Gallium-doped zinc oxide (ZnO:Ga 1, 2 3, 4 and 5 at%) samples were prepared in powder form by modifying the Pechini method. The formation of zinc gallate (ZnGa2O4) With the spinel crystal structure was observed even in ZnO:Ga 1 at% by X-ray diffraction. The presence of ZnGa2O4 in ZnO:Ga samples was also evidenced by luminescence spectroscopy through its blue emission at 430 nm, assigned to charge transfer between Ga3+ at regular octahedral symmetry and its surrounding O2- ions. The amount of ZnGa2O4 increases as the dopant concentration increases, as observed by the quantitative phase analysis by the Rietveld method. (C) 2006 Elsevier B.V. All rights reserved.
Resumo:
Oxysulphide glasses have been prepared in the pseudo binary system GeS(2.6)-Ga(2)O(3). The effect of addition of gallium oxide has been evaluated in term of thermal and optical properties. Structural behavior has been studied using Raman spectroscopy. Samples have been exposed above band gap energy (3.52 eV) varying power density and exposure time. Giant photoexpansion and photorefraction is obtained for samples containing 20% of Ga(2)O(3). (C) 2009 Elsevier B.V. All rights reserved.
Resumo:
Far-infrared transitions in polar semiconductors are known to be affected by the presence of shallow donor impurities, external magnetic fields and the electron-LO-phonon interaction. We calculate the magnetodonor states in indium phosphide by a diagonalization procedure, and introduce the electron-phonon interaction by the Frohlich term. The main effects of this perturbation are calculated by a multi-level version of the Wigner-Brillouin theory. We determine the transition energies, from the ground state to excited states, and find good qualitative agreement with recently reported absorption-spectroscopy measurements in the 100-800 cm(-1) range, with applied magnetic fields up to 30 T. Our calculations suggest that experimental peak splittings in the 400-450 cm(-1) range are due to the electron-phonon interaction.
Resumo:
In this paper, we describe the preparation of glass ceramics in the Ga2S3 - GeS2 - CsCl system Visible and infrared transmitting glass ceramics were reproducibly obtained by appropriated heat treatment of the base glass Crystals with controllable size of about 40 nm were homogeneously generated in the glassy matrix X-ray diffraction characterizations have shown that gallium acts as nucleating agent in this material, giving rise to alpha-Ga2S3 crystals Improved thermo-mechanical properties such as dilatation coefficient and resistance to fracture propagation have been observed in the prepared glass ceramics
Resumo:
ZnO has received great attention in many applications due to its electronic and optical properties. We report on the preparation of ZnO and gallium-containing ZnO (ZnO:Ga) nanoparticles by the precipitation method. The nanoparticles have the wurtzite structure and a high crystallinity. Gallium ions are present as Ga(3+), as evidenced by the binding energies through XPS. Porosity and surface area of the powder increased under increasing gallium level, explained by the smaller particle size of ZnO:Ga samples compared with ZnO. The estimated optical band gap of ZnO was 3.2 eV, comparable to ZnO:Ga.
Resumo:
To study the influence of Ga addition on photoinduced effect, GaGeS glasses with constant atomic ratio S/Ge = 2.6 have been prepared. Using Raman spectroscopy, we have reported the effect of Ga on the structural behavior of these glasses. An increase of the glass transition temperature T(g), the linear refractive index and the density have been observed with increasing gallium content. The photoinduced phenomena have been examined through the influence of time exposure and power density, when exposed to above light bandgap (3.53 eV). The correlation between photoinduced phenomena and Ga content in such glasses are shown hereby. (C) 2009 Elsevier B.V. All rights reserved.
Resumo:
Bacterial cellulose (BC) membranes produced by gram-negative, acetic acid bacteria (Gluconacetobacter xylinus), were used as flexible substrates for the fabrication of Organic Light Emitting Diodes (OLED). In order to achieve the necessary conductive properties indium tin oxide (ITO) thin films were deposited onto the membrane at room temperature using radio frequency (r.f) magnetron sputtering with an r.f. power of 30 W, at pressure of 8 mPa in Ar atmosphere without any subsequent thermal treatment. Visible light transmittance of about 40% was observed. Resistivity, mobility and carrier concentration of deposited ITO films were 4.90 x 10(-4) Ohm cm, 8.08 cm(2)/V-s and -1.5 x 10(21) cm(-3), respectively, comparable with commercial ITO substrates. In order to demonstrate the feasibility of devices based on BC membranes three OLEDs with different substrates were produced: a reference one with commercial ITO on glass, a second one with a SiO(2) thin film interlayer between the BC membrane and the ITO layer and a third one just with ITO deposited directly on the BC membrane. The observed OLED luminance ratio was: 1; 0.5; 0.25 respectively, with 2400 cd/m(2) as the value for the reference OLED. These preliminary results show clearly that the functionalized biopolymer, biodegradable, biocompatible bacterial cellulose membranes can be successfully used as substrate in flexible organic optoelectronic devices. (C) 2008 Elsevier B.V. All rights reserved.
Resumo:
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
Resumo:
We report the observation of frequency upconversion in fluoroindate glasses with the following compositions: (mol%) (39 - x)InF3-20ZnF2-20SrF2-16BaF 2-2GdF3-2NaF-1GaF3-xNdF3 (x = 0.05, 0.1, 0.5, 1, 2, 3). The excitation source was a dye laser in resonance with the 4I9/2→(2G5/2, 2G7/2) transition of the Nd3+ ions. The upconverted fluorescence spectra show emissions from ∼ 350 to ∼ 450 nm, corresponding to transitions 4D3/2→4I9/2 ;4D3/2→4I11/2; 2P3/2→ 4I9/2; 4D3/2→4I13/2; 2P3/2→4I11/2; 4D3/2→4I15/2; and 2P3/2 → 4I13/2. The dependence of the fluorescence signals on the laser intensity indicates that two laser photons participate in the process. The temporal behavior of the signal indicates that energy transfer among the Nd3+ ions is the main mechanism which contributes to upconversion at 354 and 382 nm.
Resumo:
Glasses of composition 40InF3-20SrF2-16BaF2-20ZnF 2-2GdF3-2NaF (mol%) have been prepared under controlled atmosphere. The time response of the stresses under the application of a constant strain was determined by microellipsometer technique, performed in ambient atmosphere at T < Tg = 294°C. The glasses show a Newtonian behavior at small stress level. During the relaxation process, very small grooves perpendicular to the applied strain appeared on the glass surface and affected its behavior after a time. The formation of these grooves is associated with the ambient atmosphere. Measurements in dry atmosphere showed that humidity was an important parameter in the relaxation process.
Resumo:
This paper describes the stabilizing effect of MgF2 on the binary system InF3-BaF2. A complete investigation of the In-Ba-Mg system led to samples up to 5 mm in thickness. Further optimization of this system was achieved by incorporation of other fluorides, resulting in increased resistance to devitrification. Thermal and optical data are reported.
Resumo:
Glass formation in the pseudo ternary system ZnF2-GdF3-BaF2-InF3 and other complex systems stabilized by NaF, CaF2, AlF3 and YF3 have been investigated. Samples with greater stability have been prepared and their properties measured. Optical absorption and emission spectra of Gd3+ ions doped glasses with 2, 4, 10 and 20% concentrations have been measured. Using the Judd-Ofelt theory and the experimental oscillator strengths, the Judd-Ofelt parameters have been calculated. The emission of Gd3+ ions from 6I and 6P has been detected and the lifetime has been measured.
Resumo:
Results on thermal and optical characterization of new lanthanide containing fluoroindate glasses in the system InF3-BaF2-In(PO3)3 are presented. Good optical quality and very stable glasses presenting up to 5 mm in thickness could be prepared in this system. Thermal analysis, Raman scattering and Eu3+ luminescence were the techniques utilized. A novel method for In(PO3)3 synthesis is proposed and the dependence of physical properties and structural features on the polyphosphate content is stressed. © 1998 Elsevier Science S.A.
Resumo:
The viscosity of two fluoroindate glasses was measured as a function of temperature in the range of 310 °C - 362 °C. In such interval, the viscosity values were found to be similar to those reported for fluorozirconate glasses. The log η - 1/T plots had an unexpected behavior: two viscosity regions that seem to obey Arrhenius equation were identified and the activation energy for viscous flow (EA) for the region near Tg is smaller than the value found above the transition range. This behavior is probably due to structural changes occurred around Tg. The low values of the activation energy for viscous flow obtained for the indium fluoride-based glasses studied, suggest a good resistance against the devitrification process, what can make them suitable for fiber preparation.
Resumo:
Undoped and indium-doped Zinc oxide (ZnO) solid films were deposited by the pyrosol process at 450°C on glass substrates from solutions where In/Zn ratio was 2, 5, and 10 at.%. Electrical measurements performed at room temperature show that the addition of indium changes the resistance of the films. The resistivities of doped films are less than non-doped ZnO films by one to two orders of magnitude depending on the dopant concentration in the solution. Preferential orientation of the films with the c-axis perpendicular to the substrate was detected by X-ray diffraction and polarized extended X-ray absorption fine structures measurements at the Zn K edge. This orientation depends on the indium concentration in the starting solution. The most textured films were obtained for solutions where In/Zn ratio was 2 and 5 at.%. When In/Zn = 10 at.%, the films had a nearly random orientation of crystallites. Evidence of the incorporation of indium in the ZnO lattice was obtained from extended X-ray absorption fine structures at the In and Zn K edges. The structural analysis of the least resistive film (Zn/In = 5 at.%) shows that In substitutes Zn in the wurtzite structure. © 2000 Elsevier Science B.V. All rights reserved.