Resumo:
One of the most important properties of artificial teeth is the abrasion wear resistance, which is determinant in the maintenance of the rehabilitation's occlusal pattern. OBJECTIVES: This in vitro study aims to evaluate the abrasion wear resistance of 7 brands of artificial teeth opposed to two types of antagonists. MATERIAL AND METHODS: Seven groups were prepared with 12 specimens each (BIOLUX & BL, TRILUX & TR, BLUE DENT & BD, BIOCLER & BC, POSTARIS & PO, ORTHOSIT & OR, GNATHOSTAR & GN), opposed to metallic (M & nickel-chromium alloy), and to composite antagonists (C & Solidex indirect composite). A mechanical loading device was used (240 cycles/min, 4 Hz speed, 10 mm antagonist course). Initial and final contours of each specimen were registered with aid of a profile projector (20x magnification). The linear difference between the two profiles was measured and the registered values were subjected to ANOVA and Tukey's test. RESULTS: Regarding the antagonists, only OR (M = 10.45 ± 1.42 µm and C = 2.77 ± 0.69 µm) and BC (M = 6.70 ± 1.37 µm and C = 4.48 ± 0.80 µm) presented statistically significant differences (p < 0.05). Best results were obtained with PO (C = 2.33 ± 0.91 µm and M = 1.78 ± 0.42 µm), followed by BL (C = 3.70 ± 1.32 µm and M = 3.70 ± 0.61 µm), statistically similar for both antagonists (p>0.05). Greater result variance was obtained with OR, which presented the worse results opposed to Ni-Cr (10.45 ± 1.42 µm), and results similar to the best ones against composite (2.77 ± 0.69 µm). CONCLUSIONS: Within the limitations of this study, it may be concluded that the antagonist material is a factor of major importance to be considered in the choice of the artificial teeth to be used in the prosthesis.
Resumo:
Objective: The purpose of this study was to compare the dental movement that occurs during the processing of maxillary complete dentures with 3 different base thicknesses, using 2 investment methods, and microwave polymerization.Methods: A sample of 42 denture models was randomly divided into 6 groups (n = 7), with base thicknesses of 1.25, 2.50, and 3.75 mm and gypsum or silicone flask investment. Points were demarcated on the distal surface of the second molars and on the back of the gypsum cast at the alveolar ridge level to allow linear and angular measurement using AutoCAD software. The data were subjected to analysis of variance with double factor, Tukey test and Fisher (post hoc).Results: Angular analysis of the varying methods and their interactions generated a statistical difference (P = 0.023) when the magnitudes of molar inclination were compared. Tooth movement was greater for thin-based prostheses, 1.25 mm (-0.234), versus thick 3.75 mm (0.2395), with antagonistic behavior. Prosthesis investment with silicone (0.053) showed greater vertical change compared with the gypsum investment (0.032). There was a difference between the point of analysis, demonstrating that the changes were not symmetric.Conclusions: All groups evaluated showed change in the position of artificial teeth after processing. The complete denture with a thin base (1.25 mm) and silicone investment showed the worst results, whereas intermediate thickness (2.50 mm) was demonstrated to be ideal for the denture base.
Resumo:
In this study the effects of thermal and mechanical cycles on the hardness and roughness of artificial teeth were evaluated. Materials and Methods:Specimens were prepared and stored in distilled water at 37ºC for 48 hours (n=10).The hardness and roughness readings were made in the following time intervals, according to each group:G1: after specimen storage in distilled water at 37°C for 48 hours; G2: after 600.000 constant mechanical cycles; G3: after 1.200.000 constant mechanical cycles; G4: after 2.500 thermalcycling baths, alternated between hot water (55°C) and cold water (5°C) and G5: after 5.000 thermalcycling baths, alternated between hot water (55°C) and cold water (5°C). After cycling and storage procedures, the specimens of each group were submittedto surface roughness and hardness readouts. Statistical evaluation was performed by three-way analysis of variance, complemented by the Tukey multiple comparisons of means test. The level of significance adopted was 5%. There was no significant difference between G1, G4 and G5 as regards mean roughness of different brands of artificial teeth. Groups G2 and G3 showed higher mean roughness values, and generally equivalent values in all time intervals, except for Trilux (G3> G2). Significant differences in hardness values were observed in different brands of artificial teeth, and differences in values after thermal and mechanical cycling. In conclusion, our findings suggest that thermal cyclingdid not change the roughness of the artificial teeth tested, but after the mechanical cycling the roughness values increased. Thermal and mechanical cycling influenced the hardness of the artificial teeth tested.
Resumo:
To evaluate the bond strength between two types of acrylic resin teeth and a microwave denture base resin after immersion in disinfectant solutions for 180 days. Eighty specimens made of acrylic resin teeth (Biotone and Biotone IPN) attached to a microwave polymerized denture base resin (Nature-Cryl MC) were divided into eight groups (n = 10) according to the treatment (distilled water-control, 2% chlorhexidine digluconate, 1% sodium hypochlorite and sodium perborate solution-Corega Tabs). The shear strength tests (MPa) were carried out using a universal testing machine with a 0.5 mm/min speed. Data analysis was performed using ANOVA and multiple comparison Student-Newman-Keuls post hoc test (α = 0.05). Biotone IPN showed similar results among the groups (distilled water, 8.25 ± 1.81 MPa; chlorhexidine, 7.81 ± 3.34 MPa; hypochlorite, 7.75 ± 3.72 MPa; and Corega Tabs, 7.58 ± 2.27 MPa, whereas Biotone showed significantly lower shear bond strength values for the groups immersed in Corega Tabs (5.25 ± 3.27 MPa) and chlorhexidine (6.08 ± 2.35 MPa). Soaking the dentures in 1% sodium hypochlorite could be recommended as a disinfectant solution for dentures fabricated with conventional acrylic resin denture teeth and microwave denture base resin. For dentures fabricated with IPN teeth and microwave denture base resin, all the soaking solutions evaluated in this study could be suggested to denture wearers.
Resumo:
Mode of access: Internet.
Resumo:
Aim: To evaluate, in vitro, the effect of brushing with a Ricinus communis -based experimental toothpaste on color stability and surface roughness of artificial teeth. Methods: Ninety artificial teeth (maxillary central incisors) in different shades, light and dark (NatusDent Triple Pressing, Dentbras) were used. Initial color (Spectrophotometer Easyshade, VITA) and surface roughness (Rugosimeter Surfcorder SE 1700, Kosakalab) readouts were performed. After baseline measurements, samples were assigned to 10 groups (n=9) according to the artificial tooth shade and type of toothpaste used during the mechanical brushing test (Pepsodent, MAVTEC): Sorriso Dentes Brancos – SDB, Colgate Luminous White - CLW (Colgate-Palmolive), Close up White Now - CWN (Unilever), Trihydral - THL (Perland Pharmacos) and Ricinus communis - RCE (Experimental). After 29,200 cycles of brushing, corresponding to 2 years of brushing by a healthy individual, new color and roughness readouts of the specimens were performed. Data (before and after the tests) were statistically analyzed (2-way repeated measures ANOVA, Tukey, p<0.05). Results: RCE toothpaste produced the greatest color stability for dark tooth shade and the second best color stability for light tooth shade. For surface roughness alteration, there was no difference (p>0.05) for any tested toothpaste regardless of tooth shade. Conclusions: The experimental Ricinus communis toothpaste did not cause color and surface roughness alteration in the artificial teeth, and it may be considered a suitable option for denture cleaning.
Resumo:
STATEMENT OF PROBLEM: Wear of methacrylate artificial teeth resulting in vertical loss is a problem for both dentists and patients. PURPOSE: The purpose of this study was to quantify wear of artificial teeth in vivo and to relate it to subject and tooth variables. MATERIAL AND METHODS: Twenty-eight subjects treated with complete dentures received 2 artificial tooth materials (polymethyl methacrylate (PMMA)/double-cross linked PMMA fillers; 35%/59% (SR Antaris DCL, SR Postaris DCL); experimental 48%/46%). At baseline and after 12 months, impressions of the dentures were poured with improved stone. After laser scanning, the casts were superimposed and matched. Maximal vertical loss (mm) and volumetric loss (mm(3)) were calculated for each tooth and log-transformed to reduce variability. Volumetric loss was related to the occlusally active surface area. Linear mixed models were used to study the influence of the factors jaw, tooth, and material on adjusted (residual) wear values (alpha=.05). RESULTS: Due to drop outs (n=5) and unmatchable casts (n=3), 69% of all teeth were analyzed. Volumetric loss had a strong linear relationship to surface area (P<.001); this was less pronounced for vertical loss (P=.004). The factor showing the highest influence was the subject. Wear was tooth dependent (increasing from incisors to molars). However, these differences diminished once the wear rates were adjusted for occlusal area, and only a few remained significant (anterior versus posterior maxillary teeth). Another influencing factor was the age of the subject. CONCLUSIONS: Clinical wear of artificial teeth is higher than previously measured or expected. The presented method of analyzing wear of artificial teeth using a laser-scanning device seemed suitable.
Resumo:
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
Resumo:
Objectives: To evaluate the use of the center of the incisive papilla as a guide for the selection of the proper width of maxillary dentures in 4 racial groups. Method and Materials: One hundred sixty stone casts were obtained from impressions of the maxillary arch of white, black, mixed, and Asian subjects. The occlusal surfaces of the casts were photocopied and the images placed on a digitizer. The most anterior and posterior points of the papilla and cusp tips of the canines were digitized. Dentofacial Planner Plus software was used to calculate the distance from a line passing through the cusp tips of the canines to the center of the papilla, defined as the midpoint of the anterior and posterior points of the papilla. The selection error (in millimeters) due to the clinical application of the method of the incisive papilla was calculated and analyzed. Results: In all studied racial groups, there was no coincidence between the center of the incisive papilla and the canine line. The utilization of the center of the papilla would lead to the selection of wider artificial teeth. In 24.9% of the white, 19.3% of the mixed, 32.9% of the black, and 15.5% of the Asian populations, errors greater than 4 mm would be present with the utilization of the papilla. Conclusion: The method of the center of the incisive papilla is not accurate, but may aid in initial artificial teeth selection for the racial groups studied. (Quintessence Int 2008;39:841-845)
Resumo:
Purpose: To determine whether intercommissural width is a reliable guide for the selection of maxillary denture teeth width. Materials and Methods: Casts were made of 160 subjects from 4 different racial groups. Locations of intercommissural width landmarks (the corners of the mouth) were made on the subjects and transferred to the casts. The distances between the corners of the mouth and the distal of the canines were measured on the casts and compared. Results: A weak correlation was found between the distal of the canines and the distance between the corners of the mouth in the 4 racial groups. Conclusion: The use of the corners of the mouth for the selection of artificial teeth is generally inaccurate.
Resumo:
Purpose: Selecting artificial teeth for edentulous patients is difficult when pre-extraction records are not available. Various guidelines have been suggested for determining the width of the maxillary anterior denture teeth. This study was undertaken to evaluate the use of the nasal width as a guide for the selection of proper width maxillary anterior denture teeth in four racial groups of the Brazilian population. Materials and Methods: One hundred and sixty subjects (40 Whites, 40 Mulattos, 40 Blacks, and 40 Asians) were selected. Using a sliding caliper, the nasal width and the intercanine distance were measured. The Pearson product-moment correlation coefficient was used to determine the relationship between the above measurements. A prediction was made of the percentage of subjects of the White, Mulatto, Black, and Asian populations in which the selection error due to the clinical application of the method of the nasal width would be within 0 to 2 mm, within 2 to 4 mm, and greater than 4 mm. Results: The four racial groups showed a weak correlation between the intercanine distance and the nasal width. In 39.7% of the White, 55.7% of the Mulatto, 81.9% of the Black, and 48.2% of the Asian populations, errors greater than 4 mm would be present with the use of the nasal width. Conclusions: The correlation found between the intercanine distance and the nasal width was not high enough to be used as a predictive factor. The relationship between natural tooth width and artificial tooth width as predicted by the nasal width showed that the nasal width method is not accurate for all the studied groups. Copyright © 2006 by The American College of Prosthodontists.
Resumo:
This study evaluated Knoop hardness, surface roughness and color alteration of artificial teeth for dentures after immersion in water, 1% sodium hypochlorite and an experimental solution of 2% Ricinus communis (RC). Thirty specimens of Vipi, Biolux and Trilux were analyzed. Tests of Knoop hardness, surface roughness and color alteration were conducted immediately after specimen preparation (T0) and after two immersion protocols for 15 days (ΔT15) and 183 days (ΔT183). Data variation (ΔT) were subjected to ANOVA and Tukey's test (p<0.05). At ΔT15, Vipi presented hardness increase and Biolux presented the highest variation (p=0.01). RC caused the highest increase in hardness (p=0) and the lowest increase (p=0.005) in roughness. Biolux presented the lowest color alteration (p =0). At ΔT183, Trilux underwent the highest hardness variation (p=0). Biolux presented an increase in roughness (p=0). There was no significant differences in color alteration among the artificial teeth (p=0.06) and among solutions (p=0.08) after 183 days of immersion. All solutions (distilled water, 1% sodium hypochlorite and 2% RC) caused alterations on the analyzed properties. Both immersion protocols caused alterations on the analyzed properties.
Resumo:
There is a lack of clinical studies evaluating techniques of functional impression for partially edentulous arches. The aim of this double-blind non-randomized controlled clinical trial was to compare the efficacy of altered cast impression (ACI) and direct functional impression (DFI) techniques. The efficacy was evaluated regarding the number of occlusal units on denture teeth, mucosa integrity at 24-hour follow-up and denture base extension. The sample included 51 patients (female and male) with mean age of 58.96 years treated at Dental Department of UFRN. The patients, exhibiting edentulous maxilla and mandibular Kennedy class I, were divided into two groups (group ACI, n=29; group DFI, n=22). Clinical evaluation was based on the number of occlusal units on natural and/or artificial teeth, mucosa integrity at 24-hour follow-up, and denture base extension. Statistical analysis was conducted using the software SPSS 17.0® (SPSS Inc., Chicago, Illinois). Student T-test was used to reveal association between number of occlusal units and impression technique while chi-square test showed association between mucosa integrity and impression technique. Fischer s exact test was applied for association between denture base extension and impression technique at 95% level of significance. No significant difference was observed between the groups regarding number of occlusal units, mucosa integrity and denture base extension. The altered cast technique did not provide significant improvement in comparison to the direct technique when the number of occlusal units, mucosa integrity and denture base extension