The influence of high-temperature sintering on microstructure and mechanical properties of free-standing APS CeO-YO -ZrO coatings

In this study, ceria-yttria co-stabilized zirconia (CYSZ) free-standing coatings, deposited by air plasma spraying (APS), were isothermally annealed at 1315 °C in order to explore the effect of sintering on the microstructure and the mechanical properties (i.e., hardness and Young's modulus). To this aim, coating microstructure, before and after heat treatment, was analyzed using scanning electron microscopy, and image analysis was carried out in order to estimate porosity fraction. Moreover, Vickers microindentation and depth-sensing nanoindentation tests were performed in order to study the evolution of hardness and Young's modulus as a function of annealing time. The results showed that thermal aging of CYSZ coatings leads to noticeable microstructural modifications. Indeed, the healing of finer pores, interlamellar, and intralamellar microcracks was observed. In particular, the porosity fraction decreased from ~10 to ~5% after 50 h at 1315 °C. However, the X-ray diffraction analyses revealed that high phase stability was achieved, as no phase decomposition occurred after thermal aging. In turn, both the hardness and Young's modulus increased, in particular, the increase in stiffness (with respect to "as produced" samples) was equal to ~25%, whereas the hardness increased to up to ~60%. © 2010 Springer Science+Business Media, LLC.

High temperature thermal stability studies of ultrathin Al2O3 layers deposited on native oxide and sulphur passivated InGaAs surfaces

High resolution synchrotron radiation core level photoemission measurements have been used to undertake a comparative study of the high temperature stability of ultrathin Al2O3 layers deposited by atomic layer deposition (ALD) on both sulphur passivated and native oxide covered InGaAs. The residual interfacial oxides between sulphur passivated InGaAs and the ultrathin Al2O3 layer can be substantially removed at high temperature (up to 700 °C) without impacting on the InGaAs stoichiometry while significant loss of indium was recorded at this temperature on the native oxide InGaAs surface.

Electrochemical promotion of a platinum catalyst supported on the high-temperature proton conductor La0.99Sr0.01NbO4-δ

The recently discovered, high-temperature proton conductor, La_0.99Sr_0.01NbO_4-δ, was used as a support for the electrochemical promotion of a platinum catalyst. Ethylene oxidation was used as a probe reaction in the temperature range 350-450 °C. Moderate non-Faradaic rate modification, attributable to a protonic promoting species, occurred under negative polarisation; some permanent promotion was also observed. In oxidative atmospheres, both the p_O2 of the reaction mixture and the temperature influenced the type and magnitude of the observed rate modification. Rate-enhancement values of up to ρ = 1.4 and Faradaic-efficiency values approaching Λ = -100 were obtained. Promotion was observed under positive polarisation and relatively dry, oxygen-rich atmospheres suggesting that some oxygen ion conductivity may occur under these conditions. Impedance spectroscopy performed in atmospheres of 4 kPa O₂/N₂ and of 5 kPa H₂/N₂ under dry and slightly humidified (0.3 kPa H₂O) conditions indicated that the electrical resistivity is heavily dominated by the grain-boundary response in the temperature range of the EPOC studies; much lower grain-boundary impedances in the wetter conditions are likely to be attributable to proton transport. © 2009 Elsevier B.V. All rights reserved.

Effect of high temperature, biaxial stretching on the thermal and mechanical properties of HDPE/MWCNT sheet

High density polyethylene (HDPE)/multi-walled carbon nanotube (MWCNT) composites containing 4 wt% MWCNTs were prepared by melt mixing followed by compression moulding into sheet. Compression moulded sheets were heated to just below the melting temperature and biaxially stretched at ratios (SRs) of 2, 2.5 and 3.0. The effect of stretching on the thermal and mechanical properties of the sheet was studied by differential scanning calorimetry (DSC) and tensile testing. DSC results show that the crystallinity of all the stretched samples increases by approximately 13% due to strain induced crystallization. The melting temperature of the biaxially stretched samples increases only slightly while crystallization temperature is not affected. Tensile test results indicate that at a SR of 2.5 the elastic modulus of the stretched composites increases by 17.6% relative to the virgin HDPE, but the breaking strength decreases by 33%. While the elastic modulus and breaking strength of the HDPE/MWCNT samples continue to increase as SR increases they drop off after a SR of 2.5 for the virgin HDPE. This is probably due to the constraining influence of the nanotubes preventing the relaxation of polymer chains caused by adiabatic heating at high SRs. The addition of MWCNTs results in significant strain hardening during deformation. While this will lead to increased energy requirement in forming it will also result in a more stable process and the ability to produce deep draw containers with more uniform wall thickness

High temperature thermal stability investigations of ammonium sulphide passivated InGaAs and interface formation with Al2O3 studied by synchrotron radiation based photoemission

High resolution synchrotron radiation core level photoemission measurements have been used to undertake a comparative study ofthe high temperature thermal stability ofthe ammonium sulphide passivated InGaAs surface and the same surface following the atomic layer deposition (ALD) of an ultrathin (∼1 nm) Al2O3 layer. The solution based ex situ sulphur passivation was found to be effective at removing a significant amount of the native oxides and protecting the surface against re-oxidation upon air exposure. The residual interfacial oxides which form between sulphur passivated InGaAs and the ultrathin Al2O3 layer can be substantially removed at high temperature (up to 700 ◦C) without impacting on the InGaAs stoichiometry while significant loss of indium was recorded at this temperature on the uncovered sulphur passivated InGaAs surface.

High temperature thermal stability of the HfO2/Ge (100) interface as a function of surface preparation studied by synchrotron radiation core level photo emission

High resolution soft x-ray photoemission spectroscopy (SXPS) have been used to study the high temperature thermal stability of ultra-thin atomic layer deposited (ALD) HfO2 layers (∼1 nm) on sulphur passivated and hydrofluoric acid (HF) treated germanium surfaces. The interfacial oxides which are detected for both surface preparations following HfO2 deposition can be effectively removed by annealing upto 700 °C without any evidence of chemical interaction at the HfO2/Ge interface. The estimated valence and conduction band offsets for the HfO2/Ge abrupt interface indicated that effective barriers exist to inhibit carrier injection.

High-temperature stability study of 1 nm Al2O3 deposited on InAs surfaces investigated by synchrotron radiation based photoemission spectroscopy

High-resolution soft x-ray photoemission spectroscopy (SXPS) has been used to study the high-temperature thermal stability of ultra-thin atomic layer deposited (ALD) Al2O3 layers (~1 nm) on sulfur passivated and native oxide covered InAs surfaces. While the arsenic oxides were removed from both interfaces following a 600 °C anneal, a residual indium oxide signal remained. No significant differences were observed between the sulfur passivated and native oxide surfaces other than the thickness of the interfacial oxide layer while the Al2O3 stoichiometry remained unaffected by the anneals. The energy band offsets were determined for the Al2O3 on the sulfur passivated InAs surface using both valence band edge and shallow core-level photoemission measurements.

Collisional-radiative calculations of He line emission in low-temperature plasmas

We present spectral modeling results for neutral helium. Our underlying atomic data contains radiative transition rates that are generated from atomic structure calculations and electron-impact excitation rates, that are determined from both the standard R-matrix method and the R-matrix with pseudostates RMPS method. In this paper, we focus on transitions of particular importance to diagnostic line ratios. For example, our calculated rate coefficient for the electron-impact transition 1s3s 1S→1s3p 1P, which has a pronounced effect on the 728.1 nm diagnostic spectral line, is found to be in good agreement with previous experimental mea- surements. We also consider transitions from the 1s2 1S ground and 1s2s 3S terms to terms of the n=4 shell. They are found to be affected significantly by coupling of the bound states to the target continuum continuum coupling, which is included in our RMPS calculation, but not in our standard R-matrix calculation. We perform collisional-radiative calculations to determine spectral line intensity ratios for three ratios of particular interest, namely the 504.8 nm/471.3 nm, 492.2 nm/471.3 nm, and 492.2 nm/504.8 nm line ratios. Comparing our results determined from the RMPS excitation rates with those from the standard R-matrix excitation rates, we find that continuum coupling affects the rate coefficients significantly, leading to different values for all three line ratios. We also compare our modeling results with spectral measurements taken recently on the Auburn Helicon plasma device, finding that the ground and metastable populations are not in equilibrium, and that the experimental measurements are more consistent with the 1s2s 3S metastable term populations being short lived in the plasma.

High temperature vapour-liquid equilibria of water-polyalcohol mixtures

Tese de doutoramento, Química (Química Tecnológica), Universidade de Lisboa, Faculdade de Ciências, 2014