Reabilitação estética do sorriso por meio do sistema cerâmico dissilicato de lítio: relato de caso

The reestablishment of a harmonious smile through dental ceramics, when properly conducted and with specific indications, can achieve extremely predictable results. For aesthetic and functional rehabilitation, many ceramic materials can be used such as zirconia, leucite, alumina, feldspar, and lithium disilicate. Among these materials the lithium disilicate stands out due to the following characteristics: its resistance to wear, to chemical attack, high temperatures and oxidation; low electrical conductivity; near zero thermal expansion; good optical properties and biocompatibility with periodontal; excellent esthetics; color stability and reinforcement of tooth structure. The indications for the use of lithium disilicate are not limited to multiple facets of teeth in cases where there was no favorable response to tooth whitening, and also comprehend teeth with multiple restorations, diastema closure, shape alteration, and dental contouring, replacement of missing or fractured teeth, among others. The versatility of lithium disilicate ceramics allows its utilization in several clinical situations. The concomitant use of lithium disilicate for veneers and over metal has satisfactory aesthetic results, as reported in the present studying cases that require both aesthetics and resistance.

The importance of the lifelike esthetic appearance of all-ceramic restorations on anterior teeth

The success of rehabilitation will not depend on just clinical procedures. A proper dental technique (ceramist) is required as well as the respect for some biomimetic principles to obtain the desired final result. This study has the purpose of describing a prosthetic rehabilitation with laminate veneers and all-ceramic crowns of a patient unsatisfied with a previous esthetic treatment because of the negligence of some biomimetic principles. A 45-year-old female patient was admitted to the dental clinic complaining about the lifelike appearance of her all-ceramic restorations. Before the fabrication of new restorations, a mock-up was conducted to verify the patient's satisfaction. A ceramist conducted all the fabrication process so that surface characterizations could be visually verified and the lifelike appearance of natural tooth could be reproduced. After the cementation procedure, the patient reported being satisfied with the lifelike appearance of the new restorations. Based on the clinical findings of the present case report, it can be concluded that the reproduction of the lifelike esthetic appearance of natural teeth and the visualization of the final results before definitive procedures are essential to obtain the clinical success.

Reabilitação estética com enfoque nas diferentes cores de substratos e na escolha da cor do cimento adesivo

The evolution of techniques and materials applied to adhesive ceramic restorations resulted in the intensification of its use, proving to be an excellent method of aesthetic restoration. Some important features of this technique are its conservative preparation, which avoids an excessive loss of tooth structure and its high aesthetic value provided by the ceramic even when utilized under different color of dental substrates. The aim of this paper was to report a clinical case with full crowns, porcelain veneers and non-prep veneers, enhancing peculiarities related to the material used, tooth preparation techniques, cementing, indications and contraindications.

Zirconia in dentistry

The above factors emphasize the scope of this thesis for further investigations on zirconia, the improvement of all-ceramic zirconia restorations, and especially the interaction of zirconia and veneering and its influence on the performance of the whole restoration. The introduction, chapter 1, gave a literature overview on zirconia ceramics. In chapter 2, the objective of the study was to evaluate the effect of abrading before and after sintering using alumina-based abrasives on the surface of yttria-tetragonal zirconia polycrystals. Particular attention was paid to the amount of surface stress–assisted phase transformation (tetragonal→monoclinic) and the presence of microcracks. Chapter 3 is based on the idea that the conventional sintering techniques for zirconia based materials, which are commonly used in dental reconstruction, may not provide a uniform heating, with consequent generation of microstructural flaws in the final component. As a consequence of the sintering system, using microwave heating, may represent a viable alternative. The purpose of the study was to compare the dimensional variations and physical and microstructural characteristics of commercial zirconia (Y-TZP), used as a dental restoration material, sintered in conventional and microwave furnaces. Chapter 4 described the effect of sandblasting before and after sintering on the surface roughness of zirconia and the microtensile bond strength of a pressable veneering ceramic to zirconia.

Accuracy of computer-aided design/computer-assisted manufacture (CAD/CAM) fabricated dental restorations: a comparative study

Introduction: Computer-Aided-Design (CAD) and Computer-Aided-Manufacture (CAM) has been developed to fabricate fixed dental restorations accurately, faster and improve cost effectiveness of manufacture when compared to the conventional method. Two main methods exist in dental CAD/CAM technology: the subtractive and additive methods. While fitting accuracy of both methods has been explored, no study yet has compared the fabricated restoration (CAM output) to its CAD in terms of accuracy. The aim of this present study was to compare the output of various dental CAM routes to a sole initial CAD and establish the accuracy of fabrication. The internal fit of the various CAM routes were also investigated. The null hypotheses tested were: 1) no significant differences observed between the CAM output to the CAD and 2) no significant differences observed between the various CAM routes. Methods: An aluminium master model of a standard premolar preparation was scanned with a contact dental scanner (Incise, Renishaw, UK). A single CAD was created on the scanned master model (InciseCAD software, V2.5.0.140, UK). Twenty copings were then fabricated by sending the single CAD to a multitude of CAM routes. The copings were grouped (n=5) as: Laser sintered CoCrMo (LS), 5-axis milled CoCrMo (MCoCrMo), 3-axis milled zirconia (ZAx3) and 4-axis milled zirconia (ZAx4). All copings were micro-CT scanned (Phoenix X-Ray, Nanotom-S, Germany, power: 155kV, current: 60µA, 3600 projections) to produce 3-Dimensional (3D) models. A novel methodology was created to superimpose the micro-CT scans with the CAD (GOM Inspect software, V7.5SR2, Germany) to indicate inaccuracies in manufacturing. The accuracy in terms of coping volume was explored. The distances from the surfaces of the micro-CT 3D models to the surfaces of the CAD model (CAD Deviation) were investigated after creating surface colour deviation maps. Localised digital sections of the deviations (Occlusal, Axial and Cervical) and selected focussed areas were then quantitatively measured using software (GOM Inspect software, Germany). A novel methodology was also explored to digitally align (Rhino software, V5, USA) the micro-CT scans with the master model to investigate internal fit. Fifty digital cross sections of the aligned scans were created. Point-to-point distances were measured at 5 levels at each cross section. The five levels were: Vertical Marginal Fit (VF), Absolute Marginal Fit (AM), Axio-margin Fit (AMF), Axial Fit (AF) and Occlusal Fit (OF). Results: The results of the volume measurement were summarised as: VM-CoCrMo (62.8mm3 ) > VZax3 (59.4mm3 ) > VCAD (57mm3 ) > VZax4 (56.1mm3 ) > VLS (52.5mm3 ) and were all significantly different (p presented as areas with different colour. No significant differences were observed at the internal aspect of the cervical aspect between all groups of copings. Significant differences (p< M-CoCrMo Internal Occlusal, Internal Axial and External Axial 2 ZAx3 > ZAx4 External Occlusal, External Cervical 3 ZAx3 < ZAx4 Internal Occlusal 4 M-CoCrMo > ZAx4 Internal Occlusal and Internal Axial The mean values of AMF and AF were significantly (p M-CoCrMo and CAD > ZAx4. Only VF of M-CoCrMo was comparable with the CAD Internal Fit. All VF and AM values were within the clinically acceptable fit (120µm). Conclusion: The investigated CAM methods reproduced the CAD accurately at the internal cervical aspect of the copings. However, localised deviations at axial and occlusal aspects of the copings may suggest the need for modifications in these areas prior to fitting and veneering with porcelain. The CAM groups evaluated also showed different levels of Internal Fit thus rejecting the null hypotheses. The novel non-destructive methodologies for CAD/CAM accuracy and internal fit testing presented in this thesis may be a useful evaluation tool for similar applications.

Comparação de materiais usados na confeção de facetas dentárias

A demanda na procura da reabilitação estética é um dos focos da história da humanidade ao longo das eras, mas que teve a sua acentuação nestes últimos dois séculos. Sendo a face um dos pontos que nos permite avaliar esteticamente uma pessoa, cabe ao médico dentista, como um dos profissionais que trabalha nessa zona do corpo humano, avaliar e procurar satisfazer as necessidades estéticas da população. Assim, por parte dos profissionais de Medicina Dentária, tem de haver uma procura constante para a satisfação das exigências estéticas, não só no conhecimento como no aprimoramento da técnica. Nos últimos tempos, com a necessidade de desenvolvimento de materiais para colmatar a cada vez maior busca para a perfeição estética, as facetas surgiram como tratamento de excelência. O presente trabalho teve como objectivo a comparação entre resina composta e cerâmica, na elaboração de restaurações estéticas. Para os dois tipos de materiais foram avaliados a estética e o comportamento biomecânico. Foram comparados benefícios e desvantagens, contra-indicações, indicações, plano de tratamento, diagnóstico e procedimentos clínicos dos dois materiais, utilizados na confecção das facetas cerâmicas e de resina composta. Foram utilizados os seguintes parâmetros de comparação: biocompatibilidade, adaptação marginal, preparação, resistência, cor, acabamento, potencial de reparação, custo e estética. A utilização de facetas cerâmicas tem sido um dos principais focos de desenvolvimento da Medicina Dentária no âmbito científico. A sua utilização permite uma maior predictibilidade e uma maior longevidade clínica. A sua qualidade estética, resistência à fractura, biodisponibilidade e estabilidade de cor, são as suas maiores vantagens na utilização clínica. Em sentido inverso, as facetas de resina composta apresentam menor custo, maior resistência à abrasão, possibilidade de reparação fácil e menor desgaste de estrutura dentária durante a sua preparação. Contudo apresentam menor estabilidade de cor. Portanto, torna-se esclarecedor que a escolha do material a utilizar na confecção de facetas, deve ser adaptada às especificidades de cada caso.

Rotary veneering of plantation-grown spotted gum (Corymbia citriodora subsp. variegata) and Dunn's white gum (Eucalyptus dunnii)

This report evaluates the wood and veneer properties of plantation-grown spotted gum (Corymbia citriodora subsp. variegata, or CCV) and Dunn's white gum (Eucalyptus dunnii), grown at different stockings, in thinning trials near Ellangowan in north-east New South Wales (mean annual rainfall 1050 mm) and Kingaroy in south-east Queensland (mean annual rainfall 873 mm). Thinning trials were established at age seven years. Both species showed a significant increase in stem diameter growth of the dominant trees in response to thinning. At age 10 years, trees from the unthinned (950–1270 stems ha-1) and 300 stems ha-1 treatments were selected for veneering. Five dominant trees were felled from each combination of species x sites x thinning treatment. Diameter at breast height over bark of the selected trees ranged from 20 cm to 27 cm at Ellangowan, and 19 cm to 26 cm at Kingaroy. From each tree, 1.5 m long billets were removed at two positions: a butt billet from 0.3–1.8 m above ground and a top billet from approximately 5.5–7.0 m. Log end splitting was assessed 24 hours after harvesting and again after steaming, approximately four days after harvesting. Disks from just above both billets were collected for assessment of wood properties. Billets were peeled on a spindleless veneer lathe to produce a full veneer ribbon with a target green thickness of 2.8 to 3.0 mm. The 1.55 m wide (tangential dimension) veneer sheets were dried and graded according to AS/NZ Standard 2269:2008, which describes four veneer grades. Veneer samples taken along the length of the veneer ribbon, at regular intervals of 1.55 m, were tested for stiffness, shrinkage and density. Veneer length measurements were used to calculate the radial distance of each sample from the central axis of the billet. Overall veneer gross recoveries ranged from 50% to 70%. They were significantly lower at the Kingaroy site, for both species. The veneer recoveries achieved were 2–3 times higher than typical green off saw recoveries from small plantation hardwood logs of similar diameter. Most of the veneer recovered was classified as D-grade. CCV trees from the Ellangowan site yielded up to 38% of the better C-grade and higher grade veneers. The main limiting factors that prevented veneer from meeting higher grades were the presence of kino defects and encased knots. Splits in E. dunnii veneer also contributed to reduced grade quality. Log end splits were higher for E. dunnii than for CCV, and logs from Ellangowan exhibited more severe splitting. Split index was generally higher for top than for butt billets. Split index was strongly correlated with the average veneer grade from corresponding billets. The Ellangowan site, where rainfall was higher and trees grew faster, yielded significantly denser and stiffer veneers than did the drier sites near Kingaroy, where tree growth was slower. The difference was more pronounced for E. dunnii than for CCV. Differences in measured wood properties between thinned and unthinned treatments were generally small and not significant. On average, 10% of billet volume was lost during the peeling rounding-up process. Much of the wood laid down following thinning was removed during rounding-up, meaning the effect of thinning on veneer properties could not be effectively assessed. CCV was confirmed as having high veneer density and very good veneer stiffness, exceeding 15 GPa, making it very suitable for structural products. E. dunnii also demonstrated good potential as a useful structural plywood resource, achieving stiffness above 10 GPa. Veneer stiffness and density in CCV increased from pith to bark at both sites, while for E. dunnii there was a radial increase in these properties at the Ellangowan site only. At the drier Kingaroy site, veneer stiffness and density declined from mid-radius to the log periphery. This may be associated with prolonged drought from 2005 to 2009, corresponding to the later years of tree growth at the Kingaroy site. CCV appeared to be less sensitive to drought conditions. Standing tree acoustic velocity, determined by the Fakopp time-of-flight method, provided a reliable prediction of average veneer stiffness for both species (R2=0.78 for CCV and R2=0.90 for E. dunnii) suggesting that the Fakopp method may be a useful indicator of tree and stand quality, in terms of veneer stiffness in standing trees.

A systematic review and meta-analysis of the survival of non-feldspathic porcelain veneers over 5 and 10 years

PURPOSE: This systematic review aimed to report and explore the survival of dental veneers constructed from non-feldspathic porcelain over 5 and 10 years.

MATERIALS AND METHODS: A total of 4,294 articles were identified through a systematic search involving all databases in the Cochrane Library, MEDLINE (OVID), EMBASE, Web of Knowledge, specific journals (hand-search), conference proceedings, clinical trials registers, and collegiate contacts. Articles, abstracts, and gray literature were sought by two independent researchers. There were no language limitations. One hundred sixteen studies were identified for full-text assessment, with 10 included in the analysis (5 qualitative, 5 quantitative). Study characteristics and survival (Kaplan-Meier estimated cumulative survival and 95% confidence interval [CI]) were extracted or recalculated. A failed veneer was one which required an intervention that disrupted the original marginal integrity, had been partially or completely lost, or had lost retention more than twice. A meta-analysis and sensitivity analysis of Empress veneers was completed, with an assessment of statistical heterogeneity and publication bias. Clinical heterogeneity was explored for results of all veneering materials from included studies.

RESULTS: Within the 10 studies, veneers were fabricated with IPS Empress, IPS Empress 2, Cerinate, and Cerec computer-aided design/computer-assisted manufacture (CAD/CAM) materials VITA Mark I, VITA Mark II, Ivoclar ProCad. The meta-analysis showed the pooled estimate for Empress veneers to be 92.4% (95% CI: 89.8% to 95.0%) for 5-year survival and 66% to 94% (95% CI: 55% to 99%) for 10 years. Data regarding other non-feldspathic porcelain materials were lacking, with only a single study each reporting outcomes for Empress 2, Cerinate, and various Cerec porcelains over 5 years. The sensitivity analysis showed data from one study had an influencing and stabilizing effect on the 5-year pooled estimate.

CONCLUSION: The long-term outcome (> 5 years) of non-feldspathic porcelain veneers is sparsely reported in the literature. This systematic review indicates that the 5-year cumulative estimated survival for etchable non-feldspathic porcelain veneers is over 90%. Outcomes may prove clinically acceptable with time, but evidence remains lacking and the use of these materials for veneers remains experimental.

Effect of light-curing method and indirect veneering materials on the Knoop hardness of a resin cement

This study evaluated the Knoop hardness of a dual-cured resin cement (Rely-X ARC) activated solely by chemical reaction (control group) or by chemical / physical mode, light-cured through a 1.5 mm thick ceramic (HeraCeram) or composite (Artglass) disc. Light curing was carried out using conventional halogen light (XL2500) for 40 s (QTH); light emitting diodes (Ultrablue Is) for 40 s (LED); and Xenon plasma arc (Apollo 95E) for 3 s (PAC). Bovine incisors had their buccal face flattened and hybridized. On this surface a rubber mold (5 mm in diameter and 1 mm in height) was bulk filled with the resin cement. A polyester strip was seated for direct light curing or through the discs of veneering materials. After dry storage in the dark (24 h 37°C), the samples (n = 5) were sectioned for hardness (KHN) measurements, taken in a microhardness tester (50 gF load 15 s). The data were statistically analyzed by ANOVA and Tukey's test (α = 0.05). The cement presented higher Knoop hardness values with Artglass for QTH and LED, compared to HeraCeram. The control group and the PAC/Artglass group showed lower hardness values compared to the groups light-cured with QTH and LED. PAC/HeraCeram resulted in the worst combination for cement hardness values. © 2009 Sociedade Brasileira de Pesquisa Odontológica.

A systematic review and meta-analysis of the survival of feldspathic porcelain veneers over 5 and 10 years

PURPOSE: This systematic review reports on the survival of feldspathic porcelain veneers.

MATERIALS AND METHODS: The Cochrane Library, MEDLINE (OVID), Embase, Web of Knowledge, selected journals, clinical trials registers, and conference proceedings were searched independently by two reviewers. Academic colleagues were also contacted to identify relevant research. Inclusion criteria were human cohort studies (prospective and retrospective) and controlled trials assessing outcomes of feldspathic porcelain veneers in more than 15 patients and with at least some of the veneers in situ for 5 years. Of 4,294 articles identified, 116 studies underwent full-text screenings and 69 were further reviewed for eligibility. Of these, 11 were included in the qualitative analysis and 6 (5 cohorts) were included in meta-analyses. Estimated cumulative survival and standard error for each study were assessed and used for meta-, sensitivity, and post hoc analyses. The I2 statistic and the Cochran Q test and its associated P value were used to evaluate statistical heterogeneity, with a random-effects meta-analysis used when the P value for heterogeneity was less than .1. Galbraith, forest, and funnel plots explored heterogeneity, publication patterns, and small study biases.

RESULTS: The estimated cumulative survival for feldspathic porcelain veneers was 95.7% (95% confidence interval [CI]: 92.9% to 98.4%) at 5 years and ranged from 64% to 95% at 10 years across three studies. A post hoc meta-analysis indicated that the 10-year best estimate may approach 95.6% (95% CI: 93.8% to 97.5%). High levels of statistical heterogeneity were found.

CONCLUSIONS: When bonded to enamel substrate, feldspathic porcelain veneers have a very high 10-year survival rate that may approach 95%. Clinical heterogeneity is associated with differences in reported survival rates. Use of clinically relevant survival definitions and careful reporting of tooth characteristics, censorship, clustering, and precise results in future research would improve metaanalytic estimates and aid treatment decisions.

Effect of Static and Cyclic Loading on Ceramic Laminate Veneers Adhered to Teeth with and Without Aged Composite Restorations

Purpose: Existing composite restorations on teeth are often remade prior to the cementation of fixed dental prostheses. The aim of this study was to evaluate the effect of static and cyclic loading on ceramic laminate veneers adhered to aged resin composite restorations.Materials and Methods: Eighty sound maxillary incisors were collected and randomly divided into four groups: group 1: control group, no restorations; group 2: two Class III restorations; group 3: two Class IV restorations; group 4: complete composite substrate. Standard composite restorations were made using a microhybrid resin composite (Anterior Shine). Restored teeth were subjected to thermocycling (6000 cycles). Window preparations were made on the labial surface of the teeth for ceramic laminate fabrication (Empress II). Teeth were conditioned using an etch-and-rinse system. Existing composite restorations representing the aged composites were silica coated (CoJet) and silanized (ESPE-Sil). Ceramic laminates were cemented using a bis-GMA-based cement (Variolink Veneer). The specimens were randomly divided into two groups and were subjected to either static (groups 1a, 2a, 3a, 4a) or cyclic loading (groups 1b, 2b, 3b, 4b). Failure type and location after loading were classified. Data were analyzed using one-way ANOVA and Tukey's test.Results: Significantly higher fracture strength was obtained in group 4 (330 +/- 81 N) compared to the controls in group 1 (179 +/- 120 N) (one-way ANOVA, p < 0.05). Group lb survived a lower mean number of cyclic loads (672,820 cycles) than teeth of groups 2b to 4b (846x10(3) to 873x10(3) cycles). Failure type evaluation after the fracture test showed predominantly adhesive failures between dentin and cement, but after cyclic loading, more cohesive fractures in the ceramic were seen.Conclusion: Ceramic laminate veneers bonded to conditioned aged composite restorations provided favorable results. Surface conditioning of existing restorations may eliminate the necessity of removing aged composite restorations.

Flexural Strength of Glass-Infiltrated Zirconia/Alumina-Based Ceramics and Feldspathic Veneering Porcelains

Purpose: To compare the flexural strength of two glass-infiltrated high-strength ceramics and two veneering glass-ceramics.Materials and Methods: Four ceramic materials were tested: two glass-infiltrated high-strength ceramics used as framework in metal-free restorations [In-Ceram Zirconia IZ (Gr1) and In-Ceram Alumina IA (Gr2)], and two glass-ceramics used as veneering material in metal-free restorations [Vita VM7 (Gr3) and Vitadur-alpha (Gr4)]. Bar specimens (25 x 5 x 2 mm(3)) made from core ceramics, alumina, and zirconia/alumina composites were prepared and applied to a silicone mold, which rested on a base from a gypsum die material. The IZ and IA specimens were partially sintered in an In-Ceram furnace according to the firing cycle of each material, and then were infiltrated with a low-viscosity glass to yield bar specimens of high density and strength. The Vita VM7 and Vitadur-alpha specimens were made from veneering materials, by vibration of slurry porcelain powder and condensation into a two-part brass Teflon matrix (25 x 5 x 2 mm(3)). Excess water was removed with absorbent paper. The veneering ceramic specimens were then removed from the matrix and were fired as recommended by the manufacturer. Another ceramic application and sintering were performed to compensate the contraction of the feldspar ceramic. The bar specimens were then tested in a three-point bending test.Results: The core materials (Gr1: 436.1 +/- 54.8; Gr2: 419.4 +/- 83.8) presented significantly higher flexural strength (MPa) than the veneer ceramics (Gr3: 63.5 +/- 9.9; Gr4: 57.8 +/- 12.7).Conclusion: In-Ceram Alumina and Zirconia were similar statistically and more resistant than VM7 and Vitadur-alpha.

Knoop hardness of dental resin cements: Effect of veneering material and light curing methods

This study evaluated the Knoop hardness of one resin cement (dual-cure mode or light-cure mode) when illuminated directly or through restorative materials-ceramic (HeraCeram) or composite (Artglass)-by two light curing units. Light curing was carried out using a conventional quartz tungsten halogen (QTH) light source (XL2500) for 40 s, and a light emitting diodes (LED) light source (Ultrablue Is) for 40 s. Bovine incisors had their buccal faces flattened and hybridised. on these surfaces, a mould was seated and filled with cement. A disc of the veneering material (1.5 mm thickness) was positioned over this set for light curing. After storage (24 h/37 degrees C), samples (n = 10) were sectioned for hardness (KHN) measurements. Data were submitted to ANOVA and to Tukey's test (alpha = 0.05). In general, light curing with LED resulted in higher hardness values than QTH. Distinct cement behaviour was observed with different veneering material in association with different light curing units (LCUs). (C) 2006 Elsevier Ltd. All rights reserved.

Durability of feldspathic veneering ceramic on glass-infiltrated alumina ceramics after long-term thermocycling.

This study compared the bond strength durability of a feldspathic veneering ceramic to glass-infiltrated reinforced ceramics in dry and aged conditions. Disc shaped (thickness: 4 mm, diameter: 4 mm) of glass-infiltrated alumina (In-Ceram Alumina) and glass-infiltrated alumina reinforced by zirconia (In-Ceram Zirconia) core ceramic specimens (N=48, N=12 per groups) were constructed according to the manufacturers' recommendations. Veneering ceramic (VITA VM7) was fired onto the core ceramics using a mold. The core-veneering ceramic assemblies were randomly divided into two conditions and tested either immediately after specimen preparation (Dry) or following 30000 thermocycling (5-55 oC±1; dwell time: 30 seconds). Shear bond strength test was performed in a universal testing machine (cross-head speed: 1 mm/min). Failure modes were analyzed using optical microscope (x20). The bond strength data (MPa) were analyzed using ANOVA (α=0.05). Thermocycling did not decrease the bond strength results for both In-Ceram Alumina (30.6±8.2 MPa; P=0.2053) and In-Ceram zirconia (32.6±9 MPa; P=0.3987) core ceramic-feldspathic veneering ceramic combinations when compared to non-aged conditions (28.1±6.4 MPa, 29.7±7.3 MPa, respectively). There were also no significant differences between adhesion of the veneering ceramic to either In-Ceram Alumina or In-Ceram Zirconia ceramics (P=0.3289). Failure types were predominantly a mixture of adhesive failure between the veneering and the core ceramic together with cohesive fracture of the veneering ceramic. Long-term thermocycling aging conditions did not impair the adhesion of the veneering ceramic to the glass-infiltrated alumina core ceramics tested.