Morphological evolution of tin oxide nanobelts after phase transition

This article reports a study of the thermal stability and morphological changes in tin oxide nanobelts grown in the orthorhombic SnO phase. The nanobelts were heat-treated in a differential scanning calorimetry (DSC) furnace at 800 degrees C for I It in argon, oxygen, or synthetic air atmospheres. The samples were then characterized by DSC, X-ray diffraction (XRD), high resolution transmission electron microscopy (HRTEM), and high resolution field emission scanning electron microscopy (FE-SEM). The results confirmed that the orthorhombic SnO phase is thermodynamically unstable, causing the belts to transform into the SnO2 phase when heat-treated. During the phase transition, if oxygen is available in the furnace atmosphere, nanofibers grow at the edge of nanobelts at about 50 degrees of the belts' growth direction, while particles grow on the belt surface in the absence of oxygen. Although the decomposition process reduces the nanobelt cell volume by 22%, most belts remain monocrystalline after the heat treatment. The results confirm that phase transition is a decomposition process, which explains the morphological changes in the belts based on metallic tin generated in the process.

Tin-doped indium oxide nanobelts grown by carbothermal reduction method

This communication discusses the formation of doped nanobelts produced by a simple route. Tin-doped indium oxide (ITO) nanobelts were obtained by a carbothermal reduction method. The nanostructures were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDX) and wavelength-dispersive X-ray spectroscopy (WDX). The results show that the nanobelts have a cubic structure, are single crystalline and doped with tin and grow in the [400] direction.

Comparative gas sensor response of SnO2, SnO and Sn3O4 nanobelts to NO2 and potential interferents

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermal evaporation furnace with improved configuration for growing nanostructured inorganic materials

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Estudo do crescimento e caracterização de nanofitas do sistema ITO

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo das propriedades elétricas e ópticas de nanocompósitos transparentes e condutores

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural and electrical characterization of semiconducting barium-lead-titanate ceramics

BaTiO3 is usually doped to achieve the temperature stability required by device applications, as well as to obtain a large positive temperature coefficient anomaly of resistivity (PTCR). Uniform distribution of dopants among the submicron dielectric particles is the key for optimal control of grain size and microstructure to maintain a high reliability. The system Ba0.84Pb0.16TiO3 was synthesized from high purity BaCO3, TiO2, PbO oxide powders as raw materials. Sb2O3, MnSO4 and ZnO were used as dopants and Al2O3, TiO2 and SiO2 as grain growth controllers. Phase composition was analyzed by using XRD and the microstructure was investigated by SEM. EDS attached to SEM was used to analyze phase composition specially related to abnormal grain growth. Electrical resistivities were measured as a function of temperature and the PTCR effect characterized by an abrupt increase on resistivity.

Model for zinc oxide varistor

Zinc oxide varistors are very complex systems, and the dominant mechanism of voltage barrier formation in these systems has not been well established. Yet the MNDO quantum mechanical theoretical calculation was used in this work to determine the most probable defect type at the surface of a ZnO cluster. The proposed model represents well the semiconducting nature as well as the defects at the ZnO bulk and surface. The model also shows that the main adsorption species that provide stability at the ZnO surface are O-, O2 -, and O2.

Thermal inkjet printing of copper tetrasulfonated phthalocyanine (CuTsPc) as a semiconducting layer on flexible MIS capacitors

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural study of copper oxide supported on a ceria-modified titania catalyst system

A structural study of CuO supported on a CeO2-TiO2 system was undertaken using X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS) techniques. The results of XRD revealed the presence of only two phases, TiO2 anatase and CeO2 cerianite. A trend towards smaller TiO2 crystallites was observed when cerium content increased. When the amount of cerium increased, Ti K-edge XANES analysis showed an increasing distortion of Ti sites. The results of Ce LIII-edge EXAFS showed that Ce atoms are coordinated by eight oxygen atoms at 2.32 Å. For the sample containing a small amount of cerium, the EXAFS analysis indicated that the local structure around Ce atoms was highly distorted. The catalysts presented quite different Cu K-edge XANES spectra compared to the spectra of the CuO and Cu2O reference compounds. The Cu-O mean bond length was close to that of the CuO and the Cu atoms in the catalysts are surrounded by approximately four oxygen atoms in their first shell. Copper supported on the ceria-modified titania support catalysts displayed a better performance in the methanol dehydrogenation when compared to copper supported only on titania or on ceria. © 2002 Plenum Publishing Corporation.