Properties of hydrogenated amorphous carbon films deposited by PECVD and modified by SF6 plasma

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Planejamento e produção de um criostato de baixo custo para caracterização elétrica de materiais

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Electrical and microstructural properties of microwave sintered SnO2-based varistors

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Construção e Análise do Desempenho de um Porta-amostra para Medidas Elétricas a Altas Temperaturas

A sample holder for electrical measurements with the temperature changing from 50 degrees C up to 560 degrees C is described. The performance of the system for de and ac measurements is analysed.

Effect of the fluorination of DLC film on the corrosion protection of aluminum alloy (AA 5052)

It is presented a study conducted on the physical and electrochemical properties of fluorinated a-C:H films deposited onto a commercial aluminum alloy (AA 5052). The coatings were deposited from mixtures of 91% of acetylene and 9% of argon by plasma immersion ion implantation and deposition technique, PIIID. Total gas pressure was 44 Pa and deposition time (t(dep)) was varied from 300 to 1200 s. The depositing plasmas were generated by the application of radiofrequency power (13.56 MHz, 100W) to the upper electrode and high voltage negative pulses (2400 V. 300 Hz) to the sample holder. Fluorine was incorporated in a post-deposition plasma treatment (13.56 MHz, 70W, 13 Pa) generated from sulfur hexafluoride atmosphere. Chemical structure and composition of the films were investigated using infrared reflectance/absorbance spectroscopy and X-ray photoelectron spectroscopy. The corrosion resistance of the layers was determined by electrochemical impedance spectroscopy (EIS) in a 3.5% NaCl solution, at room temperature. Films presented good adhesion to the substrates and are classified as hydrogenated amorphous carbon (a-C:H) with oxygen traces. Fluorine was detected in all the samples after the post-deposition treatment being its proportion independent on the deposition time. Film thickness presented different tendencies with t(dep), revealing the variation of the deposition rate as a function of the deposition time. Such fluorinated a-C:H films improved the corrosion resistance of the aluminum surface. In a general way the corrosion resistance was higher for films prepared with lower deposition times. The variation of sample temperature with t(dep) was found to be decisive for the concentration of defects in the films and, consequently, for the performance of the samples in electrochemical tests. Results are interpreted in terms of the energy delivered to the growing layer by ionic bombardment. (C) 2010 Elsevier B.V. All rights reserved.

Lubricating coating prepared by PIIID on a forming tool

In this work, the performance of a-C: H films produced by the hybrid Plasma Immersion Ion Implantation and Deposition technique as lubricating layers for a steel forming tool has been investigated. Hardened steel (AISI M2, 64 HRC) plates coated with a commercial TiN layer were used as substrates and the films were deposited in a vacuum chamber fitted with two parallel-plate electrodes. The discharges were generated in atmospheres composed of 91% C2H2 and 9% Ar by the application of radiofrequency power (13.56 MHz, 100 W) to the upper electrode while the lower one, also used as the sample holder, was biased with high voltage negative pulses (3.6 kV, 30 mu s, 300 Hz). A deposition time of 840 s was used. The effects of the gas pressure, p, on thickness, molecular structure, wettability, surface morphology and topography, hardness and friction coefficient of the films lwere investigated. Film thickness increased from 0.3 to 0.5 mu m when p was increased from 2.7 to 16.5 Pa. Generally, the films were slightly hydrophilic, with contact angles of around 84 degrees, and the deposition decreased the roughness of the steel. A polymer-like structure was detected in high pressure depositions and an amorphous carbon structure derived from the low pressure procedures. Hardness decreased from 8.2 to 7.0 GPa with increasing p. Improvement in tribological performance was indicated by the fall in the friction coefficient from 0.5 to 0.2 as the deposition pressure was reduced. Operating at the latter value (of mu) would lead to a significant reduction in wear and hence to significant economy in diverse industrial applications.

Sistema para realização de medidas de luminescência com excitação por raios X

In this work is presented a versatile system for X-ray excited optical luminescence (XEOL) measurements. The apparatus was assembled from a sample holder connected to an optical fiber responsibly for the acquisition of the scintillation signal. The spectrum is registered with a CCD coupled in a spectrograph provided with diffraction gratings. The system performance was analyzed by exciting GdAlO3:Eu3+ 3.0 at.% with X-rays from a diffractometer and measuring the emission spectra. The system can be used to obtain precise and reliable spectroscopic properties of samples with various conformations without the loss of the required safety when dealing with ionizing radiations.

Mechanical and tribological properties of a-C:H:F Thin Films

a-C:H films were grown by plasma-enhanced chemical vapor deposition in atmospheres composed by 30 % of acetylene and 70 % of argon. Radiofrequency signal (RF) was supplied to the sample holder to generate the depositing plasmas. Deposition time and pressure were chosen 300 s and 9.5 Pa, respectively, while the excitation power changed from 5 to 125 W. The films were exposed to a post-deposition treatment during 300 s in RF-plasmas (13.56 MHz, 70 W) excited from 13.33 Pa of SF6. Raman and X-ray photoelectron spectroscopy were used to evaluate the microstructure and chemical composition of the films. The thickness was measured by perfilometry. Hardness and friction coefficient were determined from nanoindentation and risk tests, respectively. With increasing power, the film thickness reduced, but a further shrinkage occurred upon the fluorination process. After that, the molecular structure was observed to vary with deposition power. Fluorine was detected in all samples replacing H atoms. Consistently with the elevation in the proportion of C atoms with sp3 hybridization, hardness increased from 2 to 18 GPa. Friction coefficient also increased with power due to the generation of dangling bonds during the fluorination process. © 2012 Springer Science+Business Media, LLC.

Effect of ion irradiation on the structural properties and hardness of a-C:H:Si:O:F films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Corrosion resistance of 2024 aluminum alloy coated with plasma deposited a-C:H:Si:O films

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Monitoring a CuO gas sensor at work: an advanced in situ X-ray absorption spectroscopy study

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Técnica híbrida de plasma para a deposição de filmes de alumina

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Enhancement of Corrosion Resistance AISI 304 Steel by Plasma Polymerized Thin Films

The purpose of this work is the deposition of films in order to increase the corrosion resistance of AISI 304 steel, which is a material used to construct the reactors for bioethanol production. This deposition inhibits the permeation of corrosive species to the film-metal interface. Thin films were prepared by radio-frequency plasma enhanced chemical vapor deposition (RF-PECVD) method using plasmas of hexamethyldisiloxane/argon/oxygen mixtures excited by signals of different powers. The plasma was generated by the application of RF power of 13.56 MHz to the sample holder while keeping grounded the topmost electrode and the chamber walls. The effect of the RF power on the properties of the samples was investigated by perfilometry, X-ray photoelectron spectroscopy (XPS), contact angle, and electrochemical impedance spectroscopy (EIS). The results of the corrosion resistance tests of the AISI 304 steel were interpreted in terms of the energy delivered to the growing layer by plasma excitation power.

Determination of potassium and sodium in an ash sample by gamma-ray spectroscopy

Neutron activation analysis and gamma-ray spectroscopy were used to determine the quantity of potassium and sodium in an ash sample of Tabebuia sp bombarded with thermal neutrons. These techniques, widely applied in nuclear physics, can be used in the context of wood science as an alternative for the usual physical chemistry methods applied in this area. The quantity of K and Na in an 8.60 +/- 0.10 mg of ash was determined as being 1.3 +/- 0.3 mg and 11.0 +/- 1.8 mu g, respectively. The ratio of Tabebuia sp converted into ash was also determined as 0.758 +/- 0.004%.

Dependence of the electrical conductivity and elastomeric properties on sample preparation of blends of polyaniline and natural rubber

Blend films (free-standing) containing 20% in volume of polyaniline (PANI) in 80% of natural rubber (NR) were fabricated by casting in three different ways: (1) adding PANI-EB (emeraldine base) dissolved in N-methyl-2-pyrrolidone (NMP) to the latex (NRL), (2) adding PANI-EB dissolved in in-cresol to NR dissolved in xylol (NRD), (3) overlaying the surface of a pure NR cast film with a PANI layer grown by in situ polymerization (NRO). All the films were immersed into HCl solution to achieve the primary doping (protonation) of PANI before the characterization. The main goal here was to investigate the elastomeric and electrical conductivity properties for each blend, which may be applied as pressure and deformation sensors in the future. The characterization was carried out by optical microscopy, dc conductivity, vibrational spectroscopy (infrared absorption and Raman scattering), thermogravimetry analysis (TGA), differential scanning calorimetry (DSC), dynamic mechanical thermal analysis (DMTA), and tensile stress-strain curves. The results suggest that the NRL blend is the most suitable in terms of mechanical and electrical properties required for applications in pressure and deformation sensors: a gain of conductivity without losing the elastomeric property of the rubber. (c) 2005 Wiley Periodicals, Inc.