An approach to analyzing synthesis, structure and properties of bismuth titanate ceramics

The family of bismuth titanate, Bi(4)Ti(3)O(12) (BIT) layered-structured ferroelectrics materials is attractive from the viewpoint of such as their application as electronic materials dielectrics, piezoelectrics and pyroelectrics, because they are characterized by good stability of piezoelectric properties, a high Curie temperature and a good resistance vs temperature. Bismuth titanate (Bi(4)Ti(3)O(12)) powders can be prepared using different methods, depending if the creation will be film coating or ceramics. The structure and properties of bismuth titanate materials show a significance dependence on the applied synthesis method. In this review paper, we made an attempt to give an approach to analyszing the structure, synthesis methods and properties of bismuth titanate ferroelectrics materials.

Ferroelectric properties of mechanically synthesized nanosized barium titanate

Barium titanate ceramics were prepared through mechanochemical synthesis starting from fresh prepared barium oxide and titanium oxide in rutile form. Mixture of oxides was milled in zirconia oxide jar in the planetary ball-mill during 30, 60, 120 and 240 min. Extended time of milling directed to formation of higher amount of barium titanate perovskite phase. Barium titanate with good crystallinity was formed after 240 min. Sintering without pre-calcinations step was performed at 1330 degrees C for 2 hours with heating rate of 10 degrees C/min. The XRD, DSC, IR and TEM analyses were performed. Electric and ferroelectric properties were studied. Very well defined hysteresis loop was obtained.

Dielectric thermal analysis as a tool for quantitative-evaluation of the viscosity and the kinetics of epoxy resin cure

Dielectric thermal analysis has been proved as a valuable tool for monitoring the epoxy curing process and the related rheological properties in the fabrication of polymer-matrix composite materials. This technique also has the potential to be applied in the monitoring of magnet impregnation processes as well as in quality control. In this work we present the quantitative evaluation of the viscosity changing and the curing kinetics for a commercial Stycast epoxy resin system at different temperatures through the impedance analysis. The results showed correlation between the real component of the complex impedance and the isothermal reaction extent. Comparing the dielectric analysis result with the viscosity measured by rotational rheometer we observed a similar behavior reported for dynamic mechanic analysis. The results comparison have shown that the kinetics parameters obtained from DSC and DETA analysis showed different sensitivities related to the characteristics of curing stages. We concluded that the dielectric thermal analysis should be applied in quantitative evaluation of cure kinetics.

Influence of temperature on the microstructure and electrical properties of BBT thin films

The BBT films were prepared by a spin-coating process from the polymeric precursor method (Pechini process). In order to study the influence of the temperature on the BBT microstructure and electrical properties, the films were deposited on platinum coated silicon substrates and annealed from 700degreesC to 800degreesC for 2 hours in oxygen atmosphere. The crystallinity of the films was examined by X-ray diffraction while the surface morphology was analysed by atomic force microscope. The dielectric properties and dissipation factor of BaBi2Ta2O9 films at 1 MHz were observed. The polarization-electric field hysteresis loops revealed the ferroelectric characteristics of BaBi2Ta2O9 thin films.

Growth and characterization of BaBi2Nb2O9 thin films made by RF-magnetron sputtering

The RF-magnetron sputtering technique has been used to deposit polycrystalline thin films of layered-structured ferroelectric BaBi2Nb2O9 (BBN). The XRD patterns for the films annealed at 700degreesC for 1 hour show the presence of the BBN phase as well as the BaNb2O6 secondary phase. A better crystallization of the BBN phase and an inhibition of the secondary phase is obtained with the increase of temperature. The surface of the prepared films was rather dense and smooth with no cracks. The 300 nm thick BBN thin films exhibited a room-temperature dielectric constant of about 779 with a dissipation factor of 0.09 at a frequency of 100 kHz.

Electronic structure of Pb1-xLaxTiO3 ferroelectric materials from Ti 2p and O 1s soft x-ray absorption spectroscopy

The electronic structure of Pb1-xLaxTiO3 (PLT) compounds for x ranging from 0 to 30 at. % of La is investigated by means of soft x-ray absorption near edge structure (XANES) at the Ti L-3,L-2 and O K edges. The greatest modification in the structure of the Ti 2p XANES spectra of the PLT compounds is observed in the region of the high energy peak of the L-3 edge (e(g) states), which exhibits a splitting in the undoped sample. As the amount of lanthanum increases, this splitting becomes less pronounced. This modification is interpreted as a decrease in the degree of disorder of titanium atoms, which is correlated to the substitution of Pb by La atoms. The structural changes observed at the low energy peaks of the O K-edge XANES spectra of the PLT compounds may be interpreted in terms of hybridization between O 2p, Ti 3d, and Pb 6p orbitals. A decrease in the degree of hybridization observed as Pb atoms are replaced by La atoms may be related to the differences in the ferroelectric properties observed between x=0.0 and x=0.30 compounds. (c) 2006 American Institute of Physics.

Synthesis and electrical characterization of CaBi2Nb2O9 thin films deposited on Pt/Ti/SiO2/Si substrates by polymeric precursor method

We report the successful deposition of CaBi2Nb2O9 (CBN) thin films on platinum coated silicon substrates by polymeric precursor method. The CBN thin films exhibited good structural, dielectric and CBN/Pt interface characteristics. The leakage current of the capacitor structure was around 0.15 A cm(-2) at an applied electric field of 30 kV cm(-1). The capacitance-voltage measurements indicated good ferroelectric polarization switching characteristics. The typical measured small signal dielectric constant and the dissipation factor at a frequency of 100 kHz were 90 and 0.053, respectively. The remanent polarization and the drive voltage values were 4.2 C cm(-2) and 1.7 V at an applied voltage of 10 V. No significant fatigue was observed at least up to 10(8) switching cycles. (c) 2005 Elsevier B.V. All rights reserved.

Separation of dielectric and space charge polarizations in CaCu3Ti4O12/CaTiO3 composite polycrystalline systems

The complex analysis of dielectric/capacitance is a very useful approach to separate different polarization contributions existing in polycrystalline ceramics. In this letter, the authors use this type of spectroscopic analysis to separate the bulk's dielectric dipolar relaxation contributions from the polarization contribution due to space charge in the grain boundaries of a CaCu3Ti4O12/CaTiO3 polycrystalline composite system. The bulk dielectric dipolar relaxation was attributed to the self-intertwined domain structures from the CaCu3Ti4O12 phase coupled to the dipole relaxation from the CaTiO3 phase, while the space charge relaxation was attributed to the Schottky-type potential barrier responsible for the highly non-Ohmic properties observed in this composite polycrystalline system.

Very large dielectric constant of highly oriented Pb1-xBaxTiO3 thin films prepared by chemical deposition

Highly (100) oriented Pb0.8Ba0.2TiO3/LaNiO3 structures were grown on LaAlO3(100) substrates by using a wet, soft chemical method and crystallized by the microwave oven technique. The Au/PBT/LaNiO3/LaAlO3 capacitor shows a hysteresis loop with remnant polarization, P-r, of 15 muC/cm(2), and coercive field, E-c, of 47 kV/cm at an applied voltage of 3 V, along with a dielectric constant over 1800. Atomic force microscopy showed that Pb0.8Ba0.2TiO3 is composed of large grains about 300 nm. The experimental results demonstrated that the microwave preparation is rapid, clean, and energy efficient. Therefore, we demonstrated that the combination of the soft chemical method with the microwave process is a promising technique to grow highly oriented thin films with excellent dielectric and ferroelectric properties, which can be used in various integrated device applications. (C) 2004 American Institute of Physics.

Microstructure and electrical properties of perovskite (Pb, La)TiO3 thin film deposited at low temperature by the polymeric precursor method

High-quality (Pb, La)TiO3 ferroelectric thin films were successfully prepared on a Pt(111)/Ti/SiO2/Si(100) substrate for the first time by spin coating, using the polymeric precursor method. The X-ray diffraction patterns show that the films are polycrystalline in nature. This method allows for low temperature (500 degrees C) synthesis, a high quality microstructure and superior dielectric properties. The effects on the microstructure and electrical properties were studied by changing the La content. The films annealed at 500 degreesC have a single perovskite phase with only a tetragonal or pseudocubic structure. As the La content is increased, the dielectric constant of PLT thin films increases from 570 up to 1138 at room temperature. The C-V and P-E characteristics of perovskite thin films prepared at a low temperature show normal ferroelectric behavior, representing the ferroelectric switching property. The remanent polarization and coercive field of the films deposited decreased due to the transformation from the ferroelectric to the paraelectric phase with an increased La content. (C) 2001 Kluwer Academic Publishers.

The effect of Nb doping on ferroelectric properties of PZT thin films prepared from polymeric precursors

Pure and Nb doped PbZr0.4Ti0.603 thin films was prepared by the polymeric precursor method and deposited by spin coating on Pt/Ti/SiO2/Si (100) substrates and annealed at 700 degreesC. The films are oriented in (1 1 0) and (1 0 0) direction. The electric properties of PZT thin films show strong dependence of the crystallographic orientation. The P-E hysteresis loops for the thin film with composition PbZr0.39Ti0.6Nb0.103 showed good saturation, with values for coercive field (E-c) equal to 60 KV cm(-1) and for remanent polarization (P-r) equal to 20 muC cm(-2). The measured dielectric constant (epsilon) is 1084 for this film. These results show good potential for application in FERAM. (C) 2004 Elsevier B.V. All rights reserved.

Non-Linear Dielectric Properties of PLMN-PT Relaxor Ferroelectrics

Recent investigations on the non-linear (NL) dielectric properties of relaxor ferroelectrics systems, not only as ceramic bodies, but also, in thin films, have showed a significant technological and scientific interest. The most common practical applications of relaxors include multilayer capacitors and actuators. In this work, non-linear dielectric properties of hot-pressed (1-x)[Pb1 -(3/2) yLayMg1/3Nb2/3O3]-xPbTiO3 (PLMN-PT) ferroelectric ceramics were investigated. The NL properties were obtained by using the measurements of the dielectric permittivity of the material as a function of the AC electric field with variable amplitude in the frequency and temperature range of 100 Hz-1 MHz and 50-450 K, respectively. An anomalous behavior of the non-linear dielectric response was observed when submitted to high electric fields levels. The obtained results were analyzed concerning one of the models for the dielectric response of relaxors ferroelectrics materials currently discussed in the literature.

Influence of Ca concentration on the electric, morphological, and structural properties of (Pb,Ca)TiO3 thin films

Pb1-xCaxTiO3 (0.10less than or equal toxless than or equal to0.40) thin films on Pt/Ti/SiO2/Si(100) substrates were prepared by the soft solution process and their characteristics were investigated as a function of the calcium content (x). The structural modifications in the films were studied using x-ray diffraction and micro-Raman scattering techniques. Lattice parameters calculated from x-ray data indicate a decrease in lattice tetragonality with the increasing content of calcium in these films. Raman spectra exhibited characteristic features of pure PbTiO3 thin films. Variations in the phonon mode wave numbers, especially those of lower wave numbers, of Pb1-xCaxTiO3 thin films as a function of the composition corroborate the decrease in tetragonality caused by the calcium doping. As the Ca content (x) increases from 0.10 to 0.40, the dielectric constant at room temperature abnormally increased at 1 kHz from 148 to 430. Also calcium substitution decreased the remanent polarization and coercive field from 28.0 to 5.3 muC/cm(2) and 124 to 58 kV/cm, respectively. These properties can be explained in terms of variations of phase transition (ferroelectric-paraelectric), resulting from the substitution the lead site of PbTiO(3)for the nonvolatile calcium. (C) 2002 American Institute of Physics.

Structural and electrical properties of SrBi2(Ta0.5Nb0.5)(2)O-9 thin films

SrBi2(Ta0.5Nb0.5)(2)O-9 (SBTN) thin films were obtained by polymeric precursor method on Pt/Ti/SiO2/Si(1 0 0) substrates. The film is dense and crack-free after annealing at 700 degrees C for 2 h in static air. Crystallinity and morphological characteristic were examined by X-ray diffraction (XRD), field emission scanning electron microscopy (FEG-SEM) and atomic force microscopy (AFM). The films displayed rounded grains with a superficial roughness of 3.5 nm. The dielectric permittivity was 122 with loss tangent of 0.040. The remanent polarization (P-r) and coercive field (E-c) were 5.1 mu C/cm(2) and 96 kV/cm, respectively. (C) 2007 Published by Elsevier B.V.

Dielectric relaxation and dc conductivity on the PVOH-CF(3)COONH(4) polymer system

In the present paper, the ionic conductivity and the dielectric relaxation properties on the poly(vinyl alcohol)-CF(3)COONH(4) polymer system have been investigated by means of impedance spectroscopy measurements over wide ranges of frequencies and temperatures. The electrolyte samples were prepared by solution casting technique. The temperature dependence of the sample's conductivity was modeled by Arrhenius and Vogel-Tammann-Fulcher (VTF) equations. The highest conductivity of the electrolyte of 3.41x10 (-aEuro parts per thousand 3) (Omega cm) (-aEuro parts per thousand 1) was obtained at 423 K. For these polymer system two relaxation processes are revealed in the frequency range and temperature interval of the measurements. One is the glass transition relaxation (alpha-relaxation) of the amorphous region at about 353 K and the other is the relaxation associated with the crystalline region at about 423 K. Dielectric relaxation has been studied using the complex electric modulus formalism. It has been observed that the conductivity relaxation in this polymer system is highly non-exponential. From the electric modulus formalism, it is concluded that the electrical relaxation mechanism is independent of temperature for the two relaxation processes, but is dependent on composition.