Structure and optical properties of ZnS thin films grown by glancing angle deposition

The glancing angle deposition (GLAD) technique was used to deposit ZnS films by electron beam evaporation method. The cross sectional scanning electron microscopy (SEM) image illustrated a highly orientated microstructure composed of slanted column. The atomic force microscopy (APM) analysis indicated that incident flux angle had significant effects on the nodule size and surface roughness. Under identical nominal thickness, the actual thickness of the GLAD films is related to the incident flux angle. The refractive index and in-plane birefringence of the GLAD ZnS films were discussed, and the maximum bireffingence Delta n = 0.036 was obtained at incident flux angle of alpha = 80 degrees. Therefore, the glancing angle deposition technique is a promising way to create a columnar structure with enhanced birefringent property. (c) 2005 Elsevier B.V. All rights reserved.

Surface morphology and properties of zirconia thin films prepared at different deposition rates

ZrO2 thin films were prepared on BK7 glass substrates by electron beam evaporation deposition method. The influence of deposition rate varying from 1.2 to 6.3 nm s(-1) on surface morphology and other properties of ZrO2 films were examined. With increasing deposition rate, the surface defect density increased. The decrease in half width at full maximum in X-ray diffraction pattern with deposition rate indicates an increase in crystal dimension with increasing deposition rate. Electron beam deposited ZrO2 films are known to be inhomogeneous. From the change of the peak transmittance value, it can be deduced that the inhomogeneity of ZrO2 films strengthened gradually with increasing deposition rate. The type of surface defects changed from nodules to craters when the deposition rate was high enough.

Theoretical analysis of optical properties of dielectric coatings dependence on substrate subsurface defects

A model for refractive index of stratified dielectric substrate was put forward according to theories of inhomogeneous coatings. The substrate was divided into surface layer, subsurface layer and bulk layer along the normal direction of its surface. Both the surface layer (separated into N-1 sublayers of uniform thickness) and subsurface layer (separated into N-2 sublayers of uniform thickness), whose refractive indices have different statistical distributions, are equivalent to inhomogeneous coatings, respectively. And theoretical deduction was carried Out by employing characteristic matrix method of optical coatings. An example of mathematical calculation for optical properties of dielectric coatings had been presented. The computing results indicate that substrate subsurface defects can bring about additional bulk scattering and change propagation characteristic in thin film and Substrate. Therefore, reflectance, reflective phase shift and phase difference of an assembly of coatings and substrate deviate from ideal conditions. The model will provide some beneficial theory directions for improving optical properties of dielectric coatings via substrate surface modification. (c) 2005 Elsevier B.V. All rights reserved.

Y2O3 stabilized ZrO2 thin films deposited by electron beam evaporation: Structural, morphological characterization and laser induced damage threshold

Four kinds of Y2O3 stabilized ZrO2 (YSZ) thin films with different Y2O3 content have been prepared on BK7 substrates by electron-beam evaporation method. Structural properties and surface morphology of thin films were investigated by X-ray diffraction (XRD) spectra and scanning probe microscope. Laser induced damage threshold (LIDT) was determined. It was found that crystalline phase and microstructure of YSZ thin films was dependent on Y2O3 molar content. YSZ thin films changed from monoclinic phase to high temperature phase (tetragonal and cubic) with the increase of Y2O3 content. The LIDT of stabilized thin film is more than that of unstabilized thin films. The reason is that ZrO2 material undergoes phase transition during the course of e-beam evaporation resulting in more numbers of defects compared to that of YSZ thin films. These defects act as absorptive center and the original breakdown points. (c) 2006 Elsevier B.V. All rights reserved.

Influence of different post-treatments on the structure and optical properties of zinc oxide thin films

Zinc oxide (ZnO) films with c-oriented were grown on fused quartz glass substrates at room temperature using dc reactive magnetron sputtering. The as-grown films were annealed at 700 degrees C in air and bombarded by ion beam, respectively. The effects of post-treatments on the structural and optical properties of the ZnO films were investigated by X-ray diffraction (XRD), photoluminescence (PL), optical transmittance and absorption measurements. The XRD spectra indicate that the crystal quality of ZnO films has been improved by both the post-treatments. Compared with the as-grown sample, both annealed and bombarded samples exhibited blueshift in the UV emission peaks, and a strong green emission was found in the annealed ZnO film. In both optical transmittance and absorption spectra, a blueshift of the band-gap edge was observed in the bombarded film, while a redshift was observed in the annealed film. (c) 2004 Elsevier B.V. All rights reserved.

High-reflectance 193 nm Al2O3/MgF2 mirrors

Thin-film single layers of Al2O3 and MgF2 were deposited upon super polished fused-silica by electron-beam evaporation. The subsequent optical constants n and k were reported for the spectral range of 180-230 nm. High-reflectance dense multilayer coatings for 193 nm were designed on the basis of the evaluated optical constants and produced. The spectra of the reflectance of HR coatings were compared to the theoretical calculations. HR mirrors of 27 layers with a reflectance of more than 98% were reported. (c) 2004 Elsevier B.V. All rights reserved.

Laser-induced damage of Ta2O5/S1O2 narrow-band interference filters under different 1064 nm Nd : YAG laser modes

The laser-induced damage (LID) behavior of narrow-band interference filters was investigated with a Nd:YAG laser at 1064 nm under single-pulse mode and free-running mode. The absorption measurement of such coatings was performed with surface thermal lensing (STL) technique. The damage morphologies under the two different laser modes were also studied in detail. It was found that all the filters exhibited a pass-band-center-dependent absorption and laser-induced damage threshold (LIDT) behavior, but the damage morphologies were diverse. The explanation was given with the analysis of the electric field distribution and the operational behavior of the irradiation laser. (c) 2005 Elsevier B.V. All rights reserved.

High laser-induced damage threshold HfO2 films prepared by ion-assisted electron beam evaporation

HfO2 films were deposited by electron beam evaporation with different deposition parameters. The properties such as refractive index, weak absorption, and laser induced damage thresholds (LIDTs) of these films have been investigated. It was found that when pulsed Nd:YAG 1064 nm laser is used to investigate LIDT of films: Metallic character is the main factor that influences LIDTs of films obtained from Hf starting material by ion-assisted reaction, and films prepared with higher momentum transfer parameter P have fewer metallic character; The ion-assisted reaction parameters are key points for preparing high LIDT films and if the parameters are chose properly, high LIDT films can be obtained. (c) 2004 Elsevier B.V. All rights reserved.

Annealing effects on electron-beam evaporated Al2O3 films

The effects of post-deposited annealing on structure and optical properties of electron-beam evaporated Al2O3 single layers were investigated. The films were annealed in air for 1.5 h at different temperatures from 250 to 400 degrees C. The optical constants and cut-off wavelength were deduced. Microstructure of the samples was characterized by X-ray diffraction (XRD). Profile and surface roughness measurement instrument was used to determine the rms surface roughness. It was found that the cut-off wavelength shifted to short wavelength as the annealing temperature increased and the total optical loss decreased. The film structure remained amorphous even after annealing at 400 degrees C temperature and the samples annealed at higher temperature had the higher rms surface roughness. The decreasing total optical loss with annealing temperature was attributed to the reduction of absorption owing to oxidation of the film by annealing. Guidance to reduce the optical loss of excimer laser mirrors was given. (c) 2004 Elsevier B.V. All rights reserved.

The effect of diffusion and overhangs/vacancies on the microstructure of zig-zag thin film

Basing on some growth models of thin film, we have investigated the growth mechanism of glancing angle deposition (GLAD) film. The simulation verifies that the overhangs/vacancies also contribute to the columnar growth as well as the self-shadowing effect for GLAD thin film. Besides, we have studied the effect of the deposition rate, surface and bulk diffusions on the microstructure of thin film using the time-dependent Monte Carlo method. The results show that the surface and bulk diffusions can significantly enhance the packing density of thin film in GLAD growth, and the increase of the deposition rate induce the moderate decrease of the packing density. (c) 2006 Elsevier B.V. All rights reserved.

Effect of SiO2 protective layer on the femtosecond laser-induced damage of HfO2/SiO2 multilayer high-reflective coatings

Two kinds of HfO2/SiO2 800 nm high-reflective (HR) coatings, with and without SiO2 protective layer were deposited by electron beam evaporation. Laser-induced damage thresholds (LIDT) were measured for all samples with femtosecond laser pulses. The surface morphologies and the depth information of all samples were observed by Leica optical microscopy and WYKO surface profiler, respectively. It is found that SiO2 protective layer had no positive effect on improving the LIDT of HR coating. A simple model including the conduction band electron production via multiphoton ionization and impact ionization is used to explain this phenomenon. Theoretical calculations show that the damage occurs first in the SiO2 protective layer for HfO2/SiO2 HR coating with SiO2 protective layer. The relation of LIDT for two kinds of HfO2/SiO2 HR coatings in calculation agrees with the experiment result. (c) 2006 Elsevier B.V. All rights reserved.

Optimization of thin-film design for multi-layer dielectric grating

Thin-film design used to fabricate multi-layer dielectric (MLD) gratings should provide high transmittance during holography exposure, high reflectance at use wavelength and sufficient manufacturing latitude of the grating design making the MLD grating achieve both high diffraction efficiency and low electric field enhancement. Based on a (HLL)H-9 design comprising of quarter-waves of high-index material and half-waves of low-index material, we obtain an optimum MLD coating meeting these requirements by inserting a matching layer being half a quarter-wave of Al2O3 between the initial design and an optimized HfO2 top layer. The optimized MLD coatings exhibits a low reflectance of 0.017% under photoresist at the exposure angle of 17.8 degrees for 413 nm light and a high reflectance of 99.61% under air at the use angle of 51.2 degrees for 1053 nm light. Numerical calculation of intensity distribution in the photoresist coated on the MLD film during exposure shows that standing-wave patterns are greatly minimized and thus simulation profile of photoresist gratings after development demonstrates smoother shapes with lower roughness. Furthermore, a MLD gratings with grooves etched into the top layer of this MLD coating provides a high diffraction efficiency of 99.5% and a low electric field enhancement ratio of 1.53. This thin-film design shows perfect performances and can be easily fabricated by e-beam evaporation. (c) 2006 Elsevier B.V. All rights reserved.

Influence of substrate temperature on properties of MgF2 coatings

Thermal boat evaporation was employed to prepare MgF2 single-layer coatings upon both JGS1 and UBK7 substrates at different substrate temperatures. Microstructure, transmittance and residual stress of these coatings were measured by X-ray diffraction, spectrophotometer, and optical interferometer, respectively. Measurement of laser induced damage threshold (LIDT) of the samples was performed at 355 nm, 8 ns pulses. The results showed that high substrate temperature was beneficial to crystallization of the film. Above 244 degrees C, the refractive index increased gradually with the substrate temperature rising. Whereas, it was exceptional at 210 degrees C that the refractive index was higher than those deposited at 244 and 277 degrees C. The tensile residual stresses were exhibited in all MgF2 films, but not well correlated with the substrate temperature. In addition, the stresses were comparatively smaller upon JGS1 substrates. A tendency could be seen that the LIDTs reached the highest values at about 244 degrees C, and the films upon JGS1 had higher LIDTs than those upon UBK7 substrates at the same temperature. Meanwhile, the damage morphologies showed that the laser damage of the coating resulted from an absorbing center at the film-substrate interface. The features of the damages were displayed by an absorbing center dominated model. Furthermore, the reason of the difference in LIDT values was discussed in detail. (C) 2007 Elsevier B.V. All rights reserved.

Influence of deposition conditions on the microstructure of oxides thin films

Thin films of ZrO2, HfO2 and TiO2 were deposited on kinds of substrates by electron beam evaporation (EB), ion assisted deposition (IAD) and dual ion beam sputtering (DIBS). Then some of them were annealed at different temperatures. X-ray diffraction (XRD) was applied to determine the crystalline phase and the grain size of these films, and the results revealed that their microstructures strongly depended on the deposition conditions such as substrate, deposition temperature, deposition method and annealing temperature. Theory of crystal growth and migratory diffusion were applied to explain the difference of crystalline structures between these thin films deposited and treated under various conditions. (c) 2007 Elsevier B.V. All rights reserved.

Effects of annealing on laser-induced damage threshold of TiO2/SiO2 high reflectors

The mechanism of improving 1064 nm, 12 ns laser-induced damage threshold (LIDT) of TiO2/SiO2 high reflectors (HR) prepared by electronic beam evaporation from 5.1 to 13.1 J/cm(2) by thermal annealing is discussed. Through optical properties, structure and chemical composition analysis, it is found that the reduced atomic non-stoichiometric defects are the main reason of absorption decrease and LIDT rise after annealing. A remarkable increase of LIDT is found at 300 degrees C annealing. The refractive index and film inhomogeneity rise, physical thickness decrease, and film stress changes from compress stress to tensile stress due to the structure change during annealing. (c) 2007 Elsevier B.V. All rights reserved.