Gibbs energy of formation of CuCrO4 and phase relations in the system Cu-Cr-O below 735 K

A solid state galvanic cell incorporating yttria-stabilized zirconia electrolyte and ruthenium(IV) oxide electrodes has been used to measure the equilibrium chemical potential of oxygen corresponding to the decomposition of CuCrO4 in the range 590–760 K. For the reaction CuO(tenorite) + CuCr2O4(spinel) + 1.5O2(g)→2CuCrO4(orth), ΔGXXX = −183540 + 249.6T(±900) J mol−1. The decomposition temperature of CuCrO4 in pure oxygen at a pressure of 1.01 × 105 Pa is 735(±1) K. By combining the results obtained in this study with data on the Gibbs energy of formation of CuCr2O4 and CuCrO2 reported earlier, the standard Gibbs energy of formation of CuCrO4 and the phase relations in the system Cu-Cr-O at temperatures below 735 K have been deduced. Electron microscopic studies have indicated that the decomposition of CuCrO4 to CuCr2O4 is topotactic.

Gibbs energy of formation of CaCu3Ti4O12 and phase relations in the system CaO-CUO/CU2O-TiO2

he standard Gibbs energy of formation of CaCu3Ti4O12 (CCTO) from CaTiO3, CuO and TiO2 has been determined as a function of temperature from 925 to 1350 K using a solid-state electrochemical cell with yttria-stabilized zirconia as the solid electrolyte. Combining this result with information in the literature on CaTiO3, the standard Gibbs energy of formation of CCTO from its component binary oxides, CaO, CuO and TiO2, has been obtained: View the MathML source (CaCu3Ti4O12)/J mol−1 (±600) = −125231 + 6.57 (T/K). The oxygen chemical potential corresponding to the reduction of CCTO to CaTiO3, TiO2 and Cu2O has been calculated from the electrochemical measurements as a function of temperature and compared on an Ellingham diagram with those for the reduction of CuO to Cu2O and Cu2O to Cu. The oxygen partial pressures corresponding to the reduction reactions at any chosen temperature can be read using the nomograms provided on either side of the diagram. The effect of the oxygen partial pressure on phase relations in the pseudo-ternary system CaO–CuO/Cu2O–TiO2 at 1273 K has been evaluated. The phase diagrams allow identification of secondary phases that may form during the synthesis of the CCTO under equilibrium conditions. The secondary phases may have a significant effect on the extrinsic component of the colossal dielectric response of CCTO.

The substrate dependent competitive formation of cyclobutanones and cyclopentanones in an intramolecular rhodium carbenoid CH insertion reaction: enantiospecific total synthesis of silphiperfol-6-ene

The enantiospecific total synthesis of silphiperfol-6-ene has been accomplished starting from the readily available monoterpene (R)-limonene, employing a rhodium carbenoid insertion into the CH bond of a tertiary methyl group. A substrate dependent competitive insertion of the rhodium carbenoid in the gamma- and beta-CH bonds to form cyclopentanone and cyclobutanones, respectively, has been described. (C) 2012 Elsevier Ltd. All rights reserved.

Gibbs Energy of Formation of Ca3Ti8Al12O37 and Phase Relations and Chemical Potentials in the System Al2O3-TiO2-CaO

The quaternary oxide in the system Al2O3-CaO-TiO2 is found to have the composition Ca3Ti8Al12O37 rather than CaTi3Al8O19 as reported in the literature. The standard Gibbs energy of formation of Ca3Ti8Al12O37 from component binary oxides is measured in the temperature range from 900 to 1250 K using a solid-state electrochemical cell incorporating single crystal CaF2 as the solid electrolyte. The results can be represented by the equation: delta G(f(0x))(0) (+/- 70)/J mol(-1) = -248474 - 15.706(T/K). Combining this information with thermodynamic data on calcium aluminates and titanates available in the literature, subsolidus phase relations in the pseudo-ternary system Al2O3-CaO-TiO2 are computed and presented as isothermal sections. The evolution of phase relations with temperature is highlighted. Chemical potential diagrams are computed at 1200 K, showing the stability domains of the various phases in the chemical potential-composition space. In each chemical potential diagram, chemical potential of one component is plotted against the cationic fraction of the other two components. The diagrams are valid at relatively high oxygen potentials where Ti is present in its four-valent state in all the oxide phases.

Self-Adapting Peripherally Heterofunctionalized Hyperbranched Polymers: Formation of Janus and Tripodal Structures

A peripherally clickable hyperbranched polyester carrying numerous propargyl terminal groups was prepared by a simple melt transesterification polycondensation of a suitably designed AB(2) monomer; this clickable hyperscaffold was then transformed into a variety of different derivatives by using the Cu-catalyzed azide-yne click reaction. Functionalization of the periphery with equimolar quantities of mutually immiscible segments, such as hydrocarbon, fluorocarbon, and PEG, yielded frustrated molecular systems that readapt and form structures wherein the immiscible segments appear to self-segregate to generate either Janus structures (when two immiscible segments are present) or tripodal structures (when three immiscible segments are present). Evidence for such self-segregation was obtained from a variety of studies, such as differential scanning calorimetry, Langmuir isotherms, AFM imaging, and small-angle X-ray scattering measurements. Crystallization of one or more of the peripheral segments reinforced this self-segregation; the weight-fraction-normalized enthalpies of melting associated with the different domains revealed a competition between the segments to optimize their crystalline organization. When one or more of the segments are amorphous, the remaining segments crystallize more effectively and consequently exhibit a higher melting enthalpy. AFM images of monolayers, transferred from the Langmuir trough, revealed that the thickness matches the expected values; furthermore, contact angle measurements clearly demonstrated that the monolayer films are fairly hydrophobic, and in the case of the tripodal hybramers, the presence of domains of hydrocarbon and fluorocarbon appears to impart nanoscale chemical heterogeneity that is reflected in the strong hysteresis in the advancing and receding contact angles.

Comprehending the Formation of Eutectics and Cocrystals in Terms of Design and Their Structural Interrelationships

The phenomenon of cocrystallization, which encompasses the art of making multicomponent organic solids such as cocrystals, solid solutions, eutectics, etc. for novel applications, has been less studied in terms of reliably and specifically obtaining a desired cocrystallization product and the issues that govern their formation. Further, the design, structural, and functional aspects of organic eutectics have been relatively unexplored as compared to solid solutions and cocrystals well-established by crystal engineering principles. Recently, eutectics were proposed to be designable materials on par with cocrystals, and herein we have devised a systematic approach, based on the same crystal engineering principles, to specifically and desirably make both eutectics and cocrystals for a given system. The propensity for strong homomolecular synthons over weak heteromolecular synthons and vice versa during supramolecular growth was successfully utilized to selectively obtain eutectics and cocrystals, respectively, in two model systems and in two drug systems. A molecular level understanding of the formation of eutectics and cocrystals and their structural interrelationships which is significant from both fundamental and application viewpoints is discussed. On the other hand, the obscurity in establishing a low melting combination as a eutectic or a cocrystal is resolved through phase diagrams.

Effect of inductive effect on the formation of cocrystals and eutectics

There is a growing need to understand the factors that control the formation of different yet related multicomponent adducts such as cocrystals, solid solutions and eutectics from both fundamental and application perspectives. Benzoic acid and its structural analogues, having gradation in inductive force strengths, are found to serve as excellent coformers to comprehend the formation of above adducts with the antiprotozoal drug ornidazole. The combination of the drug with para-amino and -hydroxybenzoic acids resulted in cocrystals in accordance with the induction strength complementarity between the participant hydrogen bond donor-acceptor groups. The lack of adequate inductive forces for combinations with benzoic acid and other coformers was exploited to make eutectics of the drug. The isomorphous/isostructural relationship between para-amino and -hydroxybenzoic acid-drug cocrystals was utilized to make solid solutions, i.e. solid solutions of cocrystals. All in all, we successfully steered and expanded the supramolecular solid-form space of ornidazole.

Multicomponent Adducts of Pyridoxine: An Evaluation of the Formation of Eutectics and Molecular Salts

Cocrystallization of pyridoxine (vitamin B6) with several biologically important molecules was undertaken with the intent of successfully designing various hydrogen bonded adducts such as salts, cocrystals, and eutectics. Pyridoxine formed eutectics with isoniazid (an antitubercular drug) and nicotinic acid (vitamin B3) and molecular salts with para-aminobenzoic acid (a bioactive) and saccharin (an artificial sweetener), respectively, in accordance to our design strategy. A salt cocrystal, a precisely conjugate acid-base cocrystal, was obtained for the pyridoxine-para-nitrobenzoic acid combination. The role of supramolecular affinity of hydrogen bonding functional groups and Delta pK(a) differences leading to the formation of above diverse adducts was discussed. This study underpins the need for full-fledged supramolecular compatibility studies of multivitamin/drug combinations toward the development of optimal and/or synergistic combination formulations.

Formation of Single and Multiple Deformation Twins in Nanocrystalline fcc Metals

Deformation twins are often observed to meet each other to form multi-fold twins in nanostructured face-centered cubic (fcc) metals.Here we propose two types of mechanism for the nucleation and growth of four different single and multiple twins. These mechanisms provide continuous generation of twinning partials for the growth of the twins after ucleation. A relatively high stress or high strain rate is needed to activate these mechanisms, making them more prevalent in nanocrystalline materials than in their coarse-grained counterparts.Experimental observations that support the proposed mechanisms are presented.