用不同的Mo靶溅射功率制备Mo／Si多层膜

用磁控溅射法制备了周期厚度和周期数均相同的Mo／Si多层膜，用原子力显微镜和小角X射线衍射分别研究了Mo靶溅射功率不相同时，Mo／Si多层膜表面形貌和晶相的变化。随后在国家同步辐射实验室测量了Mo／Si多层膜的软X射线反射率。研究发现，随着Mo靶溅射功率的增大，Mo／Si多层膜的表面粗糙度增加，Mo的特征X射线衍射峰也增强，Mo／Si多层膜的软X射线峰值反射率先增大后减小。

Mo／Si软X射线多层膜的界面粗糙度研究

用磁控溅射法分别制备了以Mo膜层和Si膜层为顶层的Mo／Si多层膜系列，利用小角X射线衍射确定了各多层膜的周期厚度。以不同周期数的Mo／Si多层膜的新鲜表面近似等同于同一多层膜的内界面，通过原子力显微镜研究了多层膜界面粗糙度随膜层数的变化规律。并在国家同步辐射实验室测量了各多层膜的软X射线反射率。研究表明：随着膜层数的增加，Mo膜层和Si膜层的界面粗糙度先减小后增加然后再减小，多层膜的峰值反射率先增加后减小。

退火对HfO2/SiO2多层膜残余应力的影响

用电子束蒸发方法在BK7基底上沉积了HfO2/SiO2多层膜。研究了200℃到400℃的退火对残余应力的影响。结果表明退火前的薄膜残余应力为压应力，在200℃退火后发展为张应力，然后张应力值随着退火温度的升高而增大。在400℃退火后，由于张应力太大，薄膜表面出现了裂纹。同时，随着退火温度的升高，晶粒尺寸长大，晶面间距降低。残余应力的变化与结构的演变相对应。

Thermal-mechanical modeling of nodular defect embedded within multilayer coatings

The initiation of laser damage within optical coatings can be better understood by thermal-mechanical modeling of coating defects. The result of this modeling shows that a high-temperature rise and thermal stress can be seen just inside the nodular defect compared to surrounding coating layers. The temperature rise and thermal stress tend to increase with seed diameter. Shallower seed tend to cause higher temperature rise and greater thermal stress. There is a critical seed depth at which thermal stress is largest. The composition of the seed resulting from different coating-material emission during evaporation can affect the temperature rise and thermal stress distribution.

Materials science: The ultrasmoothness of diamond-like carbon surfaces

The ultrasmoothness of diamond-like carbon coatings is explained by an atomistic/continuum multiscale model. At the atomic scale, carbon ion impacts induce downhill currents in the top layer of a growing film. At the continuum scale, these currents cause a rapid smoothing of initially rough substrates by erosion of hills into neighboring hollows. The predicted surface evolution is in excellent agreement with atomic force microscopy measurements. This mechanism is general, as shown by similar simulations for amorphous silicon. It explains the recently reported smoothing of multilayers and amorphous transition metal oxide films and underlines the general importance of impact-induced downhill currents for ion deposition, polishing, and nanopattering.

Erbium doped materials for a Si-based microphotonics

We have investigated the role of the Si excess on the photoluminescence properties of Er doped substoichiometric SiOx layers. We demonstrate that the Si excess has two competing roles: when agglomerated to form Si nanoclusters (Si-nc) it enhances the Er excitation efficiency but it also introduces new non-radiative decay channels. When Er is excited through an energy transfer from Si-nc, the beneficial effect on the enhanced excitation efficiency prevails and the Er emission increases with increasing Si content. Nevertheless the maximum excited Er fraction is only of the order of percent. In order to increase the concentration of excited Er ions, a different approach based on Er silicate thin film has been explored. Under proper annealing conditions, an efficient luminescence at 1535 nm is found and all of the Er ions in the material is optically active. The possibility to efficiently excite Er ions also through electron-hole mediated processes is demonstrated in nanometer-scale Er-Si-O/Si multilayers. These data are presented and discussed.

Growth mechanism of graphene on platinum: Surface catalysis and carbon segregation

A model of the graphene growth mechanism of chemical vapor deposition on platinum is proposed and verified by experiments. Surface catalysis and carbon segregation occur, respectively, at high and low temperatures in the process, representing the so-called balance and segregation regimes. Catalysis leads to self-limiting formation of large area monolayer graphene, whereas segregation results in multilayers, which evidently "grow from below." By controlling kinetic factors, dominantly monolayer graphene whose high quality has been confirmed by quantum Hall measurement can be deposited on platinum with hydrogen-rich environment, quench cooling, tiny but continuous methane flow and about 1000°C growth temperature. © 2014 AIP Publishing LLC.

Raman scattering of folded acoustic phonons in self-assembled Si/Ge dot superlattices

Self-assembled Si/Ge dot multilayers with small, uncorrelated dots fabricated by molecular beam epitaxy in the Stranski-Krastanov growth mode are studied by Raman scattering of folded longitudinal acoustic (FLA) modes. The FLA Raman spectra are analyzed and modeled with respect to mode frequencies and the spectral envelope of mode intensities. The deduced average superlattice properties are consistent with results from atomic force microscopy. The simple Rytov model used for Si/Ge layer structures reproduces very well the frequencies of the FLA modes up to 150 cm(-1). The nonlinearity of phonon dispersion curves in bulk Si for large momenta, however, becomes important for modeling the higher frequencies of observed FLA modes up to 22nd order. The effective dot layer width and an activation energy for thermal intermixing of 2.1+/-0.2 eV are determined from the spectral envelopes of FLA mode intensities of as-grown and annealed Si/Ge dot multilayers. (C) 2004 American Institute of Physics.

Nano-layer structure of silicon-on-insulator materials

Silicon-on-insulator (SOI) has been recognized as a promising semiconductor starting material for ICs where high speed and low power consumption are desirable, in addition to its unique applications in radiation-hardened circuits. In the present paper, three novel SOI nano-layer structures have been demonstrated. ULTRA-THIN SOI has been fabricated by separation by implantation of oxygen (SIMOX) technique at low oxygen ion energy of 45 keV and implantation dosage of 1.81017/cm2. The formed SOI layer is uniform with thickness of only 60 nm. This layer is of crystalline quality. and the interface between this layer and the buried oxide layer is very sharp, PATTERNED SOI nanostructure is illustrated by source and drain on insulator (DSOI) MOSFETs. The DSOI structure has been formed by selective oxygen ion implantation in SIMOX process. With the patterned SOI technology, the floating-body effect and self-heating effect, which occur in the conventional SOI devices, are significantly suppressed. In order to improve the total-dose irradiation hardness of SOI devices, SILICON ON INSULATING MULTILAYERS (SOIM) nano-structure is proposed. The buried insulating multilayers, which are composed of SiOx and SiNy layers, have been realized by implantation of nitride and oxygen ions into silicon in turn at different ion energies, followed by two steps of high temperature annealing process, respectively, Electric property investigation shows that the hardness to the total-dose irradiation of SOIM is remarkably superior to those of the conventional SIMOX SOI and the Bond-and-Etch-Back SOI.

Magnetic property and interface structure of Ta/NiO/NiFe/Ta

Ta/NiO/NiFe/Ta multilayers, utilizing Ta as buffer layer, were prepared by rf reactive and de magnetron sputtering. The exchange coupling field between NiO and NiFe reached a maximum value of 9.6x10(3) A/m at a NiO film thickness of 50 nm. The composition and chemical states at interface region of Ta/NiO/Ta were studied by using the X-ray photoelectron spectroscopy (XPS) and peak decomposition technique. The results show that there is an "intermixing layer" at the Ta/NiO land NiO/Ta) interface due to a thermodynamically favorable reaction 2Ta + 5NiO = 5Ni + Ta2O5. This interface reaction has a great effect on exchange coupling. The thickness of Ni+NiO estimated by XPS depth. profiles is about 8-10 nm.

X-ray diffraction and optical characterization of interdiffusion in self-assembled InAs/GaAs quantum-dot superlattices

We report on the characterization of thermally induced interdiffusion in InAs/GaAs quantum-dot superlattices with high-resolution x-ray diffraction and photoluminescence techniques. The dynamical theory is employed to simulate the measured x-ray diffraction rocking curves of the InAs/GaAs quantum-dot superlattices annealed at different temperatures. Excellent agreement between the experimental curves and the simulations is achieved when the composition, thickness, and stress variations caused by interdiffusion are taken in account. It is found that the significant In-Ga intermixing occurs even in the as-grown InAs/GaAs quantum dots. The diffusion coefficients at different temperatures are estimated. (C) 2000 American Institute of Physics. [S0003-6951(00)02440-2].

The structural and photoluminescence properties of self-organized quantum dots in InAs/In0.53Ga0.47As multilayer on InP substrate

Self-organized InAs/In0.53Ga0.47As quantum dot (QD) multilayers were grown on InP substrate by molecular beam epitaxy. The structural and optical properties were characterized by using cross-sectional transmission electron microscopy (TEM) and photoluminescence (PL), respectively. Vertically aligned InAs quantum dots multilayer on InP substrate is demonstrated for the first time. Photoluminescence with a line width of similar to 26 meV was observed from the QDs multilayer. (C) 2000 Elsevier Science B.V. All rights reserved.

A comparison of photoluminescence properties of InGaAs GaAs quantum dots with a single quantum well

Variable temperature photoluminescence (PL) measurements for In0.3Ga0.7As(6 nm)/GaAs(34 nm) quantum dot superlattices with a period of 20 and an In0.3Ga0.7As(6 nm)/GaAs(34 nm) reference single quantum well have been conducted. It is found that the temperature dependence is different between the quantum dots and the reference single quantum well. The PL peak energy of the single quantum well decreases faster than that of the quantum dots with increasing temperature. The PL peak energy for the InGaAs/GaAs quantum dots closely follows the InAs band gap in the temperature range from 11 to 170 K, while the PL peak energy for the InGaAs/GaAs quantum well closely follows the GaAs band gap. In comparison with InAs/GaAs quantum dots, the InGaAs/GaAs quantum dots are more typical as a zero-dimensional system since the unusual PL results, which appear in the former, are not obvious for the latter. (C) 1999 American Institute of Physics. [S0021-8979(99)08615-6].

Self-organization of the InGaAs GaAs quantum dots superlattice

The mechanism of self-organization of quantum dots (QDs) during the growth of InGaAs/GaAs multilayers on GaAs (1 0 0) was investigated with cross-sectional transmission electron microscopy (XTEM), and double-crystal X-ray diffraction (DCXD). We found that the QDs spacing in the first layer can affect the vertical alignment of QDs. There seems to exist one critical lateral QD spacing, below which merging of QDs with different initial size is found to be the dominant mechanism leading to perfect vertical alignment. Once the critical value of QDs spacing is reached, the InGaAs QDs of the first layer are simply reproduced in the upper layers. The X-ray rocking curve clearly shows two sets of satellite peaks, which correspond to the QDs superlattice, and multi-quantum wells (QW) formed by the wetting layers around QDs. (C) 1999 Elsevier Science B.V. All rights reserved.

Structural characterization of InGaAs/GaAs quantum dots superlattice infrared photodetector structures

InGaAs/GaAs quantum dots (QDs) superlattice grown by molecular beam epitaxy (MBE) at different substrate temperatures for fabricating 8-12 mu m infrared photodetector were characterized by transmission electron microscopy (TEM), double-crystal X-ray diffraction (DCXRD) and photoluminescence (PL). High-quality QDs superlattice can be achieved by higher growth temperature. Cross-sectional TEM shows the QDs in the successive layers are vertically aligned along growth direction. Interaction of partial vertically aligned columns leads to a perfect vertical ordering. With increasing number of bilayers, the average QDs size becomes larger in height and rapidly saturates at a certain value, while average lateral length nearly preserves initial size. This change leads to the formation of QDs homogeneous in size and of a particular shape. The observed self-organizations are attributed to the effect of strain distribution at QDs on the kinetic growth process. DCXRD measurement shows two sets of satellite peaks which corresponds to QDs superlattice and multi quantum wells formed by the wetting layers. Kinematical simulations of the wetting layers indicate that the formation of QDs is associated with a decrease of the effective indium content in the wetting layers. (C) 1999 Elsevier Science B.V. All rights reserved.