Indium composition dependence of the size uniformity of InGaAs quantum dots on (311)B GaAs grown by molecular beam epitaxy

The deposition of InxGa1-xAs (0.2 less than or equal to x less than or equal to 0.5) on (311)B GaAs surfaces using solid source molecular beam epitaxy (MBE) has been studied. Both AFM and photoluminescence emission showed that homogeneous quantum dots could be formed on (311)B GaAs surface when indium composition was around 0.4. Indium composition had a strong influence on the size uniformity and the lateral alignment of quantum dots. Compared with other surface orientation, (100) and (n11) A/B (n=1,2,3), photoluminescence measurement confirmed that (311)B surface is the most advantageous in fabricating uniform and dense quantum dots.

Two-dimensional ordering of self-assembled InxGal-xAs quantum dots grown on GaAs(311)B surfaces

Two-dimensional (2D) ordering of self-assembled InxGa1-xAs quantum dots (QDs) fabricated on GaAs(311)B surface by molecular beam epitaxy (MBE) are reported. The QDs are aligned into rows deferring from the direction of the misorientation of the substrate, and strongly dependent on the mole In content x of InxGa1-xAs solid solution. The ordering alignment deteriorates significantly as the In content is increased to above 0.5. The 2D ordering can be described as a centered rectangular unit mesh with the two sides parallel to [01 (1) over bar] and [(2) over bar 33], respectively. Their relative arrangement seems to be determined by a combination of the strongly repulsive elastic interaction between neighbouring islands and the minimization of the strain energy of the whole system. The ordering also helps to improve the size homogeneity of the InGaAs islands. Photoluminescence (PL) result demonstrates that QDs grown on (311)B have the narrowest linewidth and the strongest integrated intensity, compared to those grown on (100) and other high-index planes under the same condition. (C) 1999 Elsevier Science B.V. All rights reserved.

A novel 1.3-mu m high T-0 AlGaInAs/InP strained-compensated multi-quantum well complex-coupled distributed feedback laser diode

A 1.3-mu m AlGaInAs/InP buried heterostructure (BH) stripe distributed feedback laser with a novel AlInAs/InP complex-coupled grating grown by low-pressure metalorganic chemical vapor deposition (LP-MOCVD) is proposed and demonstrated. A high characteristic temperature (T-0 = 90K between 20-80 degrees C) and temperature-insensitive slope efficiency (0.25 dB drop from 20 to 80 degrees C) in 1.3 mu m AlGaInAs/InP DFB lasers was obtained by introducing AI(Ga)InAs graded-index separate-confinement heterostructure (GRINSCH) layers and a strained-compensated (SC) multi-quantum well (MQW).

Two-dimensional ordering of self-assembled InxGa1-xAs quantum dots grown on GaAs(311)B surfaces

The two-dimensional (2D) ordering of self-assembled InxGa1-xAs quantum dots (QDs) fabricated on GaAs(3 1 1)B surface by molecular beam epitaxy (MBE) are reported. The QDs are aligned into rows differing from the direction of the misorientation of the substrate, and strongly dependent on the mole In content x of InxGa1-As-x solid solution. The ordering alignment deteriorates significantly as the In content is increased to above 0.5. The 2D ordering can be described as a centered rectangular unit mesh with the two sides parallel to [0 1 (1) over bar] and [(2) over bar 3 3], respectively. Their relative arrangement seems to be determined by a combination of the strongly repulsive elastic interaction between the neighboring islands and the minimization of the strain energy of the whole system. The ordering also helps to improve the size homogeneity of the InGaAs islands. The photoluminescence (PL) result demonstrates that QDs grown on (3 1 1)B have the narrowest linewidth and the strongest integrated intensity, compared to those on (1 0 0) and other high-index planes under the same condition. (C) 1999 Elsevier Science B.V. All rights reserved.

A comparison of photoluminescence properties of InGaAs GaAs quantum dots with a single quantum well

Variable temperature photoluminescence (PL) measurements for In0.3Ga0.7As(6 nm)/GaAs(34 nm) quantum dot superlattices with a period of 20 and an In0.3Ga0.7As(6 nm)/GaAs(34 nm) reference single quantum well have been conducted. It is found that the temperature dependence is different between the quantum dots and the reference single quantum well. The PL peak energy of the single quantum well decreases faster than that of the quantum dots with increasing temperature. The PL peak energy for the InGaAs/GaAs quantum dots closely follows the InAs band gap in the temperature range from 11 to 170 K, while the PL peak energy for the InGaAs/GaAs quantum well closely follows the GaAs band gap. In comparison with InAs/GaAs quantum dots, the InGaAs/GaAs quantum dots are more typical as a zero-dimensional system since the unusual PL results, which appear in the former, are not obvious for the latter. (C) 1999 American Institute of Physics. [S0021-8979(99)08615-6].

Substrate surface atomic structure influence on the growth of InAlAs quantum dots

We have examined the influence of substrate surface orientation on self-assembled InAlAs/AlGaAs quantum dots grown on (0 0 1) and (n 1 1) A/B (n = 3, 5) GaAs substrates by molecular beam epitaxy (MBE). Preliminary characterizations have been performed using photoluminescence (PL) and transmission electron microscopy (TEM). The PL emission energies of quantum dots on high Miller index surface are found to be strongly dependent on the atomic-terminated surface (A or B surface) of the substrate. We observed that there were planar ordering larger islands on (3 1 1)B surface compared to (0 0 1) surface, in contrast, a rough interface and smaller "grains" on (3 1 1)A surface, this result is identical with PL emission energy from these islands. We propose that the rapid strain-induced surface "roughening" impedes the formation of 3D islands on A surface, and indicating that this is a promising approach of the realization of ordering distribution on (3 1 1)B plane for devices such as red-emitting semiconductor quantum dots lasers. (C) 1999 Elsevier Science B.V. All rights reserved.

Size quantization effects in InAs self-assembled islands on InP(001) at the onset of 2D-to-3D transition

Photoluminescence spectroscopy has been used to investigate self-assembled InAs islands in InAlAs grown on InP(0 0 1) by molecular beam epitaxy, in correlation with transmission electron microscopy. The nominal deposition of 3.6 monolayers of InAs at 470 degrees C achieves the onset stage of coherent island formation. In addition to one strong emission around 0.74 eV, the sample displaces several emission peaks at 0.87, 0.92. 0.98, and 1.04 eV. Fully developed islands that coexist with semi-finished disk islands account for the multipeak emission. These results provide strong evidence of size quantization effects in InAs islands. (C) 1999 Elsevier Science B.V. All rights reserved.

In composition dependence of lateral ordering in InGaAs quantum dots grown on (311)B GaAs substrates

Self-assembled InxGa1-xAs quantum dots (QDs) on (311)A/B GaAs surfaces have been grown by molecular beam epitaxy (MBE). Spontaneously ordering alignment of InxGa1-xAs with lower In content around 0.3 have been observed. The direction of alignment orientation of the QDs formation differs from the direction of misorientation of the (311)B surface, and is strongly dependent upon the In content x. The ordering alignment become significantly deteriorated as the In content is increased to above 0.5 or as the QDs are formed on (100) or (311)A substrates. (C) 1999 Elsevier Science B.V. All rights reserved.

Pressure behaviour of photoluminescence from InAs submonolayer in GaAs matrix

We have investigated the dependence on hydrostatic pressure of the photoluminescence of an InAs submonolayer embedded in a GaAs matrix at 15 K and for pressure up to 8 GPa. Strong InAs-related emissions are observed in all three samples at ambient pressure. The temperature dependence of the emission intensity for these Peaks can be well characterized by the thermal activation of excitons from the InAs layer to the GaAs matrix. With increasing pressure, the InAs-related peaks shift to. higher energies. The pressure coefficients of these peaks are very close to that of the free exciton in bulk GaAs. Some weak peaks observed at pressures above 4.2 GPa are attributed to indirect transitions involving X states in the InAs layer. These results are similar to the pressure behaviour observed in the InAs/GaAs monolayer structures. A group of new lines has been observed in the spectra when pressure is increased beyond 2.5 GPa, which is attributed to the N isoelectronic traps in the GaAs matrix.

Evidence of multimodal patterns of self-organized quantum dots

We have used Deep Level Transient Spectroscopy to investigate self-organized InAs/GaAs quantum dots. The existence of different dot families is confirmed by the deconvolution of the spectra in Gaussian components with full width at half maximum of 60-70meV. The strain of quantum dots is responsible for the relaxation of large quantum dots leading to generation of dislocations. (C) 1998 Academic Press.

Analysis of atomic force microscopic results of InAs islands formed by molecular beam epitaxy

Atomic force microscopy (AFM) measurements of nanometer-sized islands formed by 2 monolayers of InAs by molecular beam epitaxy have been carried out and the scan line of individual islands was extracted from raw AFM data for investigation. It is found that the base widths of nanometer-sized islands obtained by AFM are not reliable due to the finite size and shape of the contacting probe. A simple model is proposed to analyze the deviation of the measured value From the real value of the base width of InAs islands. (C) 1998 Elsevier Science B.V. All rights reserved.

Effects of growth interruption on self-assembled InAs/GaAs islands

The effect of growth interruption on the InAs deposition and its subsequent growth as self-assembled island structures, in particular the material transport process of the InAs layers has been investigated by photoluminescence and transmission electron microscopy measurements. InAs material in structures with only coherent islands transfers from the wetting layer to the formed islands and the growth interruption causes a red shift of PL peak energy. On the other hand, the PL peak shifts to higher energy in structures containing simultaneously coherent and noncoherent islands with dislocations. In this case, the noncoherent islands capture InAs material from the surrounding wetting layer as well as coherent islands, which casues a reduction in the size of these islands. The variations in the PL intensity and line width are also discussed. (C) 1998 Elsevier Science B.V. All rights reserved.

Asymmetry in the vertically aligned growth induced InAs islands in GaAs

A 10-InAs-island-layer vertically coupled quantum dot structure on (001) GaAs was grown and investigated by molecular beam epitaxy and transmission electron microscopy. The result shows that the vertically aligned InAs islands are asymmetrical along the two < 110 > directions on the (001) growth plane. Such an asymmetry in the vertically coupled quantum dot structure can be explained with the chemical polarity in the III-V compound semiconductors.

Optical anisotropy of InAs monolayer in (311)-oriented GaAs matrix

In-plane optical anisotropy which comes from the heavy hole and the light hole transitions in an InAs monolayer inserted in (311)-oriented GaAs matrix is observed by reflectance difference spectroscopy. The observed steplike density of states demonstrates that the InAs layer behaves like a two-dimensional quantum well rather than isolated quantum dots. The magnitude of the anisotropy is in good agreement with the intrinsic anisotropy of (311) orientation quantum wells, indicating that there is little structural or strain anisotropy of the InAs layer grown on (311)-oriented GaAs surface.

Quantum confinement effect in silicon quantum-well layers

The electronic states and optical transition properties of silicon quantum-well layers embedded by SiO2 layers are studied by the empirical pseudopotential homojunction model. The energy bands, wave functions, and the optical transition matrix elements are obtained for layers of thickness from 1 to 6 nm, and three oriented directions (001), (110), and (111). It is found that for Si layers in the (001) direction the energy gap is pseudodirect, for these in the (111) direction the energy gap is indirect, while for those in the (110) direction the energy gap is pseudodirect or indirect for a thickness smaller or larger than 3 nm, respectively. The optical transition matrix elements are smaller than that of diner transition, and increase with decreasing layer thickness. When the thickness of a layer is smaller than 2 nm, the Si QW layers have larger transition matrix elements. It is caused by mixing of bulk X states with the Gamma(1) state. The calculated results are compared with experimental results.