights reserved.

Evaluation of chemically modified SLA implants (modSLA) biofunctionalized with integrin (RGD)- and heparin (KRSR)-binding peptides

Enhancing osseointegration through surface immobilization of multiple short peptide sequences that mimic extracellular matrix (ECM) proteins, such as arginine-glycine-aspartic acid (RGD) and lysine-arginine-serine-arginine (KRSR), has not yet been extensively explored. Additionally, the effect of biofunctionalizing chemically modified sandblasted and acid-etched surfaces (modSLA) is unknown. The present study evaluated modSLA implant surfaces modified with RGD and KRSR for potentially enhanced effects on bone apposition and interfacial shear strength during early stages of bone regeneration. Two sets of experimental implants were placed in the maxillae of eight miniature pigs, known for their rapid wound healing kinetics: bone chamber implants creating two circular bone defects for histomorphometric analysis on one side and standard thread configuration implants for removal torque testing on the other side. Three different biofunctionalized modSLA surfaces using poly-L-lysine-graft-poly(ethylene glycol) (PLL-g-PEG) as a carrier minimizing nonspecific protein adsorption [(i) 20 pmol cm⁻² KRSR alone (KRSR); or in combination with RGD in two different concentrations; (ii) 0.05 pmol cm⁻² RGD (KRSR/RGD-1); (iii) 1.26 pmol cm⁻² RGD (KRSR/RGD-2)] were compared with (iv) control modSLA. Animals were sacrificed at 2 weeks. Removal torque values (701.48-780.28 N mm), bone-to-implant contact (BIC) (35.22%-41.49%), and new bone fill (28.58%-30.62%) demonstrated no significant differences among treatments. It may be concluded that biofunctionalizing modSLA surfaces with KRSR and RGD derivatives of PLL-g-PEG polymer does not increase BIC, bone fill, or interfacial shear strength.

Modeling Small Molecule Elution From a Hydrogel using a Microfluidic Technique

Drug release from a fluid-contacting biomaterial is simulated using a microfluidic device with channels defined by solute-loaded hydrogel. In order to mimic a drug delivery device, a solution of poly(ethylene glycol) diacrylate (PEG-DA), solute, and photoinitiator is cured inside a microfluidic device with a channel through the center ofthe hydrogel. As water is pumped through the channel, solute diffuses out of the hydrogel and into the water. Channel sizes within the devices range from 300 µm to 1000 µm to simulate vessels within the body. The properties of the PEG hydrogel were characterizedby the extent of crosslinking, the swelling ratio, and the mesh size of the gel. The structure of the hydrogel was related to the UV exposure dosage and the initial water and solute content in the PEG-DA solution.

Continuous Formation and Separation of Calcium-Alginate Capsules Containing Viable Mammalian Cells in Microfluidic Devices

Microfluidic devices can be used for many applications, including the formation of well-controlled emulsions. In this study, the capability to continuously create monodisperse droplets in a microfluidic device was used to form calcium-alginate capsules.Calcium-alginate capsules have many potential uses, such as immunoisolation of cells and microencapsulation of active drug ingredients or bitter agents in food or beverage products. The gelation of calcium-alginate capsules is achieved by crosslinking sodiumalginate with calcium ions. Calcium ions dissociated from calcium carbonate due to diffusion of acetic acid from a sunflower oil phase into an aqueous droplet containing sodium-alginate and calcium carbonate. After gelation, the capsules were separated from the continuous oil phase into an aqueous solution for use in biological applications. Typically, capsules are separated bycentrifugation, which can damage both the capsules and the encapsulated material. A passive method achieves separation without exposing the encapsulated material or the capsules to large mechanical forces, thereby preventing damage. To achieve passiveseparation, the use of a microfluidic device with opposing channel wa hydrophobicity was used to stabilize co-laminar flow of im of hydrophobicity is accomplished by defining one length of the channel with a hydrogel. The chosen hydrogel was poly (ethylene glycol) diacrylate, which adheres to the glass surface through the use of self-assembled monolayer of 3-(trichlorosilyl)-propyl methacrylate. Due to the difference in surface energy within the channel, the aqueous stream is stabilized near a hydrogel and the oil stream is stabilized near the thiolene based optical adhesive defining the opposing length of the channel. Passive separation with co-laminar flow has shown success in continuously separating calcium-alginatecapsules from an oil phase into an aqueous phase. In addition to successful formation and separation of calcium alginate capsules,encapsulation of Latex micro-beads and viable mammalian cells has been achieved. The viability of encapsulated mammalian cells was determined using a live/dead stain. The co-laminar flow device has also been demonstrated as a means of separating liquid-liquidemulsions.

A MICROFLUIDIC METHOD TO MEASURE DIFFUSION IN HYDROGELS

A novel microfluidic method is proposed for studying diffusion of small molecules in a hydrogel. Microfluidic devices were prepared with semi-permeable microchannels defined by crosslinked poly(ethylene glycol) (PEG). Uptake of dye molecules from aqueous solutions flowing through the microchannels was observedoptically and diffusion of the dye into the hydrogel was quantified. To complement the diffusion measurements from the microfluidic studies, nuclear magnetic resonance(NMR) characterization of the diffusion of dye in the PEG hydrogels was performed. The diffusion of small molecules in a hydrogel is relevant to applications such asdrug delivery and modeling transport for tissue-engineering applications. The diffusion of small molecules in a hydrogel is dependent on the extent of crosslinking within the gel, gel structure, and interactions between the diffusive species and the hydrogel network. These effects were studied in a model environment (semi-infinite slab) at the hydrogelfluid boundary in a microfluidic device. The microfluidic devices containing PEG microchannels were fabricated using photolithography. The unsteady diffusion of small molecules (dyes) within the microfluidic device was monitored and recorded using a digital microscope. The information was analyzed with techniques drawn from digital microscopy and image analysis to obtain concentration profiles with time. Using a diffusion model to fit this concentration vs. position data, a diffusion coefficient was obtained. This diffusion coefficient was compared to those from complementary NMR analysis. A pulsed field gradient (PFG) method was used to investigate and quantify small molecule diffusion in gradient (PFG) method was used to investigate and quantify small molecule diffusion in hydrogels. There is good agreement between the diffusion coefficients obtained from the microfluidic methods and those found from the NMR studies. The microfluidic approachused in this research enables the study of diffusion at length scales that approach those of vasculature, facilitating models for studying drug elution from hydrogels in blood-contacting applications.

Quantifying The Diffusion And Erosion Of Degradable Hydrogels Using A Microfluidic Technique

Hydrogels are composed of cross-linked networks of hydrophilic polymers that are biocompatible due to their high water content. Mass transfer through hydrogels has been suggested as an effective method of drug delivery, specifically in degradable polymers to minimize lasting effects within the body. Diffusion of small molecules in poly (ethylene glycol) diacrylate (PEG-DA) and dextran methacrylate (dex-MA) hydrogels was characterized in a microfluidic device and by complementary techniques. Microfluidic devices were prepared by crosslinking a formulation of hydrogel and photo-initiator, with and without visible dye, using photolithography to define a central microchannel. Channel sizes within the devices were approximately 600 ¿m to simulate vessels within the body. The microfluidic technique allows for both image and effluent analyses. To visualize the diffusive behavior within the dextran hydrogel, methylene blue and sulforhodamine 101 dyes were used in both elution and uptake experiments. Three analysis techniques for measuring diffusion coefficients were used to quantify the diffusion of solute in the hydrogel, including optical microscopy, characterization of device effluent, and NMR analyses. The optical microscopy technique analyzes images of the dye diffusion captured by a stereomicroscope to generate dye concentration v. position profiles. The data was fit to a diffusion model to determine diffusion coefficients and the dye release profile. In a typical elution experiment, aqueous solution is pumped through the microchannel and dye diffuses out of the hydrogel and into the aqueous phase. During elution, images are taken at regular time intervals and the effluent was collected. Analysis of the device effluent was performed using ultraviolet-visible (UV/Vis) spectroscopy to determine the effluent dye concentration and thus a short-time diffusion coefficient. Nuclear magnetic resonance (NMR) was used to determine a free diffusion coefficient of molecules in hydrogel without the effect of a concentration gradient. Diffusion coefficients for methylene blue and sulforhodamine 101 dyes in dex-MA hydrogel calculated using the three analysis methods all agree well. It was determined that utilizing a combination of the three techniques offers greater insight into molecular diffusion in hydrogels than employing each technique individually. The use of the same microfluidic devices used to measure diffusion is explored in the use of studying the degradation of dex-MA hydrogels. By combining what is known about the degradation rate in regards to the effect of pH and crosslinking and the ability to use a dye solution in contrast to establish the hydrogel boundaries could be a novel approach to studying hydrogel degradation.

A Microfluidic Method to Measure Small Molecule Diffusion in Hydrogels

Drug release from a fluid-contacting biomaterial is simulated using a microfluidic device with a channel defined by solute-loaded hydrogel; as water is pumped through the channel, solute transfers from the hydrogel into the water. Optical analysis of in-situ hydrogels, characterization of the microfluidic device effluent, and NMR methods were used to find diffusion coefficients of several dyes (model drugs) in poly( ethylene glycol) diacrylate (PEG-DA) hydrogels. Diffusion coefficients for methylene blue and sulforhodamine 101 in PEG-DA calculated using the three methods are in good agreement; both dyes are mobile in the hydrogel and elute from the hydrogel at the aqueous channel interface. However, the dye acid blue 22 deviates from typical diffusion behavior and does not release as expected from the hydrogel. Importantly, only the microfluidic method is capable of detecting this behavior. Characterizing solute diffusion with a combination of NMR, optical and effluent methods offer greater insight into molecular diffusion in hydrogels than employing each technique individually. The NMR method made precise measurements for solute diffusion in all cases. The microfluidic optical method was effective for visualizing diffusion of the optically active solutes. The optical and effluent methods show potential to be used to screen solutes to determine if they elute from a hydrogel in contact with flowing fluid. Our data suggest that when designing a drug delivery device, analyzing the diffusion from the molecular level to the device level is important to establish a complete picture of drug elution, and microfluidic methods to study such diffusion can play a key role. (C) 2013 Elsevier B.V. All rights reserved.