Multistage etching process for microscopically smooth tellurite glass surfaces in optical fibers

Bulk samples of tellurite glass with composition 75TeO(2)-20ZnO-5Na(2)O (TZN) were fabricated by melting and quenching techniques. In order to improve the surface quality of optical fiber preform made with this tellurite glass, the authors developed a multistage etching process. The relationship between successive etching treatments and roughness of the TZN glass surface was probed by using an atomic force microscope. The results demonstrate that this multistage etching method effectively improves this tellurite glass surface smoothness to a level comparable with that of a reference silica glass slide, and the corresponding chemical micromechanisms and fundamentals are discussed and confirmed by atomic force microscopy, potentially contributing to the development of multicomponent soft glass fibers and devices. (C) 2010 American Vacuum Society. [DOI: 10.1116/1.3437017]

THE ADSORPTION OF O2 ON FESI SURFACES

The initial adsorption stages and the interaction of oxygen on FeSi surfaces have been studied as a function of exposure and annealing temperature using a variety of techniques including HREELS, AES, LEED, XPS and UPS. O2 was found to adsorb dissociatively on the FeSi surfaces at room temperature. The whole adsorption process can be divided into four stages. Heating promotes the oxidation of Si, and a thin SiO2 overlayer is formed on the surface when annealed at 450-degrees-C, while all FeOx species are reduced. Models for adsorbed atomic O on the FeSi(100) surface exposed to different oxygen exposures have been put forward to account for the observed experimental results.

Electron diffraction and photoemission studies of clean and water-covered Si(5,5,12) and Si(112) surfaces

The structure of silicon surfaces in the orientation range (113)-(5,5,12)-(337)-(112) has been investigated using high resolution LEED and photoemission both on a spherical and on flat samples. We find that Si(5,5,12) [5.3 degrees from (113) and 0.7 degrees from (937)] is the only stable orientation between (113) and (111) and confirm the result of Baski et al. [Science 269, 1556 (1995)] that it has a 2 x 1 superstructure with a very large unit cell of 7.68 x 53.5 Angstrom(2). Adsorption measurements of water on Si(5,5,12) yield a mobile precursor kinetics with two kinds of regions saturating at 0.25 and 0.15 ML which are related to adsorption on different sites. Using these results, a modified structure model is proposed. Surfaces between (113) and (5,5,12) separate into facets of these two orientations; between (5,5,12) and (112), they separate into (5,5,12) and (111) facets. (337) facets in this range may be considered as defective (5,5,12) facets.

Morphology Evolution of (331)A High-Index Surfaces During Atomic Hydrogen Assisted Molecular Beam Epitaxy (MBE)

Step like morphology of (331)A high-index surfaces during atomic hydrogen assisted molecular beam epitaxy (MBE) growth has been investigated. Atomic Force Microscope (AFM) measurements show that in conventional MBE, the step heights and terrace widths of GaAs layers increase monotonically with increasing substrate temperatures. The terrace widths and step densities increase with increasing the GaAs layer thickness and then saturates. And, in atomic hydrogen assisted MBE, the terrace width reduces and density increases when depositing the same amount of GaAs. It attributes this to the reduced surface migration length of Ga adatoms with atomic hydrogen. Laterally ordered InAs self-aligned nano-wires were grown on GaAs (331)A surfaces and its optical polarization properties were revealed by photoluminescence measurements.

Growth of Space Ordered on GaAs（100） Vicinal 1.3μm InAs Quantum Dots Substrates by MOCVD

Space ordered 1.3μm self-assembled InAs QDs are grown on GaAs（100） vicinal substrates by MOCVD. Photoluminescence measurements show that the dots on vicinal substrates have a much higher PL intensity and a narrower FWHM than those of dots on exact substrates, which indicates better material quality. To obtain 1.3μm emissions of InAs QDs, the role of the so called InGaAs strain cap layer （SCL） and the strain buffer layer （SBL） in the strain relaxation process in quantum dots is studied. While the use of SBL results only in a small change of emission wavelength,SCL can extend the QD＇s emission over 1.3μm due to the effective strain reducing effect of SCL.