Compósitos de matriz metálica à base níquel com adição de TaC e NbC produzidos via metalurgia do pó

Carbide reinforced metallic alloys potentially improve some important mechanical properties required for the overall use of important engineering materials such as steel and nickel. Nevertheless, improved performance is achieved not only by composition enhancement but also by adequate processing techniques, such as novel sintering methods in the case of powder metallurgy. The method minimizes energy losses in addition to providing uniform heating during sintering. Thus, the general objective of this study was to evaluate the density, hardness, flexural strength, dilatometric behavior and to analyze the microstructure of metal matrix composites based nickel with addition of carbides of tantalum and / or niobium when sintered in a conventional furnace and Plasma assisted debinding and sintering (PADS). Initially, were defineds best parameters of granulation, screening and mixing procedure. After, mixtures of carbonyl Ni and 5%, 10% and 15 wt.% NbC and TaC were prepared in a Y-type mixer under wet conditions during 60 minutes. The mixtures were then dried and granulated using 1.5 wt. % paraffin diluted in hexane. Granulates were cold pressed under 600 MPa. Paraffin was then removed from the pressed pellets during a pre-sintering process carried out in a tubular furnace at 500 °C during 30 min. The heating rate was 3 ºC/min. The pellets were then sintered using either a plasma assisted reactor or a conventional resistive tubular furnace. For both methods, the heating rate was set to 8 ºC/min up to 1150 °C. The holding time was 60 minutes. The microstructure of the sintered samples was evaluated by SEM. Brinell hardness tests were also carried out. The results revealed that higher density and higher hardness values were observed in the plasma-assisted sintered samples. Hardness increased with the concentration of carbides in the Ni-matrix. The flexural strength also increased by adding the carbides. The decline was larger for the sample with addition of 5% 5% TaC and NbC. In general, compositions containing added carbide 10% showed less porous and more uniform distribution of carbides in the nickel matrix microstructural appearance. Thus, both added carbide and plasma sintering improved density, hardness, flexural strength and microstructural appearance of the composites

Optical characterization of cubic AlGaN/GaN quantum wells

Cubic phase group III-nitrides were grown using RF plasma assisted Molecular Beam Epitaxy on GaAs (001) substrates. High-resolution X-ray diffraction, photoluminescence, cathodoluminescence and photoreflectance measurements were employed to characterize the structural and optical properties of GaN/AlxGa1-xN Multi Quantum Well (MQW) structures, in which both Aluminum content and well widths were varied. The observed quantized states are in agreement with first-principles based theoretical calculations.

Environmental effects in kelvin force microscopy of modified diamond surfaces

We have explored the effects of atmospheric environment on Kelvin force microscopy (KFM) measurements of potential difference between different regions of test polycrystalline diamond surfaces. The diamond films were deposited by microwave plasma-assisted chemical vapor deposition, which naturally produces hydrogen terminations on the surface of the films formed. Selected regions were patterned by electron-beam lithography and chemical terminations of oxygen or fluorine were created by exposure to an oxygen or fluorine plasma source. For KFM imaging, the samples were mounted in a hood with a constant flow of helium gas. Successive images were taken over a 5-h period showing the effect of the environment on KFM imaging. We conclude that the helium flow removes water molecules adsorbed on the surface of the samples, resulting in differences in surface potential between adjacent regions. The degree of water removal is different for surfaces with different terminations. The results highlight the importance of taking into account the atmospheric environment when carrying out KFM analysis. (C) 2012 Wiley Periodicals, Inc.

Caratterizzazione tribologica e microstrutturale di acciai sottoposti a trattamenti duplex (trattamenti termochimici di diffusione seguiti da deposizione di rivestimenti in carbonio amorfo DLC)

Lo studio condotto in questa tesi ha lo scopo di esplorare possibili soluzioni alternative per aumentare la vita in esercizio di componenti per un contatto tribologico da strisciamento in motori idraulici. In particolare, per limitare l’usura e ridurre l’attrito fra i corpi a contatto, è stata presa in considerazione la deposizione di rivestimenti in carbonio amorfo idrogenato, appartenenti alla famiglia dei rivestimenti DLC (Diamond-Like Carbon), prodotti con tecnologia PACVD (Plasma Assisted Chemical Vapour Deposition), grazie alla collaborazione con la ditta STS srl presso la quale sono state prodotte ed in parte caratterizzate diverse tipologie di strati sottili a base carbonio-carbonio. Questa scelta è stata motivata dal fatto che i rivestimenti DLC combinano basso attrito ed alta resistenza ad usura, dato che l’elevata durezza (e resistenza ad usura) è data dalla presenza di un’elevata frazione di C ibridati sp3 (con struttura simil-diamante) fra loro interconnessi, mentre la tendenza al basso attrito contro la maggior parte degli antagonisti deriva dalla struttura lamellare (quindi a basso sforzo di taglio), tipica del C sp2 (simil-grafite), che permette lo scorrimento fra i piani basali. Nel corso del presente lavoro sono quindi stati presi in esame due gruppi di rivestimenti DLC, differenziati in base alla tipologia di interstrato impiegato per moderare le tensioni residue e migliorare l’adesione (CrN singolo strato o WC/C multistrato), depositati su acciaio 20MnV6 sottoposto preliminarmente a cementazione gassosa per ottenere una adeguata capacità di supporto del carico. Gli strati in esame sono stati caratterizzati dal punto di vista microstrutturale e meccanico (con prove sia di adesione e con prove di nanoindentazione). Successivamente, i materiali rivestiti sono stati sottoposti a prove tribologiche di laboratorio (block-on-ring) in condizioni di strisciamento non lubrificato, per effettuare una valutazione comparativa fra i rivestimenti ed identificare i meccanismi di usura prevalenti nelle diverse coppie tribologiche.

Chemical exfoliation of graphene and its application in organic electronics and energy storage devices

Graphene, the thinnest two-dimensional material possible, is considered as a realistic candidate for the numerous applications in electronic, energy storage and conversion devices due to its unique properties, such as high optical transmittance, high conductivity, excellent chemical and thermal stability. However, the electronic and chemical properties of graphene are highly dependent on their preparation methods. Therefore, the development of novel chemical exfoliation process which aims at high yield synthesis of high quality graphene while maintaining good solution processability is of great concern. This thesis focuses on the solution production of high-quality graphene by wet-chemical exfoliation methods and addresses the applications of the chemically exfoliated graphene in organic electronics and energy storage devices.rnPlatinum is the most commonly used catalysts for fuel cells but they suffered from sluggish electron transfer kinetics. On the other hand, heteroatom doped graphene is known to enhance not only electrical conductivity but also long term operation stability. In this regard, a simple synthetic method is developed for the nitrogen doped graphene (NG) preparation. Moreover, iron (Fe) can be incorporated into the synthetic process. As-prepared NG with and without Fe shows excellent catalytic activity and stability compared to that of Pt based catalysts.rnHigh electrical conductivity is one of the most important requirements for the application of graphene in electronic devices. Therefore, for the fabrication of electrically conductive graphene films, a novel methane plasma assisted reduction of GO is developed. The high electrical conductivity of plasma reduced GO films revealed an excellent electrochemical performance in terms of high power and energy densities when used as an electrode in the micro-supercapacitors.rnAlthough, GO can be prepared in bulk scale, large amount of defect density and low electrical conductivity are major drawbacks. To overcome the intrinsic limitation of poor quality of GO and/or reduced GO, a novel protocol is extablished for mass production of high-quality graphene by means of electrochemical exfoliation of graphite. The prepared graphene shows high electrical conductivity, low defect density and good solution processability. Furthermore, when used as electrodes in organic field-effect transistors and/or in supercapacitors, the electrochemically exfoliated graphene shows excellent device performances. The low cost and environment friendly production of such high-quality graphene is of great importance for future generation electronics and energy storage devices. rn

Emission control of InGaN nanocolumns grown by molecular-beam epitaxy on Si(111) substrates

This work studies the effect of the growth temperature on the morphology and emission characteristics of self-assembled InGaN nanocolumns grown by plasma assisted molecular beam epitaxy. Morphology changes are assessed by scanning electron microscopy, while emission is measured by photoluminescence. Within the growth temperature range of 750 to 650 °C, an increase in In incorporation for decreasing temperature is observed. This effect allows tailoring the InGaN nanocolumns emission line shape by using temperature gradients during growth. Depending on the gradient rate, span, and sign, broad emission line shapes are obtained, covering the yellow to green range, even yielding white emission

High quality InAlN single layers lattice-matched to GaN grown by molecular beam epitaxy

We report on properties of high quality ~60 nm thick InAlN layers nearly in-plane lattice-matched to GaN, grown on c-plane GaN-on-sapphire templates by plasma-assisted molecular beam epitaxy. Excellent crystalline quality and low surface roughness are confirmed by X-ray diffraction, transmission electron microscopy, and atomic force microscopy. High annular dark field observations reveal a periodic in-plane indium content variation (8 nm period), whereas optical measurements evidence certain residual absorption below the band-gap. The indium fluctuation is estimated to be +/- 1.2% around the nominal 17% indium content via plasmon energy oscillations assessed by electron energy loss spectroscopy with sub-nanometric spatial resolution.

InN/GaN heterojunction electrical behavior

Indium nitride (InN) has been the subject of intense research in recent years. Some of its most attractive features are its excellent transport properties such as its small band edge electron effective mass, high electron mobilities and peak drift velocities, and high frequency transient drift velocity oscillations [1]. These suggest enormous potential applications for InN in high frequency electronic devices. But to date the high unintentional bulk electron concentration (n~1018 cm-3) of undoped InN samples and the surface electron accumulation layer make it a hard task to create a reliable metalsemiconductor Schottky barrier. Some attempts have been made to overcome this problem by means of material oxidation [2] or deposition of insulators [3]. In this work we present a way to obtain an electrical rectification behaviour by means of heterojunction growth. Due to the big band gap differences among nitride semiconductors, it’s possible to create a structure with high band offsets. In InN/GaN heterojunctions, depending on the GaN doping, the magnitude of conduction and valence band offset are critical parameters which allow distinguishing among different electrical behaviours. The earliest estimate of the valence band offset at an InN–GaN heterojunction in a wurtzite structure was measured to be ~0.85 eV [4], while the Schottky barrier heights were determined to be ~ 1,4 eV [5].We grew In-face InN layer with varying thickness (between 150 nm and 1 mm) by plasma assisted molecular beam epitaxy (PA-MBE) on GaNntemplates (GaN/Al2O3), with temperatures ranging between 300°C and 450°C. The different doping in GaN template (Si doping, Fe doping and Mg doping) results in differences in band alignments of the two semiconductors changing electrical barriers for carriers and consequently electrical conduction behaviour. The processing of the devices includes metallization of the ohmic contacts on InN and GaN, for which we used Ti/Al/Ni/Au. Whereas an ohmic contact on InN is straightforward, the main issue was the fabrication of the contact on GaN due to the very low decomposition temperature of InN. A standard ohmic contact on GaN is generally obtained by high temperature rapid thermal annealing (RTA), typically done between 500ºC and 900ºC[6]. In this case, the limitation due to the presence of In-face InN imposes an upper limit on the temperature for the thermal annealing process and ohmic contact formation of about 450°C. We will present results on the morphology of the InN layers by X-Ray diffraction and SEM, and electrical measurements, in particular current-voltage and capacitance-voltage characteristics.

Substrate nanopatterning by e-beam lithography to growth ordered arrays of III-nitride nanodetectors, white light emitters, and solar cells

III-nitride nanorods have attracted much scientific interest during the last decade because of their unique optical and electrical properties [1,2]. The high crystal quality and the absence of extended defects make them ideal candidates for the fabrication of high efficiency opto-electronic devices such as nano-photodetectors, light-emitting diodes, and solar cells [1-3]. Nitride nanorods are commonly grown in the self-assembled mode by plasma-assisted molecular beam epitaxy (MBE) [4]. However, self-assembled nanorods are characterized by inhomogeneous heights and diameters, which render the device processing very difficult and negatively affect the electronic transport properties of the final device. For this reason, the selective area growth (SAG) mode has been proposed, where the nanorods preferentially grow with high order on pre-defined sites on a pre-patterned substrate

E-beam nanopatterning for the selective area growth of III-V nitride nanorods

GaN/InGaN nanorods have attracted much scientific interest during the last decade because of their unique optical and electrical properties [1,2]. The high crystal quality and the absence of extended defects make them ideal candidates for the fabrication of high efficiency opto-electronic devices such as nano-photodetectors, light-emitting diodes, and solar cells [1-3]. Nitrides nanorods are commonly grown in the self-assembled mode by plasma-assisted molecular beam epitaxy (MBE) [4]. However, self-assembled nanorods are characterized by inhomogeneous heights and diameters, which render the device processing very difficult and negatively affect the electronic transport properties of the final device. For this reason, the selective area growth (SAG) mode has been proposed, where the nanorods preferentially grow on pre-defined sites on a pre-patterned substrate [5].

Growth and characterization of InGaN/GaN quantum dots for violet/blue applications

We report on plasma-assisted molecular beam epitaxy growth and characterization of InGaN/GaN quantum dots (QDs) for violet/blue applications.

Crecimiento, fabricación y caracterización de heteroestructuras y nanocolumnas ordenadas basadas en nitruros del grupo III para aplicaciones sensoras

Esta memoria está basada en el crecimiento y caracterización de heteroestructuras Al(Ga)N/GaN y nanocolumnas ordenadas de GaN, y su aplicación en sensores químicos. El método de crecimiento ha sido la epitaxia de haces moleculares asistida por plasma (PAMBE). En el caso de las heteroestructuras Al(Ga)N/GaN, se han crecido barreras de distinto espesor y composición, desde AlN de 5 nm, hasta AlGaN de 35 nm. Además de una caracterización morfológica, estructural y eléctrica básica de las capas, también se han fabricado a partir de ellas dispositivos tipo HEMTs. La caracterización eléctrica de dichos dispositivos (carga y movilidad de en el canal bidimensional) indica que las mejores heteroestructuras son aquellas con un espesor de barrera intermedio (alrededor de 20 nm). Sin embargo, un objetivo importante de esta Tesis ha sido verificar las ventajas que podían tener los sensores basados en heteroestructuras AlN/GaN (frente a los típicos basados en AlGaN/GaN), con espesores de barrera muy finos (alrededor de 5 nm), ya que el canal de conducción que se modula por efecto de cambios químicos está más cerca de la superficie en donde ocurren dichos cambios químicos. De esta manera, se han utilizado los dispositivos tipo HEMTs como sensores químicos de pH (ISFETs), y se ha comprobado la mayor sensibilidad (variación de corriente frente a cambios de pH, Ids/pH) en los sensores basados en AlN/GaN frente a los basados en AlGaN/GaN. La mayor sensibilidad es incluso más patente en aplicaciones en las que no se utiliza un electrodo de referencia. Se han fabricado y caracterizado dispositivos ISFET similares utilizando capas compactas de InN. Estos sensores presentan peor estabilidad que los basados en Al(Ga)N/GaN, aunque la sensibilidad superficial al pH era la misma (Vgs/pH), y su sensibilidad en terminos de corriente de canal (Ids/pH) arroja valores intermedios entre los ISFET basados en AlN/GaN y los valores de los basados en AlGaN/GaN. Para continuar con la comparación entre dispositivos basados en Al(Ga)N/GaN, se fabricaron ISFETs con el área sensible más pequeña (35 x 35 m2), de tamaño similar a los dispositivos destinados a las medidas de actividad celular. Sometiendo los dispositivos a pulsos de voltaje en su área sensible, la respuesta de los dispositivos de AlN presentaron menor ruido que los basados en AlGaN. El ruido en la corriente para dispositivos de AlN, donde el encapsulado no ha sido optimizado, fue tan bajo como 8.9 nA (valor rms), y el ruido equivalente en el potencial superficial 38.7 V. Estos valores son más bajos que los encontrados en los dispositivos típicos para la detección de actividad celular (basados en Si), y del orden de los mejores resultados encontrados en la literatura sobre AlGaN/GaN. Desde el punto de vista de la caracterización electro-química de las superficies de GaN e InN, se ha determinado su punto isoeléctrico. Dicho valor no había sido reportado en la literatura hasta el momento. El valor, determinado por medidas de “streaming potential”, es de 4.4 y 4 respectivamente. Este valor es una importante característica a tener en cuenta en sensores, en inmovilización electrostática o en la litografía coloidal. Esta última técnica se discute en esta memoria, y se aplica en el último bloque de investigación de esta Tesis (i.e. crecimiento ordenado). El último apartado de resultados experimentales de esta Tesis analiza el crecimiento selectivo de nanocolumnas ordenadas de GaN por MBE, utilizando mascaras de Ti con nanoagujeros. Se ha estudiado como los distintos parámetros de crecimiento (i.e. flujos de los elementos Ga y N, temperatura de crecimiento y diseño de la máscara) afectan a la selectividad y a la morfología de las nanocolumnas. Se ha conseguido con éxito el crecimiento selectivo sobre pseudosustratos de GaN con distinta orientación cristalina o polaridad; templates de GaN(0001)/zafiro, GaN(0001)/AlN/Si, GaN(000-1)/Si y GaN(11-20)/zafiro. Se ha verificado experimentalmente la alta calidad cristalina de las nanocolumnas ordenadas, y su mayor estabilidad térmica comparada con las capas compactas del mismo material. Las nanocolumnas ordenadas de nitruros del grupo III tienen una clara aplicación en el campo de la optoelectrónica, principalmente para nanoemisores de luz blanca. Sin embargo, en esta Tesis se proponen como alternativa a la utilización de capas compactas o nanocolumnas auto-ensambladas en sensores. Las nanocolumnas auto-ensambladas de GaN, debido a su alta razón superficie/volumen, son muy prometedoras en el campo de los sensores, pero su amplia dispersión en dimensiones (altura y diámetro) supone un problema para el procesado y funcionamiento de dispositivos reales. En ese aspecto, las nanocolumnas ordenadas son más robustas y homogéneas, manteniendo una alta relación superficie/volumen. Como primer experimento en el ámbito de los sensores, se ha estudiado como se ve afectada la emisión de fotoluminiscencia de las NCs ordenadas al estar expuestas al aire o al vacio. Se observa una fuerte caída en la intensidad de la fotoluminiscencia cuando las nanocolumnas están expuestas al aire (probablemente por la foto-adsorción de oxigeno en la superficie), como ya había sido documentado anteriormente en nanocolumnas auto-ensambladas. Este experimento abre el camino para futuros sensores basados en nanocolumnas ordenadas. Abstract This manuscript deals with the growth and characterization of Al(Ga)N/GaN heterostructures and GaN ordered nanocolumns, and their application in chemical sensors. The growth technique has been the plasma-assisted molecular beam epitaxy (PAMBE). In the case of Al(Ga)N/GaN heterostructures, barriers of different thickness and composition, from AlN (5 nm) to AlGaN (35 nm) have been grown. Besides the basic morphological, structural and electrical characterization of the layers, HEMT devices have been fabricated based on these layers. The best electrical characteristics (larger carriers concentration and mobility in the two dimensional electron gas) are those in AlGaN/GaN heterostructures with a medium thickness (around 20 nm). However, one of the goals of this Thesis has been to verify the advantages that sensors based on AlN/GaN (thickness around 7 nm) have compared to standard AlGaN/GaN, because the conduction channel to be modulated by chemical changes is closer to the sensitive area. In this way, HEMT devices have been used as chemical pH sensors (ISFETs), and the higher sensitivity (conductance change related to pH changes, Ids/pH) of AlN/GaN based sensors has been proved. The higher sensibility is even more obvious in application without reference electrode. Similar ISFETs devices have been fabricated based on InN compact layers. These devices show a poor stability, but its surface sensitivity to pH (Vgs/pH) and its sensibility (Ids/pH) yield values between the corresponding ones of AlN/GaN and AlGaN/GaN heterostructures. In order to a further comparison between Al(Ga)N/GaN based devices, ISFETs with smaller sensitive area (35 x 35 m2), similar to the ones used in cellular activity record, were fabricated and characterized. When the devices are subjected to a voltage pulse through the sensitive area, the response of AlN based devices shows lower noise than the ones based on AlGaN. The noise in the current of such a AlN based device, where the encapsulation has not been optimized, is as low as 8.9 nA (rms value), and the equivalent noise to the surface potential is 38.7 V. These values are lower than the found in typical devices used for cellular activity recording (based on Si), and in the range of the best published results on AlGaN/GaN. From the point of view of the electrochemical characterization of GaN and InN surfaces, their isoelectric point has been experimentally determined. Such a value is the first time reported for GaN and InN surfaces. These values are determined by “streaming potential”, being pH 4.4 and 4, respectively. Isoelectric point value is an important characteristic in sensors, electrostatic immobilization or in colloidal lithography. In particular, colloidal lithography has been optimized in this Thesis for GaN surfaces, and applied in the last part of experimental results (i.e. ordered growth). The last block of this Thesis is focused on the selective area growth of GaN nanocolumns by MBE, using Ti masks decorated with nanoholes. The effect of the different growth parameters (Ga and N fluxes, growth temperature and mask design) is studied, in particular their impact in the selectivity and in the morphology of the nanocolumns. Selective area growth has been successful performed on GaN templates with different orientation or polarity; GaN(0001)/sapphire, GaN(0001)/AlN/Si, GaN(000- 1)/Si and GaN(11-20)/sapphire. Ordered nanocolumns exhibit a high crystal quality, and a higher thermal stability (lower thermal decomposition) than the compact layers of the same material. Ordered nanocolumns based on III nitrides have a clear application in optoelectronics, mainly for white light nanoemitters. However, this Thesis proposes them as an alternative to compact layers and self-assembled nanocolumns in sensor applications. Self-assembled GaN nanocolumns are very appealing for sensor applications, due to their large surface/volume ratio. However, their large dispersion in heights and diameters are a problem in terms of processing and operation of real devices. In this aspect, ordered nanocolumns are more robust and homogeneous, keeping the large surface/volume ratio. As first experimental evidence of their sensor capabilities, ordered nanocolumns have been studied regarding their photoluminiscence on air and vacuum ambient. A big drop in the intensity is observed when the nanocolumns are exposed to air (probably because of the oxygen photo-adsortion), as was already reported in the case of self-assembled nanocolumns. This opens the way to future sensors based on ordered III nitrides nanocolumns.

E-beam nano-patterning for the ordered growth of GaN/InGaN nanorods

E-beam lithography was used to pattern a titanium mask on a GaN substrate with ordered arrays of nanoholes. This patterned mask served as a template for the subsequent ordered growth of GaN/InGaN nanorods by plasma-assisted molecular beam epitaxy. The mask patterning process was optimized for several holes configurations. The smallest holes were 30 nm in diameter with a pitch (center-to-center distance) of 100 nm only. High quality masks of several geometries were obtained that could be used to grow ordered GaN/InGaN nanorods with full selectivity (growth localized inside the nanoholes only) over areas of hundreds of microns. Although some parasitic InGaN growth occurred between the nanorods during the In incorporation, transmission electron microscopy and photoluminescence measurements demonstrated that these ordered nanorods exhibit high crystal quality and reproducible optical properties.

Advances on MBE selective area growth of III-nitride nanostructures: from nanoLEDs to pseudo substrates

The aim of this work is to provide an overview on the recent advances in the selective area growth (SAG) of (In)GaN nanostructures by plasma assisted molecular beam epitaxy, focusing on their potential as building blocks for next generation LEDs. The first three sections deal with the basic growth mechanisms of GaN SAG and the emission control in the entire ultraviolet to infrared range, including approaches for white light emission, using InGaN disks and thick segments on axial nanocolumns. SAG of axial nanostructures is eveloped on both GaN/sapphire templates and GaN-buffered Si(111). As an alternative to axial nanocolumns, section 4 reports on the growth and characterization of InGaN/GaN core-shell structures on an ordered array of top-down patterned GaN microrods. Finally, section 5 reports on the SAG of GaN, with and without InGaN insertion, on semi-polar (11-22) and non-polar (11-20) templates. Upon SAG the high defect density present in the templates is strongly reduced as indicated by a dramatic improvement of the optical properties. In the case of SAG on nonpolar (11-22) templates, the formation of nanostructures with a low aspect ratio took place allowing for the fabrication of high-quality, non-polar GaN pseudo-templates by coalescence of these nanostructures.

Self assembled and ordered group III nitride nanocolumnar structures for light emitting applications

El objetivo de este trabajo es un estudio profundo del crecimiento selectivo de nanoestructuras de InGaN por epitaxia de haces moleculares asistido por plasma, concentrandose en el potencial de estas estructuras como bloques constituyentes en LEDs de nueva generación. Varias aproximaciones al problema son discutidas; desde estructuras axiales InGaN/GaN, a estructuras core-shell, o nanoestructuras crecidas en sustratos con orientaciones menos convencionales (semi polar y no polar). La primera sección revisa los aspectos básicos del crecimiento auto-ensamblado de nanocolumnas de GaN en sustratos de Si(111). Su morfología y propiedades ópticas son comparadas con las de capas compactas de GaN sobre Si(111). En el caso de las columnas auto-ensambladas de InGaN sobre Si(111), se presentan resultados sobre el efecto de la temperatura de crecimiento en la incorporación de In. Por último, se discute la inclusión de nanodiscos de InGaN en las nanocolumnas de GaN. La segunda sección revisa los mecanismos básicos del crecimiento ordenado de nanoestructuras basadas en GaN, sobre templates de GaN/zafiro. Aumentando la relación III/V localmente, se observan cambios morfológicos; desde islas piramidales, a nanocolumnas de GaN terminadas en planos semipolares, y finalmente, a nanocolumnas finalizadas en planos c polares. Al crecer nanodiscos de InGaN insertados en las nanocolumnas de GaN, las diferentes morfologias mencionadas dan lugar a diferentes propiedades ópticas de los nanodiscos, debido al diferente carácter (semi polar o polar) de los planos cristalinos involucrados. La tercera sección recoge experimentos acerca de los efectos que la temperatura de crecimiento y la razón In/Ga tienen en la morfología y emisión de nanocolumnas ordenadas de InGaN crecidas sobre templates GaN/zafiro. En el rango de temperaturas entre 650 y 750 C, la incorporacion de In puede modificarse bien por la temperatura de crecimiento, o por la razón In/Ga. Controlar estos factores permite la optimización de la longitud de onda de emisión de las nanocolumnas de InGaN. En el caso particular de la generación de luz blanca, se han seguidos dos aproximaciones. En la primera, se obtiene emisión amarilla-blanca a temperatura ambiente de nanoestructuras donde la región de InGaN consiste en un gradiente de composiciones de In, que se ha obtenido a partir de un gradiente de temperatura durante el crecimiento. En la segunda, el apilamiento de segmentos emitiendo en azul, verde y rojo, consiguiendo la integración monolítica de estas estructuras en cada una de las nanocolumnas individuales, da lugar a emisores ordenados con un amplio espectro de emisión. En esta última aproximación, la forma espectral puede controlarse con la longitud (duración del crecimiento) de cada uno de los segmentos de InGaN. Más adelante, se presenta el crecimiento ordenado, por epitaxia de haces moleculares, de arrays de nanocolumnas que son diodos InGaN/GaN cada una de ellas, emitiendo en azul (441 nm), verde (502 nm) y amarillo (568 nm). La zona activa del dispositivo consiste en una sección de InGaN, de composición constante nominalmente y longitud entre 250 y 500 nm, y libre de defectos extendidos en contraste con capas compactas de InGaN de similares composiciones y espesores. Los espectros de electroluminiscencia muestran un muy pequeño desplazamiento al azul al aumentar la corriente inyectada (desplazamiento casi inexistente en el caso del dispositivo amarillo), y emisiones ligeramente más anchas que en el caso del estado del arte en pozos cuánticos de InGaN. A continuación, se presenta y discute el crecimiento ordenado de nanocolumnas de In(Ga)N/GaN en sustratos de Si(111). Nanocolumnas ordenadas emitiendo desde el ultravioleta (3.2 eV) al infrarrojo (0.78 eV) se crecieron sobre sustratos de Si(111) utilizando una capa compacta (“buffer”) de GaN. La morfología y eficiencia de emisión de las nanocolumnas emitiendo en el rango espectral verde pueden ser mejoradas ajustando las relaciones In/Ga y III/N, y una eficiencia cuántica interna del 30% se deriva de las medidas de fotoluminiscencia en nanocolumnas optimizadas. En la siguiente sección de este trabajo se presenta en detalle el mecanismo tras el crecimiento ordenado de nanocolumnas de InGaN/GaN emitiendo en el verde, y sus propiedades ópticas. Nanocolumnas de InGaN/GaN con secciones largas de InGaN (330-830 nm) se crecieron tanto en sustratos GaN/zafiro como GaN/Si(111). Se encuentra que la morfología y la distribución espacial del In dentro de las nanocolumnas dependen de las relaciones III/N e In/Ga locales en el frente de crecimiento de las nanocolumnas. La dispersión en el contenido de In entre diferentes nanocolumnas dentro de la misma muestra es despreciable, como indica las casi identicas formas espectrales de la catodoluminiscencia de una sola nanocolumna y del conjunto de ellas. Para las nanocolumnas de InGaN/GaN crecidas sobre GaN/Si(111) y emitiendo en el rango espectral verde, la eficiencia cuántica interna aumenta hasta el 30% al disminuir la temperatura de crecimiento y aumentar el nitrógeno activo. Este comportamiento se debe probablemente a la formación de estados altamente localizados, como indica la particular evolución de la energía de fotoluminiscencia con la temperatura (ausencia de “s-shape”) en muestras con una alta eficiencia cuántica interna. Por otro lado, no se ha encontrado la misma dependencia entre condiciones de crecimiento y efiencia cuántica interna en las nanoestructuras InGaN/GaN crecidas en GaN/zafiro, donde la máxima eficiencia encontrada ha sido de 3.7%. Como alternativa a las nanoestructuras axiales de InGaN/GaN, la sección 4 presenta resultados sobre el crecimiento y caracterización de estructuras core-shell de InGaN/GaN, re-crecidas sobre arrays de micropilares de GaN fabricados por ataque de un template GaN/zafiro (aproximación top-down). El crecimiento de InGaN/GaN es conformal, con componentes axiales y radiales en el crecimiento, que dan lugar a la estructuras core-shell con claras facetas hexagonales. El crecimiento radial (shell) se ve confirmado por medidas de catodoluminiscencia con resolución espacial efectuadas en un microscopio electrónico de barrido, asi como por medidas de microscopía de transmisión de electrones. Más adelante, el crecimiento de micro-pilares core-shell de InGaN se realizó en pilares GaN (cores) crecidos selectivamente por epitaxia de metal-orgánicos en fase vapor. Con el crecimiento de InGaN se forman estructuras core-shell con emisión alrededor de 3 eV. Medidas de catodoluminiscencia resuelta espacialmente indican un aumento en el contenido de indio del shell en dirección a la parte superior del pilar, que se manifiesta en un desplazamiento de la emisión de 3.2 eV en la parte inferior, a 3.0 eV en la parte superior del shell. Este desplazamiento está relacionado con variaciones locales de la razón III/V en las facetas laterales. Finalmente, se demuestra la fabricación de una estructura pin basada en estos pilares core-shell. Medidas de electroluminiscencia resuelta espacialmente, realizadas en pilares individuales, confirman que la electroluminiscencia proveniente del shell de InGaN (diodo lateral) está alrededor de 3.0 eV, mientras que la emisión desde la parte superior del pilar (diodo axial) está alrededor de 2.3 eV. Para finalizar, se presentan resultados sobre el crecimiento ordenado de GaN, con y sin inserciones de InGaN, en templates semi polares (GaN(11-22)/zafiro) y no polares (GaN(11-20)/zafiro). Tras el crecimiento ordenado, gran parte de los defectos presentes en los templates originales se ven reducidos, manifestándose en una gran mejora de las propiedades ópticas. En el caso de crecimiento selectivo sobre templates con orientación GaN(11-22), no polar, la formación de nanoestructuras con una particular morfología (baja relación entre crecimiento perpedicular frente a paralelo al plano) permite, a partir de la coalescencia de estas nanoestructuras, la fabricación de pseudo-templates no polares de GaN de alta calidad. ABSTRACT The aim of this work is to gain insight into the selective area growth of InGaN nanostructures by plasma assisted molecular beam epitaxy, focusing on their potential as building blocks for next generation LEDs. Several nanocolumn-based approaches such as standard axial InGaN/GaN structures, InGaN/GaN core-shell structures, or InGaN/GaN nanostructures grown on semi- and non-polar substrates are discussed. The first section reviews the basics of the self-assembled growth of GaN nanocolumns on Si(111). Morphology differences and optical properties are compared to those of GaN layer grown directly on Si(111). The effects of the growth temperature on the In incorporation in self-assembled InGaN nanocolumns grown on Si(111) is described. The second section reviews the basic growth mechanisms of selectively grown GaNbased nanostructures on c-plane GaN/sapphire templates. By increasing the local III/V ratio morphological changes from pyramidal islands, to GaN nanocolumns with top semi-polar planes, and further to GaN nanocolumns with top polar c-planes are observed. When growing InGaN nano-disks embedded into the GaN nanocolumns, the different morphologies mentioned lead to different optical properties, due to the semipolar and polar nature of the crystal planes involved. The third section reports on the effect of the growth temperature and In/Ga ratio on the morphology and light emission characteristics of ordered InGaN nanocolumns grown on c-plane GaN/sapphire templates. Within the growth temperature range of 650 to 750oC the In incorporation can be modified either by the growth temperature, or the In/Ga ratio. Control of these factors allows the optimization of the InGaN nanocolumns light emission wavelength. In order to achieve white light emission two approaches are used. First yellow-white light emission can be obtained at room temperature from nanostructures where the InGaN region is composition-graded by using temperature gradients during growth. In a second approach the stacking of red, green and blue emitting segments was used to achieve the monolithic integration of these structures in one single InGaN nanocolumn leading to ordered broad spectrum emitters. With this approach, the spectral shape can be controlled by changing the thickness of the respective InGaN segments. Furthermore the growth of ordered arrays of InGaN/GaN nanocolumnar light emitting diodes by molecular beam epitaxy, emitting in the blue (441 nm), green (502 nm), and yellow (568 nm) spectral range is reported. The device active region, consisting of a nanocolumnar InGaN section of nominally constant composition and 250 to 500 nm length, is free of extended defects, which is in strong contrast to InGaN layers (planar) of similar composition and thickness. Electroluminescence spectra show a very small blue shift with increasing current, (almost negligible in the yellow device) and line widths slightly broader than those of state-of-the-art InGaN quantum wells. Next the selective area growth of In(Ga)N/GaN nanocolumns on Si(111) substrates is discussed. Ordered In(Ga)N/GaN nanocolumns emitting from ultraviolet (3.2 eV) to infrared (0.78 eV) were then grown on top of GaN-buffered Si substrates. The morphology and the emission efficiency of the In(Ga)N/GaN nanocolumns emitting in the green could be substantially improved by tuning the In/Ga and total III/N ratios, where an estimated internal quantum efficiency of 30 % was derived from photoluminescence data. In the next section, this work presents a study on the selective area growth mechanisms of green-emitting InGaN/GaN nanocolumns and their optical properties. InGaN/GaN nanocolumns with long InGaN sections (330-830nm) were grown on GaN/sapphire and GaN-buffered Si(111). The nanocolumn’s morphology and spatial indium distribution is found to depend on the local group (III)/N and In/Ga ratios at the nanocolumn’s top. A negligible spread of the average indium incorporation among different nanostructures is found as indicated by similar shapes of the cathodoluminescence spectra taken from single nanocolumns and ensembles of nanocolumns. For InGaN/GaN nanocolumns grown on GaN-buffered Si(111), all emitting in the green spectral range, the internal quantum efficiency increases up to 30% when decreasing growth temperature and increasing active nitrogen. This behavior is likely due to the formation of highly localized states, as indicated by the absence of a complete s-shape behavior of the PL peak position with temperature (up to room temperature) in samples with high internal quantum efficiency. On the other hand, no dependence of the internal quantum efficiency on the growth conditions is found for InGaN/GaN nanostructures grown on GaN/sapphire, where the maximum achieved efficiency is 3.7%. As alternative to axial InGaN/GaN nanostructures, section 4 reports on the growth and characterization of InGaN/GaN core-shell structures on an ordered array of top-down patterned GaN microrods etched from a GaN/sapphire template. Growth of InGaN/GaN is conformal, with axial and radial growth components leading to core-shell structures with clear hexagonal facets. The radial InGaN growth (shell) is confirmed by spatially resolved cathodoluminescence performed in a scanning electron microscopy as well as in scanning transmission electron microscopy. Furthermore the growth of InGaN core-shell micro pillars using an ordered array of GaN cores grown by metal organic vapor phase epitaxy as a template is demonstrated. Upon InGaN overgrowth core-shell structures with emission at around 3.0 eV are formed. With spatially resolved cathodoluminescence, an increasing In content towards the pillar top is found to be present in the InGaN shell, as indicated by a shift of CL peak position from 3.2 eV at the shell bottom to 3.0 eV at the shell top. This shift is related to variations of the local III/V ratio at the side facets. Further, the successful fabrication of a core-shell pin diode structure is demonstrated. Spatially resolved electroluminescence measurements performed on individual micro LEDs, confirm emission from the InGaN shell (lateral diode) at around 3.0 eV, as well as from the pillar top facet (axial diode) at around 2.3 eV. Finally, this work reports on the selective area growth of GaN, with and without InGaN insertion, on semi-polar (11-22) and non-polar (11-20) templates. Upon SAG the high defect density present in the GaN templates is strongly reduced as indicated by TEM and a dramatic improvement of the optical properties. In case of SAG on non-polar (11-22) templates the formation of nanostructures with a low aspect ratio took place allowing for the fabrication of high-quality, non-polar GaN pseudo-templates by coalescence of the nanostructures.