Effect of Substrate Temperature on the Structural and Luminescent Characteristics of RF-Magnetron-Sputtered ZnGa2O4:Dy3+ Thin Films

ZnGa2O4:Dy3+ phosphor thin films were deposited on quartz substrates by radio frequency rf magnetron sputtering and the effect of substrate temperature on its structural and luminescent properties was investigated. Polycrystalline film could be deposited even at room temperature. The crystalline behavior, Zn/Ga ratio, and surface morphology of the films were found to be highly sensitive to substrate temperature. Under UV illumination, the as-deposited films at and above 300°C gave white luminescence even without any postdeposition treatments. The photoluminescent PL emission can be attributed to the combined effect of multicolor emissions from the single luminescence center Dy3+ via host-sensitization. Maximum PL emission intensity was observed for the film deposited at 600°C, and the CIE chromaticity coordinates of the emission were determined to be x,y = 0.34, 0.31 .

Influência da temperatura e do tipo de substrato em filmes de GaN depositados por magnetron sputtering reativo

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Growth evolution of self-textured ZnO films deposited by magnetron sputtering at low temperatures

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Nanocrystalline vanadium oxide films synthesized by plasma-assisted reactive rf sputtering deposition

Plasma-assisted reactive rf magnetron sputtering deposition is used to fabricate vanadium oxide films on glass, silica and silicon substrates. The process conditions are optimized to synthesize phase-pure vanadium pentoxide (V2O5) featuring a nanocrystalline structure with the predominant (0 0 1) crystallographic orientation, surface morphology with rod-like nanosized grains and very uniform (the non-uniformity does not exceed 4%) coating thickness over large surface areas. The V2O5 films also show excellent and temperature-independent optical transmittance in a broad temperature range (20-95 °C). The results are relevant to the development of smart functional coatings with temperature-tunable properties. © 2007 IOP Publishing Ltd.

RF plasma sputtering deposition of hydroxyapatite bioceramics : synthesis, performance, and biocompatibility

Hydroxyapatite (HA) coatings have numerous applications in orthopedics and dentistry, owing to their excellent ability to promote stronger implant fixation and faster bone tissue ingrowth and remodeling. Thermal plasma spray and other plasma-assisted techniques have recently been used to synthesize various calcium phosphate-based bioceramics. Despite notable recent achievements in the desired stoichiometry, phase composition, mechanical, structural, and bio-compatible properties, it is rather difficult to combine all of the above features in a single coating. For example, many existing plasma-sprayed HA coatings fall short in meeting the requirements of grain size and crystallinity, and as such are subject to enhanced resorption in body fluid. On the other hand, relatively poor interfacial bonding and stability is an obstacle to the application of the HA coatings in high load bearing Ti6Al4V knee joint implants. Here, we report on an alternative: a plasma-assisted, concurrent, sputtering deposition technique for high performance biocompatible HA coatings on Ti6Al4V implant alloy. The plasma-assisted RF magnetron co-sputtering deposition method allows one to simultaneously achieve most of the desired attributes of the biomimetic material and overcome the aforementioned problems. This article details the film synthesis process specifications, extensive analytical characterization of the material's properties, mechanical testing, simulated body fluid assessments, biocompatibility and cytocompatibility of the HA-coated Ti6Al4V orthopedic alloy. The means of optimization of the plasma and deposition process parameters to achieve the desired attributes and performance of the HA coating, as well as future challenges in clinical applications are also discussed.

Studies on RF Magnetron Sputtered HfO2 Thin Films for Microelectronic Applications

We investigated the effect of oxygen flow rate during the reactive magnetron sputtering on the compositional, structural, optical and electrical properties of HfO2 films. We also studied the influence of annealing temperature on the structural and electrical properties of optimized HfO2 films of 25 to 30 nm thick. X-ray photoelectron study reveals that the films deposited at 15 SCCM of oxygen flow rate are stoichiometric and have an optical band gap of 5.86 eV. X-ray diffraction indicates that films without oxygen flow are amorphous, and beyond an oxygen flow rate of 5 SCCM exhibit polycrystalline monoclinic structure. At an annealing temperature of 600 degrees C, tetragonal phase was observed besides the monoclinic phase. The dielectric constant of 11 and low leakage currents of 1 x 10(-7) A/cm(2) were achieved for the stoichiometric films. As-deposited films show significant frequency dispersion due to the presence of defect states at the HfO2/Si interface, and it reduces after annealing.

RF magnetron sputtered perovskite oxide electrodes for Ferroelectric RAM

The main objective of this thesis work is to optimize the growth conditions for obtaining crystalline and conducting Lao.5Sro.5Co03 (LSCO) and Lao.5Sro.5Coo.5.5Nio.5O3 (LSCNO) thin films at low processing temperatures. The films are prepared by radio frequency magnetron sputtering under various deposition conditions. The thin films were used as electrodes for the fabrication of ferroelectric capacitors using BaO.7SrO.3 Ti03 (BST) and PbZro.52 Tio.4803 (PZT). The structural and transport properties of the La1_xSrxCo03 and Lao.5Sro.5Co1_xNix03 are also investigated. The characterization of the bulk and the thin films were performed using different tools. A powder X-ray diffractometer was used to analyze the crystalline nature of the material. The transport properties were investigated by measuring the temperature dependence of resistivity using a four probe technique. The magnetoresistance and thermoelectric power were also used to investigate the transport properties. Atomic force microscope was used to study the surface morphology and thin film roughness. The ferroelectric properties of the capacitors were investigated using RT66A ferroelectric tester.

Reactive species in RF plasma sputtering deposition of nanocrystalline calcium phosphate bio-active films

Optical emission of reactive plasma species during the synthesis of functionally graded calcium phosphate-based bioactive films has been investigated. The coatings have been deposited on Ti-6Al-4V orthopedic alloy by co-sputtering of hydroxyapatite (HA) and titanium targets in reactive plasmas of Ar + H2O gas mixtures. The species, responsible for the Ca-P-Ti film growth have been non-intrusively monitored in situ by a high-resolution optical emission spectroscopy (OES). It is revealed that the optical emission originating from CaO species dominates throughout the deposition process. The intensities of CaO, PO and CaPO species are strongly affected by variations of the operating pressure, applied RF power, and DC substrate bias. The optical emission intensity (OEI) of reaction species can efficiently be controlled by addition of H2O reactant.

Electrical and structural properties of zirconia thin films prepared by reactive magnetron sputtering

Thin films of ZrO2 were prepared by reactive magnetron sputtering. Annealing of the films exhibited a drastic change in the properties due to improved crystallinity and packing density. The root mean square roughness of the sample observed from atomic force microscope is about 5.75 nm which is comparable to the average grain size of the thin film which is about 6 nm obtained from X-ray diffraction. The film annealed at 873 K exhibits an optical band gap of around 4.83 eV and shows +4 oxidation state of zirconium indicating fully oxidized zirconium, whereas higher annealing temperatures lead to oxygen deficiency in the films and this is reflected in their properties. A discontinuity in the imaginary part of the AC conductivity was observed in the frequency range of tens of thousands of Hz, where as, the real part does not show such behavior.

dc reactive magnetron sputtering of titanium‐structural and optical characterization of TiO2 films

This paper deals with the reactive sputtering of titanium in an argon and oxygen mixture. The variation in cathode potential as a function of oxygen partial pressure has been explained in terms of cathode poisoning effects. The titania films deposited during this process have been studied for their structural and optical characteristics. The effect of substrate temperature (from 25 to 400 °C) and annealing (from 250 to 700 °C) on the packing density, refractive index, extinction coefficient, and crystallinity has been investigated. The refractive index varied from 2.24 to 2.46 and extinction coefficient from 2.6 × 10-3 to 10.4× 10-3 at 500 nm as the substrate temperature increased from 25 to 400 °C. The refractive index increased from 2.19 to 2.35 and extinction coefficient changed from 3.2× 10-3 to 11.6 × 10-3 at 500 nm as the annealing temperature was increased from 250 to 700 °C. Anatase and rutile phases have been observed in the films deposited at 400 °C substrate temperature and annealed at 300 °C. The changes in the optical constants at higher substrate temperature have been attributed to an increase in packing density, oxygen content, and crystallinity of the films.

Effect of substrate temperature on the properties of ZrO2 films prepared by d.c. reactive magnetron sputtering

Studies of ZrO2 films prepared by d.c. reactive magnetron sputtering are described. The effects of substrate temperature on the packing density, refractive index, extinction coefficient and crystallinity phase have been investigated in the temperature range 25–450 °C. The refractive index varied from 1.84 to 1.95 and extinction coefficient from 2 × 10−3 to 9.6 × 10−3. This was explained on the basis of an increase in packing density from 0.686 to 0.813. The change in packing density has been attributed to a decrease in the oxygen condensation at higher temperatures. Annealing results in a decrease in refractive index and increase in extinction coefficient. The films deposited at 150 °C showed a monoclinic phase which transforms to a tetragonal phase at higher substrate temperatures.

Rapid thermal processed thin films of niobium pentoxide (Nb2 O5) deposited by reactive magnetron sputtering

Niobium pentoxide thin films have been deposited on silicon and platinum-coated silicon substrates by reactive magnetron sputtering. The as-deposited films were amorphous and showed good electrical properties in terms of a dielectric permittivity of about 30, and leakage current density of 10(-6) A cm(-2) al a field of 120 kV cm(-1). A rapid thermal annealing process at 800 degrees C further increased the dielectric constant to 90 and increased the leakage current density to 5 x 10(-6) A cm(-2). The current-voltage characteristics observed at low and high fields suggested a combination of phenomena at different regimes of applied electric field. The capacitance-voltage characteristics performed in the metal-insulator-semiconductor configuration indicated good electronic interfaces with a nominal trap density of 4.5 x 10(12) cm(-2) eV(-1), which is consistent with the behavior observed with conventional dielectrics such as SiO2 on silicon surfaces.

Studies on the optimisation of unbalanced magnetron sputtering cathodes

The optimisation is reported on the design of unbalanced magnetron (UBM) sputtering cathodes. For the study, a planar circular cathode backed by a double-coil electromagnet (compatible for a 100 mm diameter target) was developed. The variation of the structure and strength of the magnetic field in front of the target was investigated for different current combinations in the electromagnetic coils, and its effect on the sputtering process was analysed. The observations on the magnetic field geometry revealed some interesting features, such as the balancing point of the fields along the axis (null-point), and the zero axial region over the target surface (B-z = 0 ring). The positions of both could be controlled by adjusting the ratio of the electric current in the coils. The magnetic field null-point could be used as a reference for the region of homogeneous film growth. The B-z = 0 ring was the location where the glow discharge concentrated (or where the maximum target erosion occurred). The diameter of the ring determined the area covered by the discharge and thus the sputtering efficiency. The optimum substrate position can be fixed according to the position of the null-point and optimisation of sputtering can be achieved by adjusting the diameter of the B-z = 0 ring. The results of this study should be helpful in the designing of an ideal UBM using permanent magnets as well as electromagnets. (C) 1999 Elsevier Science Ltd. All rights reserved.

Effect of substrate bias voltage on the structure, electric and dielectric properties of TiO(2) thin films by DC magnetron sputtering

Titanium dioxide (TiO(2)) films have been deposited on glass and p-silicon (1 0 0) substrates by DC magnetron sputtering technique to investigate their structural, electrical and optical properties. The surface composition of the TiO(2) films has been analyzed by X-ray photoelectron spectroscopy. The TiO(2) films formed on unbiased substrates were amorphous. Application of negative bias voltage to the substrate transformed the amorphous TiO(2) into polycrystalline as confirmed by Raman spectroscopic studies. Thin film capacitors with configuration of Al/TiO(2)/p-Si have been fabricated. The leakage current density of unbiased films was 1 x10(-6) A/cm(2) at a gate bias voltage of 1.5 V and it was decreased to 1.41 x 10(-7) A/cm(2) with the increase of substrate bias voltage to -150 V owing to the increase in thickness of interfacial layer of SiO(2). Dielectric properties and AC electrical conductivity of the films were studied at various frequencies for unbiased and biased at -150 V. The capacitance at 1 MHz for unbiased films was 2.42 x 10(-10) F and it increased to 5.8 x 10(-10) F in the films formed at substrate bias voltage of -150 V. Dielectric constant of TiO(2) films were calculated from capacitance-voltage measurements at 1 MHz frequency. The dielectric constant of unbiased films was 6.2 while those formed at -150 V it increased to 19. The optical band gap of the films decreased from 3.50 to 3.42 eV with the increase of substrate bias voltage from 0 to -150 V. (C) 2011 Elsevier B. V. All rights reserved.