Microstructural and electric properties of bismuth-layered structured ceramics - SrBi2(Ta1-xNbx)O-9

Ceramic samples of SrBi2(Nb1-xTax)O-9 (0 less than or equal to x less than or equal to 1) were prepared by the solid state reaction method in order to investigate their structural and electrical features as well as obtain useful information to improve the properties of SrBi2(Nb1-xTax)O-9 as a thin film. The X-ray diffraction patterns and the scanning electronic microscopy photomicrographs show no secondary phases but the formation of a solid-state solution for all the composition. The ac conductivity of the samples, measured at 25 degreesC and 100 kHz frequency, decreases with the increase of Ta content. Such results were explained by intrinsic conductivity of pure components.

Synthesis and characterization of CaBi4Ti4O15 thin films annealed by microwave and conventional furnaces

CaBi4Ti4O15 thin films were deposited by the polymeric precursor method and crystallized in a domestic microwave oven and conventional furnace. The films obtained for microwave energy are well-adhered, homogeneous and with good specularity, when treated at 700 degrees C for 10 min. The microstructure and the structure of the films can be tuned by adjusting the crystallization conditions. When microwave oven is employed, the films presented bigger grains with mean grain size around 80 nm. For comparison, films were also prepared by the conventional furnace at 700 degrees C for 2 h. (C) 2007 Elsevier Masson SAS. All rights reserved.

Structural and electrical properties of SrBi2Nb2O9 thin films prepared by chemical aqueous solution at low temperature

SrBi2Nb2O9 (SBN) thin films were prepared by the polymeric precursors method and deposited by dip coating onto Pt/Ti/SiO2/Si(100) substrates. The dip-coated films were specular and crack-free and crystallized during firing at 700 degrees C. Microstructure and morphological evaluation were followed by grazing incident X-ray diffraction (GIXRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM). The films exhibited somewhat porous grain structure with rounded grains of about 100 nm. For the electrical measurements, gold electrodes of 300 mu m in diameter were sputter deposited on the top surface, forming a metal-ferroelectric-metal (MFM) configuration. The remanent polarization (P-r) and coercive field (E-c) were 5.6 mu C/cm(2) and 100 kV/cm, respectively. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Preparation and characterization of nanosized SrBi2Nb2O9 powder by the combustion synthesis

This work presents the preparation of SrBi2Nb2O9 (SBN) directly by the combustion synthesis. Strontium nitrate, niobium ammonium oxalate (NH4H2[NbO-(C2O4)(3)].3H(2)O) and bismuth oxide were used as oxidant reactants and urea as fuel. The influence of the fuel was evaluated by the addition of different fuel amounts (50%, 100%, 200% and 300%), 100% being the stoichiometric proportion. The XRD patterns showed that the SBN perovskite crystallized as the majority phase. The as-synthesized stoichiometric powder presented a specific surface area of around 13 m(2)/g and a mean grain size of around 16 nm. Dilatometric measurements showed that the maximum sintering rate occurs at 1275degreesC. The determination of the ferroparaelectric transition showed a Curie temperature (T-c) of 429degreesC. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Estudo das propriedades físicas de sistemas ferroelétricos com estruturas tipo Aurivillius

Pós-graduação em Ciência dos Materiais - FEIS

Structure and ferro/piezoelectric properties of SrBi(4)Ti(4)O(15) films deposited on TiO(2) buffer layer

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structure and Properties of Barium Bismuth Titanate Prepared by Mechanochemical Synthesis

Bi4Ti4O15 [BBT], a member of Aurivillius bismuth-based layer-structure perovskites, was prepared from stoichiometric amounts of BaTiO3 [BT] and Bi4Ti3O12 [BIT] obtained via mechanochemical synthesis. Mechanochemical synthesis was performed in air atmosphere in a planetary ball mill. BBT ceramics were sintered at 1100C for 4 h without pre-calcination step within heating rate 10C/min. The formation of phase and crystal structure of BT, BIT and BBT were approved using X-ray analysis. The morphology of obtained powders and microstructure were exhamined using scanning electron microscopy. The electrical properties of sintered samples were carried out.