Exfoliation of copper hydroxysalt in water and the conversion of the exfoliated layers to cupric and cuprous oxide nanoparticles

P-aminobenzoate- intercalated copper hydroxysalt was prepared by coprecipitation at high pH (similar to 12). As the pH was reduced to similar to 7 on washing with water, the development of partial positive charge on the amine end of the intercalated anion caused repulsion between the layers leading to delamination and colloidal dispersion of monolayers of copper hydroxysalt in water. The dispersed copper hydroxysalt monolayers were used as precursors for the synthesis of copper(I)/(II) oxide nanoparticles at room temperature. While the hydroxysalt layers yielded spindle-shaped CuO particles when left to stand, they formed hollow spherical nanoparticles of Cu(2)O when treated with an alkaline solution of ascorbic acid.

Copper oxide nanoparticles: an antidermatophytic agent for Trichophyton spp.

Copper oxide (CuO) is one of the most important transition metal oxides due to its unique properties. It is used in various technological applications such as high critical temperature, superconductors, gas sensors, in photoconductive applications and so on. Recently, it has been used as an antimicrobial agent against various pathogenic bacteria. In the present investigation, we studied the structural and antidermatophytic properties of CuO nanoparticles (NPs) synthesized by a precipitation technique. Copper sulfate was used as a precursor and sodium hydroxide as a reducing agent. Scanning electron microscopy (SEM) showed flower-shaped CuO NPs and X-ray diffraction (XRD) pattern showed the crystalline nature of CuO NPs. These NPs were evaluated against two prevalent species of dermatophytes, i.e. Trichophyton rubrum and T. mentagrophytes by using the broth microdilution technique. Further, the NPs activity was also compared with synthetic sertaconazole. Although better antidermatophytic activity was exhibited with sertaconazole as compared to NPs, being synthetic, sertaconazole may not be preferred, as it shows different adverse effects. Trichophyton mentagrophytes is more susceptible to NPs than T. rubrum. A phylogenetic approach was applied for predicting differences in susceptibility of pathogens.

An organic-inorganic hybrid ultrathin film: preparation and characterization of copper phthalocyanine derivative-ferric oxide nanoparticles

A nanoparticulate ferric oxide-copper tris(2,4-di-tert-amylphenoxy)-8-quinolinolylphthalocyanine hybrid ultrathin film was constructed from alternate layers by the Langmuir-Blodgett technique. The composition, morphology and structure of the film were studied by X-ray photoelectron spectroscopy (XPS), transmission electron microscopy, atomic force microscopy, small-angle X-ray diffraction, visible spectroscopy and polarized UV-Vis spectroscopy. All the above analyses suggest that the thin film is a kind of one-dimensional superlattice, composed of organic and inorganic components. The XPS data reveal that the nanoparticulate ferric oxide exists as an alpha-Fe2O3 phase in the films. Gas-sensing measurements show that the hybrid LB film has very fast response-recovery characteristics towards 2 ppm C2H5OH vapor.

Alternating LB film of ferric oxide nanoparticles-copper phthalocyanine derivative and its gas sensitivity

Nanoparticulate ferric oxide - tris - (2,4-di-t-amylphenoxy) - (8-quinolinolyl) copper phthalocyanine Langmuir-Blodgett Z-type multilayers were obtained by using monodisperse nanoparticle ferric oxide hydrosol as the subphase. XPS data reveal that the nanoparticle ferric oxide exist as alpha -Fe2O3 phase in the films. Transition electron microscopic (TEM) image of the alternating monolayer shows that the film was highly covered by the copper phthalocyanine derivative and the nanoparticles were arranged rather closely. IR and visible spectra all give the results that the nanoparticles were deposited onto the substrate with the copper phthalocyanine derivative. The gas-sensing measurements show that the alternating LB film had very fast response-recovery characteristic to 2 ppm C2H5OH gas, and also sensitive to larger than 200 ppm NH3.

Study of ferric oxide nanoparticles-tris-(2,4-di-t-amylphenoxy)-(8-quinolinolyl) copper phthalocyanine composite LB film

The ferric oxide nanoparticles-tris-(2,4-di-t-amylphenoxy)-(8-quinolinolyl) copper phthalocyanine (CuPcA(2)) composite ultrathin film was obtained by LB (Langmuir-Blodgett) technique. Structure of the composite LB film was characterized by X-ray photoelectron spectra, transmission electron microscopy, infrared spectra and visible spectra. Gas sensitivity measurements indicate that the composite LB film is sensitive to 100-200 ppm C2H5OH at room temperature. (C) 2000 Elsevier Science S.A. All rights reserved.

Molecular orientation of copper phthalocyanine derivative ins copper phthalocyanine-Fe2O3 nanoparticles alternating LB films

Copper phthalocyanine-Fe2O3 nanoparticles alternating thin films were fabricated by Langmuir-Blodgett technique. Molecular orientation of [4-(4'-benzyloxy phenyl sulfonyl)phenoxy]-tris-4-(2,4-di-t-phenoxy) phthalocyanine copper (II) in its alternating LB films, deposited at different conditions,was studied by polarized UV-Vis spectra. The tilt extent of the copper phthalocyanine molecule omits LB films increases with the surface pressure of the subphase increasing on the same subphase, or with Fe2O3 concentration decreasing at the same pressure. The orientation of the copper phthalocyanine derivative is important for the gas-sensing properties. The bigger the tilt extent of the phthalocyanine molecule is, the greater the sensitivity of the film is.

Facile in situ synthesis of nanofluids based on ionic liquids and copper oxide clusters and nanoparticles

Two stable nanofluids comprising of mixed valent copper(_I,_II) oxide clusters (<1 nm) suspended in 1-butyl-3-methylimidazolium acetate, [C(₄)mim][OAc], and copper(_II) oxide nanoparticles (<50 nm) suspended in trioctyl(dodecyl) phosphonium acetate, [P-₈₈₈₁₂][OAc], were synthesised in a facile one-pot reaction from solutions of copper(_II) acetate hydrate in the corresponding ionic liquids. Formation of the nanostructures was studied using ¹³C NMR spectroscopy and differential scanning calorimetry (DSC). From a solution of Cu(OAc)₂ in 1-ethyl-3-methylimidazolium acetate, [C₂mim][OAc], crystals were obtained that revealed the structure of [C₂mim][Cu₃(OAc)₅(OH)₂(H₂O)]center dot H₂O, indicating the formation of copper hydroxo-clusters in the course of the reaction. Synthesised nanostructures were studied using transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). Physical properties of the prepared IL-nanofluids were examined using IR and UV-VIS spectroscopy, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and densitometry. 

Neocuproine-functionalized silica-coated magnetic nanoparticles for extraction of copper(II) from aqueous solution

Neocuproine has been covalently bound to silica-coated maghemite(c-Fe2O3) magnetic nanoparticles (MNPs) by a phenyl ether linkage. The resulting MNPs are able to remove Cu(II) from 12 ppm aqueous solution with an extraction efficiency of up to 99% at pH 2.

Copper hexacyanoferrate nanoparticles modified electrodes: A versatile tool for biosensors

Copper hexacyanoferrate nanoparticles of about 30 nm in size have been prepared by the sonochemical irradiation of a mixture of aqueous potassium ferricyanide and copper chloride solutions. The nanoparticles were immobilized onto fluorine doped tin oxide (FTO) electrodes by using the electrostatic deposition layer-by-layer technique (LbL), obtaining electroactive films with electrocatalytic properties towards H2O2 reduction, providing higher currents than those observed for electrodeposited bulk material, even in electrolytes containing NH4+, Na+ and K+. The nanoparticles assembly was used as mediator in a glucose biosensor by immobilizing glucose oxidase enzyme by both, cross-linking and LbL. techniques. Sensitivities obtained were dependent on the immobilization method ranging from 1.23 mu A mmol(-1) L cm(-2) for crosslinking to 0.47 mu A mmol(-1) L cm(-2) for LbL; these values being of the same order than those obtained with electrodes where the amount of enzyme used is much higher. Moreover, the linear concentration range where the biosensors can operate was 10 times higher for electrodes prepared with the LbL immobilization method than with the conventional crosslinking one. (C) 2008 Elsevier B.V. All rights reserved.

Fast colorimetric detection of copper ions using L-Cysteine functionalized gold nanoparticles

This communication reports an efficient visual detection method of Cu²⁺ by L-cysteine functionalized gold nanoparticles in aqueous solution. Upon exposure to Cu²⁺, the gold nanoparticle solution changed from red to blue, in response to surface plasmon absorption of dispersed and aggregated nanoparticles. This colorimetric sensor allows a rapid quantitative assay of Cu²⁺ down to the concentration range of 10⁻⁵ M. Recognition of Cu²⁺ and formation of the aggregates are proposed to occur via a 2 : 1 sandwich complex between L-cysteine and Cu²⁺.

Tunnelling current recognition through core-satellite gold nanoparticles for ultrasensitive detection of copper ions

We report a new method for ultrasensitive detection of Cu(2+), which is based on changes in the tunnelling recognition current across self-assembled core-satellite gold nanoparticles (GNPs) networks functionalised with amino acids (l-cysteine). The addition of copper ions induces the formation of GNP/l-cysteine/Cu(2+)/l-cysteine/GNP molecular junctions and generates a significant decrease in the resistance through the networks. The networks are ultrasensitive to over ten orders range of copper ion concentrations.

Voltammetric determination of sulfite using graphite paste electrode modified with nanoparticles of copper pentacyanonitrosylferrate

Copper Pentacyanonitrosylferrate (NCuNP) nanoparticles were prepared in formamide solvent. The material was characterized by Infrared (FTIR), X-Ray Diffraction (XRD) and Ultraviolet-Visible (UV-Vis) Spectroscopy. The Cyclic Voltammogram (CV) the modified graphite paste electrode with NCuNP exhibits two redox couples with (Eθ,)1 = 0.29 and (E θ,)2 = 0.86 V attribute at Cu(I)/Cu (II) and Fe(II)(CN)5NO/Fe(III)(CN) 5NO processes, respectively (KCl = 1.0 mol L-1; v = 20 mV s-1). The redox couple with (Eθ,)2 presents an electrocatalytic response for sulfite. The modified graphite paste electrode gives a linear response of 7.0 × 10-4 to 3.0 × 10-2 mol L-1 (r = 0.998), for sulfite determination with Detection Limit (DL) of 1.76 × 10-3 mol L-1 and an amperometric sensitivity of 3.38 mA/mol L-1 and relative standard desviations ± 3% (n=3). ©The Electrochemical Society.

Direct preparation and characterization of copper pentacyanonitrosylferrate nanoparticles

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Field dependent transition to the non-linear regime in magnetic hyperthermia experiments: Comparison between maghemite, copper, zinc, nickel and cobalt ferrite nanoparticles of similar sizes

Further advances in magnetic hyperthermia might be limited by biological constraints, such as using sufficiently low frequencies and low field amplitudes to inhibit harmful eddy currents inside the patient's body. These incite the need to optimize the heating efficiency of the nanoparticles, referred to as the specific absorption rate (SAR). Among the several properties currently under research, one of particular importance is the transition from the linear to the non-linear regime that takes place as the field amplitude is increased, an aspect where the magnetic anisotropy is expected to play a fundamental role. In this paper we investigate the heating properties of cobalt ferrite and maghemite nanoparticles under the influence of a 500 kHz sinusoidal magnetic field with varying amplitude, up to 134 Oe. The particles were characterized by TEM, XRD, FMR and VSM, from which most relevant morphological, structural and magnetic properties were inferred. Both materials have similar size distributions and saturation magnetization, but strikingly different magnetic anisotropies. From magnetic hyperthermia experiments we found that, while at low fields maghemite is the best nanomaterial for hyperthermia applications, above a critical field, close to the transition from the linear to the non-linear regime, cobalt ferrite becomes more efficient. The results were also analyzed with respect to the energy conversion efficiency and compared with dynamic hysteresis simulations. Additional analysis with nickel, zinc and copper-ferrite nanoparticles of similar sizes confirmed the importance of the magnetic anisotropy and the damping factor. Further, the analysis of the characterization parameters suggested core-shell nanostructures, probably due to a surface passivation process during the nanoparticle synthesis. Finally, we discussed the effect of particle-particle interactions and its consequences, in particular regarding discrepancies between estimated parameters and expected theoretical predictions. Copyright 2012 Author(s). This article is distributed under a Creative Commons Attribution 3.0 Unported License. [http://dx.doi. org/10.1063/1.4739533]