Loop bifurcation and magnetization rotation in exchange-biased Ni/FeF2

Exchange-biased Ni/FeF2 films have been investigated using vector coil vibrating-sample magnetometry as a function of the cooling field strength HFC . In films with epitaxial FeF2 , a loop bifurcation develops with increasing HFC as it divides into two sub-loops shifted oppositely from zero field by the same amount. The positively biased sub-loop grows in size with HFC until only a single positively shifted loop is found. Throughout this process, the negative and positive (sub)loop shifts maintain the same discrete value. This is in sharp contrast to films with twinned FeF2 where the exchange field gradually changes with increasing HFC . The transverse magnetization shows clear correlations with the longitudinal subloops. Interestingly, over 85% of the Ni reverses its magnetization by rotation, either in one step or through two successive rotations. These results are due to the single-crystal nature of the antiferromagnetic FeF2 , which breaks down into two opposite regions of large domains.

Ni-Mn-Ga thin films produced by pulsed laser deposition

Polycrystalline Ni-Mn-Ga thin films have been deposited by the pulsed laser deposition (PLD) technique, using slices of a Ni-Mn-Ga single crystal as targets and onto Si (100) substrates at temperatures ranging from 673 K up to 973 K. Off-stoichiometry thin films were deposited at a base pressure of 1×10-6-Torr or in a 5 mTorr Ar atmosphere. Samples deposited in vacuum and temperatures above 823 K are magnetic at room temperature and show the austenitic {220} reflection in their x-ray diffraction patterns. The temperature dependences of both electrical resistance and magnetic susceptibility suggest that these samples exhibit a structural martensitic transition at around 260 K. The magnetoresistance ratio at low temperature can be as high as 1.3%, suggesting the existence of a granular structure in the films

Epäpuhtauksien vaikutus monokaliumfosfaattikiteen kasvuun

Työssä on tutkittu epäpuhtauksien vaikutusta kastelulannoitesuolojen monokaliumfosfaatin, kaliumnitraatin ja ureafosfaatin kiteytyksessä. Kirjallisuusosassa on käsitelty kastelulannoiteprosessit ja epäpuhtauksien vaikutus kastelulannoitteiden valmistuksessa. Kiteytys ja kiteenkasvu on esitetty perusyhtälöin, joissa on otettu epäpuhtauksien vaikutus huomioon. Tarkemmin on perehdytty monokaliumfosfaatin kiteytykseen ja kolmenarvoisten kationeiden, Al3+, Fe3+ ja Cr3+, vaikutukseen kiteiden kasvuun. Kolmenarvoiset metalli-ionit adsorboituvat kiteen pintaan haitaten kiteenkasvua, mikä vaikuttaa erityisesti kiteen prismapinnan kasvuun. Lisäksi on esitelty muita kiteenkasvuun vaikuttavia olosuhteita. Lopuksi on käsitelty kompleksinmuodostajia metalli-ionien haitallisten vaikutusten ehkäisijöinä. Kokeellisessa osassa suoritettiin liukoisuuskokeita monokaliumfosfaatin liukoisuuden selvittämiseksi eri pH-olosuhteissa. Suoritetuissa yksikidekokeissa tutkittiin pH:n ja kolmenarvoisten kationeiden; Al3+, Fe3+ ja Cr3+, vaikutus monokaliumfosfaattikiteen pituus- ja leveyskasvuun ja kidemuotoon eri ylikylläisyyksillä. Lisäksi tutkittiin voidaanko lämpötilaa ja pH muuttamalla tai pyrofosfaattia lisäämällä poistaa raudan kasvua inhiboima vaikutus. Kiteytyslämpötilaa nostamalla voidaan poistaa raudan haitallinen vaikutus kiteen kasvuun.

Large Magnetoresistance in Fe/MgO/FeCo(001) Epitaxial Tunnel-Junctions on GaAs(001).

We present tunneling experiments on Fe~001!/MgO~20 Å!/FeCo~001! single-crystal epitaxial junctions of high quality grown by sputtering and laser ablation. Tunnel magnetoresistance measurements give 60% at 30 K, to be compared with 13% obtained recently on ~001!-oriented Fe/amorphous-Al2O3 /FeCo tunnel junctions. This difference demonstrates that the spin polarization of tunneling electrons is not directly related to the density of states of the free metal surface Fe~001! in this case but depends on the actual electronic structure of the entire electrode/barrier system.

Desenvolvimento de um dispositivo para obtenção de monocristais de ligas à base de cobre

This paper describes the drawing, construction and optimization of a device, which can be used to obtain single crystals of different metallic materials with melting point from 550 to 1050 ºC. Components of ease obtaining and of low cost were used. The device was based on the modified Bridgman technique and it was used to obtain single crystals of copper-based alloys. The temperature axial profiles and a difference less then 1% in the temperature between the wall and the center of the ceramic tube in the critical region for obtaining single crystals of good quality indicated that the oven presents a good thermal stability. Single crystals of CuZnAl and CuAlAg alloys of good quality were growth and characterized using optical microscopy and Laüe X-ray back reflection.

NMR in Crystals and Powders of Topazes with Different Colours

The present work is a part of the large project with purpose to investigate microstructure and electronic structure of natural topazes using NMR method. To reach this task we determined the relative contents of fluorine and hydrogen in crystals blue, colorless, wine and wine irradiated topazes. Then we determined the electric field gradients in site of aluminium atoms by NMR method, calculated EFG using ab initio method, and measured relaxation time dependence on heating temperature for blue, colorless, Swiss blue and sky blue topazes. Nuclear magnetic resonance (NMR) is an effective method to investigate the local structure in the crystal. The NMR study of the single crystal gives detailed information especially about the local crystal structure. As a result of this work we have received practical data, which is possible to use in future for making personal dosimetry and for preparation of mullite, which is widely used in traditional and advanced ceramic materials.

Quantum magnetic deflagration in Mn12 acetate

We report controlled ignition of magnetization reversal avalanches by surface acoustic waves in a single crystal of Mn12 acetate. Our data show that the speed of the avalanche exhibits maxima on the magnetic field at the tunneling resonances of Mn12. Combined with the evidence of magnetic deflagration in Mn12 acetate [Y. Suzuki et al., Phys. Rev. Lett. 95, 147201 (2005)], this suggests a novel physical phenomenon: deflagration assisted by quantum tunneling.

Síntese e caracterização estrutural do ligante isatina-3-(N4-benziltiossemicarbazona) e do seu complexo de mercúrio(II)

The reaction of 4-(phenyl)thiosemicarbazide with isatin yielded a new ligand, isatin-3-(N4-benzylthiosemicarbazone). Isatin-3-(N4-benzylthiosemicarbazone) deprotonated in ethanol/KOH reacts with an ethanolic solution of Hg(NO3)2 to give a mercury complex. The compounds were characterized by IR and X-ray single crystal structure determination. The X-ray studies revealed that the complex possesses a tetrahedral geometry with two deprotonated thiosemicarbazone ligands coordenated. The ligand and its mercury complex crystallize in the monoclinic (P2(1)/c) and triclinic (P-1) crystal system, respectively.

Combined experimental powder X-ray diffraction and DFT data to obtain the lowest energy molecular conformation of friedelin

Friedelin molecular conformers were obtained by Density Functional Theory (DFT) and by ab initio structure determination from powder X-ray diffraction. Their conformers with the five rings in chair-chair-chair-boat-boat, and with all rings in chair, are energy degenerated in gas-phase according to DFT results. The powder diffraction data reveals that rings A, B and C of friedelin are in chair, and rings D and E in boat-boat, conformation. The high correlation values among powder diffraction data, DFT and reported single-crystal data indicate that the use of conventional X-ray diffractometer can be applied in routine laboratory analysis in the absence of a single-crystal diffractometer.

Acoplamento de cloreto de 4-nitrofenildiazônio com nucleófilos alifáticos: experimento integrado de síntese orgânica e cristalografia de raios X

This article describes an undergraduate experiment for the synthesis of p-nitrophenyldiazonium chloride and its coupling with acetylacetone and two enaminones, 4-phenylamino-pent-3-en-2-one and 4-amino-pent-3-en-2-one, in an adaptation of a previously reported synthetic protocol. The azo dyes 4-(E)-phenylamino-3-[(E)-2-(4-nitrophenylazo)]-3-penten-2-one and 4-(E)-amino-3-[(E)-2-(4-nitrophenylazo)]-3-penten-2-one were obtained, and the solid state structure of this latter azo compound was characterized by single crystal X-ray diffraction studies. This two-week integrated laboratory approach involves simple synthetic experiments and microwave chemistry in the organic laboratory plus crystallography analysis, suitable for novice students on undergraduate experimental chemistry courses.

Galvanomagnetic properties of CdSb

Main aim of this work was preparation of a computer program for investigation of galvanomagnetic effects in solid state materials. These effects were investigated in magnetic field up to 6 T at temperatures 4.6 and 80.5 K. Two CdSb samples with Ni shallow impurities (concentration of impurity was 5% by mass) and one undoped CdSb single crystal were studied. Obtained results were compared with previous experimental results for these samples, and showed their identity.

Self-assembly of supermolecular species directed by hydrogen bonding and aromatic π-π stacking interactions

A new Cu(II) trimers, [Cu3(dcp)2(H2O)8]. 4DMF, with the ligand 3,5-pyrazoledicarboxylic acid monohydrate (H3dcp) has been prepared by solvent method. Its solid-state structure has been characterized by elemental analysis, thermal analysis (TGA and DSC), and single crystal X-ray diffraction. X-ray crystallographic studies reveal that this complex has extended 1-D,2-D and 3-D supramolecular architectures directed by weak interactions (hydrogen bond and aromatic π-π stacking interaction) leading to a sandwich solid-state structure.

Morfologian hallinta nikkelin sulfidisaostuksessa

Diplomityön tarkoituksena oli tutkia nikkelin sulfidisaostuksessa syntyvien kiteiden morfologiaa ja siihen vaikuttavia parametreja. Syntyvien kiteiden kasvua ja morfologiaa tutkittiin kiteen muodostumisen ja kasvun teorioiden avulla. Saostuksen olosuhteet, kuten lämpötila, paine ja pH vaikuttavat muodostuvien kiteiden morfologiaan. Muilla parametreilla, kuten liuoksen ylikylläisyydellä, epäpuhtauksilla, lisäaineilla, sekoituksella ja reaktioajalla on myös suuri merkitys. Kokeiden avulla haluttiin liuoskoostumuksen, saostusolosuhteiden ja muiden komponenttien vaikutusta nikkelisulfidikiteiden morfologiaan. Kokeissa käytettiin kahta eri sulfidilähdettä: natriumvetysulfidia ja rikkivetyä. Puolipanoskokeissa nikkelipitoisuus oli 1,5 g/l, paine 101,3 kPa ja sekoitusnopeus 650 rpm. Saostuskokeet tehtiin natriumsulfaatti- 5 g/l ja ammoniumsulfaattiliuoksissa 300 g/l. Saostuskokeissa muuttujia olivat saostimen konsentraatio ja määrä, rauta- ja magne-siumepäpuhtaudet, lämpötila ja lisäaineet. Diplomityön kokeellisessa osassa morfologiaa tutkittiin suoraan valomikroskoopin ja pyyhkäisyelektronimikroskoopin (SEM) avulla. Morfologiaa tutkittiin myös epäsuorasti laskeutumisnopeuden, keskimääräisen partikkelikoon, ja ominaispinta-alamittausten avulla. Saostimen pitoisuuden vaikutukset partikkelimuotoon olivat pieniä, mutta vaikutukset ominaispinta-alaan ja partikkelikokoon olivat suuria. Natriumlauryylisul-faatti ja EDTA ohjasivat partikkelien rakennetta levymäisemmäksi, joka johti hitaaseen laskeutumisnopeuteen. Polyakryylihappo lisäaineena muuttaa partikkelien morfologiaa kuutiomaisemmaksi. Flokkulanttien ja raudan morfologiset vaikutukset olivat pieniä. Partikkelikoko ja omaispinta-ala pienenivät selvästi magnesiumpitoisuuden kasvaessa. Lämpötilan kasvattaminen lisäsi epäsäännöllisten kiteiden määrää ja muodostuneet kiteet olivat enemmän neulamaisia.

Microcracks and Vortices in Superconducting Thin Films

In this work, superconducting YBa₂ Cu₃O_6+x (YBCO) thin films have been studied with the experimental focus on the anisotropy of BaZrO₃ (BZO) doped YBCOthin films and the theoretical focus on modelling flux pinning by numerically solving Ginzburg- Landau equations. Also, the structural properties of undoped YBCO thin films grown on NdGaO₃ (NGO) and MgO substrates were investigated. The thin film samples were made by pulsed laser ablation on single crystal substrates. The structural properties of the thin films were characterized by X-ray diffraction and atomic force microscope measurements. The superconducting properties were investigated with a magnetometer and also with transport measurements in pulsed magnetic field up to 30 T. Flux pinning was modelled by restricting the value of the order parameter inside the columnar pinning sites and then solving the Ginzburg-Landau equations numerically with the restrictions in place. The computations were done with a parallel code on a supercomputer. The YBCO thin films were seen to develop microcracks when grown on NGO or MgO substrates. The microcrack formation was connected to the structure of the YBCO thin films in both cases. Additionally, the microcracks can be avoided by careful optimization of the deposition parameters and the film thickness. The BZO doping of the YBCO thin films was seen to decrease the effective electron mass anisotropy, which was seen by fitting the Blatter scaling to the angle dependence of the upper critical field. The Ginzburg-Landau simulations were able to reproduce the measured magnetic field dependence of the critical current density for BZO doped and undoped YBCO. The simulations showed that in addition to the large density also the large size of the BZO nanorods is a key factor behind the change in the power law behaviour between BZO doped and undoped YBCO. Additionally, the Ginzburg-Landau equations were solved for type I thin films where giant vortices were seen to appear depending on the film thickness. The simulations predicted that singly quantized vortices are stable in type I films up to quite large thicknesses and that the size of the vortices increases with decreasing film thickness, in a way that is similar to the behaviour of the interaction length of Pearl vortices.

The Role of Structural Imperfections in Sr2FeMoO6 Thin Films

In this work, Sr2FeMoO6 (SFMO) thin films were studied with the main focus on their magnetic and magneto-transport properties. The fabrication process of pulsed laser deposited SFMO films was first optimized. Then the effects of strain, film thickness and substrate were thoroughly investigated. In addition to these external factors, the effect of intrinsic defects on the magnetic properties of SFMO were also clarified. Secondly, the magnetoresistivity mechanims of SFMO films were studied and a semiempirical model of the temperature dependence of resistivity was introduced. The films were grown on single crystal substrates using a ceramic target made with sol-gel method. The structural characterization of the films were carried out with X-ray diffraction, atomic force microscopy, transmission electron microscopy and high kinetic energy photoelectron spectroscopy. The magnetic properties were measured with SQUID magnetometer and the magneto-transport properties by magnetometer with a resistivity option. SFMO films with the best combination of structural and magnetic properties were grown in Ar atmosphere at 1050 °C . Their magnetic properties could not be improved by the ex situ post-annealing treatments aside from the treatments in ultra-high vacuum conditions. The optimal film thickness was found to be around 150 nm and only small improvement in the magnetic properties with decreasing strain was observed. Instead, the magnetic properties were observed to be highly dependent on the choice of the substrate due to the lattice mismatch induced defects, which are best avoided by using the SrTiO3 substrate. The large difference in the Curie temperature and the saturation magnetization between the SFMO thin film and polycrystalline bulk samples was connected to the antisite disorder and oxygen vacancies. Thus, the Curie temperature of SFMO thin films could be improved by increasing the amount of oxygen vacancies for example with ultra-high vacuum treatments or improving the B-site ordering by further optimization of the deposition parameters. The magneto-transport properties of SFMO thin films do not follow any conventional models, but the temperature dependence of resistivity was succesfully described with a model of two spin channel system. Also, evidences that the resistivity-temperature behaviour of SFMO thin films is dominated by the structural defects, which reduce the band gap in the majority spin band were found. Moreover, the magnetic field response of the resistivity in SFMO thin films were found to be superposition of different mechanisms that seems to be related to the structural changes in the film.